• 한국자동차공학회논문집
• /
• 제18권1호
• /
• pp.74-85
• /
• 2010

In order to formulate the compounded polypropylene(C-PP) which is suitable to an automotive door trim panel, 9 sorts of properties were measured after manufacturing the C-PP using an extruder and an injection machine with polypropylene(PP), ethylene-octene rubber(EOR) and talc. Mixture design, especially extreme vertices design, in DOE with MINITAB - commercial software was used to analyze the data. The relations between each property and each component, for example, $y=0.00907222x_1+0.00870556x_2+0.0155722x_3$ for specific gravity, were found out by the regression analysis and the variance analysis. The optimized formulation of the C-PP for an automotive door trim panel was acquired at PP(77.6962), EOR(11.0238) and talc(10.2800) by use of the response optimizer(mixture) in MINITAB.

• Elastomers and Composites
• /
• 제56권4호
• /
• pp.217-222
• /
• 2021

In this study, random polypropylene (rPP) was compounded with two of monoglycerides, namely, glyceryl monolaurate (GML) and glyceryl monostearate (GMS), as antifogging agents to improve its antifogging performance. rPP film samples were prepared by a film-casting method using a three-roll casting machine after melt blending through a twin screw extruder. With an increase in the monoglyceride content, the melt flow index for rPP films with GML and GMS increased, and their yield strength decreased. The incorporation of GMS in rPP was proven to be more effective in improving its physical properties than was rPP with GML. When GML and GMS were separately added to the rPP film at contents of more than 1 phr and more than 5 phr, respectively, the film exhibited antifogging performance.

• International Journal of Automotive Technology
• /
• 제6권6호
• /
• pp.665-670
• /
• 2005

Nanocomposites of polypropylene with organically modified clays were compounded on a twin-screw extruder by two-step melt compounding of three components, i.e., polypropylene, maleic anhydride grafted polypropylene (PP-g-MA), and organically modified clay. The effect of PP-g-MA compatibilizers, including PH-200, Epolene-43, Polybond-3002, Polybond-3200, with a wide range of maleic anhydride (MA) content and molecular weight was examined. Morphologies of nanocomposites and their mechanical properties such as stiffness, strength, and impact resistance were investigated. X-ray diffraction patterns showed that the dispersion morphology of clay particles seemed to be determined in the first compounding step and the further dispersion of clays didn't occur in the second compounding step. As the ratio of PP-g-MA to clay increased, the clay particles were dispersed more uniformly in the matrix resin. As the dispersibility of clays was enhanced, the reinforcement effect of the clays increased, however impact resistance decreased.

• 폴리머
• /
• 제39권2호
• /
• pp.200-209
• /
• 2015

In this study, the influence of dilauroyl peroxide on mechanical and thermal properties of different polypropylene (PP) matrices was investigated. Polypropylene matrices, different molecular weight isotactic PP containing 0.01, 0.02, 0.04, 0.06, 0.08, and 0.1 wt% of dilauroyl peroxide (DLP) were prepared by using a single-screw extruder. The effect of the visbreaking agent (DLP) on mechanical, physical, thermal and morphological properties of different molecular weight PP had been studied. Mechanical properties (tensile strength at break point, at yield and elongation at break point), melt flow index (MFI), scanning electron microscope (SEM) and differential scanning calorimetric (DSC) analyses of these matrices were examined. Melting ($T_m$) and crystallization ($T_c$) temperatures, crystallinity ratio (%) and enthalpies were determined. The microstructure of isotactic polypropylene matrix was investigated by scanning electron microscopy (SEM). From SEM analysis, it was observed that the surface disorder increased by the increasing amount of DLP. As a result of DSC analyses, the crystallinity ratio of the PP matrices has varied between 1.64-7.27%. Mechanical properties of the matrices have been improved. Particularly, the mechanical tests of PP have given interesting results when compounded with 0.06-0.08 wt% dilauroyl peroxide (DLP). Mechanical properties and thermal decomposition processes were all changed by increasing the amount of DLP in the matrix structure.

• 한국응용과학기술학회지
• /
• 제28권4호
• /
• pp.410-417
• /
• 2011

Effects of ethylene-propylene diene monomer (EPDM)/polypropylene (PP), zinc oxide, stearic acid, and clay on the combustive properties based on EDPM/PP were investigated. The EDPM/PP/clay nanocomposites was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). It was found that the specific mass loss rate (SMLR) in the nanocomposites decreased due to the fire resistance compared with unfilled EDPM/PP, while the nanocomposites showed the higher total heat release (THR), higher CO production release, and higher specific extinction area (SEA) than those of virgin EPDM/PP. The stearic acid for softening ruber increased the THR and amount of smoke by itself, combustible.

• 한국화재소방학회논문지
• /
• 제25권6호
• /
• pp.190-195
• /
• 2011

에틸렌-프로필렌 디엔 단량체/폴리프로필렌에 바탕을 둔 에틸렌-프로필렌 디엔 단량체, 폴리프로필렌, 산화아연, 스테아르산, 그리고 클레이의 효과에 대하여 연소성을 조사하였다. 에틸렌-프로필렌 디엔 단량체/폴리프로필렌/클레이 나노복합체는 성형 후 콘칼로리미터(ISO 5660-1)를 이용하여 연소시험을 하였다. 그 결과 나노복합체는 에틸렌-프로필렌 디엔 단량체/폴리프로필렌 단독 조성에 비하여 최대열방출률을 감소시켰다. 이에 반하여 고무 연화제로 사용된 스테아르산은 자체의 연소성에 의하여 평균열방출률을 증가시켰다.

• 폴리머
• /
• 제27권6호
• /
• pp.576-582
• /
• 2003

열가소성 수지인 폴리프로필렌과 나일론 블렌드를 무기나노입자인 몬모릴로나이트와 상용화제 말레산 무수물 폴리프로필렌을 사용하여 복합화한 나노복합재료에 할로젠 계열의 난연제 데카브로모다이페닐옥사이드를 첨가하였을 때의 분산성과 난연특성 및 기계적 특성의 향상에 대해 실험하였다. 고분자 수지의 난연특성과 기계적 특성은 난연제의 첨가뿐만 아니라 나노복합화를 통해서도 향상될 수 있으며, 고분자 수지 내의 나노입자의 분산정도에 따라 매우 큰 차이가 생긴다. 고분자 수지와 무기나노입자 사이의 분산성과 그에 따른 난연특성 및 기계적 특성을 난연제와 무기나노입자의 함량에 .따라 정량적으로 측정하였다 폴리프로필렌/나일론 블렌드를 몬모릴로나이트로 복합화할 때 2회 이상 컴파운딩하면 완전히 분산되는 것을 XRD 결과로 확인하였다. 폴리프로필렌/나일론 블렌드를 복합화하면 나일론의 첨가로 인한 난연성의 저하를 극복할 수 있었으며, 무기나노입자가 완전히 분산되어 있을 때에는 추가적인 난연특성의 향상을 얻었다. 그리고 폴리프로필렌은 나일론의 첨가로 인하여 인장강도와 충격강도가 약간 증가하였으며, 무기나노입자와의 복합화를 통해서 추가적인 기계적 물성의 증가를 관찰하였다. 이로부터 폴리프로필렌의 기계적 물성의 향상을 위해 첨가한 나일론은 난연특성의 저하를 초래하지만 무기나노입자와의 복합화를 통해 난연특성의 향상과 추가적인 기계적 물성의 향상을 동시에 얻을 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제34권2호
• /
• pp.10-21
• /
• 2006

Recycled polypropylene (RPP) - Wood Saw Dust (WSD) composites with and without acetylation of filler were produced at different filler loading (15%, 25%, 35% and 45% w/w) and filler size (300, 212 and $100{\mu}m$). The RPP-WSD was compounded using a Haake Rheodrive 500 twin screw compounder at $190^{\circ}C$ at 8 MPa for 30 minutes. The mechanical properties and water absorption properties of modified and unmodified WSD-PP composites were investigated. Acetylation of WSD improved the mechanical and water absorption characteristic of composites. The decrease of filler size (300 to $100{\mu}m$) of the unmodified and acetylated WSD showed increase of tensile strength and impact properties. The composites exhibited higher tensile modulus properties as the filler loading increased (15% to 45%). However tensile strength, elongation at break and impact strength showed the opposite phenomenon. Water absorption increased as the mesh number and filler loading increased. With acetylation, lower moisture absorption was observed as compared to unmodified WSD. The failure mechanism from impact fracture of the filler-matrix interface with and without acetylation was analyzed using Scanning Electron Microscope (SEM).

• 대한토목학회논문집
• /
• 제34권6호
• /
• pp.1677-1685
• /
• 2014

섬유를 콘크리트의 보강재로 소량 혼입한 섬유 보강 콘크리트는 콘크리트의 인장저항 능력과 연성능력을 향상시킬 수 있다. 최근에는 강섬유의 적용성이 확대됨에 따라 강섬유 길이의 연장을 통해 보강의 효과를 증대시키고 있다. 섬유의 길이 연장은 동일한 시공성과 품질성을 위해 섬유 혼입률을 동시에 감소시킬 필요가 있다. 따라서, 본 연구에서는 35mm, 60mm 길이의 강섬유와 화학적인 안정성과 내구성, 경제성 등이 우수한 보강 재료로 평가되어지고 있는 폴리프로필렌 섬유에 대해 섬유혼입률 1.0% 이하에서의 휨 성능을 평가하였다. 강섬유 혼입률이 0.25% 이상, 폴리프로필렌 섬유는 혼입률 0.5% 이상에서 균열강도 도달 후 취성 파괴되는 무보강보의 파괴거동을 개선하는 효과가 나타났다. 다만, 폴리프로필렌 섬유가 혼입된 보강 콘크리트는 균열 이후 deflection-softening 거동을 보였다. 그러나, 0.5%이상의 폴리프로필렌이 혼입된 보강보는 균열 이후 최대강도가 균열강도의 약 60~80%정도 강도회복을 보였으며, 강섬유에 비해 균열 이후 응력감소현상을 지연시키는 경향이 뛰어난 것으로 판단된다. 결론적으로 폴리프로필렌 보강콘크리트는 0.75% 혼입률 이상에서는 충분히 만족할 만한 구조적 휨 성능 향상을 보일 수 있을 것으로 판단된다. 특히, 폴리프로필렌 1.0% 보강 콘크리트의 에너지 흡수 성능은 0.5%, 0.75%가 혼입된 강섬유 보강 콘크리트의 에너지 흡수성능과 거의 비슷한 것으로 평가되었다.

• Composites Research
• /
• 제26권1호
• /
• pp.1-6
• /
• 2013

용액 분산법을 이용하여 CNT를 균질하게 분산시켰고, CNT-폴리프로필렌 복합재료 제조를 위해 압출기와 사출기를 사용하였다. CNT 고유의 전도성을 기반으로 CNT-PP 복합재료의 내부 손상을 감지하기 위해 전기저항 측정법을 이용하였다. CNT-PP의 기계적 및 계면 물성을 확인하고 일반 PP와 비교하였다. CNT의 강화 효과로 인하여 CNT를 함유함으로서, PP 기지의 기계적 물성은 더 증가되는 경향을 확인하였다. CNT-PP 복합재료의 내부 손상을 평가하기 위해 파괴 및 굴곡실험을 진행하며, 동시에 발생되는 전기저항 변화도를 감지하여 미세손상을 평가하였다. CNT 강화제의 첨가는 좋은감지능을 보여주었다. 낮은 CNT 함유율임에도 CNT-PP 복합재료의 감지가 가능했으며, 반복 하중 실험 중 최대 임계 응력을 확인하여, 내부에 발생된 미세 파괴를 찾아 낼 수 있었다.