• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.27-31
• /
• 2006

We propose a replication method to solve the problem of large percent failure in texturing processes of coated conductors. This problem is due to the individual texturing process for each coated conductor that is very long tape having no single defect spot. We tested two different methods of replication process that are based on a well-textured Ni template. First method has structure of Ni/BaO/STO/$CeO_2$/SmBCO/Ag. So BaO layer is dissolved in water that we can separate STO/$CeO_2$/SmBCO/Ag layers. In this processing, the property of STO is conserved but the superconductivity of SmBCO is deteriorated. So we can consider another method. Second method has structure of template(STO)/BaO/STO/Pt/STO. After dissolving BaO then we deposited YBCO. The result of these experiments showed the feasibility of replication.

• Carbon letters
• /
• v.7 no.4
• /
• pp.259-265
• /
• 2006

Carbon-coated $TiO_2$ was prepared by $CCl_4$ solvent mixing method with the different heat treated temperatures (HTTs). Since the carbon layers derived from pitch on the $TiO_2$ particles were porous, the carbon-coated $TiO_2$ sample series showed a good adsorptivity. The values of BET surface areas measured were shown independently on the HTTs. The surface states by SEM present to the characterization of porous texture on the carbon-coated $TiO_2$ sample and carbon distributions on the surfaces. From XRD data, PT700 and PT750 were shown the X-ray diffraction patterns of the anatase $TiO_2$, but PT800 and PT850 were kept anatase-type structure even after heating at $800^{\circ}C$, though small amount of the rutile-type structure appears. The results of EDX microanalyses were observed for each sample show the spectra corresponding to almost all samples similar to C, O and Ti elements with an increase of HTTs. Finally, the excellent photoactivity of carbon-coated $TiO_2$ (especially, PT700 and PT750) could be attributed to the homogeneous coated carbon on the external surface and the structural anatase phase.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 1999.04a
• /
• pp.1-6
• /
• 1999

A study was made to determine the effect of plastic pigment on the coating structure and printability of coated paper. Three basic plastic pigments were investigated such as solid-bead type of plastic pigment, binder type of plastic pigment and hollow type of plastic pigment. In the systems investigated, it was observed that particle shape and structure of plastic pigment had influenced on the rheology of coating color, the state of packing, and the properties of coated paper. The materials investigated were restricted to plastic pigments commonly uesd in paper coating formualtion. Inorganic pigments used in this research were kaolin clay which is platelets and calcium carbonate which is rhombic. Three kinds of plastic pigments were blended in the color made up with two inorganic pigments, respectively. The combination of pigments were carried out (1) to determined the effect of paticle structure of plastic pigment on the state of dispersion of coating color, (2) to observe the effect of temperature of calender on the property of coated paper prepared with plastic pigment. The data indicated that binder and hollow type of plastic pigment had the best results on improving the properties of coated paper such as paper gloss, opacity and air permeability ect. and solid-bead type of plastic pigment in the next place.

• 유체기계공업학회:학술대회논문집
• /
• 2006.08a
• /
• pp.375-376
• /
• 2006

Turbulent structure of a boundary-layer over a flat plate coated with micro riblet film(MRF) has been investigated experimentally. The turbulent structure was visualized using a dynamic particle image velocimetry (Dynamic PIV) system. We identified the vortex structures from 2-D velocity field data by applying the complex eigenvalue definition. The velocity field images acquired by using the complex eigenvalue definition showed the whole 2-D vortex structures clearly. In addition, the spatial distributions of small-scale vortices as well as large-scale vortices were obtained with high accuracy. The difference of vortex structures between the MRF coated flat plate and the smooth flat plate was analysed in detail. With varying upstream flow speed, the characteristics of vortex structure over the MRF coated flate plate was compared with those over the smooth flat plate.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.99-104
• /
• 2003

TiN coated films show a good mechanical properties, high thermal properties and wear, erosion and corrosion resistance and are widely used as a coating materials in tools, ornaments, parts and semiconductors. In spite of these good properties, the fracture of TiN coated films occur during use. The fracture of TiN thin films is related to their microstructure. Especially, the life of TiN coated layer is related to the texture of the TiN films. One researcher suggested that the corrosion and erosion resistance of the TiN thin films is related to a uniform and dense structure of films. In this study, we studied the relationships between textures and friction coefficient, erosion and corrosion in TiN coated films. The flatness of (115) texture surface of TiN thin films is flatter than that of (111) texture surface. The friction coefficient of (115) texture surface of TiN thin films is similar with that of (111) texture surface. The wear resistance of (115) texture surface of TiN thin films is better than that of (111) texture surface. The erosion and corrosion resistance of (115) texture surface of TiN thin films is better than that of (111) torture surface. As well as texture, the wear, erosion and corrosion of TiN thin films has to consider defects such as pinholes, cracks, surface roughness and open columnar structure. The life of TiN coated products is influenced by the properties of wear, erosion, and corrosion resistance of TiN thin films and is related to texture of TiN coated films, density of pinholes and cracks, density of structure, and surface flatness.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.295-301
• /
• 2010

Multi shell graphite coated Ag nano particles with core/shell structure were successfully synthesized by pulsed wire evaporation (PWE) method. Ar and $CH_4$ (10 vol.%) gases were mixed in chamber, which played a role of carrier gas and reaction gas, respectively. Graphite layers on the surface of silver nano particles were coated indiscretely. However, the graphite layers are detached, when the particles are heated up to $250^{\circ}C$ in the air atmosphere. In contrast, the graphite coated layer was stable under Ar and $N_2$ atmosphere, though the core/shell structured particles were heated up to $800^{\circ}C$. The presence of graphite coated layer prevent agglomeration of nanoparticles during heat treatment. The dispersion stability of the carbon coated Ag nanoparticles was higher than those of pure Ag nanoparticles.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.33 no.3
• /
• pp.29-36
• /
• 2001

This paper was made to evaluate the effect of the blending ration of GCC and No. 1 clay on the printability by investigating the structure of pore such as the pore rate, the number of pores, pore size and distribution of coated paper. The coated structure is mainly depended on the results of correlation between pigment and binder. It means that the structure of the pore occurred is chiefly affected by the blending ratio of GCC and No. 1 clay. This physical properties of the pore have a close relation with ink set-off associated with the drying rate and the penetration in ink into base paper and with printing gloss. Therefore it was needed to find out how the pore structure and the printability will be changed by modifying the blending ratio of GCC and No. 1 clay to vary the pore structure of coated paper. Below are the results of measurement: As the blending ratio of clay going up, water retention, sedimentation volume. smoothness, and paper gloss were increased, but relatively brightness and opacity were decreased. Pore rate was the highest at the blending ratio of No. 1 clay to GCC, 70:30. In this case, average pore radius was also increased. Ink receptivity and K&N ink receptivity were improved with the increase of the blending ratio of GCC, where was, ink setting was vice versa. No difference was observed in the weight of ink, but ink repellance decrease with the decrease of blending ratio of GCC.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.6
• /
• pp.391-400
• /
• 2002

Corrosion characteristics of Ti, Ti/Cr coated and plasma-nitrided surface for stainless steel containing Ti have been studied. Stainless steels containing 0.09-0.92wt% Ti were fabricated by using vacuum furnace and solutionized for 1hr at 105$0^{\circ}C$. Ti and Cr coatings were done on solutionized stainless steel surface by EB-PVD. The Ti coated specimen were coated by Cr and were nitrided by plasma at $450^{\circ}C$ for 5hr. Microstructure and phase analysis were performed using SEM, OM and EDX. Corrosion behavior of the coated specimen was investigated by electrochemical test. The coated surface was of fine columnar structure. The Ti/Cr coated surface was denser than the Ti coated and the Ti coated-nitrided surfaces. The corrosion and pitting potential increased in proportion to the Ti content, coating temperature, coating thickness and formation of stable oxide film. The current density in active and passive region decreased in the case of Ti/Cr coated sample and Ti coated-nitrided samples. Especially the plasma nitrided specimen after Ti coating have a good corrosion resistance compared with the Ti coated specimen. The number and size of pits decreased as Ti content of matrix increased.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.1
• /
• pp.89-98
• /
• 2003

Corrosion characteristics of Ti, Ti/Cr coated and plasma-nitrided surface for stainless steel containing Ti have been studied. Stainless steels containing 0.09-0.92wt% Ti were fabricated by using vacuum furnace and solutionized for 1hr at $1050^{\circ}C$. Ti and Cr coatings were done on solutionized stainless steel surface by EB-PVD. The Ti coated specimen were coated by Cr and were nitrided by plasma at $450^{\circ}C$ for 5hr Microstructure and phase analysis were performed using SEM, OM and EDX. Corrosion behavior of the coated specimen was investigated by electrochemical test. The coated surface was of fine columnar structure. The Ti/Cr coated surface was denser than the Ti coated and the Ti coated-nitrided surfaces. The corrosion and pitting potential increased in proportion to the Ti content, coating temperature, coating thickness and formation of stable oxide film. The current density in active and passive region decreased in the case of Ti/Cr coated sample and Ti coated-nitrided samples. Especially the plasma nitrided specimen after Ti coating have a good corrosion resistance compared with the Ti coated specimen. The number and size of pits decreased as Ti content of matrix increased.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.1 no.1
• /
• pp.71-78
• /
• 2002

Since the early 1980's the use of zinc-aluminum alloy-coated steel sheet(Galvalume) for vehicular corrosion protection has increased drastically. It is consisting of 55%Al-43.4% Zn-1.6%Si. Galvalume has a good corrosion resistance, heat reflectivity and shiny appearance, which has a dendritic structure of alloy layer. It has a good corrosion resistance due to dendritic structure. But, this also has a weak point against moisture during long period of transportation as sheeted and or coiled without any relation of chromating on the surface of steel sheet or not because of high humidity and temperature. Here, We studied the corrosion mechanism by the moisture.