• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.4
• /
• pp.344-351
• /
• 2002

The purpose of this study is to compare tensile bond strength between Cr-Co alloy and three denture base resins after surface treatment. Following the manufacturer's instructions, 180 bonded specimens were made from three denture base resins (Lucitone 199. Paladent 20. POSS resin) and three surface treatment methods (sandblasting. metal primer. silicoating) 20 samples were made in each group and a half was ther-mocycled 1000 times between $5^{\circ}C$ and $55^{\circ}C$. The tensile bond strength was measured using an Instron with 5mm/min crosshead speed. Data was analyzed with one-way ANOVA, T-test and Duncan test. The results were as follows : 1. Samples with metal primer coating had significantly high tensile bond strength than the other surface treated groups (p<.05). Significantly low tensile bond strength was shown in sand blasted groups (p<.05). 2. No significant difference was observed in metal primer coating groups before and after ther-mocycling (p>.05) 3. Tensile bond strength was decreased in silicoated samples after thermocycling (p<.05). 4. Of the surface treated groups with metal primer, Lucitone 199 had the greatest bond strength and POSS resin and Paladent 20 were followed (p<.05). 5. Of the surface treated groups with silicoating, POSS resin and Lucitone 199 had greater bond strength than Paladent 20 (p<.05).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.1
• /
• pp.73-79
• /
• 2011

Purpose of this experiment is to evaluate the effect of titanium on the castability when the titanium is added to the Co-Cr alloy. Raw materials Cobalt, Chrome, Molybdenum, Silicon, Manganase, Carbon, Nitrogen, Titanium were weighted and prepared. $Biosil^F$ (Degudent, Germany) was the control group. To the experimental group, different weight percent of titanium was added from 1 wt% to 4 wt%. The wax pattern is $30{\times}40$ cm in size, rectangular in shape and has total of 160 grids. Centrifugal machine (Neutrodyne Easy Ti: Manfredy) was used for casting. For evaluation of the castability, the number of complete grids was counted by visual inspection and X-ray inspection. The test showed similar castability with the control group in the titanium addition of 1 wt% to 3 wt%. The titanium addition of 4 wt% showed poor result. With titanium lower than 4 wt%, the experiment metals showed proper castability with high expectation of successful clinical use.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.10
• /
• pp.448-453
• /
• 2017

The purpose of this study was to compare the marginal discrepancy of coping crowns according to manufacturing method and materials by using the CAD/CAM system to compare the optimum manufacturing method and materials. The coping crowns were fabricated by using manufacturing methods and materials, and marginal fit was measured using the replica technique. For comparative analysis of manufacturing methods and materials, analysis of variance was performed. One-way ANOVA was performed to compare and analyze different mean values. For the milling method of the alloy, 114.6 was obtained for the MM group, 111.4 for the MS group, 67.2 for the MSC group, and 50.9 for the MSS group, respectively, using the milling/sintering method. In the milling/sintering method of ceramic, 35.6 and 36.3, respectively, were obtained for the SLME group and SLMR group, respectively. However,there was a significant difference according to the material. The milling/sintering method of the ceramic material gave the lowest value, and it was verified by the optimal method. However, marginal discrepancy of coping crowns fabricated using the CAD/CAM system is applicable to the clinic since it corresponds to acceptable numerical values in clinical practice.