MI(Magneto-Impedance) sensor which is made by thin films has significantly high detecting sensitivity in weak magnetic field. It also has a merit to be able to build in low power system. Its structure is simple, which makes it easier to prepare a miniature. In this study, its magnetic permeability and anisotropy field(H$\sub$k/) as a function of a thickness of sputtered amorphous CoZrNb thin film with high saturation magnetostriction and excellent soft magnetic property are investigated. In order to make a uniaxial anisotropy, thin film was subjected to post annealing with a static magnetic field with 1KOe intensity at 250, 300, and 320$^{\circ}C$ for 2 hour. Anisotropy field(H$\sub$k/)of thin film is measured by using MH loop tracer. Its magnetic permeability of thin film is measured over the frequency range from 1 MHz to 750MHz. It has shown that the magnetic permeability of amorphous CoZrNb thin film is decreased due to the skin effect with increasing a thickness of CoZrNb thin film, and hence its driving frequency is lowered.

• Journal of Magnetics
• /
• v.11 no.3
• /
• pp.130-134
• /
• 2006

The microwave power absorption for the patterned CoNbZr magnetic film has been investigated by coplanar waveguide method. The power absorption peaks of the patterned CoNbZr film (50 ${\mu}m$ ${\times}$ 2 mm ${\times}$ 2 ${\mu}m$), were observed at around 5.7 GHz. The observed resonance peak was in good agreement with calculated ferromagnetic resonance frequency including magnetic shape anisotropy effects. Compared with the coplanar waveguide without a magnetic film, the characteristic impedance of patterned film was shown to be increased. This resulted from the large increment of inductance up to 33 % without any significant changes of the capacitance.

• Current Applied Physics
• /
• v.18 no.12
• /
• pp.1523-1527
• /
• 2018

The thermal stability, magnetic and magnetocaloric properties of $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) melts-pun ribbons were studied. The relatively high reduced glass transition temperature ($T_{x1}/T_m$ > 0.60) and low melting point ($T_m$) resulted in excellent glass forming ability (GFA). The Curie temperatures ($T_C$) of melt-spun amorphous ribbons $Gd_{55}Co_{35}M_{10}$ for M = Si, Zr and Nb were 166, 148 and 173 K, respectively. For a magnetic field change of 2 T, the values of maximum magnetic entropy change $(-{\Delta}S_M)^{max}$ for $Gd_{55}Co_{35}Si_{10}$, $Gd_{55}Co_{35}Zr_{10}$ and $Gd_{55}Co_{35}Nb_{10}$ were found to be 2.86, 4.28 and $4.05J\;kg^{-1}K^{-1}$, while the refrigeration capacity (RC) values were 154, 274 and $174J\;kg^{-1}$, respectively. The $RC_{FWHM}$ values of amorphous alloys $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) are comparable to or larger than that of $LaFe_{11.6}Si_{1.4}$ crystalline alloy. Large values of $(-{\Delta}S_M)^{max}$ and RC along with good thermal stability make $Gd_{55}Co_{35}M_{10}$ (M = Si, Zr and Nb) amorphous alloys be potential materials for magnetic cooling operating in a wide temperature range from 150 to 175 K, e.g., as part of a gas liquefaction process.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.694-698
• /
• 1988

Pb(Zr, Ti)O3-Pb(Co, Nb)O3 systems were investigated by x-ray diffraction method. System contains rhombohedral, tetragonal, and pseudocubic structures at room temperature. Crystal symmetry was changed from 4-fold symmetry to 3-fold symmetry by substituting Pb(Co1/3, Nb2/3)O3 ; PCN, to Pb(Zr0.52, Ti0.48)O3 ; PZT. As the substituted PCN concentration was increased, an increase in a-axis direction and a decrease in c-axis in the perovskite structure were occurred simultaneously, so that the crystal symmetry was changed into such way. In the higher sinteringtemperatures, the unit cell distortions occurred rather in the lower substitution range of PCN. The ferroelectric properties were maximized at the region that tetragonal and rhombohedral or pseudocubic structures were coexist.

• Journal of the Korean Ceramic Society
• /
• v.34 no.9
• /
• pp.915-920
• /
• 1997

Tetragonal ZrO2 polycrystal (TZP), consisted of 90.24 mol% ZrO2-5.31 mol% Y2O3-4.45 mol% Nb2O5, were prepared using hot-press and mechanical properties and high-temperature degradation were investigated. The specimen, hot-pressed for 1 h at 140$0^{\circ}C$ in Ar atmosphere, exhibited flexural strength of 1010 MPa and fracture toughness of 7.5 MPam1/2 and experienced no low-temperature degradation below 40$0^{\circ}C$. However, as aged for 100h at temperatures higher than 40$0^{\circ}C$, TZP was suffered by high-temperature degradation due to an extensive cavitation caused by the oxidation of carbon. XPS observation revealed that the carbon incorporated in TZPs during hot-pressing exists as either an ether-type CO or a carbonyl-type C=O. Despite of the high-temperature degradation of t-ZrO2 co-doped with Y2O3 and Nb2O5, its flexural strength and fracture toughness were superior to those of the commercial 3 mol% Y2O3-TZP hot-pressed under the identical condition as determined before and after the aging treatments.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1991.05a
• /
• pp.79-80
• /
• 1991

• Proceedings of the Korean Magnestics Society Conference
• /
• 2001.10a
• /
• pp.56-57
• /
• 2001

• Proceedings of the Korean Magnestics Society Conference
• /
• 2005.12a
• /
• pp.152-153
• /
• 2005

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.05a
• /
• pp.66-67
• /
• 1994