• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.56-59
• /
• 2002

This paper presents a study on the permittivities of the E-glass fabric/epoxy composite laminates containing carbon black dispersions at microwave frequency. Measurement showed that the complex permittivities of the composites depend strongly on the natures and concentrations of the carbon black dispersion. A new scheme to obtain a mixing law for the estimation of complex permittivity is proposed. The experimental values of the complex permittivities were compared to those calculated. Simultaneously, the complex permittivity of carbon black itself was also calculated by the scheme.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.89-92
• /
• 2001

Drop weight impact tests were performed to investigate the impact behavior of carbon fiber/epoxy composite laminates reinforced by short fibers and other interleaving materials. Characterization techniques, such as cross-sectional fractography and scanning acoustic microscopy, were employed quantitatively to assess the internal damage of some composite laminates. Scanning electron microscopy was used to observe impact damage and fracture modes on specimen fracture surfaces. The results show that composite laminates experience various types of fracture; delamination, intra-ply cracking, matrix cracking and fiber breakage depending on the interlayer materials. Among the composite laminates tested in this study, the composites reinforced by Zylon fibers showed very good impact damage resistance with medium level of damage, while the composites interleaved by poly(ethylene-co-acrylic acid) (PEEA) film is expected to deteriorate the bulk strength due to the reduction of fiber volume fraction, even though the damaged area is significantly reduced.

• Composites Research
• /
• 제26권6호
• /
• pp.349-354
• /
• 2013

본 논문에서는 Carbon/Epoxy 복합재 적층판에 대하여 실사격 실험을 수행하였으며, 복합재 적층판의 흡수에너지를 예측하기 위한 개선된 방법을 제시하였다. 고속충격실험 과정에서 충격체의 질량손실을 고속카메라를 통하여 거시적으로 확인하였으며, 따라서 이를 고려하여 복합재 적층판의 흡수에너지를 계산하였다. 고속충격을 받는 복합재 적층판의 흡수에너지를 예측하기 위한 모델을 제시하였으며, 복합재 적층판의 흡수에너지는 크게 정적에너지와 동적에너지로 분류하였다. 정적에너지 계산은 섬유의 파손과 정적 탄성에너지와 관련 있는 준정적 관통실험식을 통해 구한 관통에너지를 사용하였다. 동적에너지는 변형되는 시편의 운동에너지와 손실된 파편 질량들의 운동에너지로 나뉠 수 있다. 최종적으로 충격체 질량손실을 고려하여 예측된 흡수에너지와 실험결과를 비교/분석하였다.

• Advanced Composite Materials
• /
• 제18권3호
• /
• pp.251-264
• /
• 2009

Nonlinear mechanical behaviors of unidirectional carbon fiber-reinforced plastic (CFRP) laminates using cup-stacked carbon nanotubes (CSCNTs) dispersed epoxy are evaluated and compared with those of CFRP laminates without CSCNTs. Off-axis compression tests are performed to obtain the stress-strain relations. One-parameter plasticity model is applied to characterize the nonlinear response of unidirectional laminates, and nonlinear behaviors of laminates with and without CSCNTs are compared. Clear improvement in stiffness of off-axis specimens by using CSCNTs is demonstrated, which is considered to contribute the enhancement of the longitudinal compressive strength of unidirectional laminates and compressive strength of multidirectional laminates. Finally, longitudinal compressive strengths are predicted based on a kink band model including the nonlinear responses in order to demonstrate the improvement in longitudinal strength of CFRP by dispersing CSCNTs.

• Composites Research
• /
• 제28권1호
• /
• pp.1-5
• /
• 2015

In this paper the influence of fiber orientation of basalt and carbon inter-ply fabrics on the flexural properties of hybrid composite laminates was experimentally investigated. Four types of basalt/carbon/epoxy inter-ply hybrid composite laminates with varying angle ply orientation of reinforced basalt fiber and fixed orientation of carbon fiber were fabricated using hand lay-up technique. Three point bending test was performed according to ASTM 7264. The fracture surface analysis was carried out by scanning electron microscope (SEM). The results obtained from the four laminates were compared. Lay-up pattern of $[0B/+30B/-30B/0C]_S$ exhibits the best properties in terms of flexural strength and flexural modulus. Scanning electron microscopy results on the fracture surface showed that the interfacial de-bonding between the fibers and epoxy resin is a dominant fracture mode for all fiber lay-up schemes.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.250-255
• /
• 2000

Damage induced by low velocity impact loading in aircraft composite laminates is the form of failure which is occurred frequently in aircraft. Low velocity impact can be caused either by maintenance accidents with tool drops or by in-flight impacts with debris. As the consequences of impact loading in composite laminates, matrix cracking, delamination and eventually fiber breakage for higher impact energies can be occurred. Even when no visible impact damage is observed, damage can exist inside of composite laminates and the carrying load of the composite laminates is considerably reduced. The reduction of strength and stiffness by impact loading occurs in compressive loading due to laminate buckling in the delaminated areas. The objective of this study is to determine inside damage of composite laminates by impact loading and to determine residual compressive strength and the damage growth mechanisms of impacted composite laminates. For this purpose a series of impact and compression after impact tests are carried out on composite laminates made of carbon fiber reinforced epoxy resin matrix with lay up pattern of $[({\pm}45)(0/90)_2]s$ and $[({\pm}45)(0)_3(90)(0)_3({\pm}45)]$. UT-C scan is used to determine impact damage characteristics and CAI(Compression After Impact) tests are carried out to evaluate quantitatively reduction of compressive strength by impact loading.

• Composites Research
• /
• 제25권6호
• /
• pp.191-197
• /
• 2012

본 연구에서는 수치적 시뮬레이션을 통해 탄소/에폭시 복합재 적층판의 고속충돌 관통 거동을 연구하였다. 해석은 상용유한요소 해석프로그램인 LS-DYNA를 사용하여 해석을 수행하였고, 적층판 및 구형 강철 충격체 모두 3차원 요소로 모델링 하였다. 해석에는 적층순서가 $[45/0/-45/90]_{ns}$인 16 및 24장으로 된 복합재 적층판을 고려하였으며 충격체의 초기속도는 140-250 m/s 범위의 값을 사용하였다. 해석결과 예측된 잔류속도는 실험값과 비교적 잘 일치하였다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2000년도 추계학술발표대회 논문집
• /
• pp.119-123
• /
• 2000

The characteristics of fatigue life distribution for Carbon/epoxy composite laminates was investigated under tension-tension loading(R=0.1). The statistical nature of the fatigue life of the composite materials was analyzed by Weibull, normal, lognormal distributions As a result, it was observed that the correlation between the experimental results and the theoretical predictions for the fatigue life is good. The distribution of the static ultimate strength has the characteristic of lognormal distribution and distribution of the fatigue life has characteristics of the weibull distribution.

• 한국안전학회지
• /
• 제13권4호
• /
• pp.41-48
• /
• 1998

In this paper, an investigation was performed on the dynamic interlaminar fracture toughness of CFRP(carbon fiber reinforcement plastics) composite laminates. Composite laminates used in this experimentation are CF/EPOXY and CF/PEEK laminated plates. In the experiments, Split Hopkinson's Bar(SHPE) test was applied to dynamic and notched flexure test. The mode Ⅱ fracture toughness of each unidirectional CFRP was estimated by the analyzed deflection of the specimen and J-integral with the measured impulsive load and reactions at the supported points. As an experimental result, the vibration amplitude of CF/PEEK laminates appear more than that of CF/EPOXY laminates for the J-integral and displacement velocity at a measuring point. Also, it is thought that the dynamic fracture toughness of two kind specimens(CFRP/EPOXY and CF/PEEK) with the in crease of displacement velocity becomes a little greater at a measuring point within the range of measurement.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2005년도 제25회 추계학술대회논문집
• /
• pp.422-425
• /
• 2005

가로 등방성 복합재료에서 반사되거나 굴절된 파동의 속도와 입자방향, 그리고 진폭을 운동방정식과 구성방정식 그리고 파동수와 진동수로 표현된 변위식을 사용하여 구하였다. Snell 법칙을 사용하여 Eigenvalue 문제를 풀어 파동속도를 구하였으며 그 결과는 T300 Carbon fiber/5208 Epoxy 재료 성질을 이용하여 검증하였다. 이러한 분석은 수분 침수 C-scan을 이용하여 가로등방성 복합재료의 결점을 찾아내는데 응용될 수 있다.