Hardness and surface property of coated gel materials are considerably different according to kinds(particle size/stabilized ion) of colloidal silica(CS), kinds of silanes, content ratio of silane versus CS, and reaction degree in sol solution. We report the properties of sol-gel coating materials in which the factors of reaction are kinds of CS, contents ratio of CS and MTMS, and reaction time of sol. The contact angles of the coated films obtained from the mixed CS system showed a little good relationship with MTMS content increase to those from HSA CS reaction system and the change of contact angle didn't have much effect on reaction time of sol. In the coating films obtained from HSA CS reaction system, the surface was much rough in case of that the content MTMS decreased and the reaction of sol kept long. The surface roughness of films obtained from the mixed CS reaction system showed similar tendency, though its degree was a little different. In synthesis of sol-gel coating materials, we could identify that choice of CS kinds and content ratio of CS and silane were important and it was desirable the reaction time of sol is not long.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.12
• /
• pp.28-32
• /
• 2010

Technical demands for aspheric glass lens formed in market increases its application from simple camera lens module to fiber optics connection module in optical engineering. WC is often used as a metal core of the aspheric glass lens, but the long life time is issued because it fabricated in high temperature and high pressure environment. High hard thin film coating of lens core increases the core life time critically. Diamond Like Carbon(DLC) thin film coating shows very high hardness and low surface roughness, i.e. low friction between a glass lens and a metal core, and thus draw interests from an optical manufacturing industry. In addition, DLC thin film coating can removed by etching process and deposit the film again, which makes the core renewable. In this study, DLC films were deposited on the SiC ceramic core. The process variable in FVA(Filtered Vacuum Arc) method was the substrate bias-voltage. Deposited thin film was evaluated by raman spectroscopy, AFM and nano indenter and measured its crystal structure, surface roughness, and hardness. After applying optimum thin film condition, the life time and crystal structure transition of DLC thin film was monitored.

• Nuclear Engineering and Technology
• /
• v.55 no.10
• /
• pp.3535-3542
• /
• 2023

Eutectic reactions of five kinds of Cr-coated Zr alloy cladding with different base materials (Zr-Nb-Sn alloy or Zr-Nb alloy), different coating thicknesses (6~22.5 mm), and different coating materials (Cr single layer or Cr/CrN bilayer) were studied using Differential Scanning Calorimetry (DSC). The DSC experiments demonstrated that the onset temperatures of the Cr single layer coated specimens were almost identical to ~1308 ℃, regardless of base materials or coating thicknesses. This study demonstrated that the Cr/CrN bilayer coated Zr-Nb-Sn alloy has a slightly (~10 ℃) higher eutectic onset temperature compared to the single Cr-coated specimen. The eutectic region characterized by post-eutectic microstructure proportionally increases with coating thickness. The post-eutectic characterization with different holding times at high temperature (1310-1330 ℃) reveals that progression of Zr-Cr eutectic requires time, and it dramatically changed with exposure time and temperature. The practical value of the time gain in non-instantaneous eutectic formation in terms of safety margin, however, seems to be limited.

• Journal of Power System Engineering
• /
• v.6 no.3
• /
• pp.24-30
• /
• 2002

The deformation and fracture behaviors of both Al2O3 and Ni 4.5wt.%Al plasma thermal spray coating were investigated by an acoustic emission method. Plasma thermal spray coating is formed by a process in which melted particles flying with high speed towards substrate, then crash and spread on the substrate surface cooled and solidified in a very short time, stacking of the particles makes coating. A tensile test is conducted on notch specimens in a stress range below the elastic limit of substrate. A bendind test is done on smooth specimens. The waveforms of AE generated from the both test coating specimens can be classified by FFT analysis into two types which low frequency(type I) and high frequency(type II). The type I waveform is considered to corresponds exfoliation of coating layers and type II waveform corresponds the plastic deformation of notch tip. The fracture of the coating layers can estimate by AE event and amplitude, because AE features increase when the deformation generates.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.57-62
• /
• 1995

The coating condition of reproducible anti-reflective coating film and the light transmittance characteristics of the prepared anti-reflective coating glass were investigated as a study for the preparation of single-layer anti-reflective coating glasss. In case of coating with the sol in which the solvent was substituted with the ethanol with the addition of 0.1 mol HNO3, the coated glass showed the minimum value of the refractive index of 1.464, light transmittance of 94.2% at 550nm standard wavelength which is 3.2% higher than that of the parent glass, and the reflectance in the entire wave range of visible light. The refractive index represented its minimum at the sol concentration of 1.0 mol per 100mols of water and the higher the sol concentration, the higher the refractive index, resulting in the decrease of the light transmitance. The production condition of the reproducible anti-reflective coating on glass with the maximum transmittance of 94.2% was 4cm/min of withdrawal speed, 40$0^{\circ}C$ and 1 hour of heat treatment temperature and time, resulting in the film thickness of 94nm.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.97.2-97.2
• /
• 2018

This study formed a hard TiAlSiWN coating layer using Ti, Al, Si and W raw powders that were mechanically alloyed and refined. The TiAlSi and TiAlSiW coating targets were fabricated using a single PCAS process in a short time with the optimal sintering conditions. The coating targets were deposited on the WC substrate by forming coating layers using TiAlSiN and TiAlSiWN nitride nano-composite structures with an AIP process. The properties of the nitride nano-composite coating layers were compared according to the addition of W. The microstructure of the nitride nano-composite coating layer was analyzed, focusing on the distribution of the crystalline phases, amorphous phases ($Si_3N_4$), and growth orientation of the columnar crystal depending on the addition of W. The mechanical properties of the coating layers were exhibited a hardness of approximately $3,000kg/mm^2$ and adhesion of about 117.77N in the TiAlSiN. In particular, the TiAlSiWN showed excellent properties with a hardness of more than $4,300kg/mm^2$ and an adhesion of about 181.47N.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.1-5
• /
• 2018

As structural materials, magnesium (Mg) alloys have been widely used in the fields of aviation, automobiles, optical instruments, and electronic products. There are few studies on the effect of coating conditions on the compositional variation during the formation process of the conversion coatings. Rare-earth based conversion coating on AZ91 magnesium alloy was prepared in ceric sulfate and hydrogen peroxide contained solution. The element composition and valence as well as their distribution in the coating were analyzed with energy dispersive X-ray spectroscopy (EDS), Electron probe micro-analyzer (EPMA), X-ray photoelectron spectroscopy (XPS). The effect of treating process on the element composition were also studied. It was found that the conversion coating surface consists of Mg, Al, O, Ce, and the weight content of Ce in the coating was affected by the treating solution concentration and immersion time; the Ce element was distributed in the coating non-uniformly and existed in the form of $Ce^{+3}$ and $Ce^{+4}$, while the O element existed in the form of $OH^-$, $O^{2-}$, $H_2O$. Based on microscopic analysis results, the electrochemical deposition mechanism on the micro-anode and micro-cathode in the process of the coating growth was suggested.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.45-45
• /
• 2014

The importance of magnesium alloys has significantly increased due to their low density, high strength/weight ratio, very good electromagnetic shielding features and good recyclability. However, unfortunately, Mg alloys are very susceptible to corrosion due to their high chemically activities (= -2.356 V vs. NHE at $25^{\circ}C$), hence, most commercial Mg alloys require corrosion protective coatings. Organic coating such as painting, powder coating and electrophoretic deposition of paint (E-paint) is typically used in the final stages of the coating process of Mg alloys. In this study, effect of pre-immersion time on the deposition of E-paint on AZ31 Mg alloy was investigated. It was found that during pre-immersion time, AZ31 Mg alloy rapidly reacts with E-paint solution and paint can be self-deposited on the AZ31 surface without applying of electric current. The pore size on the E-painted AZ31 Mg alloy increased with increasing pre-immersion time from 0 to 5 min. Both adhesion and corrosion resistance of E-painted AZ31 Mg alloy decreased with increasing pre-immersion time. The best E-paint AZ31 Mg alloy, which showed stronger adhesion after water immersion test and good corrosion resistance, was started to deposit after 5 s of pre-immersion time.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.4
• /
• pp.39-46
• /
• 2004

This experiment was carried out to study on the effect of surface coating on thermal insulation of farm structures to improve thermal resistance and reflective effect of solar radiation. Nine different types of experimental specimen were compared in the temperature variations of inside and outside; A, B, C, D. E and F types are box container and G, H and I types are drum container. The size of these containers is $1,500{\times}2,000{\times}2,500$ mm and ${\varphi}$ $280{\times}330$ mm, respectively. Specimen of 3-type box(A, B, C) is galvanized steel sheet of thickness 0.45 mm. D, E and F types are sandwich panel of the thickness 50 mm inserted with urethane, glass wool and polystyrene form, respectively. G, H and I types are paint pot using in general. The surface of A. D, E, F and I types didn't any treatment, B, C and G types were treated with thermal insulation coating on the outside surface(B, G) or the inside and outside surface(C). And H type was treated with water paint coating on the only outside surface. In general, the experimental results showed the following tendencies; In case of A, B and C types. it was found that the thermal insulation effect of types coated with thermal insulation coating was improved remarkably than that of no treatment. And the thermal insulation effect between steel sheet and sandwich panel type was nearly similar There was not a significant difference of thermal insulation effect between thermal insulation coating and water paint coating. In time of drum container filled with rough rice, The difference of heat transfer tendency and temperature variation among surface treatments was nearly similar that of box types of galvanized steel sheet. And there was time lag about 6 hours between the temperature of middle part of rice and that of inside or outside surface.

• Clean Technology
• /
• v.7 no.1
• /
• pp.65-74
• /
• 2001

Modified dip-coating method 8.3 times shorten in solution volume-coated and 83.3 times in coating time than existing dip-coating method. Coating weight increased nearly 2~3 times. So modified dip-coating method is evaluated that it is economic and has a efficiency. When we make an experiment in coated $LaCoO_3$ on ceramic monolith in modified dip-coating method which use 2 coating applications with relative viscosity $0.006202kg{\cdot}m/sec$, it showed a superior reaction at 88.56mg per ceramic unit gram in NO-CO reaction(optimum coating amount). When we make an experiment in the same size of ceramic filter cell with different conditions 100, 200cell per square inch, the result in low temperature($200^{\circ}C{\sim}350^{\circ}C$), 200cell3 per square inch is 6~23% higher in NO reduction and 11% in CO oxidation than 100cell per square inch. It is because the more the number of cells in the ceramic filter increase, the more catalytic surface area is expanded.