• Journal of Powder Materials
• /
• v.20 no.6
• /
• pp.445-452
• /
• 2013

Yttria-stabilized zirconia (YSZ) coatings are fabricated via suspension plasma spray (SPS) for thermal barrier applications. Three different suspension sets are prepared by using a planetary mill as well as ball mill in order to examine the effect of starting suspension on the phase evolution and the microstructure of SPS prepared coatings. In the case of planetary-milled commercial YSZ powder, a deposited thick coating turns out to have a dense, vertically-cracked microstructure. In addition, a dense YSZ coating with fully developed phase can be obtained via suspension plasma spray with suspension from planetary-milled mixture of $Y_2O_3$ and $ZrO_2$.

• Applied Biological Chemistry
• /
• v.40 no.6
• /
• pp.531-535
• /
• 1997

An efficient process for recovery of calcium from the eggshell was developed and some organic acids were used in an attempt to enhance the degree of calcium ionization. Eggshell membrane was readily separated from crushed eggshell based on the differences in specific gravities. The conditions which allowed most efficient membrane removal were found to be 30 rpm of speed, 30 min of residence time and 0.08 of volume fraction. It took 3 hours for the eggshell powder prepared at $1000^{\circ}C$ to reach L value of 90 with the Hausner ratio being 1.43. The calcium ion concentrations were 990, 3500, 3900 and 4200 ppm in pure water, acetic acid, citric acid and lactic acid$(0.05{\sim}3%)$ aqueous solution, respectively. The degrees of ionization of calcium-citrate-malate complex(CCM), calcium-citric acid complex(CC) and calcium malic acid complex(CM) increased by 4 to 5 times compared to eggshell calcium powder.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.313-319
• /
• 2020

In this study, in order to confirm the applicability of Hollow Glass Powder(HGP) in 70MPa-class high strength concrete, the fresh and hardened states were examined according to the amount of HGP, and the results are as follows. The flow characteristics showed that the slump flow increased slightly as the amount of HGP was increased, and the T500 was slightly shortened as the amount of HGP was increased, and the rebar passing ability was improved due to the ball bearing effect of HGP. In particular, it showed the best rebar passing ability at a usage of 1.0kg/㎥. The use of HGP 1.0kg/㎥ resulted in a 40% reduction in plastic viscosity, but the viscosity increased at 2.0kg/㎥. Through experiments, it was confirmed that HGP was helpful in improving the workability of high-strength concrete, and the usage of 1.0kg/㎥ is considered to be the most appropriate. It was confirmed that HGP does not affect concrete compressive strength.

• Korean Journal of Materials Research
• /
• v.23 no.7
• /
• pp.353-358
• /
• 2013

To improve coating ability and the life of the coating, Ti based composite materials with hydroxyapatite(HA) should be developed. The raw materials of Ti-26wt%, Nb-1wt%, and Si with 10wt% HA were mixed for 24 h by a mixing machine and milled for 1 h to 6 h by planetary mechanical ball milling. Ti-26%Nb-1%Si-(10%HA) composites, composed of nontoxic elements, were fabricated successfully by spark plasma sintering(SPS) at $1000^{\circ}C$ under 70MPa. The relative density of the sintered Ti-Nb-Si-HA composites using the 24 h mixed powder, and the 6 h milled powder, was 91% and 97 %, respectively. The effects of HA contents and milling time on microstructure and mechanical properties were investigated by SEM and hardness tester, respectively. The Vickers hardness of the composites increased with increasing milling time and higher HA content. The Young's modulus of the sintered Ti-26%Nb-1%Si-10%HA composite using the 6 h-milled powder was 55.6 GPa, as obtained by compression test. Corrosion resistance of the Ti-26wt%Nb-1wt%Si composite was increased by milling and by the addition of 10wt%HA. Wear resistance was improved with increasing milling time. Biocompatibility of the Ti-Nb-Si alloys was improved by the addition of HA.

• Journal of Powder Materials
• /
• v.20 no.3
• /
• pp.215-220
• /
• 2013

In the present work, 6061 Al-$B_4C$ sintered composites containing different $B_4C$ contents were fabricated and their characteristic were investigated as a function of sintering temperature. For this, composite powders and their compacts with $B_4C$ various contents from 0 to 40 wt.% were fabricated using a planetary ball milling equipment and cold isostatic pressing, respectively, and then they were sintered in the temperature ranges of 580 to $660^{\circ}C$. Above sintering temperature of $640^{\circ}C$, real density was decreased due to the occurrence of sweat phenomena. In addition, it was realized that sinterability of 6061Al-$B_4C$ composite material was lowered with increasing $B_4C$ content, resulting in the decrease in its real density and at the same time in the increment of porosity.

• Journal of Powder Materials
• /
• v.23 no.6
• /
• pp.426-431
• /
• 2016

The Fe-Cr-Al alloy system shows an excellent heat resistance because of the formation of an $Al_2O_3$ film on the metal surface in an oxidizing atmosphere at high temperatures up to $1400^{\circ}C$. The Fecralloy needs an additive that can act as a binder because of its bad compactability. In this study, the green compacts of STS434L and Al powder added to Fecralloy are oxidized at $950^{\circ}C$ for up to 210 h. Fecralloy and Al is mixed by two types of ball milling. One is vented to air and the other was performed in a sealed jar. In the case of Al addition, there are no significant changes in the electrical resistance. Before the oxidation test, Al oxides are present in the Fecralloy surface, as determined from the energy dispersive spectroscopy results. The addition of Al improves the compactability because of an increased density, and the addition of STS434L increases the electrical resistivity by forming a composite oxide.

• Advances in concrete construction
• /
• v.8 no.1
• /
• pp.65-76
• /
• 2019

This paper investigates the effect of recycled glass powder (RGP) on flowing properties of self-compacting mortars (SCMs) containing different ratios of fillers and superplasticizer dosages. Fly ash (FA), nano-silica (NS), micro-silica (MS), metakaolin (MK) and rice husk ash (RHA) are used as fillers and their synergistic effect with RFP is studied. The effects of fillers and high-range water reducer (HRWR) on flowing ability of mortars are primarily determined by slump flow and V-funnel flow time tests. The results showed that for composites with a higher RGP content, the mortar flowing ability increased but tended to decrease when the composites containing 10% MK or 5% RHA. However, the flowing ability of samples incorporating 5% RGP and 10% SF or 25% FA showed an opposite result that their slump flow spread decreased and then increased with increasing RGP content. For specimens with 3% NS, the influence of RGP content on flowing properties was not significant. Except RHA and MS, the fillers studied in this paper could reduce the dosage of HRWR required for achieving the same followability. Also, the mixture parameters were determined and indicated that the flowability of mixtures was also affected by the content of sand and specific surface area of cement materials. It is believed that excess fine particles provided ball-bearing effect, which could facilitate the movement of coarse particles and alleviate the interlocking action among particles. Also, it can be concluded that using fillers in conjunction with RGP as cementitious materials can reduce the material costs of SCM significantly.

• Journal of Powder Materials
• /
• v.29 no.5
• /
• pp.382-389
• /
• 2022

A typical trade-off relationship exists between strength and elongation in face-centered cubic metals. Studies have recently been conducted to enhance strength without ductility reduction through surface-treatment-based ultrasonic nanocrystalline surface modification (UNSM), which creates a gradient microstructure in which grains become smaller from the inside to the surface. The transformation-induced plasticity effect in Fe-Mn alloys results in excellent strength and ductility due to their high work-hardening rate. This rate is achieved through strain-induced martensitic transformation when an alloy is plastically deformed. In this study, Fe-6%Mn powders with different sizes were prepared by high-energy ball milling and sintered through spark plasma sintering to produce Fe-6%Mn samples. A gradient microstructure was obtained by stacking the different-sized powders to achieve similar effects as those derived from UNSM. A compressive test was performed to investigate the mechanical properties, including the yielding behavior. The deformed microstructure was observed through electron backscatter diffraction to determine the effects of gradient plastic deformation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.8
• /
• pp.847-853
• /
• 2011

In this study, a hybrid powder-extrusion process involving the control of temperature dwelling time for improving the formability of Zn-22Al powder was developed and the effect of dwelling time on the mechanical properties of a spur gear with a pitch circle having a diameter of 1.8 mm was investigated. General extrusion experiments were carried out at different temperatures such as 290, 300, and $310^{\circ}C$. Spur gears with good qualities and without any surface defects were obtained in the case of extrusion temperature of $310^{\circ}C$ and ball-milling duration of 32 h. The Vickers hardness distribution was non-uniform, and after the sintering process, an internal crack was generated because of the different deformation energy between gear central part and teeth. To overcome the abovementioned problems, research on controlling the dwelling time of the extrusion temperature in the powder-extrusion process was carried out. Good-quality spur gears were obtained when the dwelling time was 15 min.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.86-91
• /
• 2004

$LiCoO_2$ cathode powders with round particle shaped and nano grain sized of 70-300nm were synthesized by a mechanochemical method. The surface of Li-Co precursor prepared by freeze drying method was modified by $K_2SO_4$ coating and ball milling was used for the coating process. The precursor was crystallized to high temperature form of $LiCoO_2$ at $800^{\circ}C$ and the grain growth was inhibited by the $K_2SO_4$ coating effect. The $K_2SO_4$ coating was not decomposed at $800^{\circ}C$ and prevented the contact in the Li-Co precursor particles. The nano-sized $LiCoO_2$ powder had tetragonal phase and it affected the Li diffusion through the surface of particles. It means that the anode materials for hight performance battery should be satisfied not only small particle size but phase contol on the surface of particles. In this study, the powder characteristics and rate capabilities were compared with a commercial powder and the nano-sized $LiCoO_2$ powder fabricated by the mechanochemical method. And the crucial factor which affects on battery performance was also examined.