• Restorative Dentistry and Endodontics
• /
• 제26권1호
• /
• pp.41-50
• /
• 2001

The purpose of this study was to examine the influences of camphoroquinone on the properties of five experimental composites. The contents of camphoroquinone were varied as 0.2%, 0.3%, 0.4%, 0.5%, and 0.6%, with silanized filler 75% and tertiary amine 0.2%. Five kinds of experimental composites were prepared, and diametral tensile strength, shear bond strength, depth of cure and yellowish discoloration were tested as a measurement. Specimen numbers of 10 were applied to all test items and experimental groups. Specimens for testing the diametral tensile strengths with internal diameter of 6mm in diameter and 3mm in height were filled with 5 experimental composites which were crushed with 1mm/min cross-head speed on Instron universal testing machine (Model No. 4467). Shear bond strength was measured on specimens attached to bovine teeth enamel etched with 37% phosphoric acid. Depth of cure was measured by the measurement of height of specimens which were removed the un-polymerized portion with acetone. Yellowness measurements were made by chromometer(Minolta Co. Japan) using L$^*$a$^*$b$^*$ values. ANOVA and Multiple range tests were used analyzed data with confidence level at 95%. The mean value of the shear bond strengths ranged from 31.03MPa to 39.49MPa. Following results were obtained ; 1. Diametral tensile strength was highest in experimental group 3, then was not affected by the contents of camphoroquinone ($r^2$=0.0422). 2. Composite resins containing 0.4% camphoroquinone showed the highest shear bond strength, but there was no statistical significance (p=0.3718). 3. Camphoroquinone reduces the depth of cure in the composite resins (p=0.0004, $r^2$=0.9483). 4. Camphoroquinone made the composites yellowish ($r^2$=0.9815). These results mean that increased content of camphoroquinone reduces the depth of cure, and that camphoroquinone make composites yellowish.

• Restorative Dentistry and Endodontics
• /
• 제34권4호
• /
• pp.333-339
• /
• 2009

현행 복합레진에서 가장 많이 사용되고 있는 광중합개시제의 일종인 camphoroquinone은 중합 효과가 적고 황색을 띠기 때문에 다른 개시제에 대한 연구가 이루어져 왔다. 이에 본 연구에서는 새로운 개시제인 OPPI (p-octyloxy-phenyl-phenyl iodonium hexafluoroantimonate)를 기존의 camphoroquinone, amine과 다양한 비율로 혼합한 다음, barium glass를 첨가한 실험용 복합레진을 제조하여 각 수복재의 미세누출도를 비교, 평가하였다. 총 4종의 단량체를 제조하였으며 camphoroquinone, OPPI, amine의 조성 중량비는 다음과 같다: A군 - 0.5%, 0%, 1% / B군 - 2%, 0.2%, 2% / C군 - 0.2%, 1%, 0.2% / D군 - 1%, 1%, 2%. 이후 평균 입자 크기 1 ${\mu}m$의 3.2% silane 처리된 barium glass를 중량비 78%로 섞어 복합레진을 제조하였다. 총 55개의 소구치에 치경부를 중심으로 원형 와동을 (직경; 근원심 폭경의 2/3, 깊이; 1.5 mm) 형성한 다음, 자가부식형 접착시스템인 Hybrid Bond로 처리하고 4종의 복합레진으로 수복하였다. 연마 후 치아를 섭씨 5도와 55도에서 각기 30초씩 담궈 500회의 열순환 처리하였으며 전기화학적 방법으로 전기 전도성을 2회 (열순환 처리 후, 1주 간격으로 식염수를 교환하며 3개월 보관 후) 측정, 비교하였다. 미세누출도는 시간 경과에 따라 커지는 양상을 보였으며, 열순환 처리 직후 4종 복합레진 사이에 차이를 보이지 않았지만, 3개월 보관 후에는 D군이 가장 적었으며 C군이 가장 큰 미세누출을 보였다. 열순환 자극 직후 차이를 보이지 않았지만, 3개월 보관 후 측정치로 미루어 볼 때, OPPI와 전반적인 중합시스템이 고농도로 함유된 복합레진(D군)과 CQ와 아민만을 사용한 전통적인 복합레진(A군)이 중합개시시스템을 저농도로 함유한 복합레진(C군)에 비해 우수한 밀폐효과를 보였다. 이는 시간의 흐름에 따라 접착계면의 퇴화가 일어났거나 일부 성분이 용해가 되어 나온 것으로 보이며 앞으로 이에 대한 더 많은 연구가 필요할 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제26권2호
• /
• pp.127-133
• /
• 2001

There are several factors affecting the effectiveness of polymerization of the esthetic restorative materials. Among those factors, the initiator. camphoroquinone has the unique characteristic. of which the light sensitivity is very dependent on the wavelength of blue light. Camphoroquinone shows the most light absorption ability in the wavelength range of 470nm. So most of clinically used light curing systems adopt this phenomenon as their polymerization mechanism. The most popular way of light curing system is standard 40 second curing. But the problem of standard curing technique shows the rapid increase of resin viscosity followed by the acceleration of polymerization and the limited resin flow, resulted in reduction of the physicalproperty of restoration by retained stress. The object of this study was to verify the effects of narrow-banded wavelength on the microhardness of the esthetic restorative materials. a composite resin and a compomer, using filters which have peak wave length of 430nm, 450nm, 470nm, respectively. The results were as follows: 1. All the experimental groups showed lower hardness value than the control group. 2. In DyractAP, the hardness value by wavelength showed the same changing pattern on both upper and lower surfaces. 3. In DenFil, the hardness value by wavelength showed different changing pattern on upper and lower surfaces. 4. The hardness ratio showed similar pattern to the hardness variation of lower surface. but there was no significant difference between measurement in 10 minutes and 3 days later, besides the increase of hardness value.

• 대한소아치과학회지
• /
• 제31권2호
• /
• pp.247-255
• /
• 2004

이전의 연구에서 레진 재료를 포함한 여러 수복재료에서의 유출물이 우식 유발 세균의 성장에 영향을 줄 수 있다는 보고가 있었다. 이번 연구의 목적은 대표적인 우식 유발 세균인 Streptococcus mutans와 Streptococcus sobrinus의 성장에 대하여 레진을 구성하는 모노머들(Bis-GMA, TEGDMA, EGDMA, UDMA, HEMA, Camphoroquinone)이 어떠한 영향을 줄 수 있는지에 대하여 알아보고자 하는 것이다. 결과는 다음과 같다. 1. S. mutans와 S. sobrinus의 성장률은 6가지 레진 모노머 모두에서 0.03 mmol/L의 농도에 서 유의할만하게 감소되었다. 2. S. mutars의 성장률은 0.01 mmol/L 농도의 UDMA와 0.005mmol/L, 0.01 mmol/L 농도의 Camphoroquinone에서 대조군에 비하여 유의 할만하게 감소되었다. 3. S. sobrinus의 성장률은 0.01 mmol/L 농도의 HEMA, UDMA와 0.005 mnol/L, 0.01 mmol/L 농도의 Camphoroquinone에서 대조군에 비하여 유의할만하게 감소되었다. 4. S. sobrinus의 성장률은 0.001, 0.01, 0.03 mmol/L농도에서 대조군에 비하여 유의할만한 감소를 보였으며 각 실험군들 간에도 통계학적으로 유의 할만한 차이를 보였다. 이상의 결과를 종합하면 레진 모노머를 적용한 모든 군에서 적용하지 않은 양성 대조군에 비해 두세균의 증식률이 감소되었으며, 세균의 성장을 촉진하지 않는 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제29권6호
• /
• pp.504-514
• /
• 2004

LED 광중합기(Elipar FreeLight, 3M-ESPE)와 할로겐 광중합기(VIP Bisco)로 광조사한 수종의 상아질 접착제에 대해서 상아질 전단접착강도를 비교하였다 또한 이번 연구의 광학적 근거를 얻기 위해 두 광중합기의 파장에 따른 광강도와 스펙트럼을 비교하였다. 이번 연구에서 사용된 상아질 접착제는 Scotchbond Multipurpose (3M ESPE), Single Bond (3M ESPE). One-Step (Bisco), Clearfil SE Bond (Kuraray), Adper Prompt (3M ESPE) 이다. VIP는 487 nm에서 최대정점을 가지는 넓은 스펙트럼의 분포를 보이는 반면에, Elipar FreeLight는 465 nm에서의 최대정점을 중심으로 좁은 스펙트럼의 분포를 보였다. Clearfil SE bond를 제외하고 할로겐과 LED로 광조사 한 각 상아질 접착제에서 상아질 전단접착강도값의 유의성 있는 차이는 보이지 않았다 (P > 0.05). 이러한 결과는 camphoroquinone의 흡수스펙트럼과 LED의 좁은 영역의 스펙트럼사이에 강한 연관성으로 설명할 수 있다.

• Restorative Dentistry and Endodontics
• /
• 제26권1호
• /
• pp.23-31
• /
• 2001

The purpose of this study was to search the optimal silane concentrations for filler- silanization of seven experimental composites. Silica filer was a 25micron crushed type. 0.0%, 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, and 3.0% silane($\gamma$-methacrylooxypropyltrimethoxysilane)were added into silica-filler with weight percentage (wt%). Mixtures(silica filler/silane)were reacted at 6$0^{\circ}C$ for 72hours, and crushed into fine particles those were used as fillers for 7 experimental composites. Monomer was a 3 : 1 mixture of Bis-GMA and TEGDMA containing 0.2% tertiary amine and 0.4% camphoroquinone for light curability. A ratio for mixing the monomer and filler was 75% and 25% respectively. Seven experimental composites was classified with the concentration of silane treated, and the specimen number for each test was 10. Specimens with 6mm diameter and 3mm height dimension for measuring the diametral tensile strength were destroyed with 1mm/min cross-head speed on Instron universal testing machine (No. 4467, USA). Shear bond strength was measured on the specimens bonded to bovine enamel etched with 37% phosphoric acid solution for 1 minute Fractured surfaces were observed by SEM (Hitachi S-3200, Japan) among that of the highest values measured from each groups. Following results were obtained: 1. Experimental composites containing silanized filter showed the significantly higher diametral tensile strength and shear bond strength than the composites containing un-silanized fillers(Group1) (p<0.05). 2. In silanized filler composite resins(Group 2~7), Diametral tensile strength of Group 3 showed the significantly higher than that of Group 2 and Group 6(p<0.05). 3. Shear bond strength was higher in Group 3 than that of Group 7 (p＜0.05)in silanized fillers composite resins. 4. Fracture surface was formed in resin matrixes on the specimens from composites containing the fillers treated with 0.5% 1.0%, and 1.5% silane. These results mean that the optimal silane concentrations are exist for each fillet with its size and surface area, and that 1.0% is a optimal value for concentration to coat the 25$\mu\textrm{m}$ filler with silane.

• 구강회복응용과학지
• /
• 제33권4호
• /
• pp.245-251
• /
• 2017

1960년대 광중합 레진이 소개된 이후 현재의 수복학에서 광중합은 중요한 과정으로 고려되고 있다. 광중합을 위한 다양한 중합기들이 소개되어서 발전하면서 사용되어져 왔다. Quartz-tungsten-halogen (QTH) 광중합기는 1990년도까지 널리 사용되었으며 2000년 들어 LED 광중합기가 널리 사용되고 있다. 1세대 LED 광중합기는 여러 개의 LED가 출력을 내는 광중합기로 QTH 광중합기에 비해 높은 출력을 내짐 못했다. 2세대 LED 광중합기는 하나의 LED로도 충분한 출력을 낼 수 있게 되었으며, camphoroquinone (CQ) 이외에 부가 중합개시제를 고려하여 3세대 polywave 중합기가 시장에 출시되었다. 현재는 LED에서 방출하는 빛이 계속 switching되는 4세대 광중합기가 개발되어 출시되었다. 이러한 LED 광중합기의 발전에 따라 사용하는 광중합기의 대부분이 LED 광중합기로 자리잡고 있다. LED 광중합기의 사용의 증가에 따라 임상가들은 광중합기의 특성을 이해하고 있어야 한다. 본 리뷰 논문의 목적은 LED 광중합기에 대한 세대별 분류와 특징에 대한 정보를 주기 위함이다.

• Restorative Dentistry and Endodontics
• /
• 제25권3호
• /
• pp.421-434
• /
• 2000

The purpose of this study was to evaluate the influences of incorporation of zirconium-silicate on diametral tensile strength, shear bond strength to the enamel, and depth of cure of 7 experimental composites. One group contained no filler(group 1 or control group), and the other 6 composites contain 75% filler in which zirconium-silicate(Zr-Si) were 0%, 2%, 4%, 6%, 8%, 10% with reduced contents of silica filler, respectively. Both of fillers were treated with 1% silane (${\gamma}$-methacryloxypropyltrimethoxy silane). Light curable monomers were prepared by mixing Bis-GMA and TEGDMA with 3:1 ratio and adding camphoroquinone(CQ) 0.6% with tertiary amine 0.3%. Diametral tensile strengths of specimens with $3mm{\times}6mm$ were measured with Instron (No.4467, USA) with 1mm/min crosshead speed. Shear bond strengths of composites which bonded to bovine enamel etched with 37% phosphoric acid were measured at Instron Testing Machine with as same speed as in diametral tensile strengths. Depth of cure were measured by a method that composite was filled in cylinder mold, illuminated at one side. and uncured composite was removed with acetone, and the residual thickness of composite was measured. Following results were obtained ; 1. Composites containing 0%, 2%, or 4% zirconium-silicate filler(group 2, 3 and 4) showed the statistically higher diametral tensile strength than the others. (p<0.05) 2. Increase of zirconium-silicate filler contents reduced the diametral tensile strength of experimental composites. ($r^2$=0.8721, p=0.0002) 3. Increase of zirconium-silicate filler contents did not affect the shear bond strength of experimental composites. ($r^2$=0.2815, p=0.4067) 4. Increase of zirconium-silicate filler contents reduced significantly the depth of cure of experimental composites. ($r^2$=0.9700, p<0.0001) These results mean that the mechanical properties of composites could not be improved by incorporation of small amount of zirconium-silicate filler. Also, the increased contents of zirconium-silicates fillers was found to reduce the diametral tensile strength and depth of cure.

• Restorative Dentistry and Endodontics
• /
• 제36권4호
• /
• pp.313-323
• /
• 2011

연구목적: 여러 가지 문제점을 가지고 있는 기존의 중합개시제인 CQ와 새로운 개시제인 p-octyloxy-phenyl-phenyl iodonium hexafluoroantimonate (OPPI), 중합촉진제인 지방족 아민(DMAEMA)을 포함한 3종 중합개시시스템을 함유한 레진 모노머의 중합전환률을 증진시키기 위한 각각의 조성 비율을 알아보고 중합개시제와 중합촉진제의 비율에 따른 영향을 분석하고자 하였다. 연구 재료 및 방법: BisGMA/BisEMA/TEGDMA 조성의 레진 모노머를 제조한 다음 다양한 농도 조합의 CQ, OPPI, DMAEMA를 혼합하였다. 각각의 물질을 0.2 wt.% (저농도, L), 1.0 wt.% (중간농도, M), 2.0 wt.% (고농도, H)의 3가지 농도로 혼합하였으며, 그 농도 비율에 따라 9개의 실험군으로 제작하였다: LLL, LMM, LHH, MLM, MMH, MHL, HLH, HML, HHM (CQ-OPPI-DMAEMA의 농도) 중합 시스템이 함유된 각각의 레진 모노머를 NaCl disk에 압착한 다음 Demetron 400 광중합기를 이용하여 5초, 20초, 40초, 60초, 300초 동안 광중합 하였으며, FTIR로 전환률(Degree of Conversion, DC)을 측정하였다. 조성비율은 ANOVA와 Duncan 사후검정법을 이용하였으며 중합개시제와 중합촉진제의 비율이 같은 실험군들의 상호비교에는 T-검정도 시행하였다. 결과: 중합개시시스템을 이루는 조성들의 농도 조합에 따라 중합전환률의 차이를 보였으며, MMH 군과 HHM 군이 높은 초기 중합전환률을 보였다. 중합개시제(CQ, OPPI)와 중합촉진제인 DMAEMA의 비율에 따른 중합전환률의 차이를 보이지 않았으며, CQ의 농도는 전환률에 영향을 주지 않은 반면, OPPI의 농도는 전환률에 영향을 미쳤다. 결론: 중합전환률이 높으며 밝은 색상이 필요한 경우에는 MMH 조합을, 짙거나 불투명한 경우에는 MMH 조합이 추천된다.

• Restorative Dentistry and Endodontics
• /
• 제32권3호
• /
• pp.236-247
• /
• 2007

접착제의 술식을 간편하게 하고 효과적이며 안정적인 접착강도를 지닌 상아질 접착제를 개발하고자 isocyanate methacrylate의 농도를 달리해 상아질에 적용하여 전단결합강도를 측정하고 응집파괴양상을 분석, 평가하였다. Isocyanate methacrylate의 농도에 따라 0% (대조군), 2%, 4%, 6%, 8%, 10%, 및 12%의 7개 실험군으로 분류하였으며 , Instron (No.4466.USA)를 이용하여 복합레진의 전단 결합강도를 측정하고 Resin tag 및 응집파괴를 주사전자현미경으로 관찰해 다음 결론을 얻었다. 1. Cyanate methacrylate 8%군이 가장 높은 전단 결합강도는 나타내었으나 (33.62 KPa), 통계학적 유의성이 없었다 (P > 0.05). 2. Cyanate methacrylate 2% ,4% 및 6%군은 응집성파괴빈도가 대조군 (0%군)과 비교하여 높게 나타났다. 3. Cyanate menthacrylate군에서 레진tag의 길이는 짧게 나타났다. 이상의 연구의 결과로 cyanate methacrylate가 collagen과 반응하여 상아질 내로 침투를 방해하며 레진 tag의 길이를 짧게 하며 상아질의 유기성분과의 반응에 의하여 결합강도는 높아질 수 있으나, 상아질 자체의 강도가 낮아질 수 있어 상아질에 대한 결합강도의 실질적인 증가는 확인할 수 없었다.