• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.3
• /
• pp.547-553
• /
• 1990

With alumina ceramics to copper brazement of cylindrical shape, the thermal stress analysis was carried out by finite element method. Elastic and plastic behaviour was considered to copper, but only elastic behaviour was considered to alumina. Also material properties of alumina and copper were considered in not constant values but variable functions dependent on temperature. The result of analysis is shown that maximum tensile longitudinal stress is occurred at perimeter of alumina side interface and maximum compressive radial and tangential stresses are occurred at center of alumina side interface. Because of bending effect, tensile raidial and tangential stresses are occurred at near bottom of alumina, far from interface.

• Transactions of Materials Processing
• /
• v.7 no.5
• /
• pp.465-473
• /
• 1998

The effect of alloying elements of Ag-Cu-Zr-X brazing alloy on the microstructure and the bond strength of $Al_2O_3/Ni-Cr$ brazed steel joint was investigated. The reaction layer, $ZrO_2$ (a=5.146 ${\AA}$ , b=5.213 ${\AA}$ , c=5.311 ${\AA}$ )was formed at the interface of $Al_2O_3/Ni-Cr$ steel joint by the redox reaction between alumina and Zr. The addition of An and Al to the Ag-Cu-Zr brazing alloy gave rise to changes in the thickness of the reaction product layer and the morphology of the brazement. Sn caused the segregation of Zr was decreased b Al the $ZrO_2$ layer formed at the Ag-Cu-Zr-Al alloy was thinner than that of $ZrO_2$ formed at the Ag-Cu-Zr-An alloy. The fracture shear strength was strongly dependent on the microstructure of the brazement. Brazing with Ag-Cu-Zr-Sn alloy resulted in a better bond strength than with Ag-Cu-Zr or Ag-Cu-Zr-Al alloy.

• Laser Solutions
• /
• v.17 no.1
• /
• pp.7-12
• /
• 2014

The dissimilar welding between magnesium alloy and steel sheet was required in automobile industry to increase the strength of the dissimilar joints. Laser brazing is one of the good joining processes for Mg- steel dissimilar joint. In this study, AZ31 magnesium alloy and Zn coated steel dissimilar joint was brazed using diode direct laser with Mg600 filler wire and Superior #21 flux. The wetting of Mg filler wire on Zn coating was very good because of the formation of eutectic phase with low melting temperature. The strength of the brazed joint between AZ31 magnesium alloy and Zn coated steel was 131.3N/mm. The fracture occurred at brazement.

• Journal of Welding and Joining
• /
• v.31 no.4
• /
• pp.7-12
• /
• 2013

The dissimilar welding between magnesium alloy and steel sheet was required in automobile industry to increase the strength of the dissimilar joints. Laser brazing is one of the good joining processes for Mgsteel dissimilar joint. In this study, the effect of coating materials was evaluated on the laser brazing for the dissimilar joint between AZ31 and coated steels such as Zn, Sn and Ni. Diode direct laser was used to braze the lap-edge joint with Mg600 filler wire and Superior #21 flux. The wettability was best on Zn coated steel. The interlayer was formed at the interface between brazement and steel for all coating materials. The strengths of brazed specimen were 146.5N/mm, 204.6N/mm and 101.6N/mm for Zn, Sn and Ni coated steel respectively.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.66-66
• /
• 2009

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites(diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature 940 $^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.49-58
• /
• 2010

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites (diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature $940^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.