• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.197-208
• /
• 2003

This paper is to determine the possibility of re-using waste concrete from Incheon city area. The strength test was conducted with five aggregate compounds which was replaced a natural aggregate with recycled aggregate. After checking the physical characteristics of recycled aggregate compounds, the mix design of recycled concrete was conducted. For the relatively comparison between natural and recycled compounds, while the unit aggregate weight was changed, other conditions were fixed. The freezing and thawing test which included fly-ash and super-plastezer were performed to check the durability and workability when recycling waste concrete. In the physical characteristics of recycled aggregate, it was found that the specific gravity of recycled coarse aggregate and recycled fine aggregate satisfied the first grade of recycle specification(KS), and all compounds of recycled aggregate also satisfied the second grade of absorption specification, Especially up to the 50% substitution of recycled aggregate is equal to or a bit lower than that of convention aggregate. In comparison with conventional concrete, the recycled concrete is lower than maximum by 7% in compressive strength decreasing rate after freezing-thawing test. From now, although most of recycled concrete was used to the building lot, subgrade, asphalt admixture, through the result. It was proved that possibility of re-using recycled aggregate as the substructure of bridge, retaining wall, tunnel lining and concrete structure which is not attacked the drying shrinkage severely.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.777-783
• /
• 2004

In this study, for improving of concrete properties, those are used ground granulated blast slag(GGBS) and fly ash(FA). There are some advantage to add the GGBS and FA in plain concrete. The objective of this study is to find the characteristics of fresh and hardened antiwashout underwater concrete which is followed by blended ratio of GGBS and FA. Experimental parameters were chosen that W/C was 50%, S/a was 40% and as the blended ratio of GGBS was set at 0, 10, 20, 30, 40, 50, 60% and FA was set at 0, 10, 15, 20, 25, 30, 35% in order to prove the properties of antiwashout underwater concrete can be changed by blended ratio of GGBS md FA. It was measured pH, suspension and slump flow of fresh antiwashout underwater concrete and compressive strength of hardened antiwashout underwater concrete in age of 7 days, 28 days and 56 days. The experimental results of fresh concrete show that pH, suspension and slump flow were all satisfied with KSCE (Korea Society of Civil Engineering) standard value and mix design standard value. To synthetically consider, the optimum blended ratio is about 30% of GGBS and FA.

• Korean Journal of Agricultural Science
• /
• v.25 no.1
• /
• pp.89-96
• /
• 1998

This study was performed to evaluate the engineering properties of permeable polymer concrete with rice-husk ash. The following conclusions were drawn; 1. The highest sterngth was achieved by 50% filled rice husk-ash permeable polymer concrete, it was increased 24% by compresseve, 123% by tensile and 90% by bending strength than that of the normal cement concrete, respectively. 2. The static modulus of elasticity was in the range of $1.27{\times}10^5{\sim}1.75{\times}10^5kgf/cm^2$, which was approximately 58~70% of the normal cement concrete. The higher elastic modulus was showed by 50% filled rice-husk ash permeable polymer concrete, relatively. The poisson's number of permeable polymer concrete was less than that of the normal cement concrete. 3. The ultrasonic pulse velocity was in the range of 2,503~3,083m/sec, which was showed about the same compared to that of the normal cement concrete. The higher pulse velocity was showed by 50% filled rice-husk ash permeable polymer concrete. 4. The water permeability was in the range of $4.612{\sim}5.913{\ell}/cm^2/hr$, and it was largely dependent upon the mix design. These concrete can be used to the structures which need water permeability.

• Korean Journal of Agricultural Science
• /
• v.23 no.1
• /
• pp.61-69
• /
• 1996

This study was performed to evaluate the engineering properties of permeable polymer concrete with fillers and unsaturated polyester resin. The following conclusions were drawn. 1. The highest strength was achieved by stone dust filled permeable polymer concrete, it was increased 17% by compressive, 148% by tensile and 188% by bending strength than that of the normal cement concrete, respectively. 2. The static modulus of elasticity was in the range of $1.17{\times}10^5{\sim}1.32{\times}10^5kg/cm^2$, which was approximately 53~56% of that of the normal cement concrete. Stone dust filled permeable polymer concrete was showed relatively higher elastic modulus. The poisson's number of permeable polymer concrete was less than that of the normal cement concrete. 3. The dynamic modulus of elasticity was in the range of $1.3{\times}10^5{\sim}1.5{\times}10^5kg/cm^2$, which was approximately less compared to that of the normal cement concrete. Stone dust filled permeable polymer concrete was showed higher dynamic modulus. The dynamic modulus of elasticity were increased approximately 10~13% than that of the static modulus. 4. The water permeability was in the range of $3.076{\sim}4.390{\ell}/cm^2/h$, and it was largely dependent upon the mix design. These concrete can be used to the structures which need water permeability. 5. The compressive strength, tensile strength, bending strength and elastic modulus were largely showed with the decrease of water permeability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.581-584
• /
• 2008

Generally, durability of concrete structures under marine environment is grossly declined by detrimental ions such as chlorides, which penetrate concrete and was diffused to corrode reinforcing rod. Therefore, chloride diffusion properties in concrete are important for durability evaluation and design of concrete structure. For estimation of chloride diffusion coefficient in concrete, both evaluation methods are used for steady state and non-steady state derived from Fick's 1st and 2nd law, respectively. However, as it is very difficult to evaluate diffusion coefficient for non-steady state like service environment where concrete is actually exposed, indirect evaluation method by laboratory accelerated test is generally used. In this study, comparison of chloride diffusion behavior was investigated for fixed mix proportion and age of concrete using four accelerated test methods based on domestic and foreign standards. From test results, only relative comparison between concrete mixtures was possible using ASTM C 1202 test, and diffusion coefficient for steady state was estimated as low as 1/10 of that for non-steady state. In addition, diffusion coefficient estimated by immersion test was similar to result by NT build 492 test.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.112-118
• /
• 2011

The recycled asphalt concrete has gotten increasing attention due to the environmental issues. The volume of reclaimed asphalt has increased significantly for last few years because of city remodeling, pavement maintenance, utility excavation, and road widening. Considering the value of reclaimed asphalt, it is rather used for the recycled asphalt concrete than it is used for fill and cover up material instead of soil. This research will be a supplements incomplete issues from existing research results and suggests the quality control guideline for recycled asphalt concrete and upcoming laws. As the first step of research, the trial construction of RAP(Recycled Asphalt Pavement) performed in expressway construction sites. These trial construction sites have been checked every years. And another construction sites studied and selected for more deeper performance check of RAP. For this checks, we used automatic pavement survey equipment and computerized analysis tools. Also, DSR(Dynamic Shear Rheometer) was used for the fatigue life calculation of binder blends(RAP and virgin binder). As a consequence of this research, the application of recycled asphalt provides good enough quality for highway construction. The preceeding literatures reviewed shows that the asphalt rejuvenator are used in many countries but that type of chemical agent are not used in Korea. By using the data of trial construction and mix design in Chongwon-Sangju construction lane, the surface and base courses consisted with the 10% and 30% rap mix asphalt section maintains good performance for up to 7 years. Through the performance check and laboratory tests(DSR), the quality control and mixture's low temperature prevention are the important factor and chemical agent necessary for increasing the fatigue life of RAP binder.

• Journal of the Korea Concrete Institute
• /
• v.20 no.5
• /
• pp.653-660
• /
• 2008

The purpose of this study is to analyze the optimal mix design of the sound absorption material that is made from perlite and various binder systems for noise barrier wall. The polymer cement slurry which is made from two types of polymer dispersions, and silicone type inorganic material are used as binder. The test specimens are prepared with various polymer cement ratios, binder ratios, and tested for strengths, freezing and thawing and sound absorption performance by the tube and the reverberation room methods. From the test results, the difference of sound absorption coefficient by the tube method is a little recognized, however, noise reduction coefficient (NRC) of test specimens bound by the polymer cement slurry is in the ranges of 0.48 to 0.51. They are a little higher than those bound by cement only, and are lower values than recommended value of 0.7 by the Ministry of Environment. However, the sound absorption coefficient of test specimens at low frequency range of 250 to 500 Hz by reverberation room method shows very high values as 0.84 to 1.00, and 0.57 to 0.77 at the high frequency. The test specimens with polymer cement slurry binder have a good balance between performance and cost, and have proper properties in strengths, freezing and thawing resistance as sound absorption material for noise barrier wall. It is apparent that the good sound absorption material can be produced according to the optimum mix design that is recommended from this study.

• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.57-64
• /
• 2006

The crack presented in concrete structures causes a structural defect, the durability decrease, and external damages etc. Therefore, it is necessary to improve durability through the effort to control the crack. Fluosilicic acid($H_2SiF_6$) is recovered as aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded $H_3PO_4$ or HF. Generally, fluosilicates prepared by the reaction between $H_2SiF_6$ and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.0{\sim}2.0%$ of adding ratio of fluosilicate salt based inorganic compound. To evaluate correlation of concrete strength and adding ratio of fluosilicate salt based inorganic compound, the tests were performed about design strength(21, 24, 27 MPa) with 0.5% of adding ratio of fluosilicate salt based inorganic compound. Applications of fluosilicate salt based inorganic compound to reduce cracks resulted from plastic and drying shrinkage, to improve durability are presented in this paper. Durability was evaluated as neutralization, chloride ion penetration depth, freezing thawing resistant tests and weight loss according reinforcement corrosion. It is ascertained that the concrete added fluosilicate salt based inorganic compound showed m ability to reduce the total area and maximum crack width significantly as compared non-added concrete. In addition, the durability of concrete improved because of resistance to crack and watertightness by packing role of fluosilicate salt based inorganic compound obtained and pozzolanic reaction of soluble $SiO_2$ than non-added concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.585-593
• /
• 2021

This study investigates the compressive strength of high-strength cement composites with 64 mixture designs and 2 curing conditions. The cement composites were designed with varying water-to-binder ratios, silica fume content to cement, and binder content per unit volume of cement composite to explore compressive strength development depending on its mix design. An increase in the water-to-binder ratio decreased the compressive strength of the composites, having consistency with the trend in normal concrete. The compressive strength increased with ages at an ambient curing temperature, but it was not identified at high-temperature curing. The compressive strength development was negligible in case that silica fume content to OPC is 15%~25%, but a decrease in the con ten t below 15% reduced compressive stren gth. It was more obvious in the specimen of low water-to-binder ratio. The specimen with 840kg/m³ of binder content per unit volume had the highest compressive strength in this study, and the decrease in binder content reduced the compressive strength of high strength cement composites in low silica fume content.

• Journal of the Society of Disaster Information
• /
• v.11 no.4
• /
• pp.589-596
• /
• 2015

As urbanization progressed along with quantitative expansion of the construction industry, concrete has developed diversely as a material that is the most extensively used in the construction industry. However, aggregate resources that are an essential element of concrete production are gradually being depleted and the phenomenon of aggregate shortage has been intensifying due to the reinforcement of regulations on environmental issues. Therefore, in the present study, environment friendly mortar was made by replacing aggregate with mud that is dumped when dredging sand is dumped. To identify the dynamic characteristics of the mortar and to identify its fire resistance efficiency, the mortar was heated and its residual compressive strength was measured. In the results, the residual compressive strength values of MM1, MM2, and MM3 were 45%, 95%, and 57.7% respectively and the mix MM2 showed the highest fire resistance efficiency.