• Journal of the Korean Society of Safety
• /
• v.16 no.2
• /
• pp.44-50
• /
• 2001

The rotated bending fatigue test was conducted in air md in 3.5% NaCl salt solution to investigate the fatigue fracture behaviour of raw material and F.E.M dual phase steel made from raw material(SS41) by a suitable heat treatment. This study has compared the initial microcrack creation of material by tensile test with that by fatigue test. And the rotated bending test of cantilever type under the condition of 3.5% NaCl salt solution and air has investigated the corrosion fatigue fracture behaviour with the variation of stress concentration factor determined by each of notch shapes. The initial microcrack have been developed in fragile grainboundary with general corrosion occurring in raw material : in the pits built up by corrosion in F.E.M. dual phase steel because pits bring out stress concentration. It is small that the degree of decrease in corrosion fatigue life for F.E.M. dual phase steel compared with raw material because the notch sensitivity of F.E.M. dual phase steel is lower than raw material in reason of characteristics with two-phase construction.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.6
• /
• pp.49-55
• /
• 2011

In order to analyze feasibility of replacing a conventional 6-mm Ti bar with a 5-mm bar, a series of rotating bending fatigue tests were carried out on Ti-6Al-4V bars by strengthening the fatigue performance using a special technique called UNSM (Ultrasonic Nanocrystal Surface Modification). The results of S-N curves clearly showed that the performance of the 5-mm titanium specimen was similar to that of the 6-mm specimen when the UNSM treatment was applied. The 5-mm treated specimen converged with small scattering band into the linear line of the non-treated 6-mm one. Below the fatigue life of $10^5$ cycles, the UNSM treatment did not show any significant superiority in the bending stress and fatigue life. However, over the fatigue life of $10^5$ cycles, the effect of UNSM was superior for each fatigue life, and the bending stress became longer and higher than that of the untreated one. In the case of 6-mm Ti-bar with UNSM, the fatigue limit was about 592 MPa, and there was fatigue strength increase of about 30.7% at the fatigue life of $10^4$ cycles compared to the untreated 6-mm bar. Therefore, the compressive residual stress made by the UNSM in Ti-6Al-4V increased the fatigue strength by more than 30%.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.1
• /
• pp.55-59
• /
• 2011

Folding endurance, bending fatigue and monotonic tensile tests of 4 kinds of Cu foil on flexible substrate was performed to investigate the relationship between folding or bending endurances and tensile characteristics. The repeated 5.3 or 2.0% strain was applied to Cu foil in folding endurance test or bending fatigue test while monitoring the electrical resistance. Elastic modulus, yield strength, ultimate tensile strength, ductility, and toughness were obtained by monotonic tensile test on the same samples. The Cu foil with higher toughness and ductility showed higher reliabilities in folding or bending fatigue. However, elastic modulus and yield strength did not show any relationship with folding and bending reliability. This is because the failures of Cu foil by folding or bending fatigue were closely related to the fracture energy of metal.

• Journal of Aerospace System Engineering
• /
• v.14 no.6
• /
• pp.58-67
• /
• 2020

In this study, finite element fatigue analysis combined with a fatigue correlation factor is proposed to predict the bending fatigue life of a gear in an electro-mechanical aircraft actuator. First, stress-life curves are obtained for the gear material via a round bar fatigue test. Subsequently, stochastic stress-life (P-S-N) curves are derived for 50% and 1% failure probabilities, separately. The curves are applied to the fatigue analysis model of a single gear tooth, and the effect of the fatigue correction factor is analyzed. The analytical P-S-N curves reflecting the fatigue correction factor matched the experimental data. This shows that the analytical fatigue life is reliable and that the analysis technique is effective.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.4
• /
• pp.323-330
• /
• 2008

High cycle bending fatigue of socket welded small bore pipe was characterized, and also the fatigue crack initiation of small bore pipe was monitored in situ by the acoustic emission (AE) technique. The STS 316L stainless steel specimens were prepared by gas tungsten arc welding (GTAW) process having the artificial defect (i.e., lack of penetration) and defect free at the root. The fatigue failure was occurred at the loc for high stress and root for relatively low stress. The crack initiation cycles ($N_i$) was defined to the abrupt increase in AE counts during the fatigue test, and then the cracks were observed by the radiographic test and electron microscope before and after the fatigue crack initiation cycles. The socket welded pipe damaged by bending fatigue was studied regarding the welding defect, failure mode, and crack initiation cycles for the diagnosis and monitoring.

• Journal of the Korean Society of Safety
• /
• v.34 no.5
• /
• pp.103-110
• /
• 2019

In order to reduce the accidents occurring at construction sites, it is necessary to approach with harmonious measures considering various aspects such as systems, training, facilities, and protection equipments. Suggestion of safe construction method can be a good alternative. In the previous study, the half-depth precast deck with RC rib panel was proposed as an alternative method for safe bridge deck construction, and the performance required by the design code was verified through a four-point bending test. But the actual bridge deck is subjected to the repetitive action of the wheel load rather than the bending condition due to the four-point load. In this study, fatigue test was performed by repeating the wheel load $2{\times}10^6$ cycles to verify the safety of the half-depth precast deck with RC rib panel under actual conditions. As a result, fatigue effect due to repetition of wheel load was not significant in terms of serviceability such as crack width and deflection. In the residual strength test conducted after the fatigue test, the half-depth precast deck with RC rib panel failed by punching shear which is typical failure mode of bridge decks and the residual strength was similar to the punching strength of the RC and PSC bridge decks in spite of the fatigue effects.

• Proceedings of the KSR Conference
• /
• 2002.05a
• /
• pp.399-403
• /
• 2002

The transmission system of high speed train serve in the severe condition compared with those of other trains, namely, they have to transmit high power to run with high speed and they have to make maximum use of the limited space. To clarify the strength of gear for Korea High-Speed Train, a bending fatigue test of gear specimen is performed and compare with actual gear's. From this result, specimen test is useful to infer S-N curve and endurance limit of actual gear that much time and expense are consumed.

• Journal of the Korean Society of Safety
• /
• v.16 no.1
• /
• pp.31-36
• /
• 2001

Surface crack growth characteristics and influence of the stress amplitude in rotary bending fatigue test were evaluated for annealed S35C steel, and than fractal dimensions of fatigue crack paths estimated using the box counting method. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) Crack growth rate ds/dN and db/dN (s : half crack length at the surface crack, b : crack depth) depended on stress amplitude (${\Delta}{\sigma}/2$), stress intensity factor range (${\Delta}K_A, {\Delta}K_C$) and crack length. (2) At the effect area of 0.3 mm hole notch (s＜0.5 mm) crack growth rate did not depend on these factors. (3) The fractal dimensions (D) increased with stress amplitude (${\Delta}{\sigma}/2$) but decreased with cyclic number.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.199-204
• /
• 2001

Big accidents of flyings, vessel, subways, gas equipments, buildings and bridge happens frenquently. Therefore many people are suffering harm of property. The destruction cause of macaine components is almost accused by fatigue. This study is test for STS304 specimen using pure and cantilever bending state. Rounded specimen and notched specimen including fracture surface investigation was comparatively experimented, fatigue life according to degree of surface finishing was examined. Fatigue fracture probability of notched canilever specimens were predicted by P-S-N curve, median rank and Weibull distribution. And at the relation with the rotational speed and stress, the fatigue life of the test specimen was higher at high speed than low speed.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.31 no.7
• /
• pp.63-68
• /
• 2003

Shot peening process is most often used to improve the fatigue properties of metal parts, In order to achieve an optimum, repeatable, and reliable fatigue enhancement from the shot peening process, the important shot peening parameters must be optimized, In this paper, the optimum peening intensity(Almen intensity) condition is investigated by experiment. Rotary bending fatigue test has been adopted to investigate the effects of optimum peening on the fatigue characteristics, Experimental results show that the fatigue strength and fatigue life has been tremendously increased by optimum-peening treatment. However, the fatigue strength and fatigue life has been decreased by under or over peening.