• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.225-227
• /
• 2006

As rail steel at a crossing area must undergo much higher loading than those at regular railway, Mn-alloyed steel is normally used for its high load-carrying capability and reduced wear rate. However, as these Mn-alloyed steel is tend to have casting defects, manufacturing cost to produce defect-free Mn-alloyed steel becomes quite expensive. Therefore, in order to replace Mn-alloyed steel, we performed build-up welding using CH-90 and investigated regarding to wear characteristics of build-up weld metal.

• Steel and Composite Structures
• /
• 제34권3호
• /
• pp.347-359
• /
• 2020

The objective of this study is to experimentally scrutinize the axial performance of built-up concrete filled steel tube (CFT) columns composed of steel plates. In this case, the main parameters cross section types, compressive strength of filled concrete, and the effect of welding lines. Welded built-up steel box columns are fabricated by connecting two pieces of cold-formed U-shaped or four pieces of L-shaped thin steel plates with continuous penetration groove welding line located at mid-depth of stub column section. Furthermore, traditional square steel box sections with no welding lines are investigated for the comparison of axial behavior between the generic and build-up cross sections. Accordingly, 20 stub columns with thickness and height of 2 and 300 mm have been manufactured. As a result, welding lines in built-up specimens act as stiffeners because have higher strength and thickness in comparison to the plates. Subsequently, by increasing the welding lines, the load bearing capacity of stub columns has been increased in comparison to the traditional series. Furthermore, for specimens with the same confinement steel tubes and concrete core, increment of B/t ratio has reduced the ductility and axial strength.

• 한국산학기술학회논문지
• /
• 제15권9호
• /
• pp.5419-5424
• /
• 2014

용접 스캘럽은 작은 사분원 또는 반원 형상의 구멍으로서 용접의 작업성 향상을 위한 목적으로 용접선이 교차하는 위치에 시공된다. 선체 블록의 탑재 단계에서는 수많은 T-bar 조인트 용접이 수행되어야하며, 플랜지-웨브의 교차용접이 완료된 후에 육성용접을 통해 모든 스캘럽을 메공하는데 많은 생산시수가 소요된다. 본 연구에서는 특별한 타입의 CBM(ceramic backing material)을 고안하여 T-bar 조인트 용접 시 플랜지-웨브의 교차용접 지점에 시공되던 스캘럽을 삭제함으로써 논-스캘럽 블록 조인트 용접 공법을 개발하였다. 플랜지간 용접 시 플랜지 이면에 접촉한 웨브의 V 용접개선에 삽입이 용이하도록 CBM을 웨지 형상으로 제작하였고 웨브간 용접 개선의 루트갭에 맞추어 불필요한 부분의 절단이 용이하도록 예비 절단면들을 톱니 형상으로 배치하였다. 조선소의 실제 용접조건에 기초한 일련의 실험을 통하여 개발된 논-스캘럽 용접 공법의 유용성을 확인하였다.

• Journal of Welding and Joining
• /
• 제25권6호
• /
• pp.44-52
• /
• 2007

A welding process of a lifting lug for lifting heavy objects is one of the important welding processes directly related to the safety in shipbuilding. Welding a lifting lug is done in the manually and takes about forty minutes. Working environment for the lifting lug welding is very poor due to an radiant heat and a harmful fume. The purpose of this study is to develop methods of multi-pass welding using the lifting lug welding robot system. This study shows robot welding methods to achieve proper corner, straight and connection welding and an effectiveness of application.

• Journal of Welding and Joining
• /
• 제18권3호
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• 한국산학기술학회논문지
• /
• 제4권1호
• /
• pp.36-41
• /
• 2003

열간단조 밀폐금형의 수명연장을 위한 빌릿의 소성변형 유동해석을 유한 요소법에 의하여 실시한 결과 임프레션 형상에 대한 수정설계를 수행하였고, 임프레션 표면 마멸부위의 보수방법을 육성용접에 의한 방법으로 금형을 재생하여 사용한 결과 개발 전의 3,0(H개 생산에서 개발 후 5,000개 양산되었을 때 임프레션 표면을 관찰하였더니 3,000개 정도에서 나타났던 마멸보다 얕은 마멸이 나타났다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제28권1호
• /
• pp.109-115
• /
• 2004

The spatter and porosity could be occurred during$CO_2$CW laser welding of Primer- coated steel for shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate induced the spatter humping bead and porosity and these are main part of the welding defect. attributed to the powerful vaporizing pressure of primer attached on the base metal The zinc of Primer has a boiling point that is the lower temperature than melting point of steel zinc vapor will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position. the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Journal of Welding and Joining
• /
• 제8권3호
• /
• pp.79-88
• /
• 1990

Welded joint often contains soft or softened regions such as the HAZ of TMCP steel welded with high heat input. In this study, the equivalent yield strength of plate structure containing softened region was predicted by FEM analysis, and its incremental behavior was explained with the results of the analysis. The calculated results of yield strength indicated the following for the plate structures. 1) As the softened region starts to yield, shear stress begins to build up along the boundary between base metal and softened region. This results in multi-axial stress condition which gives restraint on the softened region. 2) Restraint effect has a significant influence on the distribution of the shear stress, the nominal stress, and the strain. 3) The yielding behavior of softened region becomes the same as that of base metal when both ratios of length to width and thickness to width of softened region are larger than 30 and 13 respectively.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 추계학술발표대회 개요집
• /
• pp.177-179
• /
• 2005

As rail steel at a crossing area must undergo much higher loading than those at regular railway, Mn-containing casting steel is normally used for its high load-carrying capability and reduced wear rate. However, as these Mn-containing casting steel is tend to have casting defects, manufacturing cost to produce defect-free Mn-containing casting steel becomes quite expensive. Therefore, in order to investigate the possibilities of replacing expensive Mn-containing casting steel with a mild steel with a surface build-up using a Mn-alloyed steel electrode.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.316-321
• /
• 2003

The spatter and porosity could be occurred during $CO_2$ CW laser welding of Primer-coated Steel for Shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate has caused the spatter, humping bead and porosity and these are main part of the welding defect, attributed to the powerful vaporizing pressure of primer attached on the base metal. The zinc of primer has a boiling point that is the lower temperature than melting point of steel. Zinc va}X)f will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.