• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 추계학술대회 논문집
• /
• pp.187-190
• /
• 2009

$LaCrO_3$ series are the most common candidate materials for a ceramic interconnect for SOFC and the thermal expansion coefficient of these matches very well with that of YSZ electrolyte. In this study, characteristics of the coated films on the anode-support, which were formed by using $La_{0.8}Ca_{0.2}CrO_3$, $La_{0.8}Sr_{0.2}CrO_3$, $La_{0.8}Ca_{0.2}Co_{0.1}Cr_{0.9}O_3$ for ceramic interconnet for SOFC, were investigated. All powders showed single perovskite phase and the precursors had spherical shapes of $2{\mu}m{\sim}30{\mu}m$. According to SEM analysis, coated film of LCC on pretreated anode-support was more thicker, whereas the coated film on untreated anode-support was densely formed. As the results of electrical conductivity of anode-support coated with the ceramic interconnects, LCCC exhibited the most excellent electrical conductivity of 0.15S/cm at $750^{\circ}C$.

• 한국연소학회지
• /
• 제17권4호
• /
• pp.5-10
• /
• 2012

The reformer system is a chemical device that drives the conversion of hydrocarbon to hydrogen rich gas under high temperature environment($600-1,000^{\circ}C$). Generally, NG(Natural Gas) or AOG(Anode Off Gas) is used as fuel of fuel cell reformer combustion system. The experimental study to analyze the combustion characteristics of a premixed ceramic burner used for 0.5-1.0 kW fuel cell reformer was performed. Ceramic burner experiments using NG and AOG were carried out to investigate the flame stability characteristics by heating capacity, equivalence ratio and different fuels respectively. The results show that surface flames can be classified into green, red, blue and lift-off flames as the equivalence ratio of methane-air mixture decreases. And the stable flames can be established using NG and AOG as reformer fuel in the perforated ceramic burner. In particular, the blue flame is found to be stable at a lean equivalence ratio under different mixture conditions of NG and AOG for the 0.5 to 1.0 kW fuel cell system power range. NOx emission is under 60 ppm between 0.70 to 0.78 of equivalence ratio and CO emission is under 50 ppm between 0.70 to 0.84 of equivalence ratio.

• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.479-490
• /
• 2000

The microstructure of Ni-YSZ composite as an anode of SOFC was investigated as a function of Ni content(10-70 vol%) in order to examine the correlation between microstructural-and electrical property. Image analysis based on quantitative microscopy theory was performed to quantify the microstructural property. We could get the informations about the size and distribution, contiguity and interfacial area of each phase or between the phases from the image analysis. According to the image analysis, contiguity between the same phae was mainly dependent on the amount of the phase while the contiguity between different phases was additionally influenced by the microstructural changes, especailly by the coarsening of the Ni phase. The whole length of pores perimeter was increased as Ni content increased, which indicated the overall microstructural evolution was mostly related with the coarsening of Ni phase. Ni-Ni interfacial area was also gradually increased as Ni content increased but controlled by pore phase at low Ni content region and by YSZ phase at intermediate Ni content region. These quantified microstructural properties were used to characterize the electrical properties of Ni-YSZ composite.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 D
• /
• pp.1544-1546
• /
• 1999

The fabrication process for ceramic fuel cell with a large electrode area was investigated. A cofired cell of two layer, electrolyte/anode, yielded a power of $200mW/cm^2$. Its performance loss was mainly due to iR drop in the anode side. The performance of the cofired of three layer. cathode/electrolyte/ anode, was much lower than that of two layer, which resulted from the large iR drop and overvoltage at the cathode side. Also a flat cell with a large area of $7.7{\times}10.8cm^2$ was fabricated successfully and tested using ceramic and metallic interconnectors. The large cell with metallic interconnectror showed a good performance of 0.6 V, 4.5 A.

• 한국세라믹학회지
• /
• 제50권2호
• /
• pp.168-172
• /
• 2013

This work presents the effects of binders on the electrochemical performance of Si-C composites as the anode of lithium ion batteries. PAI (polyamide-imide) was used as an organic binder, and PAN (polyacrylonitrile), PAA (polyacrylic acid) and CMC + SBR (carboxymethyl cellulose + styrene-butadiene rubber) were used as aqueous binders. As a result, stabilization time for the cell with a Si-C composite anode synthesized using aqueous binders became shorter than an organic binder. Particularly in the case of the cell using PAA binder, better performance was observed in terms of adhesion strength, initial efficiency, the volume expansion ratio, Coulombic efficiency, and capacity retention.

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.807-814
• /
• 2008

The Cu-Ni-YSZ cermet anodes for direct use of methane in solid oxide fuel cells have been fabricated by electroplating Cu into the porous Ni-YSZ cermet anode. The uniform distribution of Cu in the Ni-YSZ anode could be obtained via pulse electroplating in the aqueous solution mixture of $CuSO_4{\cdot}5H_{2}O$ and ${H_2}{SO_4}$ for 30 min with 0.05 A of average applied current. The power density ($0.17\;Wcm^{-2}$) of a single cell with a Cu-Ni-YSZ anode was shown to be slightly lower in methane at $700^{\circ}C$, compared with the power density ($0.28\;Wcm^{-2}$) of a single cell with a Ni-YSZ anode. However, the performance of the Ni-YSZ anode-supported single cell was abruptly degraded over 21 h because of carbon deposition, whereas the Cu-Ni-YSZ anode-supported single cell showed the enhanced durability upto 52 h.

• 방사성폐기물학회지
• /
• 제20권4호
• /
• pp.383-398
• /
• 2022

The electrochemical behavior was investigated during the electrolysis of nickel oxide in LiCl-Li₂O salt mixture at 650℃ by changing several components. The focus of this work is to improve anode design and shroud design to increase current densities. The tested components were ceramic anode shroud porosity, porosity size, anode geometry, anode material, and metallic porous anode shroud. The goal of these experiments was to optimize and improve the reduction process. The highest contributors to higher current densities were anode shroud porosity and anode geometry.

• 한국세라믹학회지
• /
• 제51권4호
• /
• pp.243-247
• /
• 2014

Spherical NiO-YSZ particles were synthesized by ultrasonic spray pyrolysis (USP). The morphology of the synthesized particles can be modified by controlling parameters such as precursor pH, carrier-gas flow-rate, and temperature of the heating zone. The synthesized spherical NiO-YSZ particles have rough surface morphology at high carrier-gas flow-rates due to rapid gas exhaustion and insufficient particle ordering. The Ni-YSZ cermet anode synthesized by ultrasonic spray pyrolysis at a flow rate of l L/min, with precursor solution at pH4, showed a higher maximum power density of 256 $mW/cm^2$ compared to a conventionally mixed Ni-YSZ anode (185 $mW/cm^2$) at $800^{\circ}C$. While the area-specific resistance of conventionally mixed Ni-YSZ anodes increases gradually with operation time (indicating performance degradation), the Ni-YSZ anode synthesized by USP does not exhibit any performance degradation, even after 500 h.

• 한국세라믹학회지
• /
• 제43권12호
• /
• pp.775-780
• /
• 2006

Mechanical and electrical performance of anode-supported SOFC single cells were analyzed after thermal cyclic operation. The experiments of thermal cyclic cell-operation were carried out four times and performance of each cell was measured at different temperatures of 650, 700, and $750^{\circ}C$, respectively. As increasing the number of thermal cycle test, single cells showed poor I-V characteristics and lower 4-point bending strength. The anode polarization was also measured by AC-impedance analysis. The observation of the microstructure of the anodes in single cells proved that the average particle size of Ni decreased and the porosity of anode increased. It is thought that the thermal cycle caused the degradation of performance of single cells by reducing the density of three-phase boundary region.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.483-488
• /
• 2016

Anode supported solid oxide fuel cells (SOFCs), consisting of Ni+YSZ anode, YSZ electrolyte, and LSM+YSZ cathode, were fabricated and constant current tested with direct internal reforming of methane (steam to carbon ratio ~ 2) as well as hydrogen fuel at $800^{\circ}C$. The cell, operated under direct internal reforming conditions, showed relatively rapid degradation (~ 1.6 % voltage drop) for 95 h; the cells with hydrogen fuel operated stably for 170 h. Power density and impedance spectra were also measured before and after the tests, and post-test analyses were conducted on the anode parts using SEM / EDS. The results indicate that the performance degradation of the cell operated with internal reforming can be attributed to carbon depositions on the anode, which increase the resistance against anode gas transport and deactivate the Ni catalyst. Thus, the present study shows that direct internal reforming SOFCs cannot be stably operated even under the condition of S/C ratio of ~ 2, probably due to non-uniform mixture (methane and steam) gas flow.