• 대한치과기공학회지
• /
• 제31권4호
• /
• pp.25-30
• /
• 2009

Zirconia($ZrO_2$) has attracted much attention in science and technology because of its high refractive index, high melting temperature, hardness, low thermal conductivity and corrosion barrier properties. And it is widely used as the dental restoration material because of its esthetic appearance. In this research, we analyzed the particle size and composition of the imported dental porcelain for zirconia. And the glass frit was produced. To decrease the glass transition temperature and softening temperature of the glass frit, $Li_2O$ was added into it and the effect of $Li_2O$ on the firing temperature was researched. Then the glass which contains leucite crystal with a high coefficient of thermal expansion(CTE) was manufactured and it was mixed with the glass frit to control the CTE. The phase composition were analyzed using the X-ray diffraction. The morphologies of the samples were observed by the scanning electron microscope. The 4wt% $Li_2O$-added glass frit has the optimal glass transition temperature and softening temperature. And 6 wt% leucite crystal was mixed with the glass frit to control the CTE. From the experimental results of crystallization, the crystal phase was found only leucite crystal.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.370-371
• /
• 2006

The particulate strengthened $Cu-MoSi_2$ composites were prepared by a PM process to develop novel copper based composites with reasonable strength, high thermal conductivity and low thermal expansion coefficient. Microstructure of the composites was investigated by SEM; the tensile strength, elongation, thermal conductivity and thermal expansion coefficient (CTE) of the composites were examined. A comparative analysis of mechanical and thermal properties of various Cu-matrix composites currently in use was given and the strengthening mechanisms for the $Cu-MoSi_2$ composites were discussed.

• Nuclear Engineering and Technology
• /
• 제54권7호
• /
• pp.2359-2366
• /
• 2022

Selecting graphite grades with superior irradiation characteristics is important task for designers of graphite moderation reactors. To provide reference information and data for graphite selection, the effects of irradiation on three fine-grained, iso-molded nuclear grade graphites, ETU-10, IG-110, and NBG-25, were compared based on irradiation-induced changes in volume, thermal conductivity, dynamic Young's modulus, and coefficient of thermal expansion. Data employed in this study were obtained from reported irradiation test results in the high flux isotope reactor (HFIR)(ORNL) (ETU-10, IG-110) and high flux reactor (HFR)(NRL) (IG-110, NBG-25). Comparisons were made based on the irradiation dose and irradiation temperature. Overall, the three grades showed similar irradiation-induced property change behaviors, which followed the historic data. More or less grade-sensitive behaviors were observed for the changes in volume and thermal conductivity, and, in contrast, grade-insensitive behaviors were observed for dynamic Young's modulus and coefficient of thermal expansion changes. The ETU-10 of the smallest grain size appeared to show a relatively smaller VC to IG-110 and NBG-25. Drastic decrease in the difference in thermal conductivity was observed for ETU-10 and IG-110 after irradiation. The similar irradiation-induced properties changing behaviors observed in this study especially in the DYM and CTE may be attributed to the assumed similar microstructures that evolved from the similar size coke particles and the same forming method.

• 한국표면공학회지
• /
• 제47권6호
• /
• pp.293-296
• /
• 2014

Fe-Ni has been of great interest because it is known as one of low thermal expansion alloys as various application areas. This alloy was fabricated by electroforming process, and effect of heat treatment on thermal expansion and hardness was investigated. Nano-crystalline structure of 13.3 - 63.5 nm in size was observed in the as-deposited alloy. To investigate the effect of heat treatment on grain growth and mechanical/thermal properties, we conducted hardness and coefficient of thermal expansion (CTE). From this, we confirmed these properties were varied by heat treatment. In this nano-crystalline alloy, we could observe abnormal behavior in thermal expansion between $350-400^{\circ}C$. Additionally, an abrupt change in hardness has also been observed. However, once the grains grow up to micro-sized the mechanical and thermal properties mentioned above were stabilized similar to those of bulk alloys due to heat treatment.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2009년도 춘계학술대회 논문집
• /
• pp.251-252
• /
• 2009

• 지질공학
• /
• 제11권3호
• /
• pp.269-278
• /
• 2001

MD 시뮬레이션을 이용하여 $\alpha$-quartz, 백운모, 조장석의 열팽창계수를 산정하였다. MD 시뮬레이션에서 가장 중요한 포텐셜 함수로는 부분이온성 두입자간 포텐셜을 이용하였다. 열팽창계수는 격자구조의 온도에 따라 변화를 NPT-ensemble 시뮬레이션을 통하여 계산하여 산정하였으며 그 결과를 실험결과와 비교하였다. 시뮬레이션을 통하여 산정된 열팽창계수는 시험결과와 잘 일치하고 있으며, 유효한 수준의 결과를 보이고 있다.

• Journal of Biosystems Engineering
• /
• 제9권2호
• /
• pp.89-96
• /
• 1984

This study was intended to search the thermal properties of rice which are necessary in preventing qualitative and quantitative losses in the drying and milling processes. First, the coefficient of cubical thermal expansion of brown rice was measured, which is required for analyzing the internal stress of rice, and then theoretical thermal and moisture stresses were calculated. The results are summarized as follows: 1. The coefficient of cubical thermal expansion of brown rice was about $2.81{\times}10^{-4}/^{\circ}C$ in the temperature range of $10^{\circ}C-60^{\circ}C$. 2. When the shape of brown rice was assumed to be a sphere or a cylinder, maximum thermal stress due to temperature change of $20^{\circ}C-60^{\circ}C$ was in the range of $25-100kg/cm^2$. And maximum moisture stress was in the range of $450-650kg/cm^2$ when the drying temperature was $35^{\circ}C$, initial and final moisture contents of brown rice were 20% and 14% (w.b.), and the moisture diffusion coefficient was assumed to be $6.79{\times}10^{-4}cm^2/hr$. 3. Consequently, it was concluded that crack formation in a rice kernel is mainly caused by moisture stress.

• 소성∙가공
• /
• 제24권1호
• /
• pp.44-51
• /
• 2015

The current study seeks to examine the effects of V and C additions on the mechanical and low thermal expansion properties of a high strength invar base alloy. The base alloy (Fe-36%Ni-0.9%Co-2.75%Mo-0.7Cr-0.23Mn-0.17Si-0.3%C, wt.%) contains $Mo_2C$ carbides, which form as the main precipitate. In contrast, alloys with additions of 0.4%V+0.3%C (alloy A) or 0.4%V+0.45%C (alloy B) contain $Mo_2C$+[V, Mo]C carbides. The average thermal expansion coefficients of these high strength invar based alloys were measured in the range of $5.16{\sim}5.43{\mu}m/m{\cdot}^{\circ}C$ for temperatures of $15{\sim}230^{\circ}C$. Moreover, alloy B showed lower thermal expansion coefficient than the other alloys in this temperature range. For the mechanical properties, the [V, Mo]C improved hardness and strengths(Y.S. and T.S.) of the high strength invar base alloy. T.S.(tensile strength) and Y.S.(yield strength) of hot forged alloy B specimen were measured at 844.6MPa and 518.0MPa, respectively. The tensile fractography of alloy B exhibited a ductile transgranular fracture mode and voids were initiated between the [V, Mo]C particles and the matrix. Superior properties of high strength and low thermal expansion coefficient can be obtained by [V, Mo]C precipitation in alloy B with the addition of 0.4%V and 0.45%C.

• 한국재료학회지
• /
• 제25권7호
• /
• pp.330-335
• /
• 2015

A low thermal expansion ceramic, cordierite ($2MgO{\cdot}2Al_2O_3{\cdot}5SiO_2$), was synthesized using pyrophyllite. Pyrophyllite usually consists of $SiO_2$ and $Al_2O_3$, which are the main components of cordierite. $MgCO_3$ and $Al(OH)_3$ were added in various amounts to pyrophyllite and fired for synthesis and sintering. ${\alpha}$-cordierite crystallized from $1000^{\circ}C$ with mixing of 20 wt% $MgCO_3$ and 1.7 wt% $Al(OH)_3$, and un-reacted cristobalite was also detected with the cordierite. As the temperature was increased to $1400^{\circ}C$, the cordierite yield was gradually increased. Powder compacts of the synthesized cordierite were sintered between $1250^{\circ}C{\sim}1400^{\circ}C$; the sintered samples showed a low thermal expansion coefficient of $2.1{\times}10^{-6}/^{\circ}C$ and typical sintering behavior. It is anticipated that it will be possible to synthesize cordierite ceramics on a mass production scale using the mineral pyrophyllite.

• 산업기술연구
• /
• 제20권A호
• /
• pp.239-245
• /
• 2000

Sintered $Al_2TiO_5$ has a very low thermal expansion and an infrared radiative selectively emitting large amounts of far infrared rays. However, it is week in mechanical strength. Spectral infrared emittance, thermal expansion coefficient, and mechanical strength of $Al_2TiO_5$-clay composites were studied to develop a material for far infrared radiators. The composites containing 10~50 mass% Jungsan clay had high emittance in the range of 2,000~500cm-1. The bending strength of the $Al_2TiO_5$-clay composites increased with increasing clay content. The $Al_2TiO_5$-clay composites with a clay content of 50mass% and heat-treated at $1,200^{\circ}C$ had a large strength for infrared radiators ; 86MPa. The average linear thermal expansion coefficient from $200{\sim}1,000^{\circ}C$ of the 50mass% jungsan clay containing compo sited heat-treated at $1,200^{\circ}C$ was lower than $3.87{\times}10-6/^{\circ}C$.