• 한국세라믹학회지
• /
• 제29권1호
• /
• pp.15-22
• /
• 1992

The reason for permanent shrinking of recycled castable refractories from alumino-silicate waste refractories was investigated and the method to control shrinking is suggested in order to increase maximum service termperature. The porosity of castable refractories with waste material as large aggregate decreases after heat treatment because the porosity of waste refractories is greater than the of green material, in which CaO around large aggregate penetrates into aggregate and promotes liquid phase sintering. The shrinking of recycled castable refractories resulted in the decrease in porosity can be controled by addition of green kaolin chamotte as large aggregate. The shrinking of recycled castable refractories caused by the differences in densities of mineral phases before and after heat treatment can be controled by addition of kyanite. The use of green kaolin chamotte and kyanite increases the service temperature of recycled castable refractories up to 1500$^{\circ}C$.

• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.345-351
• /
• 1998

Thermal shock resistance of $Al_2O_3$- and Fe-$Al_2TiO_5$-based Castable Refractories was studied using a central heating technique. Ring type specimens, 10mm thick and 20 and 100mm inner and outer diameters, respectively, were rapidly heated on the internal surface of the centre hole using a high power electrical heating element. The temperature field was measured experimentally and modelled using finite element analysis (FEA). The thermal stress field was also modelled using FEA. A radial notch was introduced to the ring specimens to enable calculation of the thermal stress intensity factors (SIF). A special LVDT device was incorporated in the thermal shock tester to monitor crack mouth opening displacement (COD). The thermal shock fracture initiation and crack propagation behaviour of the castable refractories were ascertained using the COD measurements and the fracture mechanics analysis data.

• 한국세라믹학회지
• /
• 제36권8호
• /
• pp.876-885
• /
• 1999

In order to develop high performance basic dam block for tundish vessel in steel-making binders and additives on hydration and thermal characteristics of magnesiz castable refractories were studied. Crack initiation and propagation in cement bonded magnesia castables due to slaking of magnesia clinker at drying process were suppressed by using spinel clinker instead of magnesia powder. In case of Na2O$.$2CaO$.$P2O5(NC2P) bonded castable crack initiation due to slaking of magnesia clinker did not occur but bending strength at high temperature was low. Mechanical properties of NC2P bonded castable refractories at high temperature were improved by using magnesia clinker that contains low SiO2 contents.

• 한국세라믹학회지
• /
• 제27권7호
• /
• pp.877-882
• /
• 1990

Effects of metallic Al powder addition on basic and thermal properties of castable refractories were investigated. Generally, low grade prooperties were obtained by metallic Al powder addition with the increase of temperature, comparing with those of non-addition of Al powder. Especially, Al addtion showed severe shrinkage, corrosiion and low strength above 1000$^{\circ}C$. As a result of Al addition, lower strength of and higher corrosion resistance were shown for 2% addition, but it was reversed for above 4% addition. It was found that Al addition was excellent in the explosive spalling test regardless of Al quantity.

• 자원리싸이클링
• /
• 제12권3호
• /
• pp.46-53
• /
• 2003

알루미늄드로스의 재활용은 알루미늄 재생지금 제조시에 요구되는 중요한 사항 중의 하나이다. 본 연구에서는 국내 재생 알루미늄업체에서 발생된 알루미늄드로스를 처리하여 알루미나질 내화물 원료로 재활용하고자 하였다. 드로스 시료를 크기에 따라 선별하고, 1 mm보다 작은 크기의 드로스를 수산화나트륨 용액으로 침출하여 드로스 중의 잔류 알루미늄을 용액 중으로 분리 추출하고, 침출용액에서 석출반응에 의하여 수산화알루미늄을 회수하였다. 드로스 중의 금속알루미늄을 회수한 후 발생된 침출잔사는 수세, 건조, 배소와 같은 일련의 처리를 하여 드로스 중의 잔류 금속성분을 산화물 형태로 변환시켰다. 배소 처리한 드로스 잔사를 골재 및 점결제와 배합하여 알루미나질 캐스타블내화물을 만들고, 굽힘강도와 압축강도를 시험한 결과 KS 기준치인 굽힘강도 $25\;kg/\textrm{m}^2$ 이상, 압축강도 $80\;kg/\textrm{cm}^2$ 이상을 만족하였다. 본 연구결과를 알루미늄드로스를 효율적으로 재활용할 수 있는 한가지 방안으로 제안하고자 한다.

• 한국결정성장학회지
• /
• 제25권1호
• /
• pp.27-31
• /
• 2015

내화물은 슬래그 등과의 화학반응뿐만 아니라 입자 충돌이나 마찰에 의한 물리적인 마모도 일어난다. 그러나 내화물의 에로젼에 의한 마모에 대해서는 거의 알려져 있지 않다. 본 실험에서는 내화도가 1300과 $1500^{\circ}C$인 캐스터블에 대해서 SiC 마모입자의 입사 각도에 따른 마모량의 변화를 분석하였다. 그 결과 최대 마모량을 나타내는 각도는 입자가 내화물에 수직으로 부딪힐 때가 아니라 $60{\sim}75^{\circ}$로 입사될 때인 것을 알았다. 또한 내화물의 기공률이 에로젼 마모에 가장 큰 영향을 미치는 것으로 생각되었다.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.115.2-115.2
• /
• 2000

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.196-196
• /
• 2003

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2002년도 추계총회 및 연구발표회 초록집
• /
• pp.155.2-155
• /
• 2002

• 한국결정성장학회지
• /
• 제27권2호
• /
• pp.99-104
• /
• 2017

저급탄을 가스화하는 반응기에 사용되는 내화물은 고온에서 부식성이 강한 $H_2S$ 가스에 노출되며, 경도나 내마모성과 같은 기계적 특성이 가스에 노출되는 시간이 길어짐에 따라서 떨어진다. 그러나 $H_2S$ 가스에 의한 내화물의 기계적 특성 약화 원인이 아직 잘 알려져 있지 않다. 본 실험에서는 내화도가 다른 두 종류의 케스터블 내화물을 $H_2S$ 농도가 높은 $H_2O/N_2/H_2S$ 혼합가스에 100시간 동안 $900^{\circ}C$에서 노출시키고, 미세구조, 결정상과 내마모 특성 변화를 비교하였다. 혼합가스에 노출되면서 내화물 시편의 무게는 감소하였다. 노출 후 기공률은 감소하고, 내마모 특성은 현저하게 떨어졌다. 부식에 의해서 내화물을 구성하는 상에 변화가 일어났는데, $CaAl_2O_4$와 일부의 $SiO_2$는 사라지고 $CaSO_4{\cdot}2H_2OS$와 $Al_2Si_2O_5(OH)_4$ 상이 나타났다. 내화물의 내마모 특성이 $H_2S$ 가스에 노출된 후에 감소하는 주 원인은 캐스터블 내화물에서 결합제 역할을 하는 $CaAl_2O_4$가 사라지고 기계적 특성이 나쁜 $CaSO_4{\cdot}2H_2OS$가 생성되기 때문인 것으로 생각되었다.