• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 추계학술발표대회 개요집
• /
• pp.165-167
• /
• 2004

The failure pressure for corroded pipeline was measured by burst testing and classified with respect to corrosion sizes and corroded regions - the body, the girth weld and the seam weld of pipe. A series of finite element analyses were performed to obtain a limit load solution for corrosion defects on the basis of burst test. As a result, the criteria for failure assessment of corrosion defect within the body, the girth weld and the seam weld of API 5L X65 gas pipeline were proposed.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.137-138
• /
• 2017

The Waterproofing and Anti corrosion materials applied to the water supply facility did not consider environment of water supply facility, thus defects occurred consistently on the site. In this study, it suggests safety adhesion test of wet surface and have a test for safety adhesion performance.

• Corrosion Science and Technology
• /
• 제8권4호
• /
• pp.133-138
• /
• 2009

For the corrosion protection of the natural gas transmission pipelines, two methods are used, cathodic protection and coating technique. In the case of cathodic protection, defects are embrittled by occurring hydrogen at the crack tip or material surface. It is however very important to evaluate whether cracks in the embrittled area can grow or not, especially in weld metal. In this work, on the basis of elastic plastic fracture mechanics, we performed the CTOD testing with various test conditions, such as testing rate and potential. The CTOD of the base metal and the weld metal showed a strong dependence of the test conditions. The CTOD decreased with decreasing testing rate and with increasing cathodic potential. The morphology of the fracture surface showed the quasi-cleavage at low testing rate and cathodic overprotection. The low CTOD was caused by hydrogen embrittlement at crack tip.

• 한국표면공학회지
• /
• 제50권6호
• /
• pp.432-438
• /
• 2017

AZ91D casting alloy requires an advanced plasma anodizing processing because large amount of defects are liable to generate during anodization. In this study, plasma electrolytic oxidation (PEO) of AZ91D Mg alloy was conducted by the application of either constant voltage or current using a pulse mode and its effects on pore formation, surface roughness and corrosion resistance were investigated. The PEO films showed a three-layer structure. The PEO film thickness was found to increase linearly with voltage. The surface roughness, Ra, ranged between $0.2{\mu}m$ and $0.3{\mu}m$. The corrosion resistance increased from RN 3.5 to 9.5 by the PEO treatment when evaluated according to the 72 hour salt spray test. The PEO-treated surface exhibited higher pitting potential than the raw material.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.128-129
• /
• 2015

Al-rich coatings were prepared on hot rolled low carbon steel by hot dipping method in molten Al-bath to investigate the corrosion resistance with the possible outcomes and defects of aluminized coatings in air and $Ar-0.2%SO_2$ mixed gases. Coating microstructure was composed of an inner Al-Fe intermetallic layer and outer Al-rich layer. Aluminum oxidized preferentially to the thin, outer, protective ${\alpha}-Al_2O_3$ layer, without forming the nonprotective iron/sulfur-oxide layer after heating at $800^{\circ}C$ for 20 h, in both the gases and provided the resistance against corrosion.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.122-122
• /
• 2015

Al-rich coatings were prepared on hot rolled low carbon steel by hot dipping method in molten Al-bath to investigate the corrosion resistance with the possible outcomes and defects of aluminized coatings in air and $Ar-0.2%SO_2$ mixed gases. Coating microstructure was composed of an inner Al-Fe intermetallic layer and outer Al-rich layer. Aluminum oxidized preferentially to the thin, outer, protective ${\alpha}-Al_2O_3$ layer, without forming the nonprotective iron/sulfur-oxide layer after heating at $800^{\circ}C$ for 20h, in both the gases and provided the resistance against corrosion.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.52-53
• /
• 2020

The thermal spray coating process is being used to protect the metals and alloys from wear, abrasion, fatigue, tribology, and corrosion failure. Therefore, in the present study, Al and Zn was deposited by plasma arc thermal spray process onto the steel substrate and their performance was assessed. The bond adhesion result shows that Al coating has higher value attributed to compact, dense, and less porous compared to Zn coating which contain defects/pores and uneven morphology assessed by scanning electron microscopy (SEM). Electrochemical results show that the Al coating exhibited higher impedance value compared to Zn in artificial ocean water solution at prolonged exposure periods. However, both coatings show the increment in polarization resistance with exposure periods which reveal that porosity of coatings is filled by the corrosion products.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.17-18
• /
• 2021

In the present study, Al-Zn coating was deposited by Arc thermal (AT) and plasma arc thermal (PAT) spray processes, and their corrosion characteristics were studied in 3.5% NaCl through electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) and mechanical tests. The bond adhesion result showed that plasma arc sprayed coating had a higher value attributed to compact, dense, and less porous coating compared to arc thermal spray coating which contains defects/pores and uneven morphology as revealed by scanning electron microscope analysis. Electrochemical results revealed that the plasma arc sprayed coating had a high polarization resistance at early stage of immersion, suggesting its excellent corrosion protection performance.

• 비파괴검사학회지
• /
• 제30권4호
• /
• pp.311-316
• /
• 2010

본 논문에서는 비파괴검사법 중 하나인 자기누설탐상검사법을 이용하여 지하에 매설된 가스 배관의 결함 위치를 검출하는 방법을 제안한다. 자기 누설 탐상 시스템을 통해 얻은 자기 누설 신호는 일반적으로 비선형성을 띄며 다양한 외부 요인으로 인한 신호의 왜곡이 심하다. 본 논문에서는 신호의 비선형성과 신호의 왜곡을 보정하는 신호 처리 기법 중 SQI(self quotient image)를 이용하여 배관 결함의 위치를 검출하였다. 실제로 제작된 모의시험 배관에 제작된 다양한 인공 결함에 대해 알고리즘을 적용한 결과 기존 DCT(discrete cosine transform) 계수 기반 방법에 비해 결함 검출 성능이 크게 향상됨을 확인하였다.

• Nuclear Engineering and Technology
• /
• 제40권7호
• /
• pp.607-614
• /
• 2008

Since pipes with wall-thinning defects can collapse at fluid pressure that are lower than expected, the collapse moment of wall-thinned pipes should be determined accurately for the safety of nuclear power plants. Wall-thinning defects, which are mostly found in pipe bends and elbows, are mainly caused by flow-accelerated corrosion. This lowers the failure pressure, load-carrying capacity, deformation ability, and fatigue resistance of pipe bends and elbows. This paper offers a support vector regression (SVR) model further enhanced with a fuzzy algorithm for calculation of the collapse moment and for evaluating the integrity of wall-thinned piping systems. The fuzzy support vector regression (FSVR) model is applied to numerical data obtained from finite element analyses of piping systems with wall-thinning defects. In this paper, three FSVR models are developed, respectively, for three data sets divided into extrados, intrados, and crown defects corresponding to three different defect locations. It is known that FSVR models are sufficiently accurate for an integrity evaluation of piping systems from laser or ultrasonic measurements of wall-thinning defects.