• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.3
• /
• pp.226-233
• /
• 2023

In this study, two phases were conducted to investigate the direct injection of gaseous CO₂ into cement mortar. The aim was to advance carbon capture, utilization, and storage (CCUS) technology by harnessing industrial waste CO₂ from the domestic ready-mixed concrete industry. In the first phase, the factors influencing the physical properties of cement mortar when using gaseous CO₂ were identified. This included a review of materials to achieve physical properties comparable to a reference formulation. As a result of this phase, it was confirmed that traditional approaches, such as adjusting the water-to-cement ratio, had limitations in achieving the desired physical properties. Consequently, the second phase focused on the optimization of CO₂-injected mortar. This involved studying the CO₂ application and mixing method for cement mortar. Changes in properties were observed when gaseous CO₂ was injected into the mortar. The optimal injection quantity and time to enhance the compressive strength of mortar were determinded. As a result, this study indicated that an extra mixing time exceeding 120 seconds was necessary, compared to conventional mortar. The optimal CO₂ injection rate was identified as 0.1 to 0.2 % by weight of cement, taking both flowability and compressive strength performance into account. Increasing the CO₂ injection time did not further enhance strength. For this approach to be employed as a CCUS technology, additional studies are required, including a microstructural analysis evaluating the amount of immobilized CO₂.

• Journal of the Korea Institute of Building Construction
• /
• v.24 no.1
• /
• pp.11-21
• /
• 2024

This research elucidates the fundamental properties of carbon dioxide (CO₂)-cured mortar as influenced by varying substitution rates of blast furnace slag fine powder. The findings indicate that CO₂ curing enhances the formation of calcium carbonate (CaCO₃), contributing to pore reduction and the early development of strength. While calcium hydroxide (Ca(OH)₂) plays a more pivotal role in the primary development of strength compared to CaCO₃, an increase in the substitution rate of blast furnace slag fine powder results in reduced production of Ca(OH)₂. Nonetheless, the maintenance of strength through CaCO₃ formation is observed even after the depletion of Ca(OH)₂, suggesting that the required performance can be sustained post-exposure to the atmosphere following CO₂ curing. It is noted that substitution rates exceeding 50% lead to performance deterioration due to CO₂, highlighting the necessity for careful adjustment of the substitution ratio.

• Resources Recycling
• /
• v.29 no.3
• /
• pp.3-10
• /
• 2020

The chlorination kinetics of synthetic rutile prepared by selective chlorination of ilmenite with Cl₂ and CO gas mixture were studied in a fluidized bed. Th e effects of reaction temperature, reaction time, and the ratio of Cl₂ and CO partial pressure ($p_{Cl_2}/p_{CO}$) on the conversion rate of TiCl₄ were investigated. The conversion rate of TiC₄ was low under the high $p_{Cl_2}/p_{CO}$ conditions. Moreover, it was considered that the partial pressure of CO gas was more effective than that of Cl₂ gas when comparing the stoichiometric conversion rate and experimental results of high CO partial pressure. Considering the porous structure of particles, the rate controlling step of the chlorination of synthetic rutile was determined to be chemical reaction and the activation energy was calculated as 53.77 kJ/mol.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.682-688
• /
• 2012

In this study we aimed to examine the co-doping effects of 1/6 mol% $Co_3O_4$ and 1/4 mol% $Cr_2O_3$ (Co:Cr = 1:1) on the reaction, microstructure, and electrical properties, such as the bulk defects and the grain boundary properties, of ZnO-$Bi_2O_3-Sb_2O_3$ (ZBS; Sb/Bi = 0.5, 1.0, and 2.0) varistors. The sintering and electrical properties of Co,Cr-doped ZBS, ZBS(CoCr) varistors were controlled using the Sb/Bi ratio. Pyrochlore ($Zn_2Bi_3Sb_3O_{14}$), ${\alpha}$-spinel ($Zn_7Sb_2O_{12}$), and ${\delta}-Bi_2O_3$ were formed in all systems. Pyrochlore was decomposed and promoted densification at lower temperature on heating in Sb/Bi = 1.0 by Cr rather than Co. A more homogeneous microstructure was obtained in all systems affected by ${\alpha}$-spinel. In ZBS(CoCr), the varistor characteristics were improved (non-linear coefficient, ${\alpha}$ = 20~63), and seemed to form ${Zn_i}^{{\cdot}{\cdot}}$(0.20 eV) and ${V_o}^{\cdot}$(0.33 eV) as dominant defects. From impedance and modulus spectroscopy, the grain boundaries were found to be composed of an electrically single barrier (0.94~1.1 eV) that is, however, somewhat sensitive to ambient oxygen with temperature. The phase development, densification, and microstructure were controlled by Cr rather than by Co but the electrical and grain boundary properties were controlled by Co rather than by Cr.

• Journal of the Korean Magnetics Society
• /
• v.19 no.6
• /
• pp.216-221
• /
• 2009

Y-type barium ferrite $Ba_2Co_2Fe_{12}O_{22}$ was synthesized by a solid state reaction method. Effects of metal ion mole ratio and calcination temperatures on magnetic properties and microstructures of the synthesized powders were investigated. Phase analysis and microstructure observation were performed with a XRD (X-ray diffractometer) and a FESEM (field effect scanning electron microscope), respectively. Magnetic properties of the powders were measured with a VSM (vibrating sample magnetometer). Single phase Y-type was synthesized when metal ion mole fraction $Fe^{3+}:\;Ba^{2+}:\;Co^{2+}$ was 6 : 1 : 1 and calcination temperature was $1050\;{^{\circ}C}$. High saturation magnetization value of 39.1 emu/g was obtained when metal ion mole fraction $Fe^{3+}:\;Ba^{2+}:\;Co^{2+}$ was 8 : 1 : 1 and calcination temperature was $1200\;{^{\circ}C}$.

• Clean Technology
• /
• v.26 no.1
• /
• pp.72-78
• /
• 2020

The use of fossil fuel and biogas production causes air pollution and climate change problems. Research endeavors continue to focus on converting methane and carbon dioxide, which are the major causes of climate change, into quality energy sources. In this study, a novel plasma-carbon converter was proposed to convert biogas into high quality gas, which is linked to photovoltaic and wind power and which poses a problem on generating electric power continuously. The characteristics of conversion and gas production were investigated to find a possibility for biogas conversion, involving parametric tests according to the change in the main influence variables, such as O₂/C ratio, total gas feed rate, and CO₂/CH₄ ratio. A higher O₂/C ratio gave higher conversions of methane and carbon dioxide. Total gas feed rate showed maximum conversion at a certain specified value. When CO₂/CH₄ feed ratio was decreased, both conversions increased. As a result, the production of solar fuel by plasma oxidation destruction-carbon material gasification conversion, which was newly suggested in this study, could be known as a possibly useful technology. When O₂/C ratio was 0.8 and CO₂/CH₄ was 0.67 while the total gas supply was at 40 L min^-1 (VHSV = 1.37), the maximum conversions of carbon dioxide and methane were achieved. The results gave the highest production for hydrogen and carbon dioxide which were high-quality fuel.

• Fire Science and Engineering
• /
• v.26 no.4
• /
• pp.42-47
• /
• 2012

In the study, fire extinguishing concentration of $K_2CO_3$-Zeolite composite was measured. Zeolite composite is a porous adsorbent which has small particle size, low density and anti-catalytic effect. Scanning Electron Microscopy, X-Ray diffraction and thermal analysis were also conducted to investigate the structural properties of composite. The result showed that despite of weight ratio, the extinguishing concentration of the composite was lower than pure $K_2CO_3$. The extinguishing concentration of $K_2CO_3$-Zeolite composite which has weight ratio of 7 : 3 was 5.72 times lower than that of pure $K_2CO_3$ and 1.1 times lower than that of ABC powder. The SEM and XRD patterns showed that $K_2CO_3$ was adsorbed on the Zeolite properly, and through the thermal analysis, it was founded that the composite is more effective extinguishing agent than pure $K_2CO_3$.

• Proceedings of the Korean Society of Crop Science Conference
• /
• 2022.10a
• /
• pp.168-168
• /
• 2022

According to the 5th Climate Change Report, global average temperature in 2081~2100 will increase 1.8℃ based on RCP 4.5 and 3.7℃ based on RCP 8.5 from the current climate value (IPCC Working Group I AR5). As temperature is expected to increase due to global warming and the intensity and frequency of rainfall are expected to increase, damage to crops is expected, and countermeasures must be taken. This study intends to evaluate rice growth in terms of nitrogen utilization efficiency according to future climate change conditions. In this experiment, Oryza sativa cv. Shindongjin were planted at the SPAR facility of the NICS in Wanju-gun, Jeollabuk-do on June 10, and were planted and grown according to the standard cultivation method. Cultivation conditions are high temperature, high CO₂ (current temperature+4.7℃·CO₂ 800ppm), high temperature (current temperature+4.7℃·CO₂ 400ppm), current climate (current tempreture·CO₂ 400 ppm). Nitrogen was varied as 0, 9, 18 kg/10a. The N content and C/N ratio of all rice leaves, stems, and seeds increased at high temperature, and the N content and C/N ratio decreased under high temperature and high CO₂ conditions com pared to high temperature. Compared to the current climate, NUE increases by about 8% under high temperature and high CO₂ conditions and by about 2% under high temperature conditions. This seems to be because the increase in temperature and CO₂ induced the increase in biomass. ANUE related to yield decreased by about 70% compared to the current climate under high temperature conditions, and decreased by about 45% at high temperature and high CO₂, showing a tendency to decrease compared to high temperature. This appears to be due to reduced fertility and poor ripening due to high temperature stress. However, as the nitrogen increased, the number of ears and the number of grains increased, slightly offsetting the production reduction factor.

• Transactions of the Korean hydrogen and new energy society
• /
• v.35 no.3
• /
• pp.249-256
• /
• 2024

The cement industry emits a large amount of greenhouse gases compared to other industries, with about 60% of CO₂ emissions from the decarbonation of limestone and about 40% from the combustion of fossil fuels. Therefore, the cement industry needs to reduce greenhouse gases through carbon capture, utilization, and storage technology. Capturing CO₂ and synthesizing it into methanol is feasible and also useful as raw material for the chemical industry and as marine fuel. In this study, We aimed to produce methanol from syngas produced by capturing CO₂ emissions. Process simulations were performed under various conditions such as syngas ratio, temperature, and pressure for the production of synthesis gas and methanol, and the results showed that the optimal amount of methanol production at a synthesis gas ratio of 2.03.

• Korean Journal of Materials Research
• /
• v.16 no.2
• /
• pp.106-110
• /
• 2006

We have investigated the effect of the experimental variables such as temperature and pressure on conformality of Co films deposited over high aspect ratio trenches using $Co_2(CO)_8$ as a precursor. The results show that the conformality of Co films is a strong function of temperature and process pressure. Lowering the pressure and temperature significantly improves the conformality. As the pressure decreases from 0.6 Torr to 0.2 Torr at $50^{\circ}C$, the bottom coverage of Co films over $0.2{\mu}m$ width trenches with an aspect ratio of 13 to 1 significantly increases to 85%. However, further increasing the temperature from 50 to $60^{\circ}C$ at the pressure of 0.2 Torr degrades the bottom coverage to 14%. In contrast, the extremely low pressure of 0.03 Torr allows the excellent conformal deposition of Co films up to $70^{\circ}C$. This can be attributed to the suppression of homogeneous reaction in the gas phase, which can create the intermediate products with high sticking coefficient. In addition, the Co films deposited at $50^{\circ}C$ show the low resistivity with negligible contamination. As a result, the newly developed Co process using MOCVD can be implemented into the next generation devices with complex shapes.