• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.1
• /
• pp.74-85
• /
• 2010

In order to formulate the compounded polypropylene(C-PP) which is suitable to an automotive door trim panel, 9 sorts of properties were measured after manufacturing the C-PP using an extruder and an injection machine with polypropylene(PP), ethylene-octene rubber(EOR) and talc. Mixture design, especially extreme vertices design, in DOE with MINITAB - commercial software was used to analyze the data. The relations between each property and each component, for example, $y=0.00907222x_1+0.00870556x_2+0.0155722x_3$ for specific gravity, were found out by the regression analysis and the variance analysis. The optimized formulation of the C-PP for an automotive door trim panel was acquired at PP(77.6962), EOR(11.0238) and talc(10.2800) by use of the response optimizer(mixture) in MINITAB.

• Elastomers and Composites
• /
• v.56 no.4
• /
• pp.217-222
• /
• 2021

In this study, random polypropylene (rPP) was compounded with two of monoglycerides, namely, glyceryl monolaurate (GML) and glyceryl monostearate (GMS), as antifogging agents to improve its antifogging performance. rPP film samples were prepared by a film-casting method using a three-roll casting machine after melt blending through a twin screw extruder. With an increase in the monoglyceride content, the melt flow index for rPP films with GML and GMS increased, and their yield strength decreased. The incorporation of GMS in rPP was proven to be more effective in improving its physical properties than was rPP with GML. When GML and GMS were separately added to the rPP film at contents of more than 1 phr and more than 5 phr, respectively, the film exhibited antifogging performance.

• International Journal of Automotive Technology
• /
• v.6 no.6
• /
• pp.665-670
• /
• 2005

Nanocomposites of polypropylene with organically modified clays were compounded on a twin-screw extruder by two-step melt compounding of three components, i.e., polypropylene, maleic anhydride grafted polypropylene (PP-g-MA), and organically modified clay. The effect of PP-g-MA compatibilizers, including PH-200, Epolene-43, Polybond-3002, Polybond-3200, with a wide range of maleic anhydride (MA) content and molecular weight was examined. Morphologies of nanocomposites and their mechanical properties such as stiffness, strength, and impact resistance were investigated. X-ray diffraction patterns showed that the dispersion morphology of clay particles seemed to be determined in the first compounding step and the further dispersion of clays didn't occur in the second compounding step. As the ratio of PP-g-MA to clay increased, the clay particles were dispersed more uniformly in the matrix resin. As the dispersibility of clays was enhanced, the reinforcement effect of the clays increased, however impact resistance decreased.

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.200-209
• /
• 2015

In this study, the influence of dilauroyl peroxide on mechanical and thermal properties of different polypropylene (PP) matrices was investigated. Polypropylene matrices, different molecular weight isotactic PP containing 0.01, 0.02, 0.04, 0.06, 0.08, and 0.1 wt% of dilauroyl peroxide (DLP) were prepared by using a single-screw extruder. The effect of the visbreaking agent (DLP) on mechanical, physical, thermal and morphological properties of different molecular weight PP had been studied. Mechanical properties (tensile strength at break point, at yield and elongation at break point), melt flow index (MFI), scanning electron microscope (SEM) and differential scanning calorimetric (DSC) analyses of these matrices were examined. Melting ($T_m$) and crystallization ($T_c$) temperatures, crystallinity ratio (%) and enthalpies were determined. The microstructure of isotactic polypropylene matrix was investigated by scanning electron microscopy (SEM). From SEM analysis, it was observed that the surface disorder increased by the increasing amount of DLP. As a result of DSC analyses, the crystallinity ratio of the PP matrices has varied between 1.64-7.27%. Mechanical properties of the matrices have been improved. Particularly, the mechanical tests of PP have given interesting results when compounded with 0.06-0.08 wt% dilauroyl peroxide (DLP). Mechanical properties and thermal decomposition processes were all changed by increasing the amount of DLP in the matrix structure.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.4
• /
• pp.410-417
• /
• 2011

Effects of ethylene-propylene diene monomer (EPDM)/polypropylene (PP), zinc oxide, stearic acid, and clay on the combustive properties based on EDPM/PP were investigated. The EDPM/PP/clay nanocomposites was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). It was found that the specific mass loss rate (SMLR) in the nanocomposites decreased due to the fire resistance compared with unfilled EDPM/PP, while the nanocomposites showed the higher total heat release (THR), higher CO production release, and higher specific extinction area (SEA) than those of virgin EPDM/PP. The stearic acid for softening ruber increased the THR and amount of smoke by itself, combustible.

• Fire Science and Engineering
• /
• v.25 no.6
• /
• pp.190-195
• /
• 2011

Effects of ethylene-propylene diene monomer (EPDM)/polypropylene (PP), zinc oxide, stearic acid, and clay on the combustive properties based on EPDM/PP were investigated. The EPDM/PP/clay nanocomposites was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). It was found that the combustive properties in the nanocomposites decreased due to the fire resistance compared with unfilld EDPM/PP. The nanocomposites showed the lower peak heat release rate (PHRR) than that of virgin EPDM/PP, while stearic acid for softening ruber increased the mean heat release rate (MHRR) by itself, combustible.

• Polymer(Korea)
• /
• v.27 no.6
• /
• pp.576-582
• /
• 2003

When the halogenated flame retardant, decabromodiphenyl oxide, was added to the polypropylene/nylon blend, and was compounded with montmorillonite and compatibilizer, maleic anhydride polypropylene, the improvement of flame retardancy and mechanical properties was investigated. The degree of dispersion between polymer resin and inorganic nanoparticles was investigated, and the flame retardancy and mechanical properties was measured quantitatively. XRD results showed that the montrnorillonite was com-pletely exfoliated after polypropylen/nylon nanocomposites was mixed above twice. By compounding with montmorillonite, polypropylene/nylon blend system was overcome the deterioration of flame retardancy. The tensile strength and impact strength were slightly increased, and by compounding with montmorillonite, the additional increase in mechanical properties was obtained. Therefore, the flame retardancy of polypropylene / nylon blend was decreased by adding nylon, but by compounding with inorganic nanoparticle, improvement of the flame retardancy and mechanical properties was obtained.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.2
• /
• pp.10-21
• /
• 2006

Recycled polypropylene (RPP) - Wood Saw Dust (WSD) composites with and without acetylation of filler were produced at different filler loading (15%, 25%, 35% and 45% w/w) and filler size (300, 212 and $100{\mu}m$). The RPP-WSD was compounded using a Haake Rheodrive 500 twin screw compounder at $190^{\circ}C$ at 8 MPa for 30 minutes. The mechanical properties and water absorption properties of modified and unmodified WSD-PP composites were investigated. Acetylation of WSD improved the mechanical and water absorption characteristic of composites. The decrease of filler size (300 to $100{\mu}m$) of the unmodified and acetylated WSD showed increase of tensile strength and impact properties. The composites exhibited higher tensile modulus properties as the filler loading increased (15% to 45%). However tensile strength, elongation at break and impact strength showed the opposite phenomenon. Water absorption increased as the mesh number and filler loading increased. With acetylation, lower moisture absorption was observed as compared to unmodified WSD. The failure mechanism from impact fracture of the filler-matrix interface with and without acetylation was analyzed using Scanning Electron Microscope (SEM).

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.6
• /
• pp.1677-1685
• /
• 2014

Short discrete fibers compounded with concrete can enhance the tensile resistance and ductility of concrete. Recently, the effectiveness of the reinforcement has increased according to the increasing length of steel fiber. However, the lengthening of steel fiber requires reducing the ratio of the fiber content to remain the workability and quality of concrete. Thus, the present study evaluated the flexural performance of fiber reinforced concrete with less than l.0% fiber volume ratios of steel fiber, 30mm and 60mm long, and polypropylene fiber, being evaluated as a good reinforcing material with chemical stability, long-term durability, and cost effectiveness. Concrete with more than 0.25% steel and 0.5% polypropylene fibers improved the brittle failure of concrete after reaching cracking strength. Concrete reinforced with polypropylene exhibited deflection-softening behavior, but that with more than 0.5% polypropylene delayed stress reduction and recovered flexural strength by 60 to 80% after cracking strength. In conclusion, concrete reinforced with more than 0.75% polypropylene could improve structural flexural performance. In particular, energy absorption capacity of reinforced concrete with 1.0% polypropylene fiber was similar to that with 0.5% and 0.7% steel fibers.

• Composites Research
• /
• v.26 no.1
• /
• pp.1-6
• /
• 2013

CNT-polypropylene (PP) composites were compounded by solvent dispersion method with uniform dispersion by using twin screw extruder. Damage sensing effects based on conductive carbon nanotubes (CNT) were evaluated to monitor the internal damage of CNT-PP composites using electrical resistance measurement. Mechanical and interfacial properties of CNT-PP composites were investigated and compared with neat PP. The mechanical properties of PP matrix were improved after adding CNT, because of the reinforcing effect of CNT fillers. In order to monitor the internal damage of CNT-PP composite, the change in electrical resistance of the composites was measured under fatigue loading and bending tests. CNT fillers exhibited good sensing under electrical resistance measurements. It is shown that CNT-PP composites with low CNT contents allow identifying critical cyclic loading, which are found to be accompanied with the internal failure.