• 구강회복응용과학지
• /
• 제22권3호
• /
• pp.221-230
• /
• 2006

Recently, the need for esthetic results has increased the interest for all-ceramic crown prosthesis. Furthermore, the development of zirconium core via CAD/CAM system has allowed the all ceramic restorations to be applied to almost all fixed prosthesis situations. But, the increased strength has been reported to increase in proportion with the bond strength of cement, and recently, the tribochemical system which increases the bond strength through, silica coating and silanization has been introduced. The purpose of this study was to compare the $Rocatec^{TM}$ system and $CoJet^{TM}$ system with the traditional acid etching and silanization method of the irconium based ceramic. The surface character was observed via SEM(X2000), and the bond strength with the resin cement were measured. 50 In-Ceram Zirconia (Adens, Korea) discs were fabricated and embedded in resin, group 1 was treated with glass-bead blasting and cleaning, group 2 was treated with 20% HF for 10 minutes and silanized, group 3 was treated with the $Rocatec^{TM}$ system, and group 4 was treated with the $CoJet^{TM}$ system. Each group was comprised of 10 specimens. The specimens were cemented to a $3mm{\times}5mm$ resin block with Super-Bond C&B. The shear bond strength was measured with the $Instron^{(R)}$ 8871 at a crosshead speed of 0.5mm/min. The results were as follows. 1. According to SEM results, there were little difference between group 1 & group 2, but in group 3 and 4, silica coating was detected and there was increase in surface roughness. 2. The shear bond strength decreased in the order of group 3(46.28MPa), group 4(42.04MPa), group 2(31.56MPa), and group 1(27.46MPa). 3. There was significant differnce between group 1&2 and group 3&4(p<0.05). From the results above, it can be considered that the conventional method of acid etching and silane treatment cannot increase the bond strength with resin cements, and that by applying the tribochemical system of $Rocatec^{TM}$ system and $CoJet^{TM}$ system, we can achieve a stronger all ceramic restoration. Further studies on surface treatments to increase the bond strength are thought to be needed.

• 대한치과보철학회지
• /
• 제39권1호
• /
• pp.71-83
• /
• 2001

The purpose of this study was to compare the effects of various surface treatments by measuring removal torque on bone healing around titanium implants. 40 Screw-shaped cp titanium implants with length of 4mm, outer diameter of 3.75mm, and pitch-height of 0.5mm were used Group 1 was left as machined(control), Group 2 was blasted with $50{\mu}m\;Al_2O_3$, group 3 was blasted and etched in etching solution($NH_4OH : H_2O_2:H_2O= 1 : 1 : 5$) at $90^{\circ}C$ for 1 minute group 4 was blasted and oxidated under pure oxygen at $800^{\circ}C$. The implant surface roughness was analyzed with SEM and CLSM(Confocal Laser Scanning Microscope) and implants were placed in proximal tibial metaphysis of 10 New Zealand White rabbits. After 3 months of healing period, removal torque of each implant was measured to compare bone healing around implant. The results obtained were as follows 1. In SEM view, blasting increased the roughness of the surface, but etching of that rough surface decreased the roughness due to the removal of the tip of the peak. Oxidation also decreased the roughness due to formation of needle-like oxide grains on the implant surface. 2. The Sa value from CLSM was least in the machined group($0.47{\mu}m$), greatest in blasted group($1.25{\mu}m$), and the value decreased after etching($0.91{\mu}m$) and oxidation($0.94{\mu}m$). 3. The removal torque of etched group(24.5Ncm) was greater than that of machined group(16.7Ncm) (P<0.05), and was greatest in the oxidated group(40.3Ncm) and the blasted group(34.7Ncm).

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 추계학술발표회초록집
• /
• pp.134-135
• /
• 2003

The dental implant materials required good mechanical properties, such as fatigue strength, combined with a high resistance to corrosion. For increasing fatigue resistance and delaying onset of stress corrosion cracking, shot peening has been used for > 50 years to extend service life of metal components. However, there is no information on the electrochemical behavior of shot peened and hydroxyapatite(HA) coated Ti-6Al-4V alloys. To increase fatigue strength, good corrosion resistance, and biocompatibility, the electrochemical characteristics of Ti/TiN/HA coated and shot peened Ti-6Al-4V alloys by electron beam physical vapor deposition(EB-PVD) have been researched by various electrochemical method in 0.9%NaCl. Ti-6Al-4V alloys were prepared under the condition of hydrogen and vacuum arc furnace. The produced materials were quenched at 1000$^{\circ}C$ under high purity dried Ar atmosphere and were hold at 500$^{\circ}C$ for 2 hrs to achieve the fatigue strength(1140㎫) of materials. Ti-6Al-4V alloys were prepared under the condition of hydrogen and vacuum arc furnace. Shot peening(SP) and sand blasting treatment was carried out for 1, 5, and 10min. On the surface of Ti-6Al-4V alloys using the steel balls of 0.5mm and alumina sand of 40$\mu\textrm{m}$ size. Ti/TiN/HA multilayer coatings were carried out by using electron-beam deposition method(EB-PVD) as shown Fig. 1. Bulk Ti, powder TiN and hydroxyapatite were used as the source of the deposition materials. Electrons were accelerated by high voltage of 4.2kV with 80 - 120mA on the deposition materials at 350$^{\circ}C$ in 2.0 X 10-6 torr vacuum. Ti/TiN/HA multilayer coated surfaces and layers were investigated by SEM and XRD. A saturated calomel electrode as a reference electrode, and high density carbon electrode as a counter electrode, were set according to ASTM GS-87. The potentials were controlled at a scan rate of 100 mV/min. by a potentiostat (EG&G Co.273A) connected to a computer system. Electrochemical tests were used to investigate the electrochemical characteristics of Ti/TiN/HA coated and shot peened materials in 0.9% NaCl solution at 36.5$^{\circ}C$. After each electrochemical measurement, the corrosion surface of each sample was investigated by SEM.

• The Journal of Advanced Prosthodontics
• /
• 제11권1호
• /
• pp.7-15
• /
• 2019

PURPOSE. The aim of this study was to identify the effects of three aesthetic restorative materials on the wear between tooth and restoration by a pin-on-disk manner. MATERIALS AND METHODS. Six aesthetic restorative materials were used to prepare disk specimens for wear test, which were Lava Zirconia as zirconia group, Vintage MP and Cerabien ZR as veneering porcelain group, Gradia Direct microhybrid composite containing prepolymerized fillers, Filtek Z250 microhybrid composite containing zirconia glass and colloidal silica particles, and Filtek Z350 nanocomposite as composite resin group. Vertical loss of the worn cusp, change of the surface roughness of the restoration materials, and the surface topography were investigated after wear test under 9.8-N contact load. RESULTS. The porcelain groups (Vintage MP and Cerabien ZR) caused the largest vertical loss of teeth when compared with those of the composite resin and zirconia groups, and Filtek Z250 microhybrid composite results in the second-largest vertical loss of teeth. The surface of Filtek Z350 nanocomposite was deeply worn out, but visible wear on the surface of the zirconia and Gradia Direct microhybrid composite was not observed. When the zirconia surface was roughened by sand-blasting, vertical loss of teeth considerably increased when compared with that in the case of fine polished zirconia. CONCLUSION. It was identified that microhybrid composite resin containing a prepolymerized filler and zirconia with reduced surface roughness by polishing were the most desirable restorative materials among the tested materials to prevent the two-body wear between aesthetic restorative material and tooth.