• Journal of Sensor Science and Technology
• /
• v.12 no.6
• /
• pp.273-281
• /
• 2003

A stoichiometric mixture for $CdIn_2Te_4$ single crystal was prepared from horizontal electric furnace. The $CdIn_2Te_4$ single crystal was grown in the three-stage vertical electric furnace by using Bridgeman method. The quality of the grown crystal has been investigated by the x-ray diffraction and the photoluminescence measurements. The (001) growth plane of oriented $CdIn_2Te_4$ single crystal was confirmed from back-reflection Laue patterns. The carrier density and mobility of $CdIn_2Te_4$ single crystal measured with Hall effect by van der Pauw method are $8.61{\times}10^{16}\;cm^{-3}$ and $242\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CdIn_2Te_4$ single crystal obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=1.4750\;eV-(7.69{\times}10^{-3}\;eV)T^2/(T+2147)$. After the as-grown $CdIn_2Te_4$ single crystal was annealed in Cd-, In-, and Te-atmospheres, the origin of point defects of $CdIn_2Te_4$ single crystal has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{Te}$, $Cd_{int}$, and $V_{Cd}$, $Te_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Cd-atmosphere converted $CdIn_2Te_4$ single crystal to an optical n-type. Also, we confirmed that In in $CdIn_2Te_4$ did not form the native defects because In in $CdIn_2Te_4$ single crystal existed in the form of stable bonds.

• Korean Journal of Materials Research
• /
• v.13 no.3
• /
• pp.195-199
• /
• 2003

The $p-CdIn_2$$Te_4$single crystal was grown in the three-stage vertical electric furnace by using Bridgman method. The quality of the grown crystal has been investigated by the x-ray diffraction and the photoluminescence measurements. From the photoluminescence spectra of the as-grown $CdIn_2$$Te_4$crystal and the various heat-treated crystals, the ($D^{\circ}$, X) emission was found to be the dominant intensity in the photoluminescence spectrum of the $CdIn_2$T $e_4$:Cd, while the ($A^{\circ}$, X) emission completely disappeared in the $CdIn_2$T $e_4$:Cd. However, the ($A^{\circ}$, X) emission in the photoluminescence spectrum of the $CdIn_2$T $e_4$:Te was the dominant intensity like an as-grown $CdIn_2$T $e_4$crystal. These results indicated that the ($D^{\circ}$, X) is associated with $V_{Te}$ acted as donor and that the ($A^{\circ}$, X) emission is related to $V_{cd}$ acted as acceptor, respectively. The $p-CdIn_2$T $e_4$crystal was found to be obviously converted into the n-type after annealing in the Cd atmosphere. The origin of ( $D^{\circ}$, $A^{\circ}$) emission and its TO phonon replicas is related to the interaction between donors such as $V_{Te}$ or $Cd_{int}$, and accepters such as $V_{cd}$ or T $e_{int}$. Also, the In in the $CdIn_2$X$CdIn_4$was confirmed not to form the native defects because it existed in the stable form of bonds.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1998.06a
• /
• pp.39-43
• /
• 1998

Single crystals of{{{{ { Zn}_{ 1-x} {Mn }_{x }{Te} }}}} with x=0.3-0.6 were prepared by the standard Bridgeman method. Diffuse neutron diffraction intensities due to the short range magnetic ordering is found in the vicinities of 1 1/2 0 reciprocal point and its equivalent point, indicating that the magnetic correlation of the clusters is the type III antiferromangetic one do the F-type Bravais class crystals, being identical with that of {{{{{ Cd}_{ 1-x} {Mn }_{x }Te }}}}. Neutron inelastic scattering measure-ment has been performed for {{{{{ Zn}_{ 0.6} { Mn}_{ 0.4}Te }}}} sample using the cold neutron spectrometer. AGNES. High resolution measurement with the energy resolution of {{{{ TRIANGLE E= +- .01meV}}}} was carried out in the temperature range from 10K to the ambient. Critical scattering, closely related with the spin glass transition, has been observed for the first time in this semimagnetic semi-conductor. The critical scattering is observed at temperatures in the vicinity of the spin glass transition temperature, 17K. The scattering is observed as a kind of quasielastic scattering in the reciprocal range where the elastic magnetic diffuse scattering has been observed, e.g., 11/20 reciprocal point, indicating the spin fluctuation has dynamic components in this material. Photoconductivity has been discovered below 150K in {{{{{ Zn}_{ 0.4} {Mn }_{0.6 } Te}}}}. The electric AC conductivity has been increased dramatically under the laser light with the wave lengths of {{{{ lambda =6328,5145 and4880 }}}}$\AA$ ,respectively. After the light was darkened, the conductivity was reduced to the original level after about 2000 seconds at 50K, being above the spin glass transition temperature. This phenomenon is the typical persistent photoconductivity; PPC which was similarly found in {{{{ { Zn}_{ 1-x} { Mn}_{x} Te}}}}.