• Journal of Welding and Joining
• /
• v.18 no.1
• /
• pp.91-96
• /
• 2000

Characteristics of the weld defect, such as a blowhole and a pit in lap-jointed fillet Co₂ welds of Zn-coated steel sheet were studied in order to make clear the sequence of the blowhole formation during welding. Main conclusions obtained are as follows: 1) Blowhole, wormhole and pit were found in fillet welds, although the optimum welding condition of 200A-23V-100cm/min was applied. 2) Zn was only detected at the solidification boundary at the early stage of the blowhole formation. 3) Most of the blowholes was started to form at lap-joint by the Zn vapor. With increasing of the Zn vapor and its pressure, the blowhole was develope to th bed surface until the completion of weld solidification. 4) The behavior of the blowhole in growth was similar to that of the columnar dendrite during welding.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.191-191
• /
• 2000

The mechanism of the blowhole and the pit formation in lap-jointed fillet CO₂ arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage.2) Most of the pits was back-filled at the last stage of their formation. (Received September 27, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.64-68
• /
• 2000

The mechanism of the blowhole and the pit formation in lap-jointed fillet Co₂arc welds of Zn-coated steel sheet was established by the direct observation of the gas behavior in the molten pool with the high speed camera system. Main conclusions obtained are as follows: 1) Some blowholes were formed by incomplete back-filling to the pits at the last stage of the solidification. This type of blowhole was formed through four stages of gas in the molten pool, incubation, explosion, back-filling and completion of back-filling stage. 2) Most of the pits was back-filled at the last stage of their formation.

• Journal of Welding and Joining
• /
• v.23 no.1
• /
• pp.69-76
• /
• 2005

Recently, application of arc welding to galvanized carbon steel sheet is on the increasing Ould in the fields of automobile and construction industries. In arc welding process, zinc is evaporated in weld pool, even under the appropriate welding condition and produce blowhole and/or pit. Zinc gas cause instability of arc and increase spatter and fume. This research is purposed to minimize the heat-input and the formation of porosities in the welded joint of the galvanized carbon steel sheet using variable polarity AC wave pulse MIG welding system. An appropriate welding condition which showed low spatter and good bead appearance was acquired by applying the AC pulse MIG welding machine to DC duplicated MIG welding with the solid wire. When oxygen gas was added to shield gas of MIG welding for galvanized steel sheet, arc length was increased and arc stability was improved. In the AC duplicated welding, the loss of galvanized layer was decreased as the amount of heat-input was decreased when the EN ratio was increased under the condition that average welding current was evenly set.

• Journal of Industrial Technology
• /
• v.22 no.A
• /
• pp.119-125
• /
• 2002

In Kwangjin industrial company, mill is operating for the foundry sand production at the rate of 25t/hr from quartzite. Foundry sands fall into four distinct categories: silica sand, lake sand, bank sand, and natural molding sand. Silica sand is a general term used to describe crushed, washed, graded, dried, and cooled clay-free sands. This study was conducted for the investigation of the foundry sand productivity and the life span of the hammer according to the material quality. The life time of hammer from several manufacturer were compared in order to find out the grinding efficiency of the various hammer material. In the result of tests, the life time of high-Mn hammer was 10.5 hours while that of high-Cr was 19.5 hours. The life time in case of typical worn shape hammers was about 12 hours and the average time of a blowhole hammer was about 6.5 hours.

• Journal of Korea Foundry Society
• /
• v.30 no.2
• /
• pp.55-59
• /
• 2010

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.196-196
• /
• 2000

Formation of the weld defect, such as a blowhole and a pit in lap-jointed fillet arc welds has been a serious problem in arc welding of Zn-coated steel sheet. In this study, the relationship among welding conditions, welding materials and defect formation was investigated in order to minimize these defects in the CO₂ welds. In addition, the arc stability of the commercial welding wires was evaluated for revealing their effects on defect formation. Main conclusions obtained are as follows:1) There was no difference between shear tensile strength of the sound welds and that of the welds with blowholes whose diameters are less than 0.5mm. However, the welds with blowholes whose diameters are equal or larger than 0.5mm and pits exhibited tensile strength 10~20% and 30~40% lower than that of the sound welds respectively.2) The optimum welding condition to effectively prevent or reduce the weld defects formation are as follows:- The welding variables of 220A-23V-100cm/min and 120A-190V-30cm/min were recommended for minimizing the weld defects.- The gap between the two sheets at the lap-joint should be controlled to more than 0.2mm- Solid wire was less susceptible to the formation of the weld defects than the flux-cored wire.- The low welding current condition produced less weld defects than the hihg welding current condition.3) One of the reason why the amount of the defect was reduced at the low welding current was the gas discharging by the active agitation of the molten pool, due to an increasing in the number of the short circuit. (Received September 27, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.69-76
• /
• 2000

Formation of the weld defect, such as a blowhole and a pit in lap-jointed fillet arc welds has been a serious problem in arc welding Zn-coated steel sheet. In this study, the relationship among welding conditions, welding materials and defect formation was investigated in order to minimize these defects in the CO₂welds. In addition, the arc stability of the commercial welding wires was evaluated for revealing their effects on defect formation. Main conclusions obtained are as follows: 1) There was no difference between shear tensile strength of the sound welds and that of the welds with blowholes whose diameters are less than 0.5mm. However, the welds with blowholes whose diameters are equal or large than 0.5mm and pits exhibited tensile strength 10∼ 20% and 30∼40% lower than that of the sound welds respectively. 2) The optimum welding condition to effectively prevent or reduce the weld defects formation are as follows: -The welding variables of 220A-23V-100cm/min and 120A-19V-30cm/min were recommended for minimizing the weld defects. -The gap between the two sheets at the lap-joint should be controlled to more than 0.2mm. -Solid wire was less susceptible to the formation of the weld defects than the flux-cored wire. -The low welding current condition produced less weld defects than the high welding current condition. 3) One of the reason why the amount of the defect was reduced at the low welding current was the gas discharging by the active agitation of the molten pool, due to an increasing in the number of the short circuit.

• Journal of Information Processing Systems
• /
• v.16 no.1
• /
• pp.49-60
• /
• 2020

To solve the edge ringing or block effect caused by the partial differential diffusion in image enhancement domain, a new image enhancement algorithm based on bidirectional diffusion, which smooths the flat region or isolated noise region and sharpens the edge region in different types of defect images on aviation composites, is presented. Taking the image pixel's neighborhood intensity and spatial characteristics as the attribute descriptor, the presented bidirectional diffusion model adaptively chooses different diffusion criteria in different defect image regions, which are elaborated are as follows. The forward diffusion is adopted to denoise along the pixel's gradient direction and edge direction in the pixel's smoothing area while the backward diffusion is used to sharpen along the pixel's gradient direction and the forward diffusion is used to smooth along the pixel's edge direction in the pixel's edge region. The comparison experiments were implemented in the delamination, inclusion, channel, shrinkage, blowhole and crack defect images, and the comparison results indicate that our algorithm not only preserves the image feature better but also improves the image contrast more obviously.

• Journal of Welding and Joining
• /
• v.34 no.4
• /
• pp.55-61
• /
• 2016

During laser overlap welding of galvanized steel sheets, explosion of weld pool by the high pressure zinc vapor induces weld defects like porosity and blowhole. In this study, laser 2-pass welding was implemented to prevent the weld defects. Through the 1st pass welding, zinc layers on the faying surfaces were removed when proper heat input was applied. Excessive heat input could result in explosion even during the 1st pass welding and insufficient heat input could not remove enough region of zinc layer for the 2nd pass welding. Coating weights of $45g/m^2$ and $60g/m^2$ were considered and for both cases sound welds without weld defects could be achieved. In spite of 2-pass welding, softening of weld and heat affected zone was not observed and Zn coating was not diluted into the weld metal.