• 산업기술연구
• /
• 제35권
• /
• pp.31-34
• /
• 2015

The purpose of the study was to investigate the mechanical properties (diametral tensile strength, flexural strength, compressive strength, Vickers hardness) of 4 kinds of composit resins; Bis-GMA based composit, Bis-EMA based composit, Bis-GMA/UDMA based composit, and Bis-EMA/UDMA based composit, The composit resin based Bis-GMA showed stronger mechanical properties than Bis-EMA. It was found that the addition of UDMA to both Bis-GMA based composit and Bis-EMA based composit highly improved mechanical properties. However, the mechanical properties of the composit resins prepared in this study were lower than those of the commercialized products in market(Charmfil flow(Denkist), Quadrant flow(CAVEX)), since the composit resins prepared in this study has much lower inorganic filler content of 43wt% comparing with 50~70wt% inorganic filler content of the commercialized products.

• 산업기술연구
• /
• 제35권
• /
• pp.35-39
• /
• 2015

One of the purposes of the study was to investigate and compare the physical properties(depth of light cure, degree of conversion, water absorption) of 4 kinds of composit resins prepared in this lab; Bis-GMA based, Bis-EMA based, Bis-GMA/UDMA based, and Bis-EMA/UDMA based composit. Another aim was to compare the physical properties of the composit resins with those of the commercialized products(Charmfil flow(Denkist), Quadrant flow(CAVEX)) in market. All of the composit resins and the commercialized products showed almost same values of the physical properties. It was found that all of the composit resins prepared in this lab satisfied the physical properties specified in ISO 4049.

• 대한치과의사협회지
• /
• 제54권1호
• /
• pp.16-20
• /
• 2016

There is a difficulty for many practioner in anterior direct restroation with composit resin. Because its result is various according to patient, a practioner have a fear about that unpromisable result. Moreover in esthetic region, there is difference in satisfaction by patient character. That is one of difficulty in this practice. But if we make a manual for parctice it will be easier. So I will summarize the process and things to note in direct anterior composite resin restoration.

• Restorative Dentistry and Endodontics
• /
• 제19권2호
• /
• pp.447-459
• /
• 1994

The purpose of this study is to evaluate of shear bond strength of light-curing composite resin to light-curing glass ionomer cement. Composite resin and glass ionomer cement have been widely used as an esthetic filling materials in dental clinics. To achieve better clinical results, sandwich technic was developed with conpensating for disadvantages of these two materials. Especially, light-curing glass ionomer cement provided greately improved bonding strength of teeth or composite resin, and then excellent clinical results can be acquired. In this study, 6 commercial light-curing glass ionomer cements(3 commercial restorative materials : Fuji II LC, Variglass VLC, Vitremer, and 3 commercial lining materials : Fuji Lining LC, Baseline VLC, Vitrebond) were devided two groups. According to manufacturer's appointment, no surface treatment was referred to N groups. Supposing. of clinical practice, surface grinding with water spray at 320 grit sand paper, 40 seconds etching with 37% phosphoric acid, 20 seconds washing, 20 seconds air drying was referred to N groups. Totally 12 experimental groups were devided, and all 120 specimens from 10 specimens of each groups were made. After light-curing composite resin was bonded to light-curing glass ionomer cement, shear bond strength was tested by Instron universal testing machine between glass ionomer cement and composit resin. The data were analyzed statistically by Student's t-test and ANOVA. The obtained results were as follows; 1. In light-curing glass ionomer cement, restorative materials showed higher shear bond strength to composite resin than lining materials(p<0.05). 2. Variglass VLC of restorative material group and Baseline VLC of lining material group have highest shear bond strength to composite resin(p<0.001). 3. In light-curing glass ionomer cement, surface grinding and acid etching reduced shear bond strength to composite resin(p<0.001)}. 4. VGN group 1s highest shear bond strength to composite resin, VBE group is lowest shear bond strength to composite resin(p<0.001).

• 대한소아치과학회지
• /
• 제29권2호
• /
• pp.180-188
• /
• 2002

최근에 소개된 plasma arc curing units는 비교적 높은 광 강도를 가지고 짧은 시간내에 복합레진을 적절히 중합시킨다고 한다. 이 연구는 plasma arc curing units의 강한 광도와 짧은 시간에 의한 중합이 복합레진에 미치는 영향을 평가하기 위해 기존의 가시광선 중합기를 대조군으로 하여 표면 미세경도와 5급 수복물의 변연에 나타나는 미세누출을 색소침투방법으로 측정, 분석하여 다음과 같은 결론을 얻었다. 1. 각 깊이에서의 미세경도는 AHL군이 AP3, AP6군보다 모든 깊이에서 높았고, ZHL군보다 ZP6군이 표면에서 더 높았으며(P<0.05), 1mm와 2mm에서는 차이가 없었다(P>0.05). 그 외 모든 깊이에서 ZHL군이 ZP3, ZP6군보다 높았다(P<0.05). 2. 각 중합방법내 깊이에 따른 미세경도는 AHL군의 표면-1mm와 ZHL군의 1mm-2mm를 제외하고는 모든 군에서 깊이에 따라 감소되었다(P<0.05). 3. 교합면측과 치경부측 미세누출은 모든 중합군에서 교합면측이 낮게 나타났지만 유의한 차이는 없었다(P>0.05). 4. 중합방법간 미세누출은 모든 군에서 차이가 없었다(P>0.05). 5. 각 중합방법에 따른 재료간의 미세누출은 차이가 없었다(P>0.05).