• 한국주조공학회지
• /
• 제23권2호
• /
• pp.86-93
• /
• 2003

It has been a major concern in the foundry that steel castings manufactured by the evaporative pattern casting process encounter the carbon pick-up problem. A carbon rich layer at the evaporative pattern cast surface is a result of interactions between the gaseous products from foamed polystyrene and the molten metal. The carburized layer with a high hardness makes it difficult to machine the casting. In this study, the influence of the density of EPS pattern and coatings on carbon pick-up phenomena of S25C and S45C commercial carbon cast steel were investigated. As the density of EPS pattern is increased, the carbon concentration of decomposed pattern is increased and the thickness of carburized layer at the surface of steel castings is increased. Also as the density of coatings is increased, the permeability of coatings is decreased and the thickness of carburized layer at the surface of steel castings is increased. S25C steel which has lower original carbon content compared to S45C steel exhibited severe carburization.

• 한국주조공학회지
• /
• 제12권4호
• /
• pp.305-316
• /
• 1992

Steel and iron castings made with expandable polystylene (referred to hereafter as EPS) patterns are often affected by distinctive defects associated with incomplete decomposition of the EPS as the molds are filled with metal. The effects of practical factors on carbon pick-up were investigated on the specimens, by taking successive layers of swarf and analysis, whereas the lustrous carbon is determined by using combustion analysis. The quality of the castings, with particular reference to carbon pick-up in low carbon steel and lustrous carbon on gray iron, is further influenced to a significant extent by such practical factors as reduced pressure, the pouring temperature, the density of EPS pattern, the additive in coating and in pattern and the casting thickness. The rate at which carbon pick-up and lustrous carbon deposites are formed can be reduced by reducing the density of the pattern and also reducing pressure, especially by adding $Na_2CO_3$ in coating and in pattern to promote $CO_2$ evolution. The upper parts of castings obtained using EPS patterns are slightly higher in carbon pick-up and in lustrous carbon than other parts.

• 한국주조공학회지
• /
• 제15권6호
• /
• pp.604-615
• /
• 1995

Austenitic stainless steel castings using expandable polystylene(referred to hereafter as EPS) patterns are often affected by distinctive defects associated with incomplete decomposition of the EPS as the molds are filled with metal. The quality of the castings, with particular reference to carbon pick-up in austenitic stainless steel is further influenced to a significant extent by such factors as reduced pressure, the additive by adding $Na_2CO_3$ in coating. The steel composition and microstructure were examined at the surface layer of castings, at depths of 1mm, by taking successive layers of swarf and analysis. In experiments, the carburizing atmosphere was neutralized, showing that the coating performed efficiently by decomposing almost instantly on heating and liberating $CO_2$. The upper parts of castings obtained using EPS patterns were slightly higher in carbon pick-up than other parts. Comparing the 316L and 304 stainless steel castings, qualitative and quantative differences could be found between the carbon pick-up behaviours as influence of the carbon content and alloying elements. Carbide former such as Cr makes carbon more soluble in the steel. This must make carbon pick-up in the surface layer but at the same time richer in carbon especially in the 304 stainless steel castings.

• 한국주조공학회지
• /
• 제3권3호
• /
• pp.159-166
• /
• 1983

In order to develope domestic carburizers, the experiment was carried out by applying crystallization heat treatment to domestic anthracites and also to foreign products to compare with domestic anthracites.The present work was mainly concerned with the effect of their degree of crystallization of carbon-bearing materials on carbon pick-up in molten iron.Those effects were evaluated by the measurement of density, chemical composition, specific electric resistivity, and X-ray intensity of carbon-bearing materials. Experimental results thus obtained were summurized as follows. 1. The degree of crystallization of domestic anthracites and foreign products was increased with increasing heat treatment temperature. 2. The more degree of crystallization, the shorter the dissolving time of domestic anthracites in molten iron was obtained, while that of foreign products was remained constant. 3. As the degree of crystallization of domestic anthracites and foreign products was increased, the carbon content as well as carbon recovery in molten iron was increased.

• 한국주조공학회지
• /
• 제25권1호
• /
• pp.10-15
• /
• 2005

• 한국분말재료학회지
• /
• 제6권4호
• /
• pp.307-313
• /
• 1999

The effect of carbon content on the shape of WC grains dispersed in the Co-rich matrix during liquid phase sintering of WC-35%Co hard metals has been determined. The shape of WC grains was observed using SEM stereography after removing cobalt matrix with boiling hydrochloric acid solution. The WC grains changed from hexagonal to trigonal prism as the carbon content increased in the two-phase region of(WC + $\beta$ - Co), while the morphology of WC grains changed from trigonal to hexagonal shape as the carbon content decreased. The morphology of WC grains changes reversibly along with carbon loss or carbon pick-up. Morphology change of WC grains is attributed to crystal structure of WC, which has an asymmetric array of carbon atoms. There are two types of prismatic planes having different numbers of broken W-C bonds in WC grains. It is scrutinized that as the carbon content increases, the high energy prism planes grow fast and the crystals change from hexagonal to trigonal shape. On the other hand, when the carbon content decreases, the high energy prism planes are dissolved accompanying split of (100) plane into (101) and (101) planes.

• Nuclear Engineering and Technology
• /
• 제55권5호
• /
• pp.1855-1862
• /
• 2023

Graphite crucibles are used for melting uranium and its alloys in VIM furnace. Various coating materials namely Al₂O₃, ZrO₂, MgO etc. are applied on the inner surface of the crucibles using paint brush or thermal spray technique to mitigate U-C interaction. These leads to significant amount of carbon pick-up in uranium. In this study, the attempts are made to develop multilayer coatings comprising of SiC/Y₂O₃ and Mo/Y₂O₃ on graphite to study the feasibility of minimizing U-C interaction. The parameters are optimized to prepare SiC coating of about 70㎛ thickness using CVD technique on graphite coupons and subsequently Y₂O₃ coating of about 250㎛ thickness using plasma spray technique. Molybdenum and Y₂O₃ layers were deposited using plasma spray technique with 70㎛ and 250㎛ thickness, respectively. Interaction studies of the coated graphite with molten uranium at 1450℃ for 20 min revealed that Y₂O₃ coating with SiC interlayer provides physical barrier for uranium-graphite interaction, however, this led to the physical separation of coating layer. Y₂O₃ coating with Mo interlayer provided superior barrier effect showing no degradation and the coatings remained intact after interaction tests. Therefore, the Mo/Y₂O₃ coating was found to be a promising solution for minimizing carbon pick-up during uranium/uranium alloy melting.

• 한국의류산업학회지
• /
• 제13권2호
• /
• pp.279-284
• /
• 2011

In this study, the process of preparation nonwoven with coated carbon nano fibers (CNFs) /poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) composite solution is described. The various contents of CNFs/PVDF-HFP composite coated nonwoven were prepared and characterized by morphological, mechanical, and electrical methods. Nonwovens are coated with CNFs/PVDF-HFP composite solution and decreased the pick up ratio with increasing CNFs contents in range from 0% to 16%. In the results of SEM images, it was clear that the CNFs were evenly distributed in coated nonwoven by SEM images, the existence of CNFs in coated nonwoven was confirmed regularly. The mechanical properties of various contents of CNFs/PVDF-HFP coated nonwoven were examined. The tensile linearity and compression linearity increased with increasing CNFs contents. The electrical properties of the CNFs/PVDF-HFP coated nonwoven increased with increasing CNFs contents.

• 자원리싸이클링
• /
• 제25권4호
• /
• pp.54-59
• /
• 2016

전기로 공정에서 슬래그는 Fe를 약 20 ~ 35 wt.% 함유한 채로 슬래그 포트로 배출되어 냉각되고 있다. 슬래그 배출 전에 환원하여 용강으로 회수한다면 제강회수율을 향상할 수 있으며, 슬래그 배출량을 감소할 수 있다. 일반적으로 전기로 공정에서는 슬래그 포밍과 (FetO)의 환원제로 카본계의 환원제가 활용되고 있다. 본 실험은 Metal을 유도용해로에 용해한 후 슬래그와 환원제로 흑연분탄과 저가의 Al dross powder를 Pellet으로 투입하여 (FetO)의 환원 회수와 복인(復燐)에 대한 영향성을 조사하였다. 실험결과 Al dross에 의한 환원 회수율은 흑연분탄에 비해 2.5배 이상의 효과를 나타내었으며, 복인(復燐)에 대한 영향은 50 ppm 이하로 크지 않은 것으로 나타났다.

• Applied Microscopy
• /
• 제10권1_2호
• /
• pp.7-17
• /
• 1980

Electron microscope radioautography introduced by Liquier-Milward (1956) is now used routinely in many laboratories. Most of the technical difficulties in specimen preparation have been overcome. This method is modified from loop method for improvement of EM radioautographic techniques. The advantages of this method are: 1. the use of single specimens on small corks and of a large wire loop, allows the experimenter to avoid the blemishes in the membrane; 2. the surfactant dioctyl sodium sulphosuccinate is added to diluted ILford L4, thus greatly prolonging the period of time over which good emulsion layers can be made; 3. corks can be handled in perspex holder which allows about 20 specimens to be developed simultaneously. The steps of the method comprise: 1. Cut ribbons of ultrathin sections of silver interference colour 2. Pick them up on formvar-coated 200 mesh grids 3. Prestaining of tissues 4. Coat the specimens with a thin layer of carbon by evaporation (30-60A) 5. Mount the specimens on corks (about 1cm apical diameter) using double-sided scotch tape 6. Emulsion coating; a. Take a 250m1 beaker, place it on the pan of a sliding weight balance and weigh it. Add 10 grams extra to the beam. Add pieces of ILford L4 emulsion to the beaker until the balance is swinging freely. Add the 20ml of distilled water that was previously measured out. b. Surfactant dioctyl sodium sulphosuccinate is added to diluted ILford L4. 7. Prepare a series of membranes of gelled emulsion with the wire loop and apply one to each cork-borne specimen. 8. Put the specimens away to expose by pushing the corks into short length of PVC tubing, each tube having a small hole in the side 9. Place the tubes in small boxes together with silica gel. 10. Exposure 11. Developer - Kodak Microdol X for 3 minutes 12. Fixer - A perspex holder can be manufactured which allows 20 specimens to be developed simultaneously. 12. Fixer - 30% sodium thiosulfate for 10 minutes 13. Examination with Siemens Elmiskop 1A electron microscope