• Journal of the Korean Ceramic Society
• /
• v.35 no.4
• /
• pp.406-412
• /
• 1998

The reaction bonded alumina ceramics was prepared through the addition of each SiC and ZrO2 powder to the mixture of Al metal powder and Al2O3 The mono sized (3mm) and biodal sized (3mm+5mm) balls were used in attrition milling of Al and starting powders. The milling efficiency of both cases was compared by the analysis of particle size and X-ray diffraction. After the forming and sintering of each powder batchs the weight gains dimensional changes and densities were determined. The specimens were investigated by X-ray diffraction analysis and scanning electron microscope. Bimodal sized balls had better milling effect than single ball size in the milling of Al powder. However in the milling which ceramic powders mono sized the green body during the reaction sintering at 1$600^{\circ}C$ for 5 hour was about 10% The densities attained the values of 92-98% theoretical. The SiC added specimen that was milled with 3mm ball media had 96% theoretical density and dense microstructure.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.389-398
• /
• 2014

Macroporous ceramics with tailored pore size and shape could be used for well-established and emerging applications, such as molten metal filtration, biomaterial, catalysis, thermal insulation, hot gas filtration and diesel particulate filters. In these applications, unique properties of porous materials were required which could be achieved through the incorporation of macro-pores into ceramics. In this article, we reviewed the main processing techniques which can be used for the fabrication of macroporous ceramics with tailored microstructure. Partial sintering, replica templates, sacrificial fugutives, and direct foaming techniques was described here and compared in terms of microstructures and mechanical properties that could be achieved. The main focus was given to the direct foaming technique which was simple and versatile approach that allowed the fabrication of macro-porous ceramics with tailored features and properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.157-160
• /
• 2001

Three sets of ZnO ceramic devices (reference samples with Matsuoka\`s composition; added 7o MgO, A1$_2$O$_3$, SiO$_2$) have been prepared by the conventional mixed oxide route. These additives were determined by the factors of valences and ionic radiuses. DC accelerated degradation test was performed for analysis of degradation characteristics versus the various additives. The conditions of DC degradation test were 115${\pm}$2$^{\circ}C$ for 12h. Using XRD and SEM, the Phase and microstructure of samples were analyzed respectively. E-J analysis was used to determine ${\alpha}$. Frequency analysis was accomplished to understand the relationship between R$\sub$g/ and $R_{b}$ with the electric stress at the equivalent circuit.

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.496-504
• /
• 1992

Alumina tubes suitable for the support of gas separation membranes have been prepared by the slipcasting technique. These supports have the average pore size of 0.1 ${\mu}{\textrm}{m}$ within the narrow distribution. The sol-gel dipcoating process of nanoparticulate sols is very sensitive to microstructure of the support, and the coating on the inside surface of the tube is found to be more successful than on the outside surface. Nanoparticulate silica sols (0.82 mol/ι) have been synthesized by an interfacial hydrolysis reaction between TEOS and high alkaline water. When coating an alumina tube with these sols, the minimum limits of the particle size and the aging time required for forming the coated gel layer at the given pH are provided. It is optimum to coat the support with less concentrated sols stabilized through aging for the appropriate time (more than 22 days) at the lower pH (pH 2.0) for producing a reproducible crack free thin film coating in composite membranes.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.531-540
• /
• 1991

In this study, high quality machinable ceramics was prepared from the K2O-MgO-Al2O3-SiO2-B2O3-F glass system using domestic pyrophyllite. The mixture of pyrophyllite and additives was melted at 1450$^{\circ}C$ for 1 hour and formed in a graphite mold. The base glass was heat-treated at 600$^{\circ}C$ to 1200$^{\circ}C$ with interval of 50$^{\circ}C$ for 3 hours identified by XRD. Crystalline phase were confirmed by XRD and their microstructure was observed by SEM. The glass ceramics which was prepared by heat treatment of base glass at 1150$^{\circ}C$ for short time has good physical, mechanical, thermal, chemical properties and machinability.

• Journal of the Korean Ceramic Society
• /
• v.33 no.3
• /
• pp.269-276
• /
• 1996

The effect of sintering aids on the sinterability for silcion nitride has been studied by hundreds workers. However the effect of sintering aids on the machinability as the own trobles which is the major barrier for the field applications of the ceramic components has not been fully studied. in this study the contents of Al2O3 and Y2O3 in silicon nitride were varied from 0 to 8 wt% respectively. The physical and mechanical properties of the silcion nitride were measured. The optimal microstructure of silicon nitride balls with the excellent machinability by adding with various contents of sintering aids was studied by MGF(magnetic-fluid grinding)technique. An attempt to figure out how the mechanical properties influence the machinability of silicon-nitride ball was made.

• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.380-386
• /
• 1997

The tribological properties of ceramics are very important in the application to engineering ceramic parts such as seal rings, pump parts, thread guides, and so on. In this study, the effects of graphite addition on the mechanical and tribological properties of alumina/graphite composites were investigated. The composites were prepared by the adding of graphite powder to the mixture of Al2O3, talc and calcium carbonate. Bending strength, water absorption, friction coefficient, the amount of worn out material at a certain time, and maximum surface roughness(Rmax) of the prepared composites were measured. Crystalline phases and microstructure were examined with XRD and SEM. The melt of Al2O3-CaO-MgO-SiO2 system was shown over 10 vol% graphite composition. As the amount of the graphite is increased, needle like crystals of mullite were formed and grown. We obtained the good properties of friction coefficients and wear resistance at the powder composition containing 15 vol% of graphite.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.861-862
• /
• 2006

The suitable tools for CGI material has not been developed yet because of high hardness, high toughness and very low machininability compared to the grey cast iron. And the tool life has been decreased as the contents of Ti in CGI material. From this research, we were able to do the high speed machining by using high toughness silicon nitride ceramic tools. The silicon nitride ceramic tool grade was specially designed and prepared with microstructure of elongated grains with higher aspect ratio (c/a) than conventional one.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.610-618
• /
• 1998

Alumina were added to ceria based ceramic powders upto 9.7 vol% and composite powders were sprayed by plasma spraying process in order to improve the mechanical properties such as hardness fracture tough-ness and thermal shock resistance. The ceria based coating sprayed without alumina has the typical colum-nar and lamellar structure. Alumina addition has lowered the amount of columnar and lamellar sturcture Added alumina was segreagated in the grain boundary and grain of ceria based crystal accompanied with pore. The maximum value of density and the minimum value of porosity were observed at the sprayed coating with 4.8 vol% alumina. The hardness fracture toughness and thermal shock resistance were increased with alumina addition. The improvement of mechanical properties of plasma sparyed ceria based coatings result-ed from the disapperance of the columnar and lamellar sturcture by addition of alumina.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.601-608
• /
• 1988

The effect of SiO2 addition on sintering characteristics of 8 mole percent yttria-stabilized zirconia ceramics is investigated. As the addition of SiO2 is increased, sinterbility, microstructure, and Vickers hardness of the zirconia ceramic increased but fracture toughness and electrical conductivity are decreased. It is considered that the electrical conductivity decrease with the increase of SiO2 is due to the decrease of defect concentration of ionized oxygen. From the complex impedance measurement, it is shown that the influence of SiO2 is more dominant at the resistivity of bulk region than of grain boundary region.