• Journal of Ocean Engineering and Technology
• /
• v.15 no.4
• /
• pp.60-65
• /
• 2001

Thermal spray coating is formed by a process in which melted particles flying with high speed towards substrate, then crash and spread on the substrate surface cooled and solidified in a very short time, Stacking of the particles makes coating. In this study, the exfoliation of $Al_2$O$_3$ and Ni-4.5wt.%Al thermally sprayed coating which were deposited by an atmospheric plasma spray apparatus are investigated using an AE method. A tensile test is conducted on notch specimens in a stress range below the elastic limit of substrate. The wave forms of AE generated from the three coating specimens can be classified by FFT analysis into two types which low frequency(type I waveform is considered to corresponds exfoliation of coating layers and type II waveform corresponds the plastic deformation of notch tip or the resultant fracture of coating. The fracture of the coating layers can estimate by AE event and amplitude, because AE features increase when the deformation generates.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.6
• /
• pp.343-348
• /
• 2015

In this paper, arc Zn thermal spray coating was carried out on the SS400 steel, and then various electrochemical characteristics and surface damage behavior of Zn thermal spray coating layer were analyzed. As the results, the potential of Zn thermal spray coating layer presented driving voltage above 300 mV compare to that of SS400 steel. The passivity characteristic in anodic polarization curve was not presented. It was adequate to as sacrificial anode material. In the surface damage after galvanostatic experiments, uniform corrosion tendency of Zn thermal spray coating layer was clearly observed with acceleration of the dissolution reaction. In conclusion, Zn thermal spray coating could be determined to represent the corrosion protection effect by stable sacrificial anodic cathodic protection method in seawater because it had sufficient driving voltage and uniform corrosion damage tendency for the SS400 steel.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.3
• /
• pp.196-200
• /
• 2015

In this paper, we fabricated flexible antenna radiator using the CNT/PVDF (carbon nanotube / polyvinylidene fluoride) composite film. We used polymer film as a matrix material for the flexible devices, and introduced CNTs for adding conductivity into the film resulting in obtaining performances of the antenna radiator. Spray coating method was used to form the CNT/PVDF composite radiator, and pattern formation of the radiator was done by shadow mask during the spray coating process. We investigated the electrical properties of the CNT/PVDF composite films with the CNT concentration, and also estimated the radiator performance. Finally we discuss the feasibility of the CNT/PVDF composite radiator for the flexible antenna.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.291-291
• /
• 2010

Organic solar cells have attracted much interest due to the potential advantage of the lightness, simple solution processing and flexibility. Until recently, the focus of organic solar cells research has been on optimization of material processing to improve the power conversion efficiency. However, area scaling is an important position for alternative to the market dominating solar cells. Spray deposition technologies have advantage of less material wastage and possibility of large scale photoactive area coating when compared with spin coating process. We investigated the performance of organic solar cells as a function of active area using two types of deposition process. The commonly used process is spin coating which can be fabricated organic materials deposition for devices. Spray deposition process compare with spin coating for large-area organic solar cells. The spray deposition organic layer shows excellent performance up to the active area of $4\;cm^2$ with the PCE of ~3.0 % under AM.1.5 simulated illumination with an intensity of $100mW/cm^2$. This indicates that the spray deposition process can be used as a mass production process for evaluating large-area organic solar cells.

• Plant Journal
• /
• v.6 no.4
• /
• pp.63-71
• /
• 2010

The best way to prevent the corrosion of piston rod is a selection of quality of the material and method of construction which minimize the porosity. The high velocity oxy fuel(HVOF) method, which generates lower porosity than existing plasma spray, was applied to ceramic laminated bond layer. Porosity percentage fell to bellow 2%, lower than that of plasma spray at 7%. Coating material of ceramic-coated main layer was selected as the $Cr_2O_3$ affiliation material, which is more dense than $Al_2O_3$ affiliation. To fill up the pores formed after the coating process, we sealed the bond layer and main layer. Sealing process was performed twice, once after the coating and once after the grinding. Upon the anti-corrosion test on the sealed sample and on the non-sealed sample, it is confirmed that the sealed sample was not corroded for 1,000 hours while the non-sealed sample was corroded within 48 hours.

• Journal of the Korean Society of Combustion
• /
• v.16 no.1
• /
• pp.58-65
• /
• 2011

Thermal spray technology has been used in many industrial application. Especially, thermal spray coating have been employed with the purposes of achieving better resistances in abrasion, heat and corrosion. In the previous studies on the thermal spray coating, thermal spray characteristics from the perspective of combustion engineering have not been investigated sufficiently, while the material characteristics of the coated substrates have been investigated widely. In this study, the effect of spray particles on the flame behavior was experimentally investigated. The amount of the injected particles was measured using the light scattering method and the temperature of the particles was estimated using a two-color method. Various flame-spray interactions were observed and it was found that the high temperature zone near the flame is elongated by particles density. Based on these results, the applicability of the light scattering method and the two-color method was discussed.

• Journal of the Korean Society for Precision Engineering
• /
• v.23 no.10
• /
• pp.88-95
• /
• 2006

Cold gas dynamic spray is a relatively new coating process by which coatings can be produced without significant heating during the process. Cold-spray uses supersonic gas flow to carry metallic powders to the substrate. Its low process temperature can minimize thermal stress and also reduce the deformation of the substrate. Most researches on cold-spray have focused on micro scale coating, but in this study macro scale deposition was conducted. Properties of aluminum layer by cold-spray deposition such as coefficient of thermal expansion (CTE), modulus of elasticity. hardness, and electric conductivity were measured. The results showed that properties of aluminum layer by cold-spray deposition were different from properties of pure aluminum and aluminum alloy.

• Journal of the Korean Ceramic Society
• /
• v.53 no.6
• /
• pp.628-634
• /
• 2016

The 8 wt% yttria($Y_2O_3$) stabilized zirconia ($ZrO_2$), 8YSZ, a typical thermal barrier coating (TBC) for turbine systems, was fabricated under different starting powder conditions and coating parameters by atmospheric plasma spray (APS) coating process. Four different starting powders were prepared by conventional spray dry method with different additive and process parameter conditions. As a result, large- and small-size spherical-type particles and Donut-type particles were obtained. Dense structure of 8YSZ coating was produced when small size spherical-type or Donut-type particles were used. On the other hand, 8YSZ coating with a porous structure was formed from large-size spherical-type particles. Furthermore, a segmented coating structure with vertical cracks was observed after post heat treatment on the surface of dense structured coating by argon plasma flame at an appropriate gun distance and power condition.

• Korean Journal of Materials Research
• /
• v.31 no.3
• /
• pp.172-180
• /
• 2021

In this study, using the plasma spray method, tensile and compression fatigue tests are performed in saline solution to examine the effect of Ti undercoat on corrosion fatigue behavior of alumina-coated specimens. The alumina-coated material using Ti in the undercoat shows better corrosion fatigue strength than the base material in the entire stress amplitude range. Fatigue cracking of UT specimens occurs in the recess formed by grit-blasting treatment and progresses toward the base metal. Subsequently, the undercoat is destroyed at a stage where the deformation of the undercoat cannot follow the crack opening displacement. The residual stress of the UT specimen has a tensile residual stress up to about 100 ㎛ below the surface of the base material; however, when the depth exceeds 100 ㎛, the residual stress becomes a compressive residual stress. In addition, the inside of the spray coating film is compressive residual stress, which contributes to improving the fatigue strength characteristics. A hardened layer due to grit-blasting treatment is formed near the surface of the UT specimen, contributing to the improvement of the fatigue strength characteristics. Since the natural potential of Ti spray coating film is slightly higher than that of the base material, it exhibits excellent corrosion resistance; however, when physiological saline intrudes, a galvanic battery is formed and the base material corrodes preferentially.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2005.11a
• /
• pp.183-184
• /
• 2005

Four different coatings deposited using cold spray process were studied with two different powder agglomerating techniques (spray d교 and evaporated powder) and using $TiO_2$ nano-sized powders with and without a 10wt% addition of ZnO. Characterization was performed by SEM, XRD and roughness test. Also the photocatalytic effect of the coatings was evaluated. Although the change of powder preparation techniques and the addition of ZnO into $TiO_2$ did not show appreciable variations in the surface morphology and Anatase phase transformation, it did show influence on the surface roughness of the coating, the highest roughness being found in the coatings made by spray powder prepared method. Regarding the photocatalytic effect it was observed that the using the spray dry coating and the addition of ZnO are promoter of purification at higher rates.