• Journal of Powder Materials
• /
• v.7 no.3
• /
• pp.131-136
• /
• 2000

The effect of tempering temperature on the three point bending fatigue behavior of a P/M high speed steel JYPS-23 (1.28% C, 4.20% Cr, 6.40% W, 5.00% Mo, 3.10% V, bal. Fe) was investigated. The number of cycles to failure of the specimen austenitized at $1175^{\circ}C$ drastically increased with increasing tempering temperature. As tempering temperature increased from 500 to $620^{\circ}C$, the volume fraction and average size of carbides (MC or M6C) did not significantly changed, while hardness decreased drastically. The reduced hardness is due to the softening of matrix, which increased the resistance of the fatigue crack propagation. For a practical application, powder compacting test were also conducted with the P/M high speed steel punches tempered at 500, 580, and $620^{\circ}C$. The number of compacting cycles to failure of the punches also increased with increasing tempering temperature.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.24 no.2
• /
• pp.94-100
• /
• 1988

Recently with the rapid development in marine and shipbuilding industries such as marine structures, ship, and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics was closed up an important role in mechanical design. In this study, the 5086 Al-Alloy was tested by used of a rotary bending fatigue tester and was investigated under the environments of various specific resistance and air. The specific resistance, as a corrosion environment, was changed 15, 20, 25 and 5000$\Omega$.cm. The corrosion fatigue crack initiation sensitivity was quantitatively inspected for 5086 Al-Alloy in the various specific resistance. The experimental constants of Paris rule were examined in the various specific resistances, and the influences of load and corrosion with affect the crack growth rate were compared with. Main results obtained are as follows: (1) Number of stress cycles to corrosion fatigue crack initiation delaies and corrosion fatigue crack initiation sensitivity decreases with the increasing for the specific resistance. (2) The experimental constant m of Paris rule decreases with the decreasing for specific resistance. Hence the effect of corrosion is more susceptible than that of stress intensity factor. (3) The corrosion fatigue crack of 5086 Aluminium Alloy appears intergranular fracture. (4) Corrosion sensitivity is decreased with the increasing stress intensity factor and is nearly uniform when stress intensity factor is over 40kg.mm super(-3/2)

• Journal of the Korean Society for Heat Treatment
• /
• v.3 no.4
• /
• pp.10-22
• /
• 1990

A study has been investigated on the effect of mechanical properties (tension strength, rotary bending fatigue strength, wear resistance, hardness) according to the carbide particle size variation by the treatment of 1) quenching tempering, and 2) quenching, subzero treatment and tempering. The material used in this investigation was a typical bearing steel, high C high Cr, AISI E 52100. The result obtained in this study were as follows : (1) Finer the carbide particle size increasing the hardness and retained austenite in same quenching condition. (2) Finer the carbide particle size reduced the tension and rotary bending fatigue which were resulted from austenite grain growth and carbide precipitation on grain boundry that induced by carbide refine heat treatment. (3) Finer the carbide particel size increasing the wear resistance which were resulted by uniform distribution of carbide and increased hardness induced by microstructural uniform hardenability of matrix. (4) When the carbide particles were refinded, subzero treatment is effective only wear resistance and hardness.

• Journal of the Korean Society of Safety
• /
• v.30 no.3
• /
• pp.7-12
• /
• 2015

CFRP composites are used as primary structural members in various industrial fields because their specific strength and specific stiffness are excellent in comparison to conventional metals. Their usage is expanding to high added-value industrial fields because they are more than 50% lighter than metals, and have excellent heat resistance and wear resistance. However, when CFRP composites suffer impact damage, destruction of fiber and interface delamination occur. This causes an unexpected deterioration of strength, and for this reason it is very difficult to ensure the reliability of the excellent mechanical properties. Therefore, for the destruction mechanism in bending with impact damage, this study investigated the reinforcement data regarding various external loads by identifying the consequential strength deterioration. Specimens were damaged by impact with a steel ball propelled by air pressure. Decrease in bending strength caused by the tension and compression of the impact side, and depending on the lamination direction of fiber and interface inside the specimen. From the bending test it was found that the bending strength reduced when the impact energy increased. Especially in the case of compression on the impact side, as tensile stress occurred at the damage starting point, causing rapid failure and a substantially reduced failure strength.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.34 no.1
• /
• pp.30-36
• /
• 1998

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environments and in the air. These experiments were done to investigate the corrosion fatigue crack propagation behavior, the variation of aspect ratio for part through crack and electro-chemical characteristics of the metal. The main results obtained are as follows ; 1. Comparing the same surface crack length with the crack depth, the crack depth toward the thickness of specimen in air propagated faster than that in corrosion environment. 2. The aspect variation of the half elliptical crack can be estimated as following equation; b/a=i-jb/t where a : surface crack length, b : crack depth, t : specimen thickness, i,j : experimental constants but the slope j is decreased as specific resistance decreases. 3. As the specific resistance of corrosion environment decrease or the corrosion fatigue crack propagates, the corrosion potential become less noble.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.1
• /
• pp.29-33
• /
• 2018

Flexible electronics must be stable under various deformations such as bending, folding, and rolling. The reliability of ITO (Indium Tin Oxide) film used widely as a transparent electrode for flexible electronics has been studied using rolling fatigue test and bending test. During repeated rolling deformations, the electrical resistance was in-situ measured with different number of rotation. During rolling fatigue test, the electrical resistance of ITO film was significantly increased with increasing the number of rotation. As the stress state of ITO film is different according to the relative position of ITO and substrate, the rolling fatigue test was investigated under both outer and inner bending conditions. Inner rolling fatigue test showed superior electrical stability because the crack nucleation and propagation were retarded under compressive stress state.

• Journal of the korean Society of Automotive Engineers
• /
• v.5 no.2
• /
• pp.31-40
• /
• 1983

A study was made of the effect of cold working and stabilizing temperature on the fatigue properties of Aluminum alloy 5083. The amount of cold working ranged from 14% to 35% and stabilizing temperature was 120.deg. C-160.deg. C. Rotary bending fatigue test was carried out, and it was found that 1) E specimen that had been cold worked by the cold reduction of 35% and stabilized at 160.deg. C for 2 hours was showed the most excellent fatigue limit and endurance ratio and, 2) By the results of the between crack propagation behavior and stress intensity factor, E specimen was showed the better resistance to fatigue crack growth than others.

• Journal of Welding and Joining
• /
• v.17 no.6
• /
• pp.32-37
• /
• 1999

Since stainless steel plates have good mechanical properties, weldability, appearance and resistance of corrosion, these are traditionally used for vehicles such as the bus and the train. And they are mainly fabricated by spot welding. But fatigue strength of their spot welded joint is considerably influenced by welding conditions as well as geometrical factors. Thus a reasonable and systematic criterion for long life design of spot welded body structure must be established. In this report, strain energy density was analyzed by using 3-dimensional finite element model about the IB-type spot welded lap joint under tension-shear load. Fatigue tests were conducted on them having various thickness, joint angle, lapped length and width. From their results, it was found that fatigue strength of the IB-type spot welded lap joints could be effectively and systematically rearranged by strain energy density at the edge of nugget.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.5
• /
• pp.128-133
• /
• 1997

Due to their high strength and good wear resistance, nitro-carburizing materials have been used for many machine components. However, the nitro-carburizing materials are found to have one disadvantage ; that is, their strength and fatigue life show larger scatter than those of non-heated metals. In this paper, therfore, the statistical chracteristics of non-heated and nitro-carburized specimens for SCM415 are investi- gated under two different of stress levels 1.15 .sigma. /sub .omega. / .leq. / .sigma. / sub .alpha. / .leq. / 1.25 .sigma. /sub .omega. /. Seven specimens at each stress level are tested by using rotating bending fatigue tester. The relation between a crack length and fatigue cycles can be arranged for Weibull distribution, and S-N curve using 95% reliability function is obtalined for nitro-carburized specimen.

• Journal of Sensor Science and Technology
• /
• v.33 no.2
• /
• pp.86-92
• /
• 2024

Flexible electronic devices are exposed to repeated mechanical deformation; therefore, electrode performance is an important element. Recently, a new technology has been developed to improve the adhesion strength between polymer substrates and metal thin films through the cross-linking reaction of bovine serum albumin (BSA) bioconjugation proteins; however, additional performance evaluation as an electrode is necessary. Therefore, in this study, we investigated the effect of adhesive strength between a flexible substrate and a metal thin film on the performance of a flexible electrode. Cracks and changes in the electrical resistance of the electrode surface were observed through outer bending fatigue tests and tensile tests. As a result of a bending fatigue test of 50,000 cycles and a tensile test at 10% strain, the change in the electrical resistance of the flexible electrode with a high adhesion strength was less than 40%, and only a few microcracks were formed on the surface; thus, the electrical performance did not significantly deteriorate. Through this study, the relationship between the adhesion strength and electrical performance was identified. This study will provide useful information for analyzing the performance of flexible electrodes in the commercialization of flexible electronic devices in the future.