• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.5
• /
• pp.210-213
• /
• 2011

Glass-ceramics composed of $5Na_2O-36CaO-10TiO_2-xP_2O_5$ could be obtained with $P_2O_5$ content as following procedure: 1) leaching out $Ca_3(PO_4)_2$ crystals between $Ca_3(PO_4)_2$ and $NaTi_2(PO_4)_3$ selectively in 1 N HCl solution for 2 days, and 2) exchanging $Na^+$ ion to $Ag^+$ ion in Ag($NO_3$) solution for 1 day. Scanning electron microscope (SEM) and X-rat diffractometer (XRD) were measured to verify the proper synthesis of glass-ceramics. And anti-bacteria test was accomplished using Staphylococus aureus bacteria. In the results of anti-bacteria test, the bacteria were died perfectly after 3 hours.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.93-97
• /
• 2003

Using alumina-glass infiltrated material which has been in the spotlight of biomaterials including dental material, appropriate composition of glass infiltrated material mainly depends on the thermal expansion coefficient. To obtain proper compositional glass of suitable thermal expansion coefficient effiiently. a Taguchi analysis was conducted. The influence of alkali oxide and alkali earths oxide, which affect mostly the thermal expansion coefficient of glass infiltrated material, was infiltrated material, the effect having influenced on the thermal expansion coefficient of glass was presented in this order (Na$_2$O≫K$_2$O ≫MgO≒CaO). The effect of Na$_2$O was about eight times as great as the effects of MgO, CaO and $K_2$O was about four times. Among the interaction affects of each variables the interaction affects of $K_2$O-CaO showed most significantly and thermal expansion property of specified composition was predicted by calculating contribution rate on each level of variables and interaction affects.

• Journal of the Korean Ceramic Society
• /
• v.48 no.3
• /
• pp.217-221
• /
• 2011

Glass-ceramic materials, which consist of glass matrix phase containing crystalline ${\beta}-Ca_3(PO_4)_2$ and ${\beta}-Ca_2P_2O_7$, have been prepared by heating at $750-900^{\circ}C$ of calcium phosphate invert glasses in the silica-free $CaO-P_2O_5-TiO_2-Na_2O$, system. With increasing heating temperature from 750 to $900^{\circ}C$, the crystallite size of precipitated ${\beta}-Ca_3(PO_4)_2$ in glass with $55CaO{\cdot}35P_2O_5{\cdot}3TiO_2{\cdot}7Na_2O$ (mol%) composition increased from 48 to 91 nm. With the extension of the immersion time in dilute acetic acid solution (pH = 5) to ${\geq}$200 min, the degree of dissolution of $Ca^{2+}$ and $P^{5+}$ ions in the glass-ceramics was linearly increased and the solution was constantly maintained at pH = ~7. Biomimetic nanostructured (62-88 nm in average dia.), sphere-shaped hydroxyapatite was homogeneously formed on the surface of the glass-ceramics when socked for 7-14 days in a Hanks' solution, indicating bioactivity of the prepared glass-ceramics.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.301-308
• /
• 2003

Glass-infiltrated alumina, which can be used as an all-ceramic dental crown, was prepared. The glasses in the system of SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$with various amount of $Al_2$O$_3$infiltrated into a porous sintered alumina. The effect of $Al_2$O$_3$on the infiltration characteristics and its mechanical strength were studied. The corrosion of the sintered alumina by infiltrated glasses was prevented by increasing the amount of $Al_2$O$_3$in the glass batches, this increased the bending strength of the glass infiltrated alumina composite. The crack like voids in the sintered alumina was a cause of the deteriorating the mechanical strength of the composite, and this can be eliminated by sintering the alumina at 130$0^{\circ}C$. Glass infiltration under the vacuum atmosphere enhanced the hording strength of the composite up to 453$\pm$31 MPa.

• Korean Journal of Materials Research
• /
• v.14 no.7
• /
• pp.505-510
• /
• 2004

The glass-ceramic based on LAS($Li_{2}O-Al_{2}O_3-SiO_{2}$) system was observed using SEM(Scanning Electric Microscopy) and AFM(Atomic Force Microscopy) and it was expected to get a correlation between the crystal size and the surface roughness through the result. At heat treatment conditions (the nucleation: $740\~800^{\circ}C$, the crystal growth: $900\~1150^{\circ}C$), the crystal size was increased from 72 to 450 nm so that the mean of surface roughness was also risen from 0.8 to 6.3 nm. Based on the results, the surface roughness of glass-ceramic is controlled by the factors, crystal size, crystallines, and the condition of heat treatment.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.05a
• /
• pp.103-106
• /
• 2009

Fracture characteristics of plate shape using shock tube for glass filled ceramics was carried out. Glass filled ceramics have been considered as a promising candidate material for the dome port cover of air breathing engine. This part of the air breathing engine has an important role separating solid and liquid fuel, and needs the frangible characteristics that the fracture of a part should not affect the internal components of combustion. The objectives of this study are to evaluate the fracture pressures for various thicknesses and diameters of shock impact area. Also fracture phenomena of separated membrane using a shock tube are observed. The experimental apparatus of shock tube consists of a driver, a driven section and a dump tank. The used material is glass filled ceramic made from Corning company. Specimens are used 3, 4.5 and 6mm thickness. Also diameters of shock wave area are chosen 70, 60 and 50 mm. It is expected that the results obtained from this study can be used in the basic data for the dome port cover design of an air breathing engine.

• Journal of the Korean Ceramic Society
• /
• v.56 no.2
• /
• pp.167-172
• /
• 2019

Silicate glasses with varying SiO₂ and Na₂O contents were prepared and their viscous flow property at the elevated temperature was studied. When the glass powders were packed and sintered at 550℃ to examine their feasibility as a low sintering temperature glass frit, contrary to expectations, glasses with lower SiO₂ content than 60 mol% showed no vitrification after sintering. High temperature microscopy revealed the viscous flow change of the silicate glasses with varying temperature and duration time and also indicated that the viscous flow was limited at low SiO₂ content. X-ray diffraction (XRD) on the sintered samples and Raman spectroscopy were carried out to shed light on the compositional dependency of viscous flow of silicate glasses.

• Journal of the Korean Ceramic Society
• /
• v.48 no.1
• /
• pp.40-45
• /
• 2011

In this study, the composition of optical glass for GMP(glass molding process) was designed with 'Design of Experiments' method. All the composition batch was performed by 'Create Factorial Design' method. Particularly, $SiO_2$, BaO and $Al_2O_3$ were chosen major parameters for investigating the effects of components on optical and thermal properties. BaO and $Al_2O_3$ strongly influenced on optical and thermal properties, respectively. Finally, the approximate values of desired optical and thermal values were obtained by microtuning of compositions. At the composition of $BaO:Al_2O_3:SiO_2$=10:4:48 (molar ratio), refractive index($n_d$) was 1.5833, coefficient of thermal expansion(CTE) was $104{\times}10^{-7}/^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.309-309
• /
• 2007

The LTCCs (low-temperature co-fired ceramics) are very important for electronic industry to build smaller RF modules and to fulfill the necessity for miniaturization of devices in wireless communication industry. The dielectric materials with sintering temperature $T_{sint}$<$900^{\circ}C$ are required. In this study, we investigated with glass-ceramic composition, which was crystallized with two crystals. The microstructure, crystal phases, thermal and mechanical properties, and dielectric properties of the composites were investigated using FE-SEM, XRD, TG-DTA, 4-point bending strength test and LCR measurement. The starting temperature for densification of a sintered body was at $779{\sim}844^{\circ}C$ and the glass frits were formatted to the crystal phases, $CaAl_2Si_2O_8$(anorthite) and $CaMgSi_O_6$(diopside), at sintering temperature. The sintered bodies exhibited applicable dielectric properties, namely 6-9 for ${\varepsilon}_r$. The results suggest that the glass-ceramic composite would be potentially possible to application of low dielectric L TCC materials.

• Journal of the Korean Ceramic Society
• /
• v.40 no.10
• /
• pp.936-942
• /
• 2003

In order to develop glass formulations for vitrifying Low-and Intermediate-Level radioactive Wastes (LILW) from nuclear power plants of Korea Hydro & Nuclear Power (KHNP) Co., Ltd., promising glass formulations were selected based on glass property model predictions for viscosity, electrical conductivity and leach resistance. Laboratory measurements were conducted to verify the model predictions. Based on the results, the models for electrical conductivity, US DOE 7-day Product Consistency Test (PCT) elemental release, and pH of PCT leachate are accurate for the LILW glass formulations. However, the model for viscosity was able to provide only qualitative results. A leachate conductivity test was conducted on several samples to estimate glass leach resistance. Test results from the leachate conductivity test were useful for comparison before PCT elemental release results were available. A glass formulation K11A meets all the KHNP glass property constraints, and use of this glass formulation on the pilot scale is recommended. Glass formulations K12A, K12B, and K12E meet nearly all of the processing constraints and may be suitable for additional testing. Based on the comparison between the measured and predicted glass properties, existing glass property models may be used to assist with the LILW glass formulation development.