• Corrosion Science and Technology
• /
• v.14 no.3
• /
• pp.127-131
• /
• 2015

Model alloys Fe-9Cr, Fe-20Cr and Fe-20Cr-20Ni (wt. %) with 0.1 and 0.2 % Si were exposed to $Ar-20CO_2-20H_2O$ gas at $818^{\circ}C$. The undoped alloys formed a thick iron-rich oxide scale. The additions of Si reduced scaling rates of Fe-9Cr to some extent but significantly suppressed the formation of iron oxide scales on Fe-20Cr and Fe-20Cr-20Ni. Carburisation also occurred in all undoped alloys, but not in Si-containing Fe-20Cr and Fe-20Cr-20Ni. Protection against carburisation was a result of the formation of an inner scale layer of silica.

• Journal of Surface Science and Engineering
• /
• v.24 no.2
• /
• pp.96-102
• /
• 1991

Co-Ni-P alloys were electrodeposited from NH4Cl-sulfate-hypophosphite baths under various plating conditions. Their effective anisotropic magnetic field which is one of the important properties for magnetic recording materials were investigated as the function of alloy compositions and c-axis orientation. The preferred orientation and the contents of Ni and P depend on the pH of solutions and also on the current density. It was found that the alloy films deposited from the solutions of pH4 at high current density had c-axis orientation parallel to the growth direction and the effective anisotropic fields sufficient for perpendicular magnetic recording application.

• Journal of Magnetics
• /
• v.3 no.4
• /
• pp.116-119
• /
• 1998

Influence of small additions ($\leq$2.0 at.%) of Al, Ti, Co, and Ni on the microstructural development and the magnetic properties of melt-spun Fe-Bd-C alloys was investigated. Addition of these elements tended to stabilize the crystallization of as-spun ribbons. Especially, Al and Ti preferred to stabilize$ Fe_{17}Nd_2C_x.$ The average grain size of Fe17Nd2Cx (0.1~0.3 ${\mu}{\textrm}{m}$), obtained by a proper annealing, in the ribbon treated with 0.5 at.% additive was much smaller than that of additive-free ribbons, which would be the major source of large increase in coercivity. Among the additives, Ni was very effective to increase the coercivity whereas Co had beneficial effect on $T_c.$ By adding 0.5 at.% Ni, intrinsic coercivities of more than 1.4 T, 40~50% higher than that (~1.0T) of additive-free ribbons, can be obtained after annealing at 750~80$0^{\circ}C$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.156-157
• /
• 2011

고경도 Ni-Co 합금 도금액 개발을 위하여 Ni과 Co의 함량 조성비와 전류밀도에 따라 전기도금을 실시하였다. Ni과 Co의 함량비는 Ni의 농도를 일정하게 유지시키고 Co의 농도를 10~30g/${\ell}$로 하여 실험을 하였다. Ni과 Co의 함량 조성비에 따른 합금 도금층의 성분을 EDS를 이용하여 분석하였고 전류밀도별 표면형상을 FE-SEM을 이용하여 분석하였다. 그리고 도금층의 성분에 따른 경도값을 비커스 경도계를 이용하여 분석하였다.

• Journal of the Korean Magnetics Society
• /
• v.15 no.4
• /
• pp.241-245
• /
• 2005

CoFeNi alloys are some of the most studied soft magnetic materials because of their applications as write-head core materials in HDD and MEMS. Ternary CoFeNi films with high saturation magnetic flux density, Bs and low coercivity, He were successfully grown by electrodeposition. The optimal composition was $Co_{30}\;Fe_{34}\;Ni_{36}(at\%)$, and Bs and Hc were 1.9 T and 0.16 A/m, respectively. The XRD and TEM results show that the low Hc of the CoFeNi films was due to very fine crystal particles and mixed fcc and bcc phases.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.2
• /
• pp.123-130
• /
• 1989

In order to investigate the biocompatibility of base metal alloys in dental prosthesis, the 3 types of Ni-Cr alloys and the 3 types of Co-Cr alloys were collected and each alloy was extracted in the culture medium. L-cells derived from the subcutaneous tissue of mouse and extracted medium were cultivated. The relative growth rate of L-cells in the tissue culture was calculated with N-R assay. The obtained results were as follows: 1. In the case of the Co-Cr alloys tested, its cytotoxicity proved weak. 2. In the case of the Ni-Cr alloys tested, there was no significant degree of cytotoxicity, especially 25% Victory was proved noncytotoxicity.

• Journal of Information Display
• /
• v.5 no.4
• /
• pp.27-30
• /
• 2004

This paper investigates the effects of coating such as Invar (Fe-36% Ni), Fe-Ni Alloys and $WO_3$ on the doming property of aluminum killed (AK) shadow masks, which may be used for flat CPTs. Invar and Fe-Ni Alloys are deposited on AK shadow mask in plasma atmosphere and annealed. $WO_3$ is screen-printed on the deposited layer. The coating is observed to cause a decrease in the doming property of the shadow masks due to their lower thermal expansion coefficients and anti-doming properties.

• Journal of Surface Science and Engineering
• /
• v.29 no.3
• /
• pp.195-202
• /
• 1996

The composition, the microstructure and the magnetic properties(HC and Hk) of Fe-Co-Ni alloy electrodeposits were investigated according to the electrolysis conditions using sulfate bath paddle agitated. The current efficiency of the alloys electrodeposition was considerably low in the range of 16∼50%. The Fe content(wt.%) of the alloy increased from 20% to 57% with current density, while Ni content of them decreased in the range of 70∼24% respectively, and Co content was nearly constant. As a result, Fe/Ni ratio of the alloy increased from 0.3 to 2.0 showing the anomalous codeposition. The structure of the alloy changed from fcc to the mixed one of fcc+bcc with the increase of Fe/Ni ratio. The preferred orientation of the alloy with fcc and bcc structure were (220) and (110) respectively. The alloy with Fe/Ni ratio(0.3∼l.2) had the lowest coercivity of 0.4∼0.8 Oe.

• Korean Journal of Materials Research
• /
• v.27 no.11
• /
• pp.624-630
• /
• 2017

In this study, we investigated the overpotential of precipitation related to the catalytic activity of electrodes on the initial process of electrodeposition of Co and Co-Ni alloys on polycrystalline Cu substrates. In the case of Co electrodeposition, the surface morphology and the magnetic property change depending on the film thickness, and the relationship with the electrode potential fluctuation was shown. Initially, the deposition potential(-170 mV) of the Cu electrode as a substrate was shown, the electrode potential($E_{dep}$) at the $T_{on}$ of electrodeposition and the deposition potential(-600 mV) of the surface of the electrodeposited Co film after $T_{off}$ and when the pulse current was completed were shown. No significant change in the electrode potential value was observed when the pulse current was energized. However, in a range of number of pulses up to 5, there was a small fluctuation in the values of $E_{dep}$ and $E_{imm}$. In addition, in the Co-Ni alloy electrodeposition, the deposition potential(-280 mV) of the Cu electrode as the substrate exhibited the deposition potential(-615 mV) of the electrodeposited Co-Ni alloy after pulsed current application, the $E_{dep}$ of electrodeposition at the $T_{on}$ of each pulse and the $E_{imm}$ at the $T_{off}$ varied greatly each time the pulse current was applied. From 20 % to less than 90 % of the Co content of the thin film was continuously changed, and the value was constant at a pulse number of 100 or more. In any case, it was found that the shape of the substrate had a great influence.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.1
• /
• pp.44-50
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of repeated porcelain firing process on the corrosion rates of the dental alloys. MATERIALS AND METHODS. Cr-Co, Cr-Ni and Pd-Ag alloys were used for this study. Each metal supported porcelain consisted of 30 specimens of 10 for 7, 9 and 11 firing each. Disc-shaped specimens 10 mm diameter and 3 mm thickness were formed by melting alloys with a propane-oxygen flame and casted with a centrifuge casting machine and then with the porcelain veneer fired onto the metal alloys. Corrosion tests were performed in quintuplicate for each alloy (after repeated porcelain firing) in Fusayama artificial saliva solution (pH = 5) in a low thermal-expansion borosilicate glass cell. Tamhane and Sheffe test was used to compare corrosion differences in the results after repeated firings and among 7, 9 and 11 firing for each alloy. The probability level for statistical significance was set at ${\alpha}$=0.05. RESULTS. The corrosion resistance was higher (30 mV), in case of 7 times firing (Commercial). On the other hand, it was lower in case of 11 times firing (5 mV) (P<.05). Conclusion. Repeated firings decreased corrosion resistance of Pd-Ag, Cr-Co and Cr-Ni alloys. The Pd-Ag alloy exhibited little corrosion in in vitro tests. The Cr-Ni alloy exhibited higher corrosion resistance than Cr-Co alloys in in vitro tests.