• 한국세라믹학회지
• /
• 제51권4호
• /
• pp.367-373
• /
• 2014

In this study, the reducing agent hydrazine and precipitator NaOH were used with $NiCl_2$ as a starting material in order to compound Ni-based material with spherical nano characteristics; resulting material was used as an anode for SOFC. Synthetic temperature, pH, and solvent amounts were experimentally optimized and the synthesis conditions were confirmed. Also, a 0 ~ 0.15 mole ratio of metal(Co, Fe) was alloyed in order to increase the catalyst activation performance of Ni and finally, spherical nano $Ni_{(1-x)}-M_{(x=0{\sim}0.15)}$(M = Co, Fe) alloy materials were compounded. In order to evaluate the catalyst activation for hydrocarbon fuel, fuel gas(10%/$CH_4$+10%/Air) was added and the responding gas was analyzed with GC(Gas Chromatography). Catalyst activation improvement was confirmed from the 3% hydrogen selectivity and 2.4% methane conversion rate in $Ni_{0.95}-Co_{0.05}$ alloy; those values were 4.4% and 19%, respectively, in $Ni_{0.95}-Fe_{0.05}$ alloy.

• Journal of Magnetics
• /
• 제16권4호
• /
• pp.440-443
• /
• 2011

In this study, we investigated the glass-forming ability (GFA) and magnetocaloric effect (MCE) of $Gd_{55}Co_{20}Al_{23}Si_2$ bulk glassy alloy. It is found that the addition of 2 at% Si is effective for extension of the supercooled liquid region (${\Delta}T_x$), the ${\Delta}T_x$ is 55 K for the $Gd_{55}Co_{20}Al_{25}$ glassy alloy, and increases to 79 K for the $Gd_{55}Co_{20}Al_{23}Si_2$ alloy. As a result, $Gd_{55}Co_{20}Al_{23}Si_2$ glassy alloys with diameters up to 5 mm were successfully synthesized. The alloys also exhibit large MCE, i.e., the magnetic entropy change (${\Delta}S_m$) of 8.9 J $kg^{-1}\;K^{-1}$, the full width at half maximum of the ${\Delta}S_m$ (${\delta}T_{FWHM}$) of 87 K, and the refrigerant capacity (RC) of 774 J $kg^{-1}$.

• Journal of Electrochemical Science and Technology
• /
• 제1권1호
• /
• pp.31-38
• /
• 2010

In this study, we have demonstrated the fine structure effect of PdCo electrocatalyst on oxygen reduction reaction activity with different alloy composition and heat-treatment time. In order to identify the intrinsic factors for the electrocatalytic activity, various X-ray analyses were used, including inductively coupled plasma-atomic emission spectrometer, transmission electron microscopy, X-ray diffractometer, and X-ray Absorption Spectroscopy technique. In particular, extended X-ray absorption fine structure was employed to extract the structural parameters required for understanding the atomic distribution and alloying extent, and to identify the corresponding simulated structures by using FEFF8 code and IFEFFIT software. The electrocatalytic activity of PdCo alloy nanoparticles for the oxygen reduction reaction was evaluated by using rotating disk electrode technique and correlated to the change in structural parameters. We have found that Pd-rich surface was formed on the Co core with increasing heating time over 5 hours. Such core shell structure of PdCo/C showed that a superior oxygen reduction reaction activity than pure Pd/C or alloy phase of PdCo/C electrocatalysts, because the adsorption energy of adsorbates was apparently reduced by lowering the dband center of the Pd skin due to a combination of the compressive strain effect and ligand effect.

• 대한치과기공학회지
• /
• 제36권3호
• /
• pp.149-158
• /
• 2014

Purpose: Dental casting Co-Cr-Mo based alloys of five kinds of ingot type and two kinds of shot type were analyzed the melting processes with heating time of high frequency induction centrifugal casting machine using infrared thermal image analyzer. Methods: When Co-Cr-Mo based alloys were put about 30g/charge in the ceramic crucible of high frequency induction centrifugal casting machine and heat, Infrared thermal image analyzer and IR thermometer indicated these alloys in the crucible were set and operated. Results: The melting temperatures of alloys measuring infrared thermal image analyzer were deviated ${\pm}10^{\circ}C$ compared to those of manufacturing company. On the other hand, the melting time of alloys were differently appeared with the shape of alloys(ingot and shot type). Conclusion: The melting temperatures of dental Co-Cr-Mo based alloys were measured the degree of $1,360{\sim}1410^{\circ}C$ and the heating time with the alloys of ingot and shot type were deviated ${\pm}10sec$.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2002년도 춘계연구발표회 논문개요집
• /
• pp.86-87
• /
• 2002

• 한국주조공학회지
• /
• 제34권2호
• /
• pp.60-66
• /
• 2014

A Zr-based amorphous alloy specimen was produced by vacuum die casting process. The salt spray test was carried out using the specimens in the as-cast, $Al_2O_3$ and $ZrO_2$ particle blasted state. Using these specimens, the SEM-EDX and XRD analyses, DSC measurement and bending strength test were conducted. After the salt spray test, the specimens were not experienced phase change and thermal characteristics of the alloys were remained unchanged. In the as-cast specimen, corrosion products were not observed. However, in the $Al_2O_3$ particle blasted specimen, pitting corrosion occurred and the detected corrosion products were $ZrCl_2$ and $NaZrO_3$. Due to the salt spray test, bending strength of the $Al_2O_3$ blasted specimens showed about 100 MPa lower strength than the other specimens. The bending fracture surface was vein pattern which was shown typically in the amorphous alloys.

• KEPCO Journal on Electric Power and Energy
• /
• 제1권1호
• /
• pp.109-113
• /
• 2015

초임계 이산화탄소 발전 시스템 구축을 위해서는 고온, 고압의 열악한 환경에 노출되는 터빈, 열 교환기, 압축기와 같은 핵심 부품들의 내식성 평가는 반드시 수행되어야 한다. 이를 위해 후보소재 3종 Ferritic-Martensitic Steel (T92), Austenitic Steel (SS316L), Ni-based Alloy (IN738LC)를 선정하여 고온의 유사 초임계 $CO_2$ 발전 환경에서의 내식성 평가를 진행하였다. $600^{\circ}C$, $700^{\circ}C$의 2개의 온도 구간에서 $CO_2$ 분위기를 조성하여 800 시간 동안 노출시킨 뒤, Weight Change, Surface Morphology, Cross Section, Composition을 분석하였다. Cr-rich Protective Layer를 형성하는 Ni-based Alloy와 Fe/Cr-rich oxide를 형성하는 Austenitic Steel은 우수한 부식 저항성을 보인 반면에 Ferritic-Martensitic Steel은 높은 Weight Change와 Fe-rich Non-Protective Oxide가 관찰되어 상대적으로 낮은 부식 저항성을 보였다.

• 조명전기설비학회논문지
• /
• 제20권2호
• /
• pp.45-49
• /
• 2006

본 논문은 마이크로 전극 시스템에 의하여 연료전지 및 Ni-MH 전지로의 응용을 가정한 $AB_5$계 수소저장합금인 $MmNi_{3.55}Co_{0.75}Mn_{0.4}Al_{0.3}$의 단일 입자에 대하여 전기화학적인 평가를 수행하였다. 즉 Carbon fiber 마이크로 전극을 합금 입자 한개 위에 전기적인 접촉을 이루도록 조정하고, 합금 입자 내에서 수소원자의 겉보기 화학적 확산계수를 계산하기 위하여 Potential-Step 실험을 실시하였다. 여기에서 사용되는 합금입자는 치밀하고 전도성이 있는 구형이므로 데이터 해석을 위해 구형확산 모델을 적용하였다. 실험결과로서 겉보기 확산계수($D_{app}$)는 수소 흡장 및 방출되는 전 과정에서 $10^{-9}$과 $10^{-10}[cm^2/s]$ 수준인 것으로 확인되었다. 마이크로 전극 측정 시스템에 의한 단일 입자의 전기화학적 평가는 기존의 Composite Film 전극에 비해 수소저장합금에 대해 보다 상세하고 정확한 정보를 쉽게 얻을 수 있었다.

• 한국주조공학회지
• /
• 제32권2호
• /
• pp.98-103
• /
• 2012

Recently, development of Al-based alloys for high mechanical performance has been an important issue in automotive industry. The present study focused on the design of a high strength Al-based alloy for rheo-diecasting. The research was based on thermodynamic calculation and experimentals to optimize the alloy compositions. Two important considerations were carried out: i) to obtain uniform slurry with fine and globular microstructures for rheo-diecasting, ii) to be strengthend by T6 heat treatment. In order to evaluate the effect of Si content on the slurry microstructure and castability, thermodynamic calculation and fluidity test were carried out. The effects of various alloying components, such as Mg, Cu and Zn, on age hardenability were also investigated. The mechanical properties of the rheo-diecasting products using the newly developed alloy are 324MPa in tensile strength, 289MPa in yield strength, and 11.2% in elongation after T6 heat treatment.

• 한국재료학회지
• /
• 제19권6호
• /
• pp.319-324
• /
• 2009

The deposition behavior and structural and magnetic properties of electroless Co-B and Co-Fe-B deposits, as well as the amorphous ribbon substrates, were investigated. These Co-based alloy deposits exhibited characteristic polycrystalline structures and surface morphology and magnetic properties that were dependent on the type of amorphous substrates. The catalytic activity sequence of the amorphous ribbon electrodes for anodic oxidation of DMAB was estimated from the current density-potential curve in the anodic partial electrolytic bath that did not contain the metal ions. Both the deposition rate and potential in the initial region were obtained in order of the catalytic activity, depending on the alloy compositions of the substrates. The deposition rate linearly varied against the deposition time. The initial deposition potential may have also determined the structural and magnetic properties of the deposit based on the thickness of ${\mu}m$ order. Furthermore, a basic study of the electroless deposition processes on an amorphous ribbon substrate has been carried out in connection with the structural and magnetic properties of the deposits.