• 한국신뢰성학회:학술대회논문집
• /
• 한국신뢰성학회 2006년도 학술발표대회 논문집
• /
• pp.357-361
• /
• 2006

Fatigue fracture behavior of a hybrid joint part with bolting was evaluated in comparison to the case of static fracture. Hybrid joint part specimens for bending test were made with layers of CFRP and aluminum honeycomb. Characteristic fracture behaviors of those specimens were obviously different under static and cyclic loads. Static bending load showed the shear deformation at the honeycomb core, whereas cyclic bending load caused the delamination between CFRP skin layers and honeycomb core. Experimental results obtained by static and fatigue tests were considered in modifications of design parameters of the hybrid joint.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.74-77
• /
• 2001

The impact response and damage of CLAS panel was investigated experimentally. The facesheet material used was RO4003 woven-glass hydrocarbon/ceramic and the core material was Nomex honeycomb with a cell size of 3.2mm and a density of 96 kg/$\textrm{m}^{3}$. The shield plane used was RO4003 and 2024-T3 aluminum. Static indentation and impact test was conducted to characterize the type and extent of the damage observed in two CLAS panels, and the performance of antenna used in a wireless LAN system. Correlation of peak contact force, residual indentation and the delamination area shows impact damage of the panel with an aluminum shield plane is larger than that of the panel with RO4003 shield plane, although tile former is more penetration resistant. The damage was observed by naked eye, ultrasonic inspection and cross sectioning. The shape and size of delamination was estimated by ultrasonic inspection, and the area of delamination linearly increases as impact energy increases. The performance of impact damaged antenna was estimated by measuring return loss and radiation pattern.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2005년도 전기학술대회논문집
• /
• pp.388-394
• /
• 2005

A typical honeycomb sandwich panel consists of two thin, high-strength facings bonded to a thick, light-weight core. Each component by itself is relatively weak and flexible, but when it combind in a sandwich panel they produce a structure that is stiff, strong, and lightweight. In addition to use in honeycomb sandwich panels, honeycomb is used for energy absorption, radio frequency shielding, light diffusion, and to direct air flow.Accordingly, the usage of honeycomb sandwich structure is very widely applied to the aircraft, the automobile, and marine industry, etc., because of these advantages. Generally, this honeycomb sandwich structure is manufactured by autoclave process.In this study, the honeycomb sandwich structure was produced by prepreg. To prove the suitability the honeycomb sandwich structure with prepreg, The optimum design of the skin materials and honeycomb sandwich structure were evaluated with the theory of stress analysis.

• Composites Research
• /
• 제19권1호
• /
• pp.9-14
• /
• 2006

본 연구는 KS F 2278 2003 (창호의 단열성 시험 방법)에 의하여 철도차량 및 버스의 내/외장재로 적용 가능한 카본/에폭시 스킨-알루미늄 하니콤 & 발사코어 샌드위치 판넬(두께 : 37mm), 카본/에폭시 스킨-알루미늄 하니콤 코어 샌드위치 판넬(두께 : 57mm, 단열재 포함) 및 카본/에폭시 스킨-알루미늄 하니콤 코어 샌드위치 판넬(두께 : 37mm)에 대한 열관류율 시험을 하였다. 또한 KS F2277 . 2002 (건축용 구성재의 단열성 측정방법-교정열상자법 및 보호열상자법)에 의하여 추가로 알루미늄 스킨-알류미늄 하니콤 샌드위치 판넬들 (두께 : 27mm, 35n1m)과 알루미늄 스킨-포밍 알루미늄 샌드위치 판넬 (두께27mm)에 대한 열관류율 시험을 수행하였다. 본 연구를 통해 면제와 심재사이에 열전달은 실제 단면적이 넓을수록 열관류율이 높았으며, 하이브리드형 복합재 일수록 단열성능이 우수함을 확인하였다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.78-82
• /
• 2001

Impact behaviors of Aluminum Honeycombs Sandwich Panel(AHSP) by drop weight test were investigated. Two types of specimens with 1/2" and 1/4" cell size were tested by two impactors which are weight of $5.25\textrm{kg}_{\textrm{f}}$ and $11.9\textrm{kg}_{\textrm{f}}$. Parametric studies were achieved including the impactor weight and impact sites which consist face, long-edge, short-edge, and point of the specimen. Face one of impact sites was the strongest and short-edge one of impact sites was the weakest. The damaged area of AHSP was enlarged with the increase of impactor weight that is equal to impact energy. After 3 point bending test, fracture modes of AHSP were analyzed with AE counts. Lower facesheet was fractured in the long-edge direction and then separated between facesheet and core. In the short-edge direction after core wrinkled, lower facesheet tear occurred. Impact behavior by FE analysis were increased localized damage in fast velocity because the faster velocity of the impact was, the smaller the stress of core was. Consequently, impactor weight had an effect on widely damaged area, while the impact velocity was caused on the localized damaged area.aged area.

• 대한기계학회논문집A
• /
• 제31권2호
• /
• pp.166-173
• /
• 2007

Fatigue fracture behavior of a hybrid bolted joint was evaluated in comparison to the case of static fracture. Two kinds of specimens were fabricated for the mechanical tests; a hybrid bolted joint specimen for the shear test and a hybrid joint part specimen applied in the real tilting car body for the bending test. Characteristic fracture behaviors of those specimens under cyclic toads were obviously different from the case under static loads. For the hybrid bolted joint specimen, static shear loading caused the fracture of the bolt body itself in a pure shear mode, whereas cyclic shear loading brought about the fracture at the site of local tensile stress concentration. For the hybrid joint part specimen, static bend loading caused the shear deformation and fracture in the honeycomb core region, while cyclic bend loading did the delamination along the interface between composite skin and honeycomb core layers as well as the fracture of welded joint part. Experimental results obtained by static and fatigue tests were reflected in modifications of design parameters of the hybrid joint structure in the real tilting car body.

• 대한기계학회논문집A
• /
• 제25권1호
• /
• pp.115-126
• /
• 2001

In this paper, through a series of comparative experiments, effects of two different cure processing methods, cocure and precure, on the mechanical properties of honeycomb core materials for aircraft applications are considered. Mass of moisture accumulated into the closed cells of the sandwich panel specimen from the measured mass of moisture diffused to the full saturation state into the elements(skin, adhesive layer, Nomex honeycomb), consisting the honeycomb sandwich specimen has been calculated. Water reservoir of 70$\^{C}$ was used to have specimens absorb moisture to see the influence of moisture absorbed into sandwich panel on its mechanical properties. For the repair condition holding for 2 hours at 177$\^{C}$(350℉) temperature, a pressure due to the vapor expansion in each cell of the sandwich panel, which may result in the local separation of the interface between laminated skin and the surface of the honeycomb, has been estimated by vapor pressure-temperature relation from the thermodynamic steam table and compared to the pressure from the ideal gas state equation. The bonding strengths of the laminated skins on the flat surface of the Nomex honeycomb have been compared by the flatwise tension test and climbing drum peel test performed at room temperature for dry, wet and wet-repair specimens, respectively.

• Composites Research
• /
• 제14권1호
• /
• pp.22-29
• /
• 2001

본 논문의 목적은 샌드위치 구조물의 오토클레이브 성형시 발생하는 승압률, 승온율, 금형 라운드 각도, 코어의 두께, 그리고 결함에 대한 저글 높이의 영향을 결정하고, 하니콤으로 보강된 항공기용 샌드위치 구조의 결함을 최소화시키는 것이다. 결과는 항공기용 샌드위치 구조와 금형 라운드 각도와 같은 금형의 형상, 코어의 두께, 저글의 높이, 그리고 승압률, 승온율과 같은 오토클레이브의 성형 조건이 코어의 무브먼트. 코어의 주름, 프리프레그의 뜨임 현상 그리고 코어의 침하에 영향을 기침을 보여주었다.

• Composites Research
• /
• 제22권6호
• /
• pp.23-31
• /
• 2009

압축하중 및 굽힘하중을 받는 유리섬유플라스틱(GFRP) 표피/ 알루미늄 하니컴 코어(GF-AH) 하이브리드 복합재료의 음향방출(AE) 특성을 다양한 파괴과정과 연결시켜 연구하였다. 표피층 파괴, 표피/코어간의 계면박리, 하니컴 알루미늄 벽의 국부적인 소성항복 좌굴 및 셀벽간의 접착수지 박리와 같은 다양한 파괴모드가 하니컴 코어/GFRP표피 복합재를 이용한 AE주파수 분포 해석과 진폭분포 해석결과를 통해 분류되었다. 높은 진폭을 가진 AE 사상율의 분포는 셀벽 접착수지의 파괴, 표피층과 심층 사이의 박리및 미세파괴, 섬유파단에 대응하였으며 다른 피크 주파수의 분포는 알루미늄 셀벽의 소성변형, 셀벽간의 마찰로부터 발생한 것이다. 결론적으로 GF-AH 하이브리드 복합재료의 파괴거동 특성은 AE기법을 활용한 비파괴 평가를 통해 분석 가능하였다.

• Steel and Composite Structures
• /
• 제44권1호
• /
• pp.105-117
• /
• 2022

Impact resistance efficiency of the newly designed sandwich beam with a laterally arched core as bio-inspired by the woodpecker is numerically investigated. The principal components of the beam comprise a dual-core system sandwiched by the top and bottom laminated CFRP skins. Different materials, including hot melt adhesive, high-density polyethylene (HDPE), acrylonitrile butadiene styrene (ABS), epoxy resin (EPON862), aluminum (Al6061), and mild carbon steel (AISI1018), are considered for the side-arched core layer of the beam for impact efficiency assessment. The aluminum honeycomb takes the role of the second core. Contact force, stress, damage formation, and impact energy for beams equipped with different materials are examined. A diversity in performance superiority is noticed in each of these indicators for different core materials. Therefore, for overall performance appraisal, the impact resistance efficiency index, which covers several chief impact performance parameters, of each sandwich beam is computed and compared. The impact resistance efficiency index of the structure equipped with the AISI1018 core is found to be the highest, about 3-10 times greater than other specimens, thus demonstrating its efficacy as the optimal material for the bio-inspired dual-core sandwich beam system.