• Nuclear Engineering and Technology
• /
• v.52 no.10
• /
• pp.2394-2401
• /
• 2020

Octadecylamine is an effective film-forming amine that protects carbon steel from corrosion. In the present study, the effect of octadecylamine concentration on adsorption on a carbon steel surface was investigated in anaerobic alkaline solution by using SEM/EDS, TEM and the Materials Studio simulation techniques. TEM morphology observation and EDS elemental detection determine the thicknesses of octadecylamine film on a carbon steel surface, which are confirmed by the in-situ electrochemical impedance spectroscopy measurement and resistance calculation. The Materials Studio simulation reveals the number of octadecylamine film layers at different concentrations. Results obtained in this study indicate that adsorption of octadecylamine film on carbon steel proceeds with the multi-layer adsorption mechanism.

• The Korean Journal of Ceramics
• /
• v.3 no.2
• /
• pp.92-95
• /
• 1997

Because of the novel characteristics such as chemical stability, hardness, electrical resistivity and thermal conductivity, diamond-like carbon (DLC) film is a suitable material for the passivation layers. For this purpose, using the PECVD, DLC films were synthesized at room temperature. The adhesion and the hardness of the DLC films deposited on Si an SiO2 substrate were measured. The resistivity of 5.3$\times$$10^8$$\Omega$.cm was measured by automatic spreading resistance probe analysis method. The thermal conductivities of different DLC films were measured and compared with that of phospho silicate glass (PSG) film which is commonly used as passivation layers. The thermal conductivity of DLC film was improved by increasing hydrogen flow rate up to 90 sccm and was better than that of PSG film. The patterning techniques of the DLC film developed using the RIE and the lift-off method to form 5$\mu\textrm{m}$ line. Finally, the thermal characteristics of the power transistor with the DLC film as passiviation layer was analyzed.

• Korean Journal of Materials Research
• /
• v.18 no.5
• /
• pp.253-258
• /
• 2008

A simple method to deposit carbon nanotube films uniformly on large area substrates using an arc discharge method is reported in this paper. The arc discharge method was modified to deposit carbon nanotube films in situ on the substrates. The substrates were scanned several times over the arcing point for a uniform film thickness. Deposition was carried out under variable dc bias conditions at 600 torr of $H_2$ gas. The thickness uniformity of the single-wall carbon nanotube films as characterized by a four-point probe was within 30% deviation. The morphology and crystal quality of the single-wall carbon nanotube film were also characterized by field emission scanning electron microscopy and Raman spectroscopy.

• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.662-666
• /
• 2008

Electrochemical properties of carbon cryogel electrode for the application of composite electrode materials mixed with metal oxide in supercapacitor have been studied. Carbon cryogels were synthesized by sol-gel polycondensation of resorcinol with form aldehyde, followed by a freeze drying, and then pyrolysis in an inert atmosphere. Physical properties of carbon cryogel were characterized by BET, X-ray diffraction (XRD) and scanning electron microscopy (SEM). It is found that carbon cryogel is amorphous material. The electrochemical properties of carbon cryogel were measured by cyclic voltammetry as a function of concentration of liquid electrolyte, galvanostatic charge-discharge with different scan rates and electrochemical impedance measurements. The result of cyclic voltammetry indicated that the specific capacitance value of a carbon cryogel electrode was approximately 150.2 F/g (at 5 mV/s in 6M KOH electrolyte).

• Journal of the Korean Vacuum Society
• /
• v.13 no.4
• /
• pp.157-163
• /
• 2004

Dependence of residual compressive stress of diamond-like carbon (DLC) films on relative humidity was investigated. Polymeric, graphitic and diamond-like carbon films were prepared by r.f.-PACVD using methane or benzene with the negative self bias voltage of the substrate ranging from -100 to -800 V. In-situ measurements of the residual stress were carried out in an environment chamber where the relative humidity was varied from 10％ to 90％. In dense DLC film of high residual compressive stress and hardness, we could not observe any change in the residual compressive stress with relative humidity. However, in the cases of graphitic and polymeric DLC films, abrupt change in the residual stress occurred by changing the relative humidity. The quantity of the stress change was inversely proportional to the film thickness, which means that the stress change with humidity is not due to the penetration of the water molecule into the film structure, but due to surface interaction between water molecules and film surface.

• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.105-109
• /
• 2006

The effects of negative carbon ion beam energy on the bonding configuration, hardness and surface roughness of DLC film prepared by a direct metal ion beam deposition system were investigated. As the negative carbon ion beam energy increased from 25 to 150 eV, the $sp^3$ fraction of DLC films was increased from 32 to 67%, while the surface roughness was decreased. The films prepared at 150 eV showed the more flat surface morphology of the film than that of the film prepared under another ion beam energy conditions. Surface roughness of DLC film varied from 0.62 to 0.22 nm with depositing carbon ion beam energy. Surface nano-hardness increased from 12 to 57 Gpa when increasing the negative carbon ion beam energy from 25 to 150 eV, and then decreased when increasing the ion beam energy from 150 to 200 eV.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.303.1-303.1
• /
• 2016

Polymer-like amorphous carbon films were deposited on polyethylene naphthalate (PEN) substrate by plasma-enhanced chemical vapor deposition (PECVD) and their water vapor transmission rates (WVTR) were tested. propane was used as precursors. To make a polymer-like amorphous carbon film the deposition rate, surface roughness, light transmittance, and WVTR of the films were characterized as a function of the precursor feed ratio and plasma power. The water vapor transmission rates of bare PEN film and single layer PAC on PEN substrate were 6.95 g/m2/day and 0.3 g/m2/day, respectively. The superior property the water vapor permeability of thin layers of PAC was attributed to uniform coverage and good adhesion between PAC film and PEN substrate.

• Journal of the Korean Society for Precision Engineering
• /
• v.32 no.8
• /
• pp.673-680
• /
• 2015

A roll-to-roll (R2R) continuous manufacturing system for a carbon-nanotube (CNT)-/silver-nanowire (AgNW)- based large-area transparent conductive film was introduced in this study. The systemic guidelines of the R2R slot-die coating process including roll eccentricity, wrap angle, pump accuracy, and blower influence were discussed. To simulate the coating phenomenon, we investigated the governing parameters of the coating process by incorporating the estimated relative thickness that was defined by combining the viscocapillary model and volume model. By using experimental and mathematical approaches, an excellent transparent conductive layer with a $40{\Omega}/{\Box}$ sheet resistance and 88 % transmittance was obtained; moreover, a dimensionless number identifies the correlation between the transparent conductive film and the anti-reflection film.

• Korean Journal of Materials Research
• /
• v.13 no.5
• /
• pp.303-308
• /
• 2003

Amorphous carbon nitride films deposited on Si(001) substrates by a plasma enhanced chemical vapor deposition (PECVD) technique using CH$_4$and $N_2$as reaction gases were thermally annealed at various temperatures under$ N_2$atmosphere, then their physical properties were investigated particularly as a function of annealing temperature. Above $600^{\circ}C$ a small amount of crystalline $\beta$-$C_3$$N_4$ phase evolves, while the film surface becomes very rough due to agglomeration of fine grains on the surface. As the annealing temperature increases, both the hardness and the $sp^3$ bonding nature are enhanced. In contrast to our expectation, higher annealing temperature results in a relatively higher friction mainly due to big increase in roughness at that temperature.