• Journal of Powder Materials
• /
• v.24 no.4
• /
• pp.326-331
• /
• 2017

The structural formation of inorganic nanoparticles dispersed in polymer matrices is a key technology for producing advanced nanocomposites with a unique combination of optical, electrical, and mechanical properties. Barium titanate ($BaTiO_3$) nanoparticles are attractive for increasing the refractive index and dielectric constant of polymer nanocomposites. Current synthesis processes for $BaTiO_3$ nanoparticles require expensive precursors or organic solvents, complicated steps, and long reaction times. In this study, we demonstrate a simple and continuous approach for synthesizing $BaTiO_3$ nanoparticles based on a salt-assisted ultrasonic spray pyrolysis method. This process allows the synthesis of $BaTiO_3$ nanoparticles with diameters of 20-50 nm and a highly crystalline tetragonal structure. The optical properties and photocatalytic activities of the nanoparticles show that they are suitable for use as fillers in various nanocomposites.

• Journal of the Korean Ceramic Society
• /
• v.46 no.2
• /
• pp.170-174
• /
• 2009

$BaTiO_3$ powder was synthesized by the solid-state reaction of fine $BaTiO_3$ and $TiO_2$ raw materials. Fine grinding media of 50 and 300 microns were used for obtaining fine particulate mixture of $BaTiO_3$ and $TiO_2$ with high homogeneity. Effect of the size of grinding media on the synthesis mechanism of $BaTiO_3$ was discussed on the basis of the particulate morphology and thermogravimetry data for the mixture powders. By using the finer grinding media, $BaTiO_3$ was formed at the lower temperature and the particle size with the relatively narrower distribution could be obtained. $BaTiO_3$ powder with the average size of 100 nm was synthesized by the solid reaction in vacuum atmosphere.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.189-189
• /
• 2008

Due to the environmental issue vast research is going on to replace the widely used lead contented piezoelectric materials. Bismuth sodium titanate (abbreviated as BNT) based bismuth sodium titanate-barium titanate (abbreviated as BNBT) ceramic was prepared by using modified method rather than conventional mixed oxide method. This modification was made to improve the properties of BNT based ceramic. In this procedure $BaTiO_3$ (abbreviated as BT) was prepared using conventional mixed oxide method. Analytical grade raw materials of $BaCO_3$ and $TiO_2$ were weighted and ball milled using ethanol medium. The mixed slurry was dried and sieved under 80 mesh. Then the powder was calcined at $1100^{\circ}C$ for 2 hours. This calcined BT powder was used in the preparation of BNBT. Stoichiometric amount of $Bi_2O_3$, $Na_2CO_3$, $TiO_2$ and BT were weighted and mixed by using ball mill. The used calcination temperature was $850^{\circ}C$ for 2 hours. Calcined powder was taken for another milling step. BNBT disks were pressed to 15 mm of diameter and then cold isostatical press (CIP) was used. Pressed samples were sintered at $1150^{\circ}C$ for 2 hours. The SEM microstructure analysis revealed that the grain shape of the sintered ceramic was polyhedral and grain boundary was well matched where as the sample prepared by conventional method showed irregular arrangement and grain boundary not well matched. And sintered density was better (5.78 g/cc) for the modified method. It was strongly observed that the properties of BNBT ceramic near MPB composition was found to be improved by the modified method compare to the conventional mixed oxide method. The piezoelectric constant dB of 177.33 pC/N, electromechanical coupling factor $k_p$ of 33.4%, dielectric constant $K_{33}^T$ of 688.237 and mechanical quality factor $Q_m$ of 109.37 was found.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.343-353
• /
• 1999

Microwave(2.45 GHz) was used as energy source in hydrothermal reaction to fabricate ultrafine BaTiO3 powder. Using microwave of 700 W, crytal BaTiO3 began to fom after 5 min in microwave-autoclave sys-tem. The crystallinity was not noticeably increased with increasing longer reaction time than 10 min. On the other hand in microwave-reflux system crytal BaTiO3 began to form after 15min and the crystallinity was not noticeably increased with increasing longer reaction time than 1hr,. In either case particle size dis-tribution was considerably uniform due to the effect of homogeneous heating by microwave. In addition mi-crowave heating gave an extremely small degree of particle agglomeration compared to electric heating. Av-erage sizes of as-synthesized powders were 30-60nm. Ba/Ti ratio in sol played an important role in det-ermining the particle size. It seems that excess barium forms different phases such as Ba(OH)2 which makes thin layer on the surface of BaTiO3 powder. This thin layer would inhibit the agglomeration of Ba-TiO3 powders and keep the small grain size. In microwave-autoclave system tetragonal-BaTiO3 was formed directly by the reaction of only 15 min. In the case of microwave-reflux system tetragonal-BaTiO3 was formed by driyng over 25$0^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.31.1-31.1
• /
• 2009

In an approach to acclimate ourselves torecent ecological consciousness trend, a lead-free piezoelectric material, bismuth sodium titanate (abbreviated as BNT) based bismuth sodium barium titanate (abbreviated as BNT-BT), was considered as an environment-friendly alternative for a lead based piezoelectric system. Ceramic specimens of0.94[(BixNa0.5)TiO3]-0.06[BaTiO3] (x = 0.500~0.515) compositions were prepared by a modified mixed oxide method. To increase the chemical homogeneity andre action activity, high energy mechanical milling machine and pre-milled nanosized powder has been used. In this method (BixNa0.5)TiO3 (x=0.500~0.515) andBaTiO3 were prepared separately from pre-milled constituent materials at low calcination temperature and then separately prepared BNTX (X=1, 2, 3 and 4) and BT were mixed by high energy mechanical milling machine. Without further calcination step the mixed powders were pressed into disk shape and sintered at $1110^{\circ}C$. Microstructures, phase structures and electrical properties of the ceramic specimens were systematically investigated. Highly dense ceramic specimens with homogenous grains were prepared in spite of relatively low sintering temperature. Phase structures were not significantly influenced by the excess amount Bi. Large variation on the piezoelectric and dielectric properties was detected at relative high excess Bi amounts. When $x{\leq}0.505$, the specimens exhibit insignificant variation in piezoelectric and dielectric constant though depolarization temperature is found to be decreased. Considerable amount of decrease in piezoelectric and dielectric properties are observed with higher excess of Bi amounts ($x{\geq}0.505$). This research indicates the advantages of high energy mechanical milling and importance of proper maintenance of Bi stoichiometry.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.8
• /
• pp.679-687
• /
• 2001

It is known that amorphous BaTiO$_3$ thin films have good insulating properties[1][2]. In this investigation, amorphous BaTiO$_3$ thin films were deposited by rf magnetron sputtering on thick BaTiO$_3$ films of AC powder EL devices which were fabricated by screen-printing. The electrical and optical properties of the EL devices were then investigated. Adding amorphous BaTiO$_3$ thin film, it showed that leakage current density was decreased. Especially, leakage current density was decreased more with he sample of 0.5-hour deposition than the sample of 4-hours deposition. This result led to the improvement of luminous efficiency by 11%. It could be concluded that proper amorphous BaTiO$_3$ thin film deposition improved the surface property of dielectric layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.31-34
• /
• 2003

($Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ (BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on alumina substrates using the BSCT paste. The structural and the electrical properties were investigated for various composition ratio and sintering temperature. BSCT thick film thickness, obtained by four printings, was approximately 110 ~ 120 ${\mu}m$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at $1420^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.4
• /
• pp.304-310
• /
• 2003

(Ba$\sub$0.6-x/Sr$\sub$0.4/Ca$\sub$x/)TiO$_3$(BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-Bel method, were mixed with organic binder and then BSCT thick films were fabricated by the screen printing techniques on alumina substrates using the BSCT paste. The structural and the dielectric Properties were investigated for various composition ratio and sintering temperature. The second phase appeared in BSCT(40/40/20) thick film sintered at 1450$^{\circ}C$. BSCT thick film thickness, obtained by four printings, was approximately 110∼120$\mu\textrm{m}$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at 1420$^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5㎸/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.311-312
• /
• 2006

The dielectric Properties of add $Li_2CO_3$ to ($Ba_{0.6}Sr_{0.4})TiO_3$ powder in this research, made thick film by tape casting method and annealing at $970^{\circ}C$ for 2 hours each from the $O_2$, Ar and O2-plasma atmosphere were investigated. The dielectric Properties of Ar atmosphere was to higher with tunability. The dielectric constant was increased and Curie temperature was shifted to higher temperature with increasing of annealing temperature.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.2
• /
• pp.44-48
• /
• 2017

We explain optical and electrical properties of top and bottom-emission structured alternating-current powder electroluminescent devices (ACPELDs) with Ga-doped ZnO(GZO) transparent electrode. The top-emission ACPELDs were layered as the metal electrode/dielectric layer/emission layer/top transparent electrode and the bottom-emission ACPELDs were structured as the bottom transparent electrode/emission layer/dielectric layer/metal electrode. The yellow-emitting ZnS:Mn, Cu phosphor and the barium titanate dielectric layers were layered through the screen printing method. The GZO transparent electrode was deposited by the sputtering, its sheet resistivity is $275{\Omega}/{\Box}$. The transparency at the yellow EL peak was 98 % for GZO. Regardless of EL structures, EL spectra of ACPELDs were exponentially increased with increasing voltages and they were linearly increased with increasing frequencies. It suggests that the EL mechanism was attributed to the impact ionization by charges injected from the interface between emitting phosphor layer and the transparent electrode. The top-emission structure obtained higher EL intensity than the bottom-structure. In addition, charge densities for sinusoidal applied voltages were measured through Sawyer-Tower method.