• 대한기계학회논문집
• /
• 제17권6호
• /
• pp.1529-1540
• /
• 1993

본 연구에서는 금속 열처리를 위한 고온면의 막비등 급냉각에 관한 1차적 연구로서 과냉과도 비등곡선의 정확한 형상과 냉각제의 냉각조건이 강재의 과냉과도 비등열전달에 미치는 영향, $A_1$변태점 부근의 $A_1$냉각속도와 상변태열량광의 관계, 그리고 상변태열이 냉각곡선에 미치는 영향 등을 규명하고자 한다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2001년도 추계학술발표회 초록집
• /
• pp.29-30
• /
• 2001

This paper presents some results of plasma nitriding on hard chromium deposit. The substrates were C45 steel and $30~50{\;}\mu\textrm{m}$ of chromium deposit by electroplating was formed. Plasma nitriding was carried out in a plasma nitriding system with $95NH_3{\;}+{\;}SCH_4$ atmosphere at the pressure about 600 Pa and different temperature from $450^{\circ}C{\;}to{\;}720^{\circ}C$ for various time. Optical microscopy and X-ray diffraction were used to evaluate the characteristics of surface nitride layer formed by nitrogen diffusion from plasma atmosphere inward iCr coating and interface carbide layer formed by carbon diffusion from substrate outward Cr coating. The microhardness was measured using microhareness tester at the load of 100 gf. Corrosion resistance was evaluated using the potentiodynamic measurement in 3.5% NaG solution. A saturated calomel electrode (SiCE) was used as the reference electrode. Fig.1 shows the typical microstructures of top surface and cross-section for nitrided and unnitrided samples. Aaer plasma nitriding a sandwich structure was formed consisting of surface nitride layer, center chromium layer and interface carbide layer. The thickness of nitride and carbide layers was increased with the increase of processing temperature and time. Hardness reached about 1000Hv after nitriding while 900Hv for unnitrided hard chromium deposit. X-ray diffraction indicated that surface nitrided layer was a mixture of $Cr_2N$ and CrN at low temperature and erN at high temperature (Fig.2). Anodic polarization curves showed that plasma nitriding can greatly improve the corrosion resistance of chromium e1ectrodeposit. After plasma nitriding, the corrosion potential moved to noble direction and passive current density was lower by 1 to 4 orders of magnitude compared with chromium deposit(Fig.3).

• International Journal of Concrete Structures and Materials
• /
• 제11권2호
• /
• pp.327-341
• /
• 2017

Openings in slabs are usually required for many different applications such as aeriation ducts and air conditioning. Opening in concrete slabs due to cutouts significantly decrease the member stiffness. There are different techniques to strengthen slabs with opening cutouts. This study presents experimental and numerical investigations on the use of Carbon Fiber Reinforced Polymers (CFRP) as strengthening material to strengthen and restore the load carrying capacity of R.C. slabs after having cutout in the hogging moment region. The experimental program consisted of testing five (oneway spanning R.C. flat slabs) with overhang. All slabs were prismatic, rectangular in cross-section and nominally 2000 mm long, 1000 mm width, and 100 mm thickness with a clear span (distance between supports) of 1200 mm and the overhang length is 700 mm. All slabs were loaded up to 30 kN (45% of ultimate load for reference slab, before yielding of the longitudinal reinforcement), then the load was kept constant during cutting concrete and steel bars (producing cut out). After that operation, slabs were loaded till failure. An analytical study using finite element analysis (FEA) is performed using the commercial software ANSYS. The FEA has been validated and calibrated using the experimental results. The FE model was found to be in a good agreement with the experimental results. The investigated key parameters were slab aspect ratio for the opening ratios of [1:1, 2:1], CFRP layers and the laminates widths, positions for cutouts and the CFRP configurations around cutouts.

• 한국해양공학회지
• /
• 제33권4호
• /
• pp.340-349
• /
• 2019

In the case of a fire accident on a ship or an offshore plant, the design of the bulkhead penetration piece must be verified via a fire test procedure (FTP), as specified by the Maritime Safety Committee (MSC). The purpose of this study is to verify both the numerical analysis results and the design specifications for penetration pieces that could be applied to the A60 class bulkhead division. In this study, the FTP was carried out in accordance with the test procedure prescribed in the MSC regulation. In order to review the fire resistance performance according to the material type, bulkhead penetration pieces for the FTP were made from brass, carbon steel for machine structures (S45C), and austenite stainless steel (SUS316). In addition, spray-type insulation and mechanical fastener-type insulation were applied to investigate the fire resistance performance according to the type of insulation. To verify the heat transfer numerical analysis results for the A60 class bulkhead penetrating piece from this test study, the design specifications of the penetrating piece material and the insulation type applicable to a ship and an offshore plant were identified.