• Nuclear Engineering and Technology
• /
• 제49권4호
• /
• pp.663-667
• /
• 2017

Delayed hydride cracking (DHC) was first observed in pressure tubes in Canadian CANDU reactors. In light water reactors, DHC was not observed until the late 1990s in high-burnup boiling water reactor (BWR) fuel cladding. In recent years, the focus on DHC has resurfaced in light of the increased interest in the cladding integrity during interim conditions. In principle, all spent fuel in the wet pools has sufficient hydrogen content for DHC to operate below $300^{\circ}C$. It is therefore of importance to establish the critical parameters for DHC to operate. This work studies the threshold stress intensity factor ($K_{IH}$) to initiate DHC as a function of temperature in Zry-4 for temperatures between $227^{\circ}C$ and $315^{\circ}C$. The experimental technique used in this study was the pin-loading testing technique. To determine the $K_{IH}$, an unloading method was used where the load was successively reduced in a stepwise manner until no cracking was observed during 24 hours. The results showed that there was moderate temperature behavior at lower temperatures. Around $300^{\circ}C$, there was a sharp increase in $K_{IH}$ indicating the upper temperature limit for DHC. The value for $K_{IH}$ at $227^{\circ}C$ was determined to be $2.6{\pm}0.3MPa$ ${\surd}$m.

• 방사성폐기물학회지
• /
• 제17권4호
• /
• pp.375-387
• /
• 2019

본 연구에서는 최근 개발중인 360 다발 장전용량의 중수로 사용후핵연료 운반용기에 대한 설계기준연료의 방사선원항 평가와 용기외부에서의 방사선량률 계산을 수행하였다. 그리고 국·내외 방사선적 안전성평가와 관련한 기술기준 부합여부를 판단하고 결과의 적합성을 제시하였다. 방사선원항으로 작용하는 설계기준연료 선정을 위해 월성원전에서 운영중인 운반 용기 및 두 가지 방식의 건식저장시설에 적용된 설계기준연료의 사양 및 특성을 조사하였다. 각 운반·저장 시스템 별 설계 기준연료의 연소도, 최소 냉각기간 및 중간저장시설로의 운반시점 등을 바탕으로 연소도 7,800 MWD/MTU와 최소 냉각기간 6년을 설계기준연료로 설정하였다. 설계기준연료의 방사선원항은 SCALE 전산코드의 ORIGEN-ARP모듈을 이용하여 평가하였다. 운반용기의 방사선차폐평가는 MCNP6 전산코드를 이용하였으며, 기술기준에서 요구하는 운반용기 외부에서의 방사선량률 평가를 정상 및 사고조건으로 구분하여 수행하였다. 방사선량률 평가결과, 정상운반조건의 운반용기 표면 및 운반용기 표면 2 m 이격지점에서 계산된 최대 방사선량률은 각각 0.330 mSv·h^-1와 0.065 mSv·h^-1로 도출되어 선량률 제한치인 2.0 mSv·h^-1와 0.1 mSv·h^-1를 모두 만족하는 결과를 도출하였다. 또한 운반사고조건하 운반용기 표면 1 m 지점에서의 최대 방사선량률은 0.321 mSv·h^-1로서 기술기준인 10.0 mSv·h^-1 미만으로 평가되어, 대용량 중수로 사용후핵연료 운반용기는 방사선적 안전성을 확보하는 것으로 나타났다.

• Nuclear Engineering and Technology
• /
• 제28권4호
• /
• pp.349-358
• /
• 1996

The leaching behavior of uranium from unirradiated CANDU UO$_2$ fuel pellet in the spent fuel wet storage and disposal conditions has been investigated. A modified IAEA leach test method was used, and then the extent of leaching was monitored by analysis for uranium in the leachant. The leach test has been performed in various leachants(demineralized water and boric acid solution at pH=6, synthetic granite groundwater) for a long-term period of 5.4 years, and the effect of temperature on the leach rate of uranium has been analyzed. The leach rates of uranium at $25^{\circ}C$ were dependent on the leachants. Over initial 100 days of leach periods, the leach rate in groundwater was the highest in three leachants and no significant differences of leach rates ore observed in the demineralized oater and boric acid solution. But these leach rates in three leachants around 2,000 days at $25^{\circ}C$ appeared to be reached the steady rates in the range of 1~5$\times$10$^{-8}$ g/$\textrm{cm}^2$ day. The leach rate of uranium in groundwater shooed to be independent of the temperature, but those in both demineralized water and boric acid solution increased with temperature. These results show that the leaching behavior of uranium from UO$_2$ fuel in both the demineralized water ann boric acid may be controlled tv the surface oxidative.dissolution reaction of UO$_2$ and the leach rate of uranium in groundwater at room temperature could mainly be controlled by the complex reaction of dissolved uranyl ions with carbonate ions and no variation of leach rate of UO$_2$ in groundwater with temperature may be due to the local deposition of passivating uranyl phases on the surface.