• 한국막학회:학술대회논문집
• /
• 한국막학회 2001년도 춘계 총회 및 학술발표회(한국막학회)
• /
• pp.65-67
• /
• 2001

• Korean Membrane Journal
• /
• 제6권1호
• /
• pp.61-69
• /
• 2004

Small angle light scattering (SALS) and field emission scanning electron microscope (FE-SEM) have been used to investigate the effects of alcohol on phase separation of chlorinated poly(vinyl chloride) (CPVC)/tetrahydrofuran (THF)/alcohol (9/61/30 wt%) solution during water vapor induced phase separation. A typical scattering pattern of nucleation & growth (NG) was observed for all casting solutions of CPVC/THF/alcohol. In the case of the phase separation of CPVC dope solution containing 30 wt% ethanol or n-propanol, the demixing with NG was observed to be heterogeneous. Meanwhile, the phase separation of CPVC dope solution with 30 wt% n-butanol was found to be predominantly homogeneous NG. Although the different phase separation behavior of NG was observed with types of alcohol additives, the resultant surface morphology had no remarkable differences. That is, even though the NG process by water vapor is either homogeneous or heterogeneous, this difference does not play a main role on the final surface morphology. However, it was estimated from the result of hydraulic flux that the phase separation by homogeneous NG provided the membrane geometry with lower resistance in comparison with that by heterogeneous one.

• 한국화재소방학회논문지
• /
• 제33권1호
• /
• pp.1-6
• /
• 2019

열중량 분석법(TGA)을 이용하여 소방용 합성수지 배관으로 사용되는 CPVC의 활성화 에너지를 측정하였다. 열중량 분석법을 이용한 활성화 에너지는 Kissinger method와 Flynn-Wall-Ozawa method를 이용하여 계산하였다. 활성화 에너지를 계산한 결과 Kissinger method에 의해 128.07 kJ/mol, Flynn-Wall-Ozawa method에 의해 145.60 kJ/mol로 나타났다. Kissinger method와 Flynn-Wall-Ozawa method에 의해 계산된 활성화 에너지의 차이는 해석 방법이 다르다는 점을 감안했을 때 큰 차이가 없다고 판단된다. 향후 가속열화을 이용한 열적 열화평가 및 공기오븐노화시험을 통한 CPVC의 연소특성을 시험하고, 수명을 예측하고자 한다.

• 한국산학기술학회논문지
• /
• 제17권11호
• /
• pp.355-362
• /
• 2016

배관 내에 유체가 흐를 때 사용되는 유체의 물리 화학적 성질에 따라 배관재질이 선택이 결정된다. 수계소화설비에 사용하는 유체는 대부분 물을 사용하므로 물속에 용해된 각종 이물질들은 관 벽에 스케일을 발생시키고 부식 및 배관 노후화를 촉진하여 마찰손실을 증가시켜 펌프의 효율을 저하시킨다. 이러한 요인을 가져오는 강관의 대체가능한 CPVC 배관은 부식에 강하고, 매끄러운 조도를 가지고 있어서 유체이송능력이 뛰어나고 배관무게가 가볍고 접착제결합 방식의 배관작업으로 시공성이 우수한 점을 들 수 있다. 그래서 설계 및 시공단계에서 마찰손실을 줄이기 위해 Hazen-Williams식을 CPVC(Chlorinated Poly-Vinyl Chloride)배관에 적용하여 조도계수에 따라 마찰손실을 조사하였다. 실제 아파트 현장에서의 적용사례를 통해 조도계수의 차이에 따라 손실수두를 조사한 결과 조도계수의 수치가 120인 강관일 때 마찰손실은 76.64MPa이고 150인 CPVC배관일 때 마찰손실은 50.72 MPa로서 34% 정도의 마찰손실이 개선되었음을 확인하였다. 또한 시공비 절감차원에서는 강관으로 시공할 때 1,585,158원이고 CPVC배관으로 시공 시에는 931,842원으로 41%정도의 시공비가 절감되는 것을 확인하여 전체 설비용량의 감소로 인한 소화시스템의 안정성 향상 및 시공비를 절감할 수 있는 것을 알 수 있었다.

• 한국염색가공학회지
• /
• 제32권2호
• /
• pp.111-120
• /
• 2020

In this study, lignin/chlorinated poly(vinyl chloride)(CPVC) blended fibers have been produced for the development of low-cost carbon fiber. Carbon fiber manufacturing was accomplished through stabilization and carbonization process. The lignin/CPVC blended fibers were prepared by wet spinning method. Dimethylacetamid e(DMAc) and cychlohexanone in a ratio of 5:1(wt%) was employed as co-solvent. The ratio of lignin/CPVC was prepared at 0/10, 1/9, 2/8, 3/7, 4/6, and 5/5(wt%). The spinning solution was extruded at a rate of 0.1 to 0.4ml/min according to the blending ratio. The speed of the rollers was the same for all ratios(draw ratio=1). Analysis of fiber cross-section by scanning eletron microscopy(SEM) showed that as the lignin ratio increased in the same coagulation bath and distilled water, the pore size of the spinning fiber decreased. Therefore, the highest tensile strength of the blending fibers was 6.3±1.2MPa at the 5/5 ratio. The carbon fiber also showed the best tensile strength of 120.78±2.43MPa at 5/5 ratio.

• 멤브레인
• /
• 제12권2호
• /
• pp.97-106
• /
• 2002

Polysulfone (PSf/NMP/alcohol 용액과 chlorinated poly(vinyl chloride) (CPVC)/THF/Alcohol 용액에 대한 광산란 패턴을 SALS (Small angle light scattering)와 FE-SEM (field emission scanning electron microscope)을 이용하여 조사하였다. PSf 용액에서는 시간에 따라 q값의 최대 산란 강도를 보이는 광산란 거동을 나타내어 스피노달 (SD) 상분리 거동을 나타내는 반면, CPVC 용액에서는 q값이 증가함에 따라 광산란 강도가 줄어드는 핵성장 (NG) 거동을 나타냈다. 각 고분자 용액에서 상분리 중반과 후반부에서 비용매 첨가제로 사용된 알코올의 탄소수가 증가할수록 농도분극의 증가율은 줄어들었다. 또한, SD에서의 초반부의 시간에 따른 산란 강도는 비용매 첨가제의 종류에 무관하게 Cahn의 건형 이론에 잘 부합되었다. 또한, SALS 장치로 얻어진 기공크기와 전자현미경으로 얻어진 영역 크기는 상호간에 비교되었다. 20PSf/70NMP/10n-butano1 (w/w%) 용액에 대한 산란 패턴은 초기 상분리 거동에서부터 후기 거동까지 매우 선명하게 관측되었고, 초반, 중반, 그리고 후반부에 대한 SD에 대한 이론적 결과와 잘 일치하였다. 최고의 산란강도를 나타낸 각도의 크기는 n-butanol>n-propanol>methanol>no alcohol 순으로 관찰되었으며, 이 순서로 최종 형성된 막 단면의 기공 크기가 감소되는 것으로 조사되었다.