• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1437-1442
• /
• 1994

Self propagating synthesis and thermal explosion of combustion reactions were applied to Al/K2Cr2O7/Al2O3 system as the first stage for a production of magnesia-chromium refractory. Several factors related to products made by two combustion reactions were considered and properties of products were characterised. Two processes were required to preheat upto at least 80$0^{\circ}C$ for the thermal explosion and the self propagating synthesis. These processes were so violent and explosive that alumina as diluent was added to the system in order to absorb the reaction heat and reduce the reaction rate. The products consisted of crystal phases of KAl5O8, Cr2O3, Al2O3, K2CrO4, and K2Al2O4.3H2O. The amount of KAl5O8 and K2Al2O4.3H2O crystal phases of products were decreased with further addition of alumina.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.620-625
• /
• 2012

A general synthetic method to make $Fe_3O_{4-{\delta}}$ (activated magnetite) is the reduction of $Fe_3O_4$ by $H_2$ atmosphere. However, this process has an explosion risk. Therefore, we studied the process of synthesis of $Fe_3O_{4-{\delta}}$ depending on heat-treatment conditions using $FeC_2O_4{\cdot}2H_2O$ in Ar atmosphere. The thermal decomposition characteristics of $FeC_2O_4{\cdot}2H_2O$ and the ${\delta}$-value of $Fe_3O_{4-{\delta}}$ were analyzed with TG/DTA in Ar atmosphere. ${\beta}-FeC_2O_4{\cdot}2H_2O$ was synthesized by precipitation method using $FeSO_4{\cdot}7H_2O$ and $(NH_4)_2C_2O_4{\cdot}H_2O$. The concentration of the solution was 0.1 M and the equivalent ratio was 1.0. ${\beta}-FeC_2O_4{\cdot}2H_2O$ was decomposed to $H_2O$ and $FeC_2O$4 from $150^{\circ}C$ to $200^{\circ}C$. $FeC_2O4$ was decomposed to CO, $CO_2$, and $Fe_3O_4$ from $200^{\circ}C$ to $250^{\circ}C$. Single phase $Fe_3O_4$ was formed by the decomposition of ${\beta}-FeC_2O_4{\cdot}2H_2O$ in Ar atmosphere. However, $Fe_3C$, Fe and $Fe_4N$ were formed as minor phases when ${\beta}-FeC_2O_4{\cdot}2H_2O$ was decomposed in $N_2$ atmosphere. Then, $Fe_3O_4$ was reduced to $Fe_3O_{4-{\delta}}$ by decomposion of CO. The reduction of $Fe_3O_4$ to $Fe_3O_{4-{\delta}}$ progressed from $320^{\circ}C$ to $400^{\circ}C$; the reaction was exothermic. The degree of exothermal reaction was varied with heat treatment temperature, heating rate, Ar flow rate, and holding time. The ${\delta}$-value of $Fe_3O_{4-{\delta}}$ was greatly influenced by the heat treatment temperature and the heating rate. However, Ar flow rate and holding time had a minor effect on ${\delta}$-value.

• Advances in concrete construction
• /
• v.3 no.4
• /
• pp.283-293
• /
• 2015

This paper presents the effects of elevated temperatures of $400^{\circ}C$ and $800^{\circ}C$ on the residual compressive strength and failure behaviour of fibre reinforced concretes and comparison is made with that of unreinforced control concrete. Two types of short fibres are used in this study e.g., steel and basalt fibres. The results show that the residual compressive strength capacity of steel fibre reinforced concrete is higher than unreinforced concrete at both elevated temperatures. The basalt fibre reinforced concrete, on the other hand, showed lower strength retention capacity than the control unreinforced concrete. However, the use of hybrid steel-basalt fibre reinforcement recovered the deficiency of basalt fibre reinforced concrete, but still slightly lower than the control and steel fibres reinforced concretes. The use of fibres reduces the spalling and explosive failure of steel, basalt and hybrid steel-basalt fibres reinforced concretes oppose to spalling in deeper regions of ordinary control concrete after exposure to above elevated temperatures. Microscopic observation of steel and basalt fibres surfaces after exposure to above elevated temperatures shows peeling of thin layer from steel surface at $800^{\circ}C$, whereas in the case of basalt fibre formation of Plagioclase mineral crystals on the surface are observed at elevated temperatures.

• The KIPS Transactions:PartC
• /
• v.13C no.4 s.107
• /
• pp.441-446
• /
• 2006

In recent years, WDM networks have received much attention as the Internet backbone networks because of the explosive growth of the Internet IP-based traffic. The Optical Burst Switching (OBS) has been proposed as an effective optical switching technology in the WDM networks. The OBS has the advantages in 1) the high usage rate of the bandwidth, and 2) no necessity of optical buffer. However, the OBS has the burst-contention problem in the networks. The deflection routing is proposed as one of means to solve this problem. In this paper, we propose a new routing method to minimize burst loss in the deflection routing based networks. In addition, we propose a QoS control method using a new routing algorithm. Finally, we show the variety of the proposed methods by computer simulations.

• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.253-258
• /
• 2012

Activated magnetite ($Fe_3O_{4-{\delta}}$) was applied to reducing $CO_2$ gas emissions to avoid greenhouse effects. Wet and dry methods were developed as a $CO_2$ removal process. One of the typical dry methods is $CO_2$ decomposition using activated magnetite ($Fe_3O_{4-{\delta}}$). Generally, $Fe_3O_{4-{\delta}}$ is manufactured by reduction of $Fe_3O_4$ by $H_2$ gas. This process has an explosion risk. Therefore, a non-explosive process to make $Fe_3O_{4-{\delta}}$ was studied using $FeC_2O_4{\cdot}2H_2O$ and $N_2$. $FeSO_4{\cdot}7H_2O$ and $(NH_4)_2C_2O_4{\cdot}H_2O$ were used as starting materials. So, ${\alpha}-FeC_2O_4{\cdot}2H_2O$ was synthesized by precipitation method. During the calcination process, $FeC_2O_4{\cdot}2H_2O$ was decomposed to $Fe_3O_4$, CO, and $CO_2$. The specific surface area of the activated magnetite varied with the calcination temperature from 15.43 $m^2/g$ to 9.32 $m^2/g$. The densities of $FeC_2O_4{\cdot}2H_2O$ and $Fe_3O_4$ were 2.28 g/$cm^3$ and 5.2 g/$cm^3$, respectively. Also, the $Fe_3O_4$ was reduced to $Fe_3O_{4-{\delta}}$ by CO. From the TGA results in air of the specimen that was calcined at $450^{\circ}C$ for three hours in $N_2$ atmosphere, the ${\delta}$-value of $Fe_3O_{4-{\delta}}$ was estimated. The ${\delta}$-value of $Fe_3O_{4-{\delta}}$ was 0.3170 when the sample was heat treated at $400^{\circ}C$ for 3 hours and 0.6583 when the sample was heat treated at $450^{\circ}C$ for 3 hours. $Fe_3O_{4-{\delta}}$ was oxidized to $Fe_3O_4$ when $Fe_3O_{4-{\delta}}$ was reacted with $CO_2$ because $CO_2$ is decomposed to C and $O_2$.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.2 s.17
• /
• pp.109-117
• /
• 2004

We synthesized energetic prepolymer(2-nitrato ethyl oxirane, NEO) for plastic-bonded explosive and measured its thermodynamic parameters. 2-Nitrato ethyl oxirane(NEO) as a monomer was synthesized from 4-butene-ol, the first-step was preparation of 1-nitrate-3-butene and second-step was synthesized 2-nitrate-ethyl oxirane from 1nitrate-3-butene and then polymerized by cationic ring opening polymerization. The unreacted monomer concentration was measured by GC. The thermodynamic parameters were obtained from the ceiling temperature(Tc) values of 1 mole monomer at each reaction temperature. We varied feed rate of monomer, concentration of initiator and monomer to control molecular weight and polydispersity of perpolymer(NEO). Number average molecular weight(Mn), polydispersity(PD), and glass transition temperature(Tg), viscosity of prepolymer(NEO) were 2000, 1.07, $-55^{\circ}C$ and 300 poise respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.837-841
• /
• 2003

Duplex microstructure of zirconia and alumina has been achieved via an organic-inorganic solution technique. Zirconium 2,4-pentanedionate, aluminum nitrate and polyethylene glycol were dissolved in ethyl alcohol without any precipitation. The organicinorganic precursor gels were turned to porous powders having volume expansion through explosive, exothermic reaction during drying process. The volume expansion was caused by abrupt decomposition of the organic groups in the gels during the vigorous exothermic reaction. The volume expanded, porous powders were crystallized and densified at 1500$^{\circ}C$ for 1 h. At the optimum amount of the PEG polymer, the metal cations were well dispersed in the solution and a homogeneous polymeric network was formed. The polymer content also affected on the specific surface area of the synthesized powder and the grain size of the sintered composite.

• Journal of the Korean Professional Engineers Association
• /
• v.14 no.3
• /
• pp.9-21
• /
• 1981

The rationalization for Tunnel Drifting is based on the high productivity which is achievable due to Continuous work with a Jumbo Drill, resulting in a much higher efficiency them the Conventional method of blasting, mucking and supporting services. Large projects of over 4,000m Tunnel Drifting are condidated to justify the use of a Jumbo Drill with a combination of superior explosives, machinery and techniques. During a Tunnel Drifting test, Gulita, Nabit and slurry made by Nitro Nobel were employed with following results. 1, Conditions: a. Granite Rock with Two free face b. Burden (W), 2m c. Diameter of hole, 42mm d. Depth of hole 3.5m e. Hole pitch 0.6m f. Charged Explosive per hole Gelatin Dynamite 4 pieces (112.5${\times}$4ea)+Guuita 5 pieces(110g${\times}$5ea) g. Simal-taneous Detonation h. After the blasting resultant rock size was Less 40% of the 0.3m Lumps. 2. Calculation results W=q/Wn=100cm‥‥‥Burden in simultaneous blasting 0.865kg(7.7ea)/hole ‥‥‥Amount of charge but hole pitch is 1.5W-2W The estimated cost of using a Jumbo Drill for the Construction of a 3,000,000 bbL sub-surface oil storage would be as follows: This calculation is based on the Jumbo Drill advancing 3.6m per blasting cycle. Unit cost/bbL Excavation $3.13 The attached sheet shows ideal Drilling pattern with Burn Cut & Smooth blasting method. In conclusion, it is my opinion that this method will assure safety and save cost and improve our technical know-how.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.4C
• /
• pp.283-290
• /
• 2006

Concrete has advantages in fire situations as it is non-combustible and has low thermal conductivity. However, concrete that is not designed against fire can experience significant explosive spalling from the build-up of pore pressures and internal tensile stresses when heated. In this study, the performance of wet-mixed high strength sprayed polymer mortar for fire resistance of tunnel system was evaluated by experimentally and numerically. The fire test was performed in fire resistance(electric) furnace according to RABT(Richtlinien fur die Ausstatung und den Betrieb von $Stra{\beta}entunneln$) time heating temperature curve, so as to evaluate the temperature distribution with cover thickness of wet-mixed high strength sprayed polymer mortar for fire resistance of tunnel system. Based on experimental results and numerical analysis, the proper cover thickness of wet-mixed high strength sprayed polymer mortar determined the more than 4cm.

• Proceedings of the Korea Society for Industrial Systems Conference
• /
• 2002.06a
• /
• pp.356-360
• /
• 2002

Polluting the air with such pollutants as CO, H₂S and SO₂, industrial development huts increased the danger of gas toxication. Futhermore, as the: living standard goes higher, the consumption of explosive hydrocarbonic gases such as butane(C₄H/sub 10/) or propane(C₃H/sub 8/) has been soaring, which results in the danger of a gas explosion. As measures to cope with such dangers, the development of highly sensitive gas sensors, gas detectors adopting gas-sensing technologies, and gas recognition systems are urgently required. The objective of the present research is to develop a gas recognition system that is capable of identifying specific types of selected gases by formulating a semiconductor-typed gas sensor array, which not only improves the selectivity of semiconductor-typed gas sensors but also minimizes the erect of drifts on a single sensor signal, and applying the input pattern data of gases detected by the array to a neural network.