• 한국세라믹학회지
• /
• 제43권5호
• /
• pp.315-319
• /
• 2006

There have been some studies on the use of coal waste as a raw material for clay bricks due to the lack of naturally producing minerals. It can help resolving the problems of pollution, forest conservation and flood control by utilizing coal waste. However, high content of carbon materials usually leads to the black core in clay bricks after firing process, and diminishes the mechanical and aesthetical properties of clay brick. In this study, the effect of firing process is investigated for the removal of black core in clay bricks with carbon content. The removal kinetics of black core are also compared and investigated with the firing schedule and black core removal.

• 한국추진공학회지
• /
• 제18권2호
• /
• pp.67-72
• /
• 2014

본 연구에서는 HTPB에 보강제로 Carbon black이 충전된 라이너의 점도, 기계적 특성, 추진제와의 접착력을 고찰하였다. Carbon black이 충전된 라이너는 점도가 높아 수평원심 주조 방법으로 라이닝에 문제가 있었다. 이 문제점을 해결하기 위해 프리믹스를 $60^{\circ}C$에 6일 숙성시킴으로써, 점도 464 posie에서 200 posie로 감소시킬 수 있었다.

• 한국결정성장학회지
• /
• 제15권5호
• /
• pp.208-215
• /
• 2005

골재를 제조할 때 골재의 중앙에 만들어지는 블랙코어(black core)의 형성 메커니즘을 살펴보기 위해 적점토, 탄소(carbon), 산화철$(Fe_2O_3)$이 혼합된 직경 10mm 구형골재의 조성, 소성온도, 소성시간, 소성분위기, 소성방법을 변화시키면서 각각의 비중, 흡수율, 블랙코어 면적비$(\%)$, 파괴강도, Fe 총량분석, XRF를 측정하고 비교하였다. 소량의 산화철 첨가는 골재의 물성에 큰 영향을 미치지 않는 반면 탄소는 많이 첨가될수록, 소성온도가 증가할수록 블랙코어가 더 많이 형성되었고, 블랙코어의 비율이 증가하면 그만큼 비중은 감소하고 흡수율은 증가하였다 산화분위기에서 소성시킨 골재는 껍질 (shell)과 블랙코어가 뚜렷하게 구분되는 반면 환원분위기에서 소성한 시편에서는 시편의 단면전체에 블랙코어가 형성되었고, 산화분위기와 중성분위기와는 달리 환원분위기에서 소성된 시편에서는 탄소첨가량이 증가할수록 비중이 증가했으며, 전반적인 비중은 가장 낮았다. 흡수율은 모든 분위기에서 탄소 첨가량이 증가할수록 증가했다. 소성방법을 달리하여 실험한 결과 직화소성한 시편에서는 블랙코어가 잘 형성되었고, 승온소성한 시편에 비해 비중은 작고 흡수율은 높았다. 또한 파괴강도의 측정결과를 통해 블랙코어가 형성되지 않은 골재시편의 강도가 블랙코어가 형성된 시편보다 다소 크다는 사실을 알 수 있었다. Fe총량분석결과 블랙코어에서 껍질보다 많은 Fe와 FeO가 분포하였고, 껍질에는 적색을 띠는 $Fe_2O_3$가 많이 분포되어 있었다. XRF 분석 결과를 통해 탄소는 블랙코어 형성부위에서만 존재한다는 것을 알 수 있었다.사 결과 외형은 YF04 $1.0\%$ 처리구가 3.64으로 높게 나타났으며 YM03 $0.1\%$ 처리구가 3.00으로 가장 낮았다(P>0.05). 색은 YF04 $1.0\%$ 처리구가 4.00으로 높았으며 YF04 $0.1\%$ 처리구는 2.93으로 가장 낮았다(P<0.05). 다즙성은 YF04 $1.0\%$ 처리구가 3.50으로 가장 높게 나타났으며 YM03 $0.1\%$와 YM03 $1.0\%$ 처리구가 각각 3.07로 낮았다 (P>0.05).구보다 약간 증가하였으나 큰 차이를 나타내지 않았다.다리살의 콜레스테롤 함량도 감소하는 경향을 보였으나 유의적인 차이는 없었다.적으로 작용하였다.있다.>16$\%$>0$\%$ 순으로 좋게 평가되었다. 결론적으로 감농축액의 첨가는 당과 탄닌성분을 함유함으로써 인절미의 노화를 지연시키고 저장성을 높이는데 효과가 있는 것으로 생각된다. 또한 인절미를 제조할 때 찹쌀가루에 8$\%$의 감농축액을 첨가하는 것이 감인절미의 색, 향, 단맛, 씹힘성이 적당하고 쓴맛과 떫은맛은 약하게 느끼면서 촉촉한 정도와 부드러운 정도는 강하게 느낄수 있어서 전반적인 기호도에서 가장 적절한 방법으로 사료된다.비위생 점수가 유의적으로 높은 점수를 나타내었다. 조리종사자의 위생지식 점수와 위생관리 수행수준의 상관관계를 조사한 결과, 위생지식의 기기설비위생은 위생관리 수행수준의 합계(p<0.01)에서 유의적인 상관관계(p<0.01)를 나타내었으며, 위생지식의 식중독 및 미생물은

• 한국결정성장학회지
• /
• 제16권2호
• /
• pp.71-75
• /
• 2006

소성 분위기를 변화시켜 골재를 제조할 때 골재의 중앙에 만들어지는 블랙코어(black core) 형성정도의 차이와 골재 물성의 차이점을 알아보기 위해 적점토, 탄소(carbon), 산화철($Fe_2O_3$)이 혼합된 직경 10mm 구형골재를 조성별로 산화분위기, 중성분위기, 환원분위기에서 각각 소성시키고 각각의 비중, 흡수율, 블랙코어 면적비(%)를 측정하고 비교하였다. 산화분위기에서 소성시킨 골재는 껍질(shell)과 블랙코어가 뚜렷하게 구분되는 반면 중성 및 환원분위기에서 소성한 시편에서는 시편의 단면전체에 블랙코어가 형성되었다. 산화분위기와 중성분위기와는 달리 환원분위기에서 소성된 시편에서는 탄소첨가량이 증가할수록 비중이 증가했으며, 전반적인 비중은 가장 낮았다. 흡수율은 모든 분위기에서 탄소첨가량이 증가할수록 증가하는 경향을 보였다.

• 한국세라믹학회지
• /
• 제41권2호
• /
• pp.176-181
• /
• 2004

지정폐기물인 전기로 제강 분진은 현재 대부분이 매립 등 부적절하게 처리되고 있어 지하수 오염 등의 환경파괴를 일으킬 위험이 있다. 전기로 제강 분진의 자원화를 위하여 전기로 제강 분진/점토의 조성으로 다공체를 제조하였으며, 다공체의 기공 특성 분석을 하였다. 다공체는 서로 다른 두 개의 미세구조로 형성되어있으며, 표면부위의 미세구조는 치밀하고 검은색이 아니고, 내부부위는 검은색이며 다공성의 미세구조(black coring)를 갖는다. 블랙코아 부위의 면적과 경량화정도를 정량화하기 위하여 Ic(core index)와 Is(shell index)를 정의하였으며, 인공경량골재로서의 최적 경량화 조건은 Ic가 0.5이상이고, Is는 0.4이상이다.

• Elastomers and Composites
• /
• 제45권1호
• /
• pp.7-11
• /
• 2010

본 논문에서는 polyethyleneimine (PEI)를 커플링제로 사용하여 간단한 공정을 통하여 아세틸렌 블랙/실리카 복합체 입자를 제조하였다. 복합체 입자는 PEI를 아세틸렌 블랙 표면에 흡착시키고 졸-겔 합성공정을 통하여 실리카를 아세틸렌 블랙 위에서 합성하는 두단계 공정을 통하여 제조되었다. 복합체 입자의 모폴로지 분석 결과 실리카가 아세틸렌 블랙위에 존재하는 core-shell 구조를 확인하였으며, 표면에 상당한 미세기공이 존재함을 알 수 있었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.25-26
• /
• 2023

The internal core material and external color of a sandwich panel have a significant impact on the performance of the sandwich panel. For use on roofs and walls, the internal core material and external color must be considered. Therefore, the surface and back side temperatures were measured for each exterior color and inner core material type. For the internal core materials, urethane foam and Expanded Poly Styrene(EPS), which are core materials mainly used in sandwich panels, were selected. As colors, black and ivory were selected according to brightness, and a total of five colors were selected: red, blue, and green, which are the three primary colors of light. As a result, there were differences in surface and temperature depending on the external color and type of internal core material. Regardless of the color, the temperature was measured lower for panels with urethane foam than for panels with an internal core of EPS. This is believed to have been influenced by the difference in thermal conductivity of urethane foam being 0.023W/(m·K) and that of EPS being 0.032W/(m·K). In addition, panels with a black exterior color were found to have higher surface and back temperatures than panels of other colors, and ivory-colored panels had lower back temperatures regardless of the core material. This is proportional to the brightness and light-absorbing characteristics.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 추계학술대회 초록집
• /
• pp.93-93
• /
• 2011

Nanostructures consisting of $TiO_2$ particles as a core and carbon as a shell ($TiO_2$@C) were prepared by heat treatment of $TiO_2$ nanoparticles at high temperature in a methane atmosphere. X-ray diffraction and transmission electron microscopy showed that a carbon shell layer was formed well. These structures were used as supports for platinum nanoparticles and the hybrid particles exhibit improved catalytic activity and stability toward ORR compared to Pt on a carbon black (Vulcan XC-72R). It is likely that enhanced catalytic properties of the Pt on $TiO_2$@C could be due to the stability of the core-shell support in comparison with carbon black support.

• 천문학회보
• /
• 제41권1호
• /
• pp.42.3-43
• /
• 2016

We present multiband photometric analyses of 10 core-collapse supernovae in the near-infrared and visible wavebands. Our infrared data is from observations of the supernovae using the Wide Field Infrared Camera at the Palomar 5-m telescope as part of the Caltech Core-Collapse Supernova Program, while we obtain the visible data from publicly available data base. By fitting the broadband spectral energy distribution with a black body and, when necessary, modified black body component, we estimate physical parameters of the supernovae more accurately and also conduct a systematic investigation of when the supernovae show any indication of dust formation.

• 한국결정성장학회지
• /
• 제19권1호
• /
• pp.54-59
• /
• 2009

기존의 로타리 킬른으로는 융착 현상 때문에 3 mm 이하 크기의 세골재를 제조하기 어려웠다. 이를 해결할 수 있는 수직형 유동층로를 설계, 제작하고 이로부터 점토 : 석분슬러지 :폐백토 =60 : 30 : 10(wt%)조성의 성형체를 소성하여 비중 $1.1{\sim}1.7$, 흡수율 $11{\sim}19%$의 다양한 특성을 갖는 경량 세골재를 제조하였다. 골재를 발포시키기 위한 최소 소성온도는 $1130^{\circ}C$이었다. $1140^{\circ}C$ 이상으로 소성된 시편은 전형적인 발포 경량골재 특성을 보였으며, 표면에 균열이 크게 벌어져서 내부 층이 드러나 보였다. 그러나 표면에 발생된 균열은 black core 내부로 진행되지 않았기 때문에 흡수율에 영향을 주지 않았다. 소성온도가 증가하면 골재의 shell 두께는 감소하고 black core 영역은 넓어졌으나 유지시간은 미세구조에 따른 영향을 주지 않았다. 소성온도가 증가되면 표면에 액상 발생량이 증가하여 골재의 흡수율은 감소하였다. 또한 소성시간도 골재 흡수율에 큰 영향을 주었는데, 이는 액상을 형성하고 또 생성된 액상이 표면의 개기공을 막아 폐기공으로 변화시키는데 시간이 필요하기 때문인 것으로 생각된다.