• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.338-343
• /
• 2006

The effects of lead-borosilicate glass frits on the sintering behavior and microwave dielectric properties of ceramic-glass composites were investigated as functions of glass composition of glass addition ($10{\sim}50vol%$), softening point (Ts) of the glass, and sintering temperature of the composites ($500{\sim}900^{\circ}C$ for 2 h). The addition of 50 vol% glass ensured successful sintering below $900^{\circ}C$. Sintering characteristics of the composites were well described in terms of Ts. PbO addition in to the glass enhanced the reaction with $Al_{2}O_3$ to form liquid phase and $PbAl_{2}Si_{2}O_8$, which was responsible to lower Ts. Dielectric constant(${\epsilon}_r$), $Q{\times}f_0$ and temperature coefficient of resonant frequency (${\tau}_f$) of the composite with 50 vol% glass contents ($B_{2}O_{3}:PbO:SiO_{2}:CaO:Al_{2}O_3$ = 5:40:45:5:5) demonstrated 8.5, 6,000 GHz, $-70\;ppm/^{\circ}C$, respectively, which is applicable to substrate requiring a low dielectric constant. When the same glass composition was applied sinter $MgTiO_3\;and\;TiO_2,\;at\;900^{\circ}C$ (50 vol% glass in total), the properties were 23.8, 4,000 GHz, $-65ppm/^{\circ}C$ and 31.1, 2,500 GHz, $+80ppm/^{\circ}C$ respectively, which is applicable to filter requiring an intermidiate dielectric constant.

• Korean Journal of Metals and Materials
• /
• v.50 no.10
• /
• pp.729-734
• /
• 2012

This study investigated the effect of water absorption on the tensile properties of carbon-glass/epoxy hybrid composites at room temperature and $-30^{\circ}C$. To investigate the effect of the position of glass fabric in the hybrid composite on the tensile properties, the stacking pattern of the fiber fabrics for reinforcing was created in three different ways: (a) glass fabrics sandwiched between carbon fabrics, (b) carbon fabrics sandwiched between glass fabrics and (c) alternative layers of carbon and glass fabrics. They were manufactured by a vacuum-assisted resin transfer molding (VARTM) process. The results showed that there was surprisingly little difference in tensile strength at the two different temperatures with dry and wet conditions. However, the water absorption into the hybrid system affected the tensile properties of the hybrid composites at RT and $-30^{\circ}C$. When the glass fabrics were at the outermost layers, the hybrid composite had the lowest tensile properties. This is attributed to the fact that the composite had a relatively high water absorption rate.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.468-470
• /
• 2004

CNT pastes with different inorganic binder such as glass frit and spin on glass (SOG) were synthesized by using multi-walled nanotube (MWNT) grown by CVD. The uniformity of cathode layer after firing was enhanced and the emission current density at an applied field of 7.95V/${\mu}m$ increased from 133${\mu}A$/$cm^2$ to 265${\mu}A$/$cm^2$ when inorganic binder changed from glass frit to SOG. The emission properties of CNT pastes with SOG were stable and uniform although firing was carried out at relatively high temperature of 450$^{\circ}C$ under air. It is concluded that SOG is more suitable inorganic binder than glass frit for field emission application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.1
• /
• pp.19-24
• /
• 2007

The effects of $B_2O_3-SiO_2-R(R;CaO,\;BaO,\;ZnO,\;Bi_2O_3)$ borosilicate glass system on the sintering behavior and microwave dielectric properties of ceramic/glass composites were investigated as functions of modifier, glass addition ($30{\sim}50\;vol%$) and sintering temperature ($500{\sim}900^{\circ}C$ for 2 hrs). The addition of 50 and 45 vol% glass ensured successful sintering below $900^{\circ}C$. Sintering characteristics of the composites were well described in terms of modifier. Borosilicate glass enhanced the reaction with $Al_{2}O_{3}$ to form pores, second phases and liquid phases, which was responsible to component of modifier. Dielectric constant (${\varepsilon}_{r},\;Q{\times}f_{o}$) and temperature coefficient of resonant frequency (${\tau}_{f}$) of the composite with 50 and 45 vol% glass contents($B_{2}O_{3}:SiO_{2}:R=25:10:65$) demonstrated A-CaBS(7.8, 2,560 GHz, -81ppm/$^{\circ}C$), A-BaBs(5.8, 3.130 GHz, -64 ppm/$^{\circ}C$), A-ZnBS(5.7, 17,800 GHz, -21 ppm/$^{\circ}C$), A-BiBs(45 vol% glass in total)(8.3, 2,700 GHz, -45 ppm/$^{\circ}C$) which is applicable to substrate requiring an low dielectric properties.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.229-233
• /
• 2003

By using an oxynitride glass as a sintering additive, the effects of BN content on microstructure and mechanical properties of the hot-pressed and subsequently annealed SiC-BN composites were investigated. The microstructures developed were analyzed by image analysis. The morphology of SiC grains was strongly dependent on BN content in the starting composition. The aspect ratio of SiC decreases with increasing BN content and the average diameter of SiC shows a maximum at 5 wt% BN and decreases with increasing BN content in the starting powder. The fracture toughness increased with increasing BN content while the strength decreased with increasing BN content. The strength and fracture toughness of SiC or SiC-TiC composites were strongly dependent on the morphology of SiC grains, but the strength and fracture toughness of SiC-BN composites were strongly dependent on BN content rather than morphology of SiC grains. These results suggest that fracture toughness of SiC ceramics can be tailored by manipulating BN content in the starting composition. Typical fracture toughness and strength of SiC-10 wt% BN composites were 8 MPa$.$m$\^$1/2/ and 445 MPa, respectively.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.595-605
• /
• 2000

Dental ceramics have good aesthetics, biocompatibility, low thermal conductivity, abrasion resistance, and color stability. However poor resistance to fracture and shrinkage during firing process have been limiting factors in their use, particularly in multiunit ceramic restorations. A new method for making all-ceramic crowns that have high strength and low processing shrinkage has been developed and is referred to as the Vita In-Ceram method. This study was performed to investigate the effect of $CeO_2$ addition in borosilicate glasses on the strength of alumina-glass composites. Porous alumina compacts were prepared by slip casting and sintered at $1,100^{\circ}C$ for 2 hours. Dense composites were made by infiltration of molten glass into partially sintered alumina at $1,140^{\circ}C$ for 4 hours. Specimens were polished sequentially from #800 to #2000 diamond disk. and the final surface finishing on the tensile side was received an additional polishing sequence through $1{\mu}m$ diamond paste. Biaxial flexure test was conducted by using ball-on-three-ball method at a crosshead speed of 0.5mm/min. To examine the microstructural aspect of crack propagation in the alumina-glass composites, Vickers-produced indentation crack was made on the tensile surface at a load of 98.0 N and dwell time of 15 sec, and the radial crack patterns were examined by an optical microscope and a scanning electron microscope. The results obtained were summarized as follows; 1. The porosity rates of partially sintered alumina decreased with the rising of firing temperature. 2. The maximum biaxial flexure strength of 423.5MPa in alumina-glass composites was obtained with an addition of 3 mol% $CeO_2$ in glass composition and strength values showed the aspect of decrease with the increase of $CeO_2$ content. 3 The biaxial flexure strength values of alumina-glass composites were decreased with rising the firing temperature. 4. Observation of the fracture surfaces of alumina-glass composites indicated that the enhancement of strength in alumina-glass composites was due to the frictional or geometrical inter-locking of rough fracture surfaces and ligamentary bridging by intact islands of materials left behind the fracture front.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.71-75
• /
• 2005

For the damage tolerance improvement of conventional laminated composites, stitching process have been utilized for providing through-thickness reinforcements. 2D preforms were stacked with S-2 glass plain weave and S-2 glass MWK (Multi-axial Warp Knit) L type. 3D preforms were fabricated using the stitching process. All composite samples were fabricated by RTM (Resin Transfer Molding) process. To examine the damage resistance performance the low speed drop weight impact test has been carried out. For the assessment of damage after the impact loading, specimens were examined by scanning image. CAI (Compressive After Impact) tests were also conducted to evaluate residual compressive strength. Compared with 2D composites, the damage area of 3D composites was reduced by 20-30% and the CAI strength showed 5-10% improvement.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.99-104
• /
• 2003

Alumina/zirconia-glass composites prepared by melt-infiltration were investigated to evaluate the influence of zirconia addition on mechanical and optical properties of the composites and glass penetration kinetics. The infiltration distance was parabolic with respect to time as described by the Washburn equation and the penetration rate constant, K, decreased due to the reduction In pore size as the amount of zirconia rose. The zirconia addition increased lightness ($L^*$) but reduced K, transmittance and color sharpness ($C^*$) It can be concluded that the zirconia addition was not effective to the mechanical properties of the composites due to the increase in porosity even though the toughness of the composites increased when zirconia was added up to 15 wt%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.265-265
• /
• 2007

In the present work, we have studied low temperature sintering and microwave dielectric properties of $ZnAl_2O_4$-zinc borosilicate (ZBS, 65ZnO-$25B_2O_3-10SiO_2$) glass composites. The focus of this paper was on the improvement of sinterability, low dielectric constant, and on the theoretical proof regarding of microwave dielectric properties in $ZnAl_2O_4$-ZBS glass composites, respectively. The $ZnAl_2O_4$ with 60 vo1% ZBS glass ensured successful sintering below $900^{\circ}C$. It is considered that the non-reactive liquid phase sintering (NPLS) occurred. In addition, $ZnAl_2O_4$ was observed in the $ZnAl_2O_4$-(x)ZBS composites, indicating that there were no reactions between $ZnAl_2O_4$ and ZBS glass. $ZnB_2O_4\;and\;Zn_2SiO_4$ with the willemite structure as the secondary phase was observed in the all $ZnAl_2O_4$-(x)ZBScomposites. In terms of dielectric properties, the application of the $ZnAl_2O_4$-(x)ZBS composites sintered at $900^{\circ}C$ to LTCC substrate were shown to be appropriate; $ZnAl_2O_4$-60ZBS (${\varepsilon}_r$= 6.7, $Q{\times}f$ value= 13,000 GHz, ${\tau}_f$= -30 ppm/$^{\circ}C$). Also, in this work was possible theoretical proof regarding of microwave dielectric properties in $ZnAl_2O_4$-(x)ZBS composites.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.1
• /
• pp.11-21
• /
• 1999

For microelectronic packaging application, the crystallizable glass powder in CaO-$A1_2O_3-SiO_2-B_2O_3$system was mixed with various amounts of alumina inclusions (\approx 4 $\mu \textrm{m}$), and its sintering behavior, crystallization behavior, and dielectric constant were examined in terms of vol% of alumina and the reaction between the alumina and the glass. Sintering of the CASB glass powder alone at $900^{\circ}C$ resulted in full densification (99.5%). Sintering of alumina-filled composite at $900^{\circ}C$ also resulted in a substantial denslfication higher than 97% of theoretical density, In this case, the maximum volume percent of alumina should be less than 40%. XRD analysis revealed that there was a partial dissolution of alumina into the glass. This alumina dissolution, however, did not show the particle growth and shape accommodation. Therefore, the sintering of both the pure glans and the alumina-filled composite was mainly achieved by the viscous flow and the redistribution of the glass. Alumina dissolution accelerated the crystallization initiation time at $1000^{\circ}C$ and hindered the densification of the glass. Dielectric constants of both the alumina-filled glass and the glass-ceramic composites were increased with increasing alumina content and followed rule of mixture. In case of the glass-ceramic matrix composites showed relatively lower dielectric constant than the glass matrix composite. Furthermore, as alumina content increased, crystallization behavior of the glass was changed due to the reaction between the glass and the alumina. As alumina reacted with the glass matrix, the major crystallized phase was shifted from wollastonite to gehlenite. In this system, alumina dissolution strongly depended on the particle size: When the particle size of alumina was increased to 15 $\mu\textrm{m}$, no sign of dissolution was observed and the major crystallized phase was wollastonite.