• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.381-387
• /
• 2000

Si3N4/stainless steel 316 joints with Ni buffer layer were fabricated by direct active brazing method (DIB) using Ag-Cu-Ti brazing alloy only and double brazing method (DOB) using Ag-Cu brazing alloy with Si3N4 pretreated with Ag-Cu-Ti brazing alloy. For the joint brazed by DIB method, Ti was segregated at the Si3N4/brazing alloy interface, but was not enough to form a stable joint interface. In addition, large amounts of Ni-Ti inter-metallic compounds were formed in tehbrazing alloy near the joint interface, which could deplete the contents of Ti involved in the interfacial reaction. However, for the joint brazed by DOB method, segregation of Ti at the joint interface were enough to enhance the formation of stable interfacial reaction products such as TiN and Ti-Si-Ni-N-(Cu) multicompounds, which restricted the formation of Ni-Tio inter-metallic compounds in the brazing alloy during brazing with Ni buffer layer. Fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was much improved by using DOB method rather than DIB method. It could be deduced that the differences of fracture strength of the joint with Ni buffer layer depending on brazing process adapted were directly affected by the formation of stable joint interface and the change in microstructure of the brazing alloy near the joint interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of Ni buffer layer in the joint was increased from 0.1 mm to 10 mm. It seems to due to the increased residual stress in the joint as the thickness of Ni buffer layer is increased. The maximum fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was 386 MPa, and the fracture of joint was originated at Si3N4/brazing alloy joint interface and propagated into Si3N4 matrix.

• 한국항공우주학회지
• /
• 제30권8호
• /
• pp.65-70
• /
• 2002

본 연구에서는 로켓엔진에 사용되고 있는 2상 스테인리스강의 브레이징 접합성에 관하여 접합 현상과 기계적 강도의 두가지 측면의 고찰을 통하여 검증하였다. UNS32550을 모재로, MBF-50을 인서트금속으로 사용하여 브레이징 접합온도를 1473K, 1498K로 변화시키고, 접합 시간은 0~1.8ks로 변화시키면서 각 조건에서의 접합현상을 고찰한 결과, 접합부에서는 모재와 인서트금속간의 반응으로 인해 다양한 상이 생성되었다. 접합 초기에는 접합계면 및 접합부 근방의 모재에서 BN가 생성되고, 접합계면에서는 Cr질화물이 생성되어 접합 시간이 증가함에 따라 BN과 Cr질화물의 양이 감소하였다. 전단시험 결과 500MPa의 우수한 전단강도를 얻었다.

• International Journal of Korean Welding Society
• /
• 제4권1호
• /
• pp.46-52
• /
• 2004

To combine the mechanical advantages of ceramics with those of metals, one often uses both materials within one composite component. But, as known, they have different material properties and fracture behaviors. In this study, a four-point bending test is carried out on $Si_3N_4$ joined to ANSI 304L stainless steel with a Ti-Ag-Cu filler and a Cu interlayer at room temperature to evaluate their longitudinal strain behaviors. And, to detect localized strain, a couple of strain gages are pasted near the joint interfaces of the ceramic and metal sides. The normal strain rates are varied from $3.33{\times}10^5$ to $3.33{\times}10^{-1}s^{-1}$ Within this range, the experimental results showed that the four-point bending strength and the deflection of the interlayer increased with increasing the strain rate.

• Journal of Advanced Marine Engineering and Technology
• /
• 제24권1호
• /
• pp.59-66
• /
• 2000

To investigate the optimum brazing condition, variation of bonded structure and mechanical properties of novel brazed pure Al with bonding condition (brazing temperature, time and Si/flux ratio) was studied. A basic study of the bonding mechanism was also examined. The optimum brazing condition was obtained at $590^{\circ}$ for 2 minutes and the bonded structure showed that it is composed of almost entirely eutectic Al-Si with near eutectic composition. At higher brazing temperature $630^{\circ}$, hypoeutectic Al-Si structure was observed in the bonded area and resulted in erosion of base metal. The thickness of eutectic layer formed in optimum brazing temperature increased linearly with the square root of time, showing a general diffusion controlled process. The ultimate tensile strength of bonded joint brazed at an optimum brazing condition was about 60% of base metal and its fracture surface showed a brittle mode.

• 한국항공우주학회지
• /
• 제31권7호
• /
• pp.112-117
• /
• 2003

본 연구에서는 재생 냉각용 연소기에 적용되고 있는 동합금과 2상 스테인리스강의 최적 브레이징 조건을 구하였다. 모재는 C18200 동합금과 S31803 2상 스테인레스강을, 삽입금속으로 두께가 각각 50${\mu}m$, 80${\mu}m$인 AMS4764를 사용하였다. 브레이징한 시제에 대하여 X선 검사, 강도/기밀 및 파괴시험, 파단면 관찰을 한 결과 두께 50${\mu}m$인 삽입금속을 사용한 경우 강도특성과 접합면이 양호함을 확인하였다. 반면 두께 80${\mu}m$인 삽입금속을 사용한 경우는 강도특성은 양호하였으나 냉각유로의 막힘 현상과 유로 확대를 확인하였다.

• Journal of Welding and Joining
• /
• 제28권3호
• /
• pp.49-58
• /
• 2010

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites (diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature $940^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• Journal of Welding and Joining
• /
• 제35권2호
• /
• pp.23-29
• /
• 2017

Mechanical properties and hardness distributions in arc brazed joints of Dual phase steel using Cu-Al insert metal were investigated. The maximum tensile shear load was 10.4kN at the highest brazing current. It was about 54% compared to tensile load of base metal. This joint efficiency is higher than that of joint of DP steel using Cu-based filler metals which are Cu-Si, Cu-Sn. Fracture positions can be divided into two types. Crack initiation commonly occurred at three point junction among upper sheet, lower sheet and the fusion zone. However crack propagations were different with increasing the brazing current. In case of the lower current, it instantaneously propagated along with the interface between fusion zone and upper base material. On the other hand, in case of higher current, a crack propagation occurred through fusion zone. When the brazing current is low (60, 70A), the interface shape is flat type. However the interface shape is rough type, when the brazing current is high (80A). It is thought that the interface shapes were the reason why the crack propagations were different with brazing current. The interface was the intermetallic compounds which consisted of $(Fe,Al)_{0.85}Cu_{0.15}$ IMC formed by crystallization at $1200^{\circ}C$during cooling. Therefore the maximum tensile shear load and the fracture behavior were determined by a interface shape and effective sheet thickness of the fracture position.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.228-230
• /
• 2003

Recently, lots of joining methods of thin metal sheets are being developed in order to improve joint quality and productivity in manufacturing area. Current existing welding methods are continuously challenged as new materials and smaller thickness of metal sheets are required. In this study, laser plug brazing process was investigated as a new joining method of thin metal sheets. A CO2 laser system with automatic feeding of filler metal wire and flux was developed, and laser plug brazing experiments were conducted. The brazed joints were analyzed using various methods.

• Journal of Welding and Joining
• /
• 제13권3호
• /
• pp.106-115
• /
• 1995

To know the bonding phenomena of Ti/Cu brazed joint, a characteristic of microstructures in bonding interlayer of vacuum brazed pure Ti to Cu has been studied in the temperature range from 1088 to 1133K for various bonding times using Ag-28wt%Cu filler metal. Also intermediate phases formed in bonded interlayer and behavior of layer growth have been investigated. The obtained results in this study are as follows: 1) Liquid insert metal width at the each brazing temperature was proportional to the square root of brazing time, and it was considered that the liquid insert metal width was controlled by the diffusion rate process of primary .alpha.-Cu formed at the Ti side. 2) Intermediate phases formed near the Ti interface were .betha.-Ti and intermetallic compounds TiCu, Ti$_{2}$Cu, Ti$_{3}$Cu, and TiCu. 3) .betha.-Ti formed in Ti base metal durig brazing transformed to lamellar structure, .alpha.-Ti + Ti$_{2}$Cu. The structure came from the eutectoil decomposition reaction in cooling. And the width of .betha.-Ti layer was proportional to the square root of brazing time, and it was considered that the growth of .betha.-Ti layer was controlled by interdiffusion rate process in .betha.-Ti. 4) The layer growth of TiCu, Ti$_{3}$Cu$_{4}$ and TiCu, phases formed near the Ti interface was linerface was linearly proportional to the brazing time, and it was considered that the layer growth of these phases was controlled by the chemical reaction rate at the interface.

• 한국재료학회지
• /
• 제3권6호
• /
• pp.668-677
• /
• 1993

Cu-P계, 4종의 Cu-P-Pn계 및 3종의 Cu-P-Sn-Ag계 용가재를 사용해 Ar분위기 하에서 1003 및 1033K로 1.2Ks동안 노브레이징한 ST304, STS430 및 저탄소강과 동 접합체들을 전단시험 및 조직시험하였다. 계면에서의 미세조직은 제 종류 즉 첫째,균열을 포함하는 반응층 둘째, 분산층 세째, 균열을 포함하는 반응층과 분산층으로 분류된다. 분산층만이 존재할때 40-60MPa 이상의 상대적으로 높은 전단강도가 얻어지며, 동모재파단을 일으킨다. 이 반응층이 형성되었을때는 반드시 균열이 형성되며, 낮은 전단강도를 나타내고 접합부파단을일으킨다. 이 반응층은 Fe-P계의 화합물이다. 이러한 미소조직 및 강도 경향은 용가재내 Sn의 존재 및 모재내 Ni(또한 Cr)의 존재 유무에 따라 변화한다.