• Fire Science and Engineering
• /
• v.28 no.5
• /
• pp.71-79
• /
• 2014

This study was performed to test the combustive properties of Medium Density Fibreboards (MDFs) treated with chemicals of the bis-(dimethylaminomethyl) phosphinic acid (DMDAP), N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (DMDEDAP), piperazinomethyl-bis-phosphonic acid (PIPEABP), and methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP). MDFs were painted in three times with 15 wt% solution of the bis-(dimethylaminomethyl) phosphinic acid and alkylenediaminoalkyl-bis-phosphonic acids at the room temperature, respectively. After drying MDF treated with chemicals, combustive properties and volatile organic compounds (VOCs) contents were examined by the cone calorimeter (ISO 5660-1), test for flame retardant (NEMA Notice No. 2012034), and gas chromatography (KS M ISO 11890-2), respectively. It was indicated that the MDFs treated with chemicals showed the longer time to combustion time (CT) = (442~492) s than that of virgin plate by reducing the burning rate except for CT treated with DMDAP. In adition, the MDFs treated with chemicals showed both of the higher char area (44.33~61.33) kg/kg and char length (10.33~11.67) cm than those of virgin plate. Especially, the MDFs treated with chemicals showed the higher mean volatile organic compounds (VOCs) (0.188~0.333) g/L than that of virgin plate within the prescribed limits. Thus, It is supposed that the combustion- retardation properties were improved by the partial due to the treated chemicals in the virgin MDF.

• Applied Chemistry for Engineering
• /
• v.24 no.6
• /
• pp.633-638
• /
• 2013

This study was performed to test the combustive properties of pinus rigida specimens treated with bis-(dimethylaminomethyl) phosphinic acid, bis-(diethylaminomethyl) phosphinic acid (DEDAP), and bis-(dibuthylaminomethyl) phosphinic acid. Pinus rigida specimens were painted in three times with 15 wt% bis-(dialkylaminoalkyl) phosphinic acid solutions at the room temperature. After drying the treated specimens, combustive properties were examined by the cone calorimeter (ISO 5660-1). Combustion-retardation properties were found to be improved partially due to the treated bis-(dialkylaminoalkyl) phosphinic acids in the virgin pinus rigida. In particular, the specimens treated with DEDAP showed both the lower total heat release rate ($60.9MJ/m^2$) and effective heat of combustion (15.20 MJ/kg) than those of virgin plates. Compared with virgin pinus rigida plates, specimens treated with the bis-dialkylamimoalkyl phosphinic acid derivatives showed partially low combustive properties.

• Fire Science and Engineering
• /
• v.30 no.4
• /
• pp.65-72
• /
• 2016

This study examined the generation of combustion toxic gases of pinus rigida specimens processed with bis-(dimethylaminomethyl) phosphinic acid (DMDAP), bis-(diethylaminomethyl) phosphinic acid (DEDAP), and bis-(dibutylaminomethyl) phosphinic acid (DBDAP). Each pinus rigida plate was coated three times with 15 wt.% flame retardants in an aqueous solution. The specimens were then dried at room temperature. The production of combustion toxic gases was investigated using a cone calorimeter (ISO 5660-1). The first time to peak mass loss rate ($1^{st}-TMLR_{peak}$) processed with the chemical additives decreased to 5.9 from 41.2% compared with the unprocessed specimen. The second time to the peak mass loss rate ($2^{nd}-TMLR_{peak}$) for the processed specimens was decreased 1.8% for DMDAP and 5.3% for DBDAP and increased 1.8% for DEDAP. The peak carbon monoxide ($CO_{peak}$) production was 1.5 to 2.0 times higher than that of the unprocessed plate. The peak carbon dioxide ($CO_{2peak}$) production was reduced 0.01 times for DMDAP and increased 1.15 to 1.19 times for DEDAP and DBDAP compared with the unprocessed specimens. In particular, the oxygen concentration was much higher than 15%, which can be fatal to humans and the resulting hazard can be eliminated. Overall, the combustion toxicity of flammable gas were increased partially by the chemical additives compared with those of the unprocessed plate.

• Fire Science and Engineering
• /
• v.27 no.4
• /
• pp.21-26
• /
• 2013

This study was performed to test the combustive properties of Pinus rigida plates treated with bis-(dimethylaminomethyl) phosphinic acid (DMDAP), bis-(diethylaminomethyl) phosphinic acid (DEDAP), and bis-(dibuthylaminomethyl) phosphinic acid (DBDAP). Pinus rigida specimens were painted in three times with 15 wt% bis-(dialkylaminoalkyl) phosphinic acid solutions at the room temperature. After drying specimen treated with chemicals, combustive properties were examined by the cone calorimeter (ISO 5660-1). It is supposed that the combustion-retardation properties were improved by the partial due to the treated bis-(dialkylaminoalkyl) phosphinic acids in the virgin Pinus rigida. Especially, the specimens treated with chemicals showed both the lower total smoke release rate (TSRR) ($16.94{\sim}18.92m^2/m^2$) and lower $CO_{2mean}$ production (1.98~2.09 kg/kg) than those of virgin plate. However the specimens treated with chemicals showed both the higher peak mass loss rate (PMLR) (0.1250~0.1297 g/s) and higher 1st-smoke production rate (SPR) (0.0153~0.0167 g/s) than those of virgin plate. Compared with virgin Pinus rigida plate, the specimens treated with the bis-dialkylamimoalkyl phosphinic acids showed partially low combustive properties.

• Applied Chemistry for Engineering
• /
• v.28 no.1
• /
• pp.112-117
• /
• 2017

This study demonstrated the emission of combustion gases of medium density fibreboard (MDF)s coated with piperazinomethyl-bis-phosphonic acid (PIPEABP), methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP), N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (MDEDAP), or bis-(dimethylaminomethyl) phosphinic acid (DMDAP). Each MDFs were coated in three times with a brush with 15 wt% aqueous solution of the phosphorus-nitrogen acid additives. After the specimens were dried at room temperature, the emission of combustion gases was tested using a cone calorimeter (ISO 5660-1, 2). The peak smoke production rate ($SPR_{peak}$) of the specimens coated with phosphorus-nitrogen acids was 18.5 to 41.5%, which is lower than that of using the virgin plate. However, the production of peak carbon monoxide ($CO_{peak}$) was 6.7 to 24.2% higher than that of using the virgin plate. Also, the peak carbon dioxide ($CO_{2peak}$) was 4.2 to 24.4% lower than that of using virgin plate. While the peak oxygen depletion rate was much higher than the level of 15%, which can be fatal to humans and the resulting risk could thus be eliminated. Overall, the combustibility of coated specimens was partially suppressed, but showed a negative effect on the reduction of carbon monoxide.

• Applied Chemistry for Engineering
• /
• v.25 no.5
• /
• pp.481-486
• /
• 2014

This study was performed to test combustive properties of medium density fibreboard (MDF) plates treated with piperazinomethyl-bis-phosphonic acid (PIPEABP), methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP), and N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (MDEDAP). MDF specimens were painted three times with 15 wt% solution of the alkylenediaminoalkyl-bis-phosphonic acids at room temperature. After drying specimen treated with chemicals, combustive properties were examined using the cone calorimeter (ISO 5660-1). As a result, combustion-retardation properties increased due to the treatment of bare MDF with alkylenediaminoalkyl-bis-phosphonic acid solution. Especially, the specimens treated with chemicals showed the ignition (TTI) (148 s~116 s) was retarded and the flameout (Tf) (633 s~529 s) time increased, while the total heat release rate (THRR) (61.1~67.0) $MJ/m^2$ was lowered than those of using virgin plate by reducing the burnig rate. Compared with virgin MDF plate, the specimens treated with the alkylenediaminoalkyl-bis-phosphonic acids showed low combustive properties. However the specimens treated with bis-(dimethylaminomethyl) phosphinic acid (DMDP) showed the higher peak heat release rate (PHRR) ($185.08kW/m^2$) than that of the virgin plate.