• Korean Journal of Heritage: History & Science
• /
• v.53 no.1
• /
• pp.168-183
• /
• 2020

Efforts had been made to eliminate the brittleness unique to cast ironware from 5 BC up until the time that cast ironware became widely used. One of the techniques used to this end was to produce the cast ironware in one kiln and then anneal it in another kiln. This technique condensed or removed the carbon in the structure to eliminate the brittleness of cast ironware and enable forging. To clarify the nature of this technique, this study examined cast ironware made of malleable cast iron, which manifests the characteristics of the annealing technique for cast ironware excavated on the Korean peninsula, based on current steelmaking technology and research results from China and Japan. Results confirmed that all cast ironware made of malleable cast iron had been imported into Korea until the Proto-Three Kingdoms Period. Also, since the Chiljido (Seven-Branched Sword), which is housed at the Ishigami Shrine in Japan, appears to have been produced in the Korean peninsula, it is determined that Baekje in the 4^th century must have possessed such an annealing technique. At that time, however, iron was produced mainly with an iron bloom, and a large amount of forged iron was produced with a steel bloom smelted from an iron bloom. In addition, most of the cast ironware that was used previously, except for cast iron hoes, had been replaced by forged ironware. In other words, this annealing technique was not used frequently until the Three Kingdoms Period. However, it spread broadly during the Unified Silla Period in so much as it was identified in the Jangan-ri remains, which represented the regional hub of iron production and distribution.

• Journal of Conservation Science
• /
• v.29 no.4
• /
• pp.367-378
• /
• 2013

Microstructures and nonmetallic inclusions of five forged iron axes and one cast iron axe were analyzed. The axes were excavated from the Proto-Three Kingdom Period site located in Yangchon, Gimpo. The forging objects were made of almost pure iron and low carbon steel, and only one among five were quenched after its figuration. Malleable cast iron structures showing on the casting suggest that the decarbonized casting method were applied. According to the results of nonmetallic inclusion analysis, the axes were produced by hammering the iron bloom which was attained with low-temperature -solid-reduction-method. Showing higher Fe content over $SiO_2$, it is assumed that the re-collecting rate of Fe was low because of the insufficient forging temperature and the impurities were included during the smelting process. It is assumed that the lime was used as a preparation because of detecting high Ca contents.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.95-101
• /
• 2014

Joining of grey cast iron by fusion welding has much difficulties for its extremely low ductility and low toughness because of the flake form of the graphite. And the brittle microstructure, i.e. ledeburite may be formed during fusion welding by its rapid cooling rates. By these kinds of welding problem, preheat and post heat treatment temperature must be increased to avoid weld crack or welding problems. In order to avoid these fusion welding problem, friction welding of cast iron was carried out for improving joint soundness, establishing friction welding variables. There is no factor for evaluating friction weldability in continuous drive type friction welding. In this point of view, this study proposed the parameters for calculating friction weld heat input. The results obtained are as follows ; 1. There was a close relationship between tensile strength and flash appearance of friction welded joint. 2. Tensile strength was decreased and flash was severely oxidized as increasing frictional heating time. 3. As increased forging pressure $P_2$, flash had a large crack and tensile strength was decreased. 4. As powdered graphite by rotational frictional force induced flat surface and hindered plastic flow of metal, tensile strength of welded joint was decreased. 5. Heat input for continuous drive type friction welding could be calculated by the factors of $P_1$, $P_2$ and upset distance(${\delta}$).

• Transactions of Materials Processing
• /
• v.16 no.2 s.92
• /
• pp.126-131
• /
• 2007

Voids in a large rotor are formed in solidification process of a cast ingot. The voids have to be eliminated from the rotor by a forming process, because they would became stress-intensity factors which suddenly fracture the rotor in the operation. Previous studies on void-elimination of a large rotor have mainly focused on finding the process variables affecting the void-closure. But the study on the amount of void closure in a large rotor has been very rare. This study was performed to obtain an equation which predicts the amount of void-closure in a forging process of a large rotor and to evaluate the availability of the void-closure equation through finite element analyses. Firstly, 2D FE analysis was carried out to find effects of time integral of hydrostatic stress and effective strain on void volume rate of a large rotor in the upsetting process for various diameters and shapes of void, and material temperature. From the 2D FE analysis, we found that effective strain was suitable for predicting the void-closure of a large rotor, because there was a constant relationship between void volume rate and effective strain. And a void-closure equation was proposed fur predicting void-closure of a large rotor in the upsetting process. Finally, ken the 3D FE analysis, the proposed void-closure equation was verified to be useful for upsetting and cogging processes.

• Journal of Korea Foundry Society
• /
• v.39 no.1
• /
• pp.7-13
• /
• 2019

Few studies of large blooms over 700 mm thick among those used for the forging of raw materials have been reported. The cooling rate difference between the surface and the center of a large bloom is large, and the degradation of the mechanical properties is likely in cases involving excessively coarse precipitates resulted from the slow cooling rate of a large bloom after casting. Therefore, a schematic investigation of the growth behaviors of precipitates while varying their locations in blooms is necessary. The dissolution behaviors of precipitates were investigated by simulating a reheating process during which the bloom is heated to a high temperature. The segregation behavior of the as-cast large bloom was also investigated. Reheating specimens were obtained after an isothermal heat treatment at $1150^{\circ}C$ with various holding times to simulate the reheating process, with the samples undergoing a subsequent water quenching step. The precipitates were extracted using an electrolytic extractor and a particle size analysis was conducted with the aid of SEM, EDS, and TEM. In the present work, Al oxide, MnS and Nb carbide were mainly observed.

• Korean Journal of Heritage: History & Science
• /
• v.35
• /
• pp.138-158
• /
• 2002

To compare and analyze technical system related to manufacturing of ironware during the period of the Three Kingdoms, an analysis was conducted on the minute system of metalwork, as study objects, of the remains of the Mt. Wolpyeong fortress wall in Daejeon in the period of capital during the era of the Three Kingdoms in the 5th century, the Sanwol-ri remains in the 6th century in Gunsan and the remains of ironware excavated from the great ancient tomb of Hwangnam of the Silla dynasty in the 5th century. The result of analysis shows that in the most of the casting products, the minute system of white cast iron were contained. While the iron part of decarbonization was in the system by casting as white cast iron in the central part, on the surface layer it was turned out that comparatively uniform 100% pearlite system of about 1~2mm degree was existing. The part of pearlite on the surface layer was caused by decarbonization, which appears in all the parts of blade front end and handle. Therefore, it was found that the iron part of decarbonization was manufactured by casting, and then was processed at the high temperature by decarbonization. For the products of forging, after processing the products on the basis of pure iron for materials, they manufactured the ironware that raises the strength by carbonizing that keeps carbon infiltrated on the necessary part, by the method of black smith welding that add pure iron to steel, or by varying the method of heat processing onto the part required of strength. Though limited, we could understand that the technical systems for manufacturing skill of ironware in the areas of Baekje and Silla were different each other. In the technical system for Hwangnam great ancient tomb in the Silla area, it is found that they had raised the strength on the necessary part by applying the steelmaking method of carbonizing in the last stage of production of products, in the meantime in Baekje area, it appears that they had produced steel in advance in the first stage of production of the products, and used the produced steel only to the necessary part.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.143-148
• /
• 2010

A bronze dagger excavated from the historical site at Bongili in Gyeongju was examined for its microstructure and chemical compositions. The results show that it was forged out of the Cu-10 weight % Sn alloy having no lead. The application of forging in fabrication and the use of an unleaded alloy distinguish this artifact from other bronze daggers that have been reported in Korea, the majority of which were cast from leaded Cu-Sn alloys. This dagger is a rare and valuable archaeological material suggesting a unique bronze technology practiced in ancient Gyeongju area.

• Korean Journal of Materials Research
• /
• v.26 no.10
• /
• pp.528-534
• /
• 2016

The aim of this paper is to consider the effect of the manufacturing processes on corrosion and centerline cracking of ancient bronze spoons. The ancient bronze spoons in question were made by several steps of forging, in reheated condition with cast ingots. The manufacturing method is similar to that of the modern spoons. The investigations include observations from light and scanning electron microscopes of the microstructure in terms of the crack propagation. Cracks in the centerline are caused by solute segregation in the center-line region; this solute is solidified in the final stage of bronze spoon manufacture. Centerline cracking is also caused by ${\alpha}$ phase segregation, accompanied by forged overlapping along the longitudinal direction of the spoons. A vertical stripe with cracks along the centerline of the spoon's width is formed by folding in the wrought process. The overlapping area causes crack propagation with severe corrosion on the spoon surfaces over a period of a thousand years. The failure mechanisms of ancient bronze spoons may be similar to that of modern spoons, and the estimation of the failure mechanisms of ancient spoons can be appropriate to determine failure causes for such modern spoons.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.5
• /
• pp.239-249
• /
• 2015

Various amount of NbC carbide was intentionally formed in a matrix-type cold-work tool steel by controlled amount of Nb and C addition. And the effect of NbC addition on the mechanical properties was investigated. Four alloys with different Nb and C contents were cast by vacuum induction melting, then hot forging and spheroidizing annealing were conducted. The machinability of the annealed specimens was examined with 3 different cutting tools. And tensile tests at room temperature were conducted. After quenching and tempering, hardness and impact toughness were measured, while wear resistance was evaluated by disk-on-plate type wear test. The increasing amount of NbC addition resulted in degraded machinability with increased strength, whereas the absence of NbC also led to poor machinability due to high toughness. After quenching and tempering, the additional NbC improved wear resistance with increasing hardness, whereas it deteriorated impact toughness. Therefore, it could be found that a moderate addition of NbC was desirable for the balanced combination of mechanical properties.

• Conservation Science in Museum
• /
• v.16
• /
• pp.56-81
• /
• 2015

Ring in the scroll painting is one of the mounting elements which are fixed string and tassel to hang, these differ widely in shape and produce a variety of metals. Most traditional shapes of ring have been lost, because of remount, there are used Japanese style rings in present.Therefore, this study examines to shape, production technique and analyze component traditional style rings of 19 traditional scroll paintings in National Museum of Korea for restoration of original style. Ring has been recorded official names; Wonhwan(Ring), Gukhwadong(Chrysanthemum shaped ornaments), Baemok(Ring-shaped nail) in Uigwe. Result of an optical microscope (Leica, M205A), Wonhwan has two type of production technique; one is cutting and bending a metal rod and other is cast. Baemok is made to forging process after metal rod or plate by casting alloy. Baemok decoration is metal plate cutting shape, and then decorates it with pattern by using kicking line engraving, chasing and so on. Component analysis result from portable X-ray fluorescence found various metals, such as, brass, iron silver-cooper. Brass based on copper and zinc used rings of 17 scroll painting. Baemok of Yun Sidal portrait is used iron and plated with a tin-lead alloy. Yi Seogu portrait is silver-cooper alloy in whole ring.