• Structural Engineering and Mechanics
• /
• 제72권3호
• /
• pp.305-312
• /
• 2019

This paper investigates the effect of utilizing vacuum bagging process to enhance the bond behavior between fiber reinforced polymer (FRP) composites and concrete substrate. Sixty specimens were prepared and tested using double-shear bond test. The effect of various parameters such as vacuum, fiber type, and FRP sheet length and width on the bond strength were investigated. The experimental results revealed that utilizing vacuum leads to improve the bond behavior between FRP composites and concrete. Both the ultimate bond forces and the maximum displacements were enhanced when applying the vacuum which leads to reduction in the amount of FRP materials needed to achieve the required bond strength compared with the un-vacuumed specimens. The efficiency of the enhancement in bond behavior due to vacuum highly depends on the fiber type; using carbon fiber showed higher enhancement in the bond strength compared to the glass fiber when vacuum was applied. On the contrary, specimens with glass fiber showed higher enhancement in the maximum slippage compared to specimens with carbon fibers. Utilizing vacuum does not affect the debonding failure modes but lead to increase in the amount of attached concrete on the surface of the debonded FRP sheet.

• 대한건축학회논문집:구조계
• /
• 제35권1호
• /
• pp.3-10
• /
• 2019

The purpose of this paper is to find the fire-protection method for keeping on the bond capacity of Near-Surface-Mounted (NSM) FRP under high temperature. Experiments have been carried out to evaluate the bond capacity of NSM FRP by using CFRP-plates and to confirm the heat transfer to the concrete block when the refractory insulation is attached to the surface of NSM FRP. Bond test of NSM FRP under room temperature was conducted to obtain the maximum bond strength. And then a heating tests were carried out with keeping the bond stress of 30% of the maximum bond strength. As a result, the bond capacity of NSM FRP was disappeared when the temperature at epoxy reached to its glass transition temperature (GTT). In order to secure the bond capacity of the NSM FRP, it is necessary to protect the front as well as side by using insulation materials.

• Steel and Composite Structures
• /
• 제38권3호
• /
• pp.241-255
• /
• 2021

In order to study the interfacial bond-slip behavior of steel reinforced recycled concrete (SRRC) under cyclic loading, thirteen specimens were designed and tested under cyclic loading and one under monotonic loading. The test results indicated that the average bond strength of SRRC decreased with the increasing replacement ratio of recycled concrete, whereas the bond strength increased with an increase in the concrete cover thickness, the volumetric stirrup ratio, and the strength of recycled concrete. The ultimate bond strength of the cyclically-loaded specimen was significantly (41%) lower than that of the companion monotonically-loaded specimen. The cyclic phenomena also showed that SRRC specimens went through the nonslip phase, initial slip phase, failure phase, bond strength degradation phase and residual phase, with all specimens exhibiting basically the same shape of the bond-slip curve. Additionally, the paper presents the equations that were developed to calculate the characteristic bond strength of SRRC, which were verified based on experimental results.

• The Journal of Advanced Prosthodontics
• /
• 제5권3호
• /
• pp.305-311
• /
• 2013

PURPOSE. Over the past years, the adhesion of fiber posts luted with simplified adhesive systems has been a matter of great interest. The aim of this study was to assess the post retentive potential of a self-adhesive resin cement using different adhesive systems to compare the push-out bond strengths of fiber posts. MATERIALS AND METHODS. The post spaces of 56 mandibular premolar roots were prepared and divided into 4 experimental groups and further divided into 2 subgroups according to testing time (n=7). The fiber posts (Rely X Fiber Post) were luted with a self-adhesive resin cement (RelyX Unicem) and one of the following adhesive systems: no adhesive, a total-etch adhesive resin (Single Bond), a two-step self-etch adhesive resin (Clearfil SE Bond) and a one-step self-etch adhesive resin (Clearfil S3 Bond). Each root was cut horizontally, and 1.5 mm thick six root segments were prepared. Push-out tests were performed after one week or three months (0.5 mm/min). Statistical analysis were performed with three-way ANOVA (${\alpha}$=.05). RESULTS. Cervical root segments showed higher bond strength values than middle segments. Adhesive application increased the bond strength. For one week group, the total-etch adhesive resin Single Bond showed higher bond strength than the self-adhesive resin cement RelyX Unicem applied without adhesive resin at middle region. For 3 months group, the two-step self-etch adhesive resin Clearfil SE Bond showed the highest bond strength for both regions. Regarding the time considered, Clearfil SE Bond 3 months group showed higher bond strength values than one week group. CONCLUSION. Using the adhesive resins in combination with the self-adhesive resin cement improves the bond strengths. The bond strength values of two-step self-etch adhesive resin Clearfil SE Bond improved as time passes.

• Restorative Dentistry and Endodontics
• /
• 제30권1호
• /
• pp.22-30
• /
• 2005

수복물의 변연 미세 누출과 마모 개선을 위해 표면 전색제가 개발되었으며 이의 효과에 대해 알아보기 위해, 규격화된 치경부 5급 와동을 25개의 소구치의 협면에 형성하고 Single Bond와 Z-250으로 수복한 뒤, $37^{\circ}C$의 증류수에 7일간 보관한 후 무작위로 5군으로 나누고 다음과 같은 재료로 제조사의 지시에 따라 표면 처리하였다 : No sealing ; Single Bond Adhesive ; Biscover ; Fortify ; Optiguard. 그 후 잇솔질 마모시험을 시행하였다. 표면 조도는 잇솔질 전후에 profilometer로 측정되었고 paired t-test와 ANOVA로 비교하였다. 접착면과 표면변화는 전자현미경으로 관찰하였다. 미세누출 평가를 위해 시편은 $2\%$ methylene blue 용액으로 염색한 뒤, 협설로 잘라 제작하였다. 입체현미경을 이용하여 교합면쪽과 치경부쪽 계면에서 미세누출을 관찰하고 Kruskal-Wallis와 Mann-Whitney U test를 이용하여 그 결과를 비교하였다. 표면 조도는 잇솔질 후 수치가 증가하였으나 통계학적으로 유의한 차이를 나타내지는 않았다. 전자 현미경 관찰 결과, 표면 전색제가 접착면에 부분적으로 남아있기도 하였으나 많은 부분에서 떨어져 나간 상태였다. 특히, 미세 틈새가 치경부쪽 변연에서 나타났다. 미세누출 실험에서는 법랑질에서 더 봉쇄효과가 좋았으며 교합면쪽 변연에서 군간에 유의할만한 차이를 나타내었다. 조절군과 Single Bond를 도포한 군에서는 치경부쪽 변연보다 법랑질쪽 변연에서 유의하게 좋은 변연 봉쇄 효과를 나타내었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.57-60
• /
• 2006

The purpose of this study is to assess performance of prepacked DFRCC material compared with the DFRCC material which is made by using general mixing method. From 4r-point bending test, bond strength test and chlorine ion penetration test, flexural stress, -deflection relations, bond strengths, and durability assessment have been obtained. From the experiments, premixed DFRCC shows relatively good performance.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.211-216
• /
• 2003

Coated bars are protecting reinforcing bars from corrosion and enhancing durabilities of reinforced concrete structures are tested to evaluate corrosion protection properties. Tests are performed based on the relevant standards of ACI and ASTM, such as chemical resistance, salt water spray, salt crack test and chloride permeability test with the main variable of the coating thickness. Three type materials are tested by Polyethylene, epoxy and bare bar. Test results show good chemical protection property and chloride permeability. Polyethylene coated bar is good coating material than any other materials.

• 대한치과보철학회지
• /
• 제42권1호
• /
• pp.30-40
• /
• 2004

Purpose : The purpose of this study was aimed to compare the shear bond strength on dentin of three dentin bonding agents and two resin cements used in conjunction with self-cured composite resin core material. Material and method : Control group and six experimental groups were divided for this study. Control group was designated as specimens bonded with Tenure$ A&B^{(R)}$. Experimental groups were as follows : PB-BL group : specimens bonded with Prime&Bond $NT^{(R)}$, $BondLink^{(R)}$ SB-BL group : specimens bonded with $^{(R)}$, BondLink$SingleBond^{(R)}$ PB group : specimens bonded with Prime&Bond $NT^{(R)}$ SB group : specimens bonded with $SingleBond^{(R)}$ PF group : specimens bonded with $Panavia-F^{(R)}$ BI group specimens bonded with Bistite $II^{(R)}$ All specimens were stored in $37^{\circ}C$ distilled water for 24 hours, followed by the shear bond strength was tested by universal testing machine. The data was analysed statistically by Mann-Whitney test. Results : 1. For Prime&Bond $NT^{(R)}$ and $SingleBonde^{(R)}$, the shear bond strength was 0.24 MPa and 7.19 MPa each by each, while Tenure $A&B^{(R)}$ group control was measured at 13.93 MPa (p<0.05). Especially for Prime&Bond $NT^{(R)}$ it did not get conjunction with dentin. 2. For Prime&Bond $NT^{(R)}$ and $SingleBond^{(R)}$ using $BondLink^{(R)}$, there was no significant difference as a result of 11.73 MPa and 14.00 MPa each by each (p<0.05). 3. For $Panavia-F^{(R)}$ and Bistite $II^{(R)}$, they showed the highest shear bond strength as measured by 18.24 MPa and 16.09 MPa each (p<0.05).

• The Journal of Advanced Prosthodontics
• /
• 제9권2호
• /
• pp.130-137
• /
• 2017

PURPOSE. The purpose of this study was to evaluate the effect of nano-structured alumina surface coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements. MATERIALS AND METHODS. A total of 90 disk-shaped zirconia specimens (HASS CO., Gangneung, Korea) were divided into three groups by surface treatment method: (1) airborne particle abrasion, (2) tribochemicalsilica coating, and (3) nano-structured alumina coating. Each group was categorized into three subgroups of ten specimens and bonded with three different types of dual-cured resin cements. After thermocycling, shear bond strength was measured and failure modes were observed through FE-SEM. Two-way ANOVA and the Tukey's HSD test were performed to determine the effects of surface treatment method and type of cement on bond strength (P<.05). To confirm the correlation of surface treatment and failure mode, the Chi-square test was used. RESULTS. Groups treated with the nano-structured alumina coating showed significantly higher shear bond strength compared to other groups treated with airborne particle abrasion or tribochemical silica coating. Clearfil SA Luting showed a significantly higher shear bond strength compared to RelyX ARC and RelyX Unicem. The cohesive failure mode was observed to be dominant in the groups treated with nano-structured alumina coating, while the adhesive failure mode was prevalent in the groups treated with either airborne particle abrasion or tribochemical silica coating. CONCLUSION. Nano-structured alumina coating is an effective zirconia surface treatment method for enhancing the bond strength between Y-TZP ceramic and various dual-cured resin cements.

• 대한치과기공학회지
• /
• 제35권1호
• /
• pp.19-27
• /
• 2013

Purpose: The aim of this research was to evaluate the shear bond strength of different zirconia veneering ceramics with and without liner glass materials to yttria partially-stabilized tetragonal zirconia polycrystalline(Y-TZP). Methods: Five co mmercial zirconia veneering ceramics were used in this study, E-Max(EM), Creation ZI(CR), Cercon ceram kiss(CE), Triceram(TR) and Zirkonzahn ICE(ZI). All samples were prepared according to manufacturer's instructions. Experimental industrially manufactured Y-TZP ceramic blocks(diameter: 2.7 mm; height: 13.5 mm) were used in this study. Shear bond strength between zirconia ceramic coping and zirconia veneering ceramics were evaluated by the push-shear bond test. The fracture load data were analyzed using ANOVA and Scheffe's test(${\alpha}$=0.05). The fractured surfaces of zirconia core ceraimc and zirconia veneering ceramics were observed using a scanning electron microscope(SEM). Results: The mean shear bond strengths ranged from 20 MPa ($20.12{\pm}6.34$ MPa) to 66.6 MPa ($66.62{\pm}10.01$ MPa). The Triceram(TRG) showed the highest value and Creation ZI(CR) showed the lowest value. In all groups, Zirconia liner and glass material groups was significantly higher shear bond strength than without liner(P<0.05), with the exception of Cercon ceram kiss(CE)groups. Conclusion: Zirconia bonding materials may have the advantage of improved bond strength between zirconia ceramic core and veneering ceramics.