• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.3 no.3
• /
• pp.79-85
• /
• 2004

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular, fatigue failure phenomena, which happen in metal, bring on danger in human life and property. Therefore, antifatigue failure technology takes an important part of current industries. Currently, the shot peening is used for removing the defects from the surface of steel and improving the fatigue strength on surface. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9)by shot peening on fatigue crack growth characteristics in stress ratio(R=0 1, R=0 3, R=0 6)was investigated considering fracture mechanics. By using the methods mentioned above, I arrived at the following conclusions: (1) The fatigue crack growth rate(da/dN) of the shot peening material was lower than the unpeening material And in stage I, ${\Delta}K_{th}$, the threshold stress intensity factor, of the shot peening material is high in critical parts unlike the unpeening material. (2) Fatigue life shows more Improvement in the shot peening material than in the unpeening material. And compressive residual stress of surface on the shot peening processed operate the resistance of fatigue crack propagation.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.4
• /
• pp.426-435
• /
• 2005

The lightness of components required in automobile and machinery industries is requiring high strength of components. Therefore this requirement is accomplished as the process of shot-peening method that the compressive residual stress is made on the metal surface as one of various improvement methods. Special research is, therefore, needed about compressive residual stress on the metal surface in the process of shot-peening method. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in environmental condition(temperature) and mechanical condition(shot velocity, stress ratio) was investigated with considering fracture mechanics. By using the methods mentioned above, the following conclusions have been drawn. (1) The fatigue crack growth rate(da/dN) of the shot-peened material was lower than that of the un-peened one. In high temperature range. fatigue crack growth rate decreased with increasing temperature range, while fatigue crack growth rate increased by decreasing temperature in low temperature. (2) Fatigue life shows more improvement in the shot-peened material than in the un-peened material. And compressive residual stress of surface on the shot-peen processed operate resistance force of fatigue crack propagation.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.4
• /
• pp.71-78
• /
• 2008

In the case of the railway bridges, uplift forces were occurred at the edge of the segments when vehicular loads were applied. These forces caused the compressive and tensile forces in the fastening system. In the past, a structural analysis has been performed to investigate the safety of fastening system which was modeled with one directional spring elements based on the compressive test of fastening system. In this case, the stiffness of the spring element was obtained from experimental study which was conducted by compressive load. Therefore, to perform rational and exact structural analysis, the translational stiffness of the fastening system obtained from the experimental study applied the tensile load and the rotational stiffness should be considered because it was occurred the tensile force as well as the compressive force in fastening system. In this study, an elastic and inelastic experimental study was performed for six specimens. The translational stiffness along the vertical axis of rail and the rotational stiffness along the strong axis of rail were investigated, also structural behavior of the fastening system was analyzed.

• Journal of Korean Society of Steel Construction
• /
• v.29 no.3
• /
• pp.229-236
• /
• 2017

The purpose of this study is to investigate the behavior and characteristics of rubber springs and calculate the compressive stiffness by performing dynamic compression tests of rubber springs. In order to carry out the dynamic compression test of rubber spring, total 9 rubber springs were tailored by calculating the shape factor of L80-D55, L90-D58, and L100-D60, and used for the experiments. Experiments were performed by controlling the compression according to the length of the rubber spring, and the compression was increased in the order of 5%, 10%, 15%, 20% and 25% of the strain. From the experimental results, the force-strain curves were obtained and it was confirmed that strength decrease and strength increase phenomenon occurred as the strain increased. In addition, it was confirmed that the decrease of stiffness and the increase of stiffness were clearly observed according to the size and diameter of the rubber spring, and the effective compression stiffness was estimated using the slope of the force-strain curve. By using the effective compressive stiffness, design values that can be used in actual design were presented.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.2 no.1
• /
• pp.22-31
• /
• 2003

The compressive residual stress, which is induced by shot peening process, seems to be an Important factor in increasing the fatigue strength. And then it was showed that residual stress was disappearenced at the high temperature. The fatigue charateristic investigation of a SUP9 spring steel processed shot peening is performed by considering the high temperature service conditions in the range of room temperature through $180^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. The fatigue resistance characteristics and fracture strength at high temperature is considerable lower than that of room temperature in the early stage and stable of fatigue crack growth region.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.11a
• /
• pp.421-424
• /
• 2000

Valve springs with high fatigue strength corresponding to the incresement of working stresses, are required for the higher generating power and the better fuel economy of automobile engines. For this purpose, high strength oil tempered wires are being used. By a method of the high strength for the valve spring, modification of manufacturing processes is being applied. In this case, the cause and effect for the improvement of the fatigue strength has not yet been explained obviously. Therefore, in this report, comparison of fatigue life between valve springs of conventional processes with oil tempered wires and new manufacturing processes was made. As a result of the fatigue test, the fatigue life of the latter was attained maximum 7 times than that of the former. It was cleared that the improvement of the fatigue life was caused by difference of compressive residual stresses at depth of 0.2mm below the inner side surface of both valve springs.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.314-319
• /
• 2004

High temperature fracture toughness characteristics of shot peened spring steel(SUP-9), which is used for automobile suspension system and railroad, was investigated in this paper. Fracture tougness test for room temperature, $100^{\circ}C$ , and $200^{\circ}C$ were evaluated by material test system(MTS). The experimental results show that the fracture toughness was improved by peened and unpeened. The fracture toughness for high temperature were also improved by peened and unpeened.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.10a
• /
• pp.347-353
• /
• 2002

The compressive residual stress, which is induced by shot peening process, seems to be an important factor of increasing the fatigue strength. And then it was showed that residual stress was disappearenced at the high temperature. The fatigue characteristic study of a SUP9 spring steel processed shot peening is performed by considering the high temperature service conditions in the range of room temperature through $180^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. The fatigue resistance characteristics and fracture strength at high temperature is considerable lower than that of room temperature in the early stage and stable of fatigue crack growth region.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.325-330
• /
• 2004

Recently, the request for the high strength of material is more and more increased in the area of industrial environment and machinery. To accomplish the high strength of materials, carbonizing treatment, nitrifying treatment, shot-peening method are representatively applied, however, shot-peening method is generally used among the surface processes. Shot peening is a cold working process used to impact Compressive residual stressed in the exposed surface layers. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in 3.5% NaCl. The immersion test as performed on the two kinds of specimens. Corrsion potential, polarization curve, residual stress and etc, were investigated from experiment results. From test result the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened on the environment corrosion of spring steels are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent mental. Surface of specimen, which is treated with the shot peened is placed as more activated state against inner base metal. It can cause t도 anti-corrosion effect on the base metal.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.1
• /
• pp.159-165
• /
• 2005

Shot peening can be defined as the process of work hardening of the surface of components by means of propelled stream of spherical shot. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in $3.5\%\;NaCl$. The immersion test was performed on the two kinds of specimens. Corrosion potential, polarization curve, residual stress and etc. were investigated from experimental results. From test results, the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened spring steels on the environment corrosion are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent metal. Surface of specimen, which is treated with the shot peened, is placed as more activated state against inner base metal. It can cause the anti-corrosion effect on the base metal.