• Textile Coloration and Finishing
• /
• v.29 no.2
• /
• pp.55-61
• /
• 2017

A non-fluorinated polystearyl methacrylate water repellent was synthesized by emulsion polymerization. The number and weight averaged molecular weights were obtained at around 137,277 and 237,754g/mole. The melting point was observed at $32^{\circ}C$. The contact angle of water droplet on fabrics treated with the water repellent was $140{\sim}145^{\circ}$ for cotton and polyester, and $125{\sim}130^{\circ}$ for wool and nylon. Since the critical surface tension was estimated at 20.7mN/m, even though relatively not so strong as fluorinated water repellent, it is considered to be used as a good water repellent practically.

• Journal of the Korean Ceramic Society
• /
• v.20 no.4
• /
• pp.289-296
• /
• 1983

The Wetting of fusion cast $Al_2O_3$ brick and $Al_2O_3 -ZrO_2$ brick by liquid Ag was studied by the sessile drop technique in Ar atmosphere. In this experiment the specimens were photographed per 2$0^{\circ}C$with increasing temperature from 96$0^{\circ}C$ melting point of Ag. And the method of photographing was carried out by shadow technique. The cosine of the contact angle increased linearly with increasing temperature in both systems. And the relation between the cosine of the contact angle and the temperature was Cos$\theta$=1.132+$0.75{\times}10^{-3}T$ for $Al_2O_3$ brick and Cos$\theta$=-1.706+$1.125{\times}10^{-3}T$ for $Al_2O_3 -ZrO_2$ brick In both systems the contact angle decreased as the surface of substrate became smoother. The work of adhesion which was 503.5ergs/$cm^2$ for $Al_2O_3$brick and 393.6 ergs/cm2 for $Al_2O_3 -ZrO_2$ brick at 96$0^{\circ}C$ increased parabolically with increasing temperature in both system.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.6
• /
• pp.561-565
• /
• 2007

Because of a good wear resistance and a stable contact resistance, Ag-CdO is widely used as electrical contact material. But, the Cd-oxide mainly exists as a coarse particle and adversely affected to environment. As a reason, $Ag-SnO_2$ alloy has been developed. The Sn-oxide maintains stable and fine particle even at high temperature. In order to investigate the effect of Misch metal (Mm) additional that affects the formation of the oxide and the formation of fine matrix Ag, we studied the microstructures and properties of Ag-Sn-In(-Mm) material fabricated by rapid solidification process. The experimental procedure were melting using high frequency induction, melt spinning, and internal oxidation. The Mm addition makes Ag matrix more fine than no Mm addition. The reason is that the addition of Misch metal decreased a latent heat of fusion of alloy, as a result the rapid solidification effect of alloy is increased. The maximum hardness shows at 0.3 wt%Mm. after that the hardness is decreased until 0.4 wt% Mm, but still larger than no Mm addition alloy. At 0.5 wt% Mm alloy, the precipitation of Misch metal causes a decrease of hardness than no Mm addition alloy.

• Journal of Korea Foundry Society
• /
• v.31 no.2
• /
• pp.66-70
• /
• 2011

Hot dip aluminizing (HDA) is widely used in industry for improving corrosion resistance of material. The formation of intermetallic compound layers during the contact between dissimilar materials at high temperature is common phenomenon. Generally, intermetallic compound layers of $Fe_2Al_5$ and $FeAl_3$ are formed at the Al alloy and Fe substrate interface. In case of cast iron, high contact angle of graphite existed in the matrix inhibits the formation of intermetallic compound layer, which carry with it the disadvantage of a reduced reaction area and mechanical properties. In present work, the process for the removal of graphite existed on the surface of specimen has been investigated. And also HDA was proceeded at $800^{\circ}C$ for 3 minutes in aluminum alloy melt. The efficiency of graphite removal was increased with the reduction of particle size in sanding process. Graphite appears to be present both in the region of melting followed by re-solidification and in the intermetallic compound layer, which could be attributed to the fact that the surface of cast iron is melted down by the formation of low melting point phase with the diffusion of Al and Si to the cast iron. Intermetallic compound layer consisted of $Fe(Al,Si)_3$ and $Fe_2Al_5Si$, the layer formed at cast iron side contained lower amount of Si.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.20 no.8
• /
• pp.1546-1552
• /
• 2016

In addition, because it uses preheating to dissolve an alloy in general, it is hard to regulate the appropriate melting temperature of the alloy and brewing time and shows the defect of the supplementation thing due to the super-heating. Once the alloy is molten and then most of the casting by attaching a sight glass or non-contact temperature sensor is suitable casting temperature the operator pressing a button to generate a centrifugal force to inject the molten alloy into a crucible in the casting ring. These results, and most of the cast temperature is too high or too low to generate a lot of casting defects do not get into a uniform cast body. In this paper, we developed a dental casting machine for high frequency using a single temperature sensor which can measure the actual temperature of the alloy than the temperature of the external non-contact measurement using a temperature sensor.

• Resources Recycling
• /
• v.24 no.1
• /
• pp.21-27
• /
• 2015

The present study describes the process of producing low oxygen content alloy powder from Ti-6Al-4V and Ti-8Al-1Mo-1V (AMS 4972) alloy scraps using hydrogenation-dehydrogenation (HDH) and deoxidation in solid state (DOSS) processes. Each prepared powder was deoxidized with Ca contact and non-contact method to compare the deoxidation capability. It is known that the non-contact deoxidation method, using Ca vapor above the melting temperature $T_m$ of Ca, has greater deoxidation capability. However, Oxygen contents in Ti-6Al-4V and Ti-8Al-1Mo-1V powder after non-contact deoxidation method were higher than those after contact deoxidation method. Therefore, we investigate the effect of Al - the richest alloy element in theses Ti based metals - on the deoxidation processes.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.74-79
• /
• 2000

In an attempt to estimate the wetting properties of wettable metal layers by wetting balance method, an analysis of wetting curves of the coating layer was performed. Based on the analysis, wetting properties of UBM-coated Si-plate were estimated by the new wettability indices. The wetting curves of the one and both sides-coated UBM layers have the similar shape and show the similar tendency to the temperature. So the wetting property estimation of one side coating is possible with wetting balance method. For UBM of Si-chip, Cr/Cu/Au UBM is better than Ti/Ni/Au in the point of wetting time. At general reflow temperature, the wettability of high melting point solders(Sn-Sb, Sn-Ag) is better than that of few melting point ones(Sn-Bi, Sn-In).The contact angle of the one side coated plate to the solder can be calculated from the farce balance equation by measuring the static state force and the tilt angle.

• Resources Recycling
• /
• v.12 no.4
• /
• pp.44-50
• /
• 2003

Separation of mixed plastics is not a simple task due to similarities of specific gravity and limitations of sizes, etc. In this study, a new technique was developed to separate plastics selectively by a thermal adhesion method using the different softening or melting temperatures of various types of plastics. Tests were conducted to investigate softening or melting temperatures and adhesion probabilities of plastics with change in temperature. Tests also were conducted to analyze the operating variables, including contact times, size and color pigment. It was founded that LDPE, HDPE and PVC, PET, etc among mixed plastics could be separated selectively according to the change of temperature.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2010.03a
• /
• pp.167-168
• /
• 2010

Non coating type Low melting yarn(L/M PET) not to use the polyurethane resin causing some problems was knitting and evaluated its dyeing characteristics, heat setting properties and flame-retardant properties without flame retardant agent or flame retardant fabric. In order to investigate the dyeing property of fabric of L/M PET, the dyeing of L/M PET was experimented at each different dyeing temperature. Higher exhaustion yield was achieved at lower temperature of L/M PET compared to regular PET. According to result of the study for the heat setting properties of L/M fiber, the K/S value of dyed L/M fiber increased as much as the heat setting temperature did. The experiment for the light fastness reached similar result to dyed PET. However washing fastness in L/M fiber showed lower grade compared with regular PET. flame-retardant efficiency of L/M PET without flame retardant agent or flame retardant fabric measured by $45^{\circ}$ burn test and Contact burn test. The flame?retardant performance of the sample was carried out according to the Korea Fire-fighting Standard.[KOFEIS 1001].

• Journal of Pharmaceutical Investigation
• /
• v.32 no.2
• /
• pp.73-80
• /
• 2002

Cefuroxime axetil is a cephalosporin antibiotic having a high activity against a wide spectrum of Grampositive and Gram-negative microorganisms. It is a cephalosporin antibiotic which exist as 2 diastereoisomers: diastereoisomer A and B. It shows polymorphism of three forms: a crystalline form having a melting point of about $180^{\circ}C$, a substantially amorphous form having a high melting point of about $135^{\circ}C$ and a substantially amorphous form having a low melting point of about 70^{\circ}C$. The crystalline form of cefuroxime axetil is slightly soluble in water because diastereoisomer A has lower solubility than B in water. Substantially amorphous form of which there are no difference in solubility between diastereoisomer A and B has better solubility than crystalline form, but it forms a thicker gel than crystalline form upon contact with an aqueous medium. Based on this reason, cefuroxime axetil is not readily absorbable in the gastrointestinal tract, rendering its bioavailability on oral administration very low. The object of this study was to develop an improved non-crystalline cefuroxime axetil composition having a high physicochemical stability and bioavailability. A non-crystalline cefuroxime axetil solid dispersant showing no peak on a Differential Scanning Calorimetry (DSC) scan is prepared by dissolving cefuroxime axetil and a surfactant in an organic solvent; suspending a water-insoluble inorganic carrier in the resulting solution; and spray drying the resulting suspension to remove the organic solvent, said solid dispersant having an enhanced dissolution and stability of cefuroxime axetil and being useful for the preparation of a pharmaceutical composition for oral administration. Tablet was formulated with this cefuroxime axetil solid dispersant, disintegrants and other ingredients. It disintegrated and dissolved easily and dynamically in dissolution medium, so showed a good dissolution profile.