Mechanical and optical properties of alumina/zirconia-glass dental crown composites

Alumina/zirconia-glass composites prepared by melt-infiltration were investigated to evaluate the influence of zirconia addition on mechanical and optical properties of the composites and glass penetration kinetics. The infiltration distance was parabolic with respect to time as described by the Washburn equation and the penetration rate constant, K, decreased due to the reduction In pore size as the amount of zirconia rose. The zirconia addition increased lightness ($L^*$) but reduced K, transmittance and color sharpness ($C^*$) It can be concluded that the zirconia addition was not effective to the mechanical properties of the composites due to the increase in porosity even though the toughness of the composites increased when zirconia was added up to 15 wt%.

인공치관용 알루미나/지르코니아-유리 복합체의 기계적 및 광학적 특성

용융침투법으로 알루미나/지르코니아-유리 복합체를 제조하여 지르코니아 첨가가 복합체의 기계적 및 광학적 특성과 유리 침투 kinetic에 미치는 영향을 조사하였다. 유리 침투시간이 증가할수록 침투깊이는 Washburn식에 의한 포물선관계로 증가하였으며 침투 상수인 K는 기공 크기의 함수로 지르코니아 첨가량이 증가할수록 기공 크기의 감소로 감소하였다. 지르코니아 양이 증가함에 따라 명도($L^*$)는 증가하지만 유리 침투 상수(K), 투과율(transmittance), 채도($C^*$)가 감소하였다. 지르코니아가 15 wt% 첨가될 때까지 알루미나/지르코니아-유리 복합체의 인성값 증가를 보였지만 기공률의 증가로 인하여 기계적 특성 향상에는 크게 기여하지 않았다.