• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.03a
• /
• pp.177-182
• /
• 1996

The objective of this thesis is to investigate the influence of welding residual stresses on the fatigue growth behavior of welding residual stresses on the fatigue growth behavior of cracks located transverse to the weld bead. For this purpose, G.T.A. (Gas Tungsten Arc) welding was performed on the Al. Alloy 1100-0 plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base metal respectively. C.T.(Compact Tension) specimens were used as experimental material. Initial welding residual stresses were measured by using strain gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1

• Journal of Welding and Joining
• /
• v.14 no.5
• /
• pp.87-94
• /
• 1996

It has been well known in GMA welding process that wire feeding speed (WFS) or deposition rate increases linealy with the increase of wire extension. In this investigation, however, such an well-known relationship was .reconsidered in terms of contact-tube to work distance (CTWD) instead of wire extension. To verify the proposed relationship between WFS and CTWD, bead-on-plate welding was performed with various CTWDs in the range of 15∼35mm under the condition of near-constant voltage and current As expected, the test results showed an excellent linear relation between WFS and CTWD. Furthermore, the value of the slope turned out to be quite similar to those of previous investigators obtained either theoretically or experimentally through the Precise measurement of electrode extension. Present result also demonstred that the increase of CTWD could be very practical measure for increaring deposition rate without any increase of heat input Depending on the tip recess the practical maximum of CTWD was appeared to be limited somewhere in 25∼30mm mainly due to the entrappment of porocity.

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.100-102
• /
• 2004

인장강도 600MPa 이상을 가지는 TRIP형 고장력 강판인 60TR-R과 석출경화형 합금인 CHSP60C는 자동차용 소재로 주목을 받고 있다. 또한 레이저 용접은 열 변형이 적고 비드 외관이 미려할 뿐만 아니라 연속 및 고속 용접이 가능하여 생산성 및 정밀성, 안정성이 높아 자동차조립 및 부품 제조공정에 적용되고 있다. (중략)

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.110-117
• /
• 2005

Underwater wet arc welds were experimentally performed on 11mm thick KR-RA steel plate using six different types of flux coated electrodes of 4.0mm diameter, KSKR, KSKT, USBL, JPUW, UWEA and UWEB. From analysis of bead appearance, detachability of weld slag, spatter occurrence and arc stability, JPUW gives the best result, and UWEB is superior to KSKR and KSKT. By experimental result of hardness distribution on the weld bonds, UWEB weld has the narrowest bond structure which is probable condition to get the best mechanical properties of weld. UWEB and JPUW welds have more even hardness distribution across weld deposit and base metal. Upon polarization test to measure the respondency of corrosion, the electrode of UWEB shows the most excellent degree due to the low open circuit potential difference.

• Journal of Welding and Joining
• /
• v.10 no.2
• /
• pp.32-42
• /
• 1992

A method of optimization of process parameters in Arc Welding has been discussed in this paper. The method of investigation is based on the numerical calculation of weld bead by a finite element method and non-linear optimization technique is applied to estimated the optimization process parameters from the numerical calculation. The common package program(ANSYS 4.4A) was used to obtain the process parameters for a thin plate arc welding (TIG, CO$_{2}$). The results on some test are satisfactory and the used method of this paper is a useful guide to the optimum welding condition.

• Journal of Power System Engineering
• /
• v.10 no.4
• /
• pp.111-118
• /
• 2006

Underwater wet arc welds were experimentally performed on 11mm thick KR-RA steel plate using six different types of flux coated electrodes of 4.0mm diameter, KSKR, KSKT, USBL, JPUW, UWEA and UWEB. From analysis of bead appearance, detachability of weld slag, spatter occurrence and arc stability, JPUW gives the best result, and UWEB is superior to KSKR and KSKT. By experimental result of hardness distribution on the weld bonds, UWEB weld has the narrowest bond structure which is probable condition to get the best mechanical properties of weld. UWEB and JPUW welds have more even hardness distribution across weld deposit and base metal. Upon polarization test to measure the respondency of corrosion, the electrode of UWEB shows the most excellent degree due to the low open circuit potential difference.

• Journal of Welding and Joining
• /
• v.27 no.6
• /
• pp.74-79
• /
• 2009

Titanium and titanium alloy can be reproduced immediately even if oxide films($TiO_2$) break apart in sea water. Therefore, since titanium demonstrates large specific strength and outstanding resistance to stress corrosion cracking, crevice corrosion, pitting and microbiologically influenced corrosion in sea water environment, it has been widely applied to heat exchanger for ships. In particular, with excellent elongation, pure titanium may be deemed as optimal material for production of heat exchanger plate which is used with wrinkles formed for efficient heat exchange. Conventional plate type heat exchanger prevented leakage of liquid through insertion of gasket between plates and mechanical tightening by bolts and nuts, but in high temperature and high pressure environment, gasket deterioration and leakage occur, so heat exchanger for LPG re-liquefaction device etc do not use gasket but weld heat exchanger plate for use. On the other hand, since welded plate cannot be separated, it is important to obtain high quality reliable welds. In addition, for better workability and production performance, lasers that can obtain weldment with large aspect ratio and demonstrate fast welding speed even in atmospheric condition not in vacuum condition are used in producing products. So far, 1st report and 2nd report compared and analyzed embrittlement degrees by bead colors of weldment through quantitative analysis of oxygen and nitrogen and measurement of hardness as fundamental experiment for the evaluation of titanium laser welding, and evaluated the welding performance and mechanical properties of butt welding. This study welded specimens in various conditions by using laser and GTA welding machine to apply edge welding to heat exchanger, and evaluated the mechanical strength through tensile stress test. As a result of tensile test, laser weldment demonstrated tensile strength 4 times higher than GTA welds, and porosity could be controlled by increasing and decreasing slope of laser power at overlap area.

• Journal of Welding and Joining
• /
• v.11 no.1
• /
• pp.52-61
• /
• 1993

Laser welding of ASTM no. 1060 Al plate with a pulsed Nd: YAG laser of 200W average power was performed for end capping of KMRR nuclear fuel elements In this research, we performed basic welding experiments. Firstly, laser output parameters which affect laser welding parameters were studied by changing laser input parameters for effective welding of 1060 Al plates. We found that laser power density and pulse energy are important parameters for smooth bead shape. Secondly, welding parameters which affect weld width-to-depth ratio were studied by changing power density and pulse energy, shielding gas, and defocusing. We found that power density must be higher than 0.3 Mw/cm$^{2}$ pulse energy must be higer than 3 J. travel speed must not exceed 200mm/sec, laser focus must be existed beneath 2-3mm from plate surface and helium is proper shielding gas. Thirdly, we studied the weld defects of Al-1060 such as crack and porosity in lap-joint welding. We designed new welding geometry for crack free welding of Al-1060 plates, and obtained crack free weldment but with lack of fusion. However, with Ti, Zr grain refiner elements, we can weld Al plates without solidification hot crack. Finally, we studied the origin of porosity by changing shielding gas. And we found that porosity was resulted from entrapment of shielding gas by the collapsing keyhole.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.244-249
• /
• 2002

The purpose of this study is to develope the prediction method of liquation crack initiation in HAZ of laser weldment. Thermal two dimensional strain analyses were performed by FEM for bead-on-plate welding in order to obtain the plastic strain at elevated temperature in HAZ of the laser weldment. From these results, it became clear that the plastic strain at elevated temperature affected liquation crack initiation in HAZ, and it could be proposed that the critical strain, which controlled liquation crack initiation, existed. Moreover, an attempt was made to develop thermal and dynamic three dimensional strain analysis method for the laser weldment in order to obtain the plastic strain at elevated temperature in HAZ of the laser weldment in more detail and precisely.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.20 no.5
• /
• pp.8-12
• /
• 2012

Application for laser welding have increased steadily in recent years due to its benefits such as high speed, high productivity and high density energy heat source. In this study, the influence of welding parameters was investigated on penetration characteristics, mechanical properties including formability test in disk laser welded 1000MPa class steels. A shielding gas was used and bead-on-plate test was performed with various welding speeds. The main welding test was performed by butt welding with various welding speeds at 2.5 kW laser power.