• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 1999.10c
• /
• pp.294-300
• /
• 1999

After researching the physical properties of the concrete included Rice Husk Ash(RHA concrete) and workability of fresh concrete admixed RHA, we have tested durability of RHA-concrete against freeaing and thawing in the winter using rapid freezing and thawing test method(KS F 2456) . There aretwo hypotheses to explain the failure mechanism of a freezing and thawing action. First, the hydraulic pressure in the pores of freezing concrete make an internal stress of concrete structures outbreaking micro crack in the face of concrete, Second, Frost action causing damage to cement paste repeatedly come from soil frost action, freezing water in the capillaries. Initial Relative Dynamic Modulus of Elasticity (DME) was biggest in cae of unit binder weight 600kgf/㎥ and relative dynamic modulus of elasticity increased until 300cycles. In general , initial relative DME was proportional to unit binder weight . Relative DME was decreased in proportion to unit binder weight in the case of 300, 400, 500kgf/㎥ , but relative DME fo the others remained more than 90% until 300 cycles. It was not good effect of intermixed RHA to concrete in case of below unit binder weight 300kgf/㎥ and the resistance of freezing and thawing was not good either.

• Journal of the Korea Concrete Institute
• /
• v.29 no.4
• /
• pp.407-413
• /
• 2017

The fundamental property of magnesia phosphate cement (MPC) for concrete repair material was investigated in this research. For mechanical properties, setting time, compressive strength and tensile/flexural bond strength were measured, and hydration products were detected by X-ray diffraction. The specimens were manufactured with dead burnt magnesia and potassium dihydrogen phosphate was admixed to activate the hydration of magnesia and a borax was used as a retarder. To observe the pore structure and ionic permeability of MPC mortar, mercury intrusion porosimetry was performed together with rapid chloride penetration test (RCPT). As a result, time to set of Fresh MPC mortar was in range of 16 to 21 min depend on the M/P ratio. Borax helped delaying setting time of MPC to 68 min. The compressive strength of MPC with M/P of 4 was sharply developed to 30 MPa within 12 hours. The compressive strength of MPC mortar was in range of 11.0 to 30.0 MPa depend on the M/P ratio at 12 hours of curing. Both tensile and flexural bond strength of MPC to old substrate (i.e. MPC; New substrate to OPC; Old substrate) were even higher than ordinary Portland cement mortar (i.e. [OPC; New substrate] to [OPC; Old substrate]) does, accounting 19 and 17 MPa, respectively. The total pore volume of MPC mortar was lower than that of OPC mortar. MPC mortar had the entrained air void rather than capillary pore. The RCPT showed that total charge passed of OPC mortar had more than that of MPC mortar, which can be explained by the pore volume and pore distribution.

• Journal of the Korea Concrete Institute
• /
• v.21 no.3
• /
• pp.245-253
• /
• 2009

The importance of chloride ions in the corrosion of steel in concrete has led to the concept for chloride threshold level (CTL). The CTL can be defined as the content of chlorides at the steel depth that is necessary to sustain local passive film breakdown and hence initiate the corrosion process. Despite the importance of the CTL, due to the uncertainty determining the actual limits in various environments for chloride-induced corrosion, conservative values such as 0.4% by weight of cement or 1.2 kg in 1 $m^3$ concrete have been used in predicting the corrosion-free service life of reinforced concrete structures. The paper studies the CTL for blended cement concrete by comparing the resistance of cementitious binder to the onset of chloride-induced corrosion of steel. Mortar specimens were cast with centrally located steel rebar of 10 mm in diameter using cementitious mortars with ordinary Portland cement (OPC) and mixed mortars replaced with 30% pulverized fuel ash (PFA), 60% ground granulated blast furnace slag (GGBS) and 10% silica fume (SF), respectively, at 0.4 of a free W/B ratio. Chlorides were admixed in mixing water ranging 0.0, 0.2, 0.4, 0.6, 0.8, 1.0, 1.5, 2.0, 2.5 and 3.0% by weight of binder(Based on $C1^-$). Specimens were curd 28 days at the room temperature, wrapped in polyethylene film to avoid leaching out of chloride and hydroxyl ions. Then the corrosion rate was measured using the polarization resistance method and the order of CTL for binder was determined. Thus, CTL of OPC, 60%GGBS, 30%PFA and 10%SF were determined by 1.6%, 0.45%, 0.8% and 2.15%, respectively.