• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.285-291
• /
• 2019

In this study, the corrosion characteristics of T22 and T92 steel were investigated in 6O₂ + 16CO₂ + 2SO₂ gas environment at 650 ℃. Corrosion characteristics were characterized by weight gain, oxide layer thickness, scanning electron microscope, optical microscope, energy dispersive X-ray spectroscopy, and X-ray diffraction. T22 and T92 steel tended to stagnate oxide layer growth over time. Oxidation kinetics were analyzed using the data of oxide layer thickness, and a regression model was presented. The regression model was significantly acceptable. The corrosion rate between the two steels through the regression model showed significant difference. The T92 steel was approximately twice as large as the time exponent and showed very good corrosion resistance compared to the T22 steel. In both steels, the oxide layer mainly formed a Fe-rich oxide layer composed of hematite (Fe₂O₃), magnetite (Fe₃O₄), and spinel (FeCr₂O₄). Sulfide segregation occurred in the oxide layer due to SO₂ gas. However, the locations of segregation for the T22 and T92 steel were different.

• Journal of Mechanical Science and Technology
• /
• v.14 no.2
• /
• pp.152-158
• /
• 2000

The contents of this paper include the evaluation of corrosion characteristics and the behaviour of stress corrosion cracking (SCC) for the weldment and post weld heat treatment (PWHT) specimen and parent of HT -60 steel using a slow strain rate test (SSRT) in synthetic seawater. Corrosion characteristics were obtained from the polarization curves by potentiostat, and SCC phenomena were evaluated through the parameters such as reduction of area and time to failure by comparing the experimental results in corrosive environment with those obtained in air. Corrosion rate of the weldment was the fastest, followed by parent and PWHT specimen. SCC phenomena between the weldment of HT-60 steel and synthetic seawater were shown. Besides, SCC was dependent upon the pulling speed greatly. Maximum severity of SCC was obtained at a speed of $10^{-6}mm/min$, whereas SCC could not be seen almost at $10^{-4}mm/min$. The resistance to SCC for PWHT specimen was improved considerably compared that of the weldment at $10^{-6}mm/min$. In case of SCC failure, it was verified from SEM examination that brittle mode and lots of pits could be seen at the fractured region near the surface of the specimen.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.3
• /
• pp.88-94
• /
• 2006

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, the effect of shot peening in corrosion environment was not known. In this study, investigated is the effect of shot peening on corrosion fatigue crack growth of SAE 5155 steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of SAE 5155 are as follows; the fatigue crack growth rate of the shot peening material was lower than that of the non-peening material. And fatigue life shows more improvement in the shot peening material than in non-peening material. This is due to the compressive residual stress of surface increases resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.6
• /
• pp.965-971
• /
• 2001

To estimate the reliability of 12Cr alloy steel, the material of turbine blade in the steam power plant, Its corrosion susceptibility and fatigue characteristics in NaCl and Na$_2$SO$_4$solution with the difference of concentration and temperature was investigated. The polarization tests recommended in ASTM G5 standard for corrosion susceptibility in the various corrosive solutions was estimated. It showed that the higher temperature, the faster corrosion rates and corrosion rates were the fastest in 3.5 wt.% NaCl and 1M Na$_2$SO$_4$solution. From these results, the degradation conditions were determined in distilled water, 3.5 wt.% NaCl and 1M Na$_2$SO$_4$solution at room temperature, 60$\^{C}$ and 90$\^{C}$ during 3, 6 and 9 months. Its surface had a few pits for long duration. But, it was not susceptible in sulfide and chloride condition of several temperatures. If the degraded 12Cr alloy steel and non-degraded one were compared with fatigue characteristics, Any differences were not found regardless of temperature and degradation period.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.1
• /
• pp.23-29
• /
• 2019

Electrolytic corrosion of the ship's hull can be occurred due to stray current during welding work using shore power and electrical leakage using shore power supply. The electrolytic corrosion characteristics were investigated for Al5083-H321 through potentiodynamic polarization and galvanostatic corrosion test in natural seawater. Experiments of electrolytic corrosion were tested at various current densities ranging from $0.01mA/cm^2$ to $10mA/cm^2$ for 30 minutes, and at various applied time ranging from 60 to 240 minutes. Evaluation of electrolytic corrosion was carried out by Tafel extrapolation, weight loss, surface analysis after the experiment. In the electrolytic corrosion characteristics of Al5083-H321 as the current density increased, the surface damage tended to proportionally increase. In the current density of $0.01mA/cm^2$ for a applied long time, the damage tended to grow on the surface. In the case of $10mA/cm^2$ current density for a applied long time, the damage progressed to the depth direction of the surface, and the amount of weight loss per hour increased to 4 mg/hr.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.347-360
• /
• 2021

Currently, the demand for eco-friendly energy sources is high, which has prompted research on polymer electrolyte membrane fuel cells. Both aluminum alloys and nickel alloys, which are commonly considered as materials of bipolar plates in fuel cells, oxide layers formed on the metal surface have excellent corrosion resistance. In this research, the electrochemical characteristics of 6061-T6 aluminum alloy and Inconel 600 were investigated with chloride concentrations in an acid environment that simulated the cathode condition of the PEMFC. After potentiodynamic polarization experiments, Tafel analysis and surface analysis were performed. Inconel 600 presented remarkably good corrosion resistance under all test conditions. The corrosion current density of 6061-T6 aluminum alloy was significantly higher than that of Inconel 600 under all test conditions. Also, 6061-T6 aluminum alloy and Inconel 600 presented uniform corrosion and intergranular corrosion, respectively. The Ni, Cr, and Fe, which are the main chemical compositions of Inconel 600, are higher than Al in the electromotive force series. And a double oxide film of NiO-Cr₂O₃, which is more stable than Al₂O₃, is formed. Thus, the corrosion resistance of Inconel 600 is better.

• Journal of Fisheries and Marine Sciences Education
• /
• v.10 no.1
• /
• pp.69-78
• /
• 1998

Thermal sprayed Cu-Ni alloy coating on the carbon steel was carried out impingement erosion-corrosion test and electrochemical corrosion test in the marine environment. The impingement erosion-corrosion behavior and electrochemical corrosion characteristics of substrate(SS400) and thermal sprayed Cu-Ni coating was investigated, and the corrosion control efficiency of Cu-Ni coating to substrate was estimated quantitatively. Main results obtained are as follows : 1) The weight loss rate of Cu-Ni coating layer by the impingement erosion-corrosion compared with substrate was smaller in high specific resistance solution than in low specific resistance solution. 2) The corrosion potential of Cu-Ni coating layer spray coating in the marine environment became more noble than that of substrate. 3) With the lapse of time, corrosion current density of Cu-Ni coating layer became stable, but that of substrate was increased. 4) As the corrosion control efficiency of Cu-Ni coating layer in the marine environment was over 90%, its anti-corrosion characteristics was excellent.

• Journal of Korean Society of Water and Wastewater
• /
• v.22 no.3
• /
• pp.379-387
• /
• 2008

The pH & alkalinity adjustment method by lime and carbon dioxide($CO_2$) for corrosion control in water distribution system was investigated to evaluate the corrosion characteristics of metal pipes, such as galvanized iron, copper, stainless steel, and carbon steel. When the pH in sand filtered and ozone+GAC treated water was increased with lime and $CO_2$ from 7.5 to 8.0, the concentration of residual chlorine decreased at higher pH and longer reaction time; the concentration of trihalomethane increased. The corrosion rate of coupons with corrosion control using lime and carbon dioxide was showed much smaller than those without corrosion control using pilot-scale simulated distribution system. The galvanized iron was corroded much faster than carbon steel, copper, and stainless steel. Especially, copper and stainless steel coupons were hardly corroded. The galvanized iron and carbon steel coupons with corrosion control were produced the corrosion products less than those without corrosion control by the results of environmental scanning electron microscope(ESEM) and energy dispersive x-ray spectroscopy(EDS) analyses. The galvanized iron coupon with pH and alkalinity adjustment by lime and carbon dioxide was detected about 30 percent of zinc, when the carbon steel was detected about 30 percent of calcium by calcium carbonate products formation. For the results of X-ray diffraction(XRD) analyses, the goethite(${\alpha}$-FeOOH) was identified as primary corrosion product of galvanized iron without corrosion control, while the Zinc oxide(ZnO) was found on corrosion products of galvanized iron coupon with corrosion control as the results of EDS analyses. However, the carbon steel corrosion products regardless of corrosion control were composed predominantly of maghemite(${\gamma}-Fe_2O_3$) and hematite(${\alpha}-Fe_2O_3$).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.6
• /
• pp.996-1003
• /
• 2001

In order to investigate the fatigue fracture characteristics by corrosion degradation of 12Cr alloy steel, both the fatigue characteristics in air of them artificially degraded during long period and the corrosion fatigue characteristics were experimentally evaluated in various environments which were determined from electro-chemical polarization tests. And also, their fracture mechanisms were analyzed and compared, fractographyically. From their results, the fracture mechanical characteristics of it artificially degraded during long period in the distilled water, 3.5 wt.% NaCl solution and 12.7wt.%(1M) Na$_2$SO$_4$solution of 25, 60 and 90$\^{C}$ did not show distinguishable difference comparing with non-corroded one in regardless of temperature and degradation period. It means that degradation of the material by just surface corrosion does not remarkably affect to fatigue crack growth. On the other hand, the crack growth rates by corrosion fatigue increased due to activity increase of corrosive factors such as OH(sub)-,Cl(sup)- and SO$_4$(sup)- at the crack tip with temperature increase. Therefore, the crack growth rates by corrosion fatigue were more faster than that in air of the artificially degraded specimen due to the such difference of crack growth mechanism.

• Journal of Advanced Marine Engineering and Technology
• /
• v.25 no.2
• /
• pp.344-350
• /
• 2001

This paper was studied on the characteristics of galvanic corrosion and its protection on heat exchanger tube plate in the sea water. In this paper, behavior of pitting corrosion of Ni-al bronze connected with Ti tube was measured af flow velocity of 0 m/s and 2.4 m/s. To protect galvanic corrosion, the protection characteristics of Ni-Al bronze connected with Ti tube by Zn-base alloys galvanic anode and hexagonal nylon insert was investigated. Main results obtained asre al follows: 1) The galvanic corrosion of Ni-Al bronze connected with Ti-tube is more active than single Ni-al bronze. 2) As the circuit resistance increase under the cathodic protection employing Zn-base alloys galvanic anode, Ni-al bronze connected with Ti tube is cathodically unpolarized. 3) The corrosion of Ni-Al bronze connected with Ti tube by nylon insert controls approximately 73% than not nylon insert.