• Corrosion Science and Technology
• /
• v.6 no.1
• /
• pp.24-28
• /
• 2007

Alumina coated SiC whiskers were prepared by homogeneous precipitation of aluminum sulfate. The Si3N4 composites reinforced with coated SiC whiskers were fabricated by hot-pressing at $1800^{\circ}C$ for 2 h under an $N_{2}$ atmosphere of 0.1 MPa to examine the effects of coated whiskers on the mechanical properties of SiC whisker reinforced $Si_{3}N_{4}$ composite. By the addition of alumina coated SiC whiskers instead of as received ones, the fracture toughness of composite was about 6.7 $MPam^{1/2}$ which was slightly lower than as received SiC whisker reinforced composite. This result seems to be caused by the fact that the crack deflection and whisker pull-out were decreased. Thus, alumina coated SiC whiskers were considered to form relatively strong interface bond with $Si_{3}N_{4}$ matrix.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.4
• /
• pp.16-18
• /
• 2007

We report the results of MOD-processed YBCO coated conductors on the IBAD-MgO template. The precursor solution was coated on the $CeO_2-buffered$ IBAD-MgO template using a slot-die coating method, calcined at a temperature of $550^{\circ}C$, and fired at high temperatures for 2.5 h in a reduced oxygen atmosphere. The $J_C$ value of YBCO coated conductors was found to be very sensitive to the microstructure, and thus higher $J_C$ value could be achieved when the in-plane texture was higher and the difference in $T_{C,zero}$. was negligible. Optimally processed YBCO coated conductor exhibited $J_C$ value of $0.75MA/cm^2$ at 77 K in self-field, which might be due to somewhat depressed $T_{C,zero}$ of 87.3 K caused by possible $Sm^{3+}$ substitution on the $Ba^{2+}$ site.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.176-179
• /
• 2000

In the recognition of the gases using the quartz crystal microbalance (QCM) coated with the film materials, it is important to obtain the recognition ability of gases, and the stability of film coated above the QCM. Especially, the thickness of film coated above the QCM is decreased according with the using circumstance and time of QCM gas sensor. Therefore, the sensing chararcteristics of film is changed with these. In this paper, we coated the lipid PC (Phosphatidyl Choline) materials varing with the blended amount of PVC(Poly Vinyl Chloride) and solution (Tetra Hydrofan:THF) above QCM to obtain the stability of lipid PC film. QCM gas sensors coated with film materials were measured the frequency change in the chamber of stationary gas sensing system injected 1-hexane, ethyl acetate, ethanol and benzene of $20{\mu}{\ell}$, respectively. We obtained the principal component analysis (PCA) from the frequency change due to the absorption of gas. Also, we measured the degradation characteristics of QCM gas sensor to show the properties of stability.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.295-301
• /
• 2010

Multi shell graphite coated Ag nano particles with core/shell structure were successfully synthesized by pulsed wire evaporation (PWE) method. Ar and $CH_4$ (10 vol.%) gases were mixed in chamber, which played a role of carrier gas and reaction gas, respectively. Graphite layers on the surface of silver nano particles were coated indiscretely. However, the graphite layers are detached, when the particles are heated up to $250^{\circ}C$ in the air atmosphere. In contrast, the graphite coated layer was stable under Ar and $N_2$ atmosphere, though the core/shell structured particles were heated up to $800^{\circ}C$. The presence of graphite coated layer prevent agglomeration of nanoparticles during heat treatment. The dispersion stability of the carbon coated Ag nanoparticles was higher than those of pure Ag nanoparticles.

• Nuclear Engineering and Technology
• /
• v.55 no.10
• /
• pp.3535-3542
• /
• 2023

Eutectic reactions of five kinds of Cr-coated Zr alloy cladding with different base materials (Zr-Nb-Sn alloy or Zr-Nb alloy), different coating thicknesses (6~22.5 mm), and different coating materials (Cr single layer or Cr/CrN bilayer) were studied using Differential Scanning Calorimetry (DSC). The DSC experiments demonstrated that the onset temperatures of the Cr single layer coated specimens were almost identical to ~1308 ℃, regardless of base materials or coating thicknesses. This study demonstrated that the Cr/CrN bilayer coated Zr-Nb-Sn alloy has a slightly (~10 ℃) higher eutectic onset temperature compared to the single Cr-coated specimen. The eutectic region characterized by post-eutectic microstructure proportionally increases with coating thickness. The post-eutectic characterization with different holding times at high temperature (1310-1330 ℃) reveals that progression of Zr-Cr eutectic requires time, and it dramatically changed with exposure time and temperature. The practical value of the time gain in non-instantaneous eutectic formation in terms of safety margin, however, seems to be limited.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.22-26
• /
• 2006

Total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcination process, and XRD measurement shows that $BaF_2,\;CuO,\;and\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcination was measured to be ${\sim}2.8$ um by applying slot-die coating method. In particular, addition of Samarium shows critical current of Ic=226 A/cm-w($Jc=3.4\;MA/cm^2$). Also discussed are recent developments in the reel-to-reel processing using F-free Y & Cu precursor solutions. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solutions in MOD process.

• Particle and aerosol research
• /
• v.10 no.4
• /
• pp.177-182
• /
• 2014

In this study, nickel-coated aluminum (Ni/Al) powders were synthesized for the utilization of energetic applications. Oxide materials present at the surface of Al powders of $45{\mu}m$ in averaged size were removed by using sodium hydroxide(NaOH) solution which is used for controlling pH. Nickel material is coated into the surface of oxide-removed Al powders by electroless-plating process. The microstructure of fabricated Ni/Al powders shows that nickel layers with a few hundreds nm were very homogeneously formed onto the surface of Al powders. The oxidation behavior of Ni/Al exihibit somewhat faster oxidation rate than that of pure Al with surface oxidation. Also, the higher exothermic reaction was observed from the Ni/Al powders. From the result of this, nickel coating is very promising method to obtain highly reactive and safe Al powders for energetic applications.

• Korean Journal of Metals and Materials
• /
• v.47 no.9
• /
• pp.550-557
• /
• 2009

In this study, bronze or SUS304 powders blended with 10 wt.% diamond particles were used to prepare metal/diamond composite materials deposited by cold spraying. The effects of matrix metal, diamond partical size, and the thickness of the Ni coating on the diamond were studied on Al 6061 substrate. The results showed that the hardness of the metal/diamond composite coating layers was higher than that of the same composite materials when using the sintering method. The fraction of diamond content in the coated layer increased when the metal matrix was soft. When the size of the diamond particles was reduced, the fraction of the diamond particles increased. In addition, in the case of diamond with a thicker Ni-coated layer, the fracturing of diamonds was mitigated in the composite coating layers.

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.7-7
• /
• 2006

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.68-68
• /
• 2008