• 한국재료학회지
• /
• 제18권12호
• /
• pp.678-682
• /
• 2008

This study investigates $Bi_2O_3$-$B_2O_3$-BaO-ZnO glass with variations of the $Co_3O_4$ content (0.25, 0.5, 1, and 2 wt%) and the interaction between transparent dielectric and Ag electrodes heat-treated at $500-560^{\circ}C$ for 30 min. The glass transition temperature, softening temperature and thermal expansion coefficient were $432^{\circ}C$, $460^{\circ}C$ and $81.4{\times}10^{-7}/^{\circ}C$, respectively. The transmittance of 0.25 wt% $Co_3O_4$ to which dielectric was added was highest and was decreased due to coloration with the addition of more than 0.25 wt%. However, without $Co_3O_4$, the transmittance of the transparent layer was decreased due to the formation of $Ba_5Bi_3$; however, the occurrence of the crystal phase decreased as a result of the addition of $Co_3O_4$. The amount of $Co^{2+}$ ions increased as the $Co_3O_4$ increased. With a maximum of $Co^{3+}$ ions, the highest transmittance was observed.

• Nuclear Engineering and Technology
• /
• 제51권8호
• /
• pp.2005-2012
• /
• 2019

This work investigated the radiation attenuation characteristics of three series of tellurite glass systems with the following compositions: 30PbO-10ZnO-xTeO₂-(60-x)B₂O₃ where x = 10, 30, 40, 50 and 60 mol%, xBaO-xB₂O₃-(100-2x)TeO₂ with x = 15-40 mol% and 50ZnO-(50-x)P₂O₅-xTeO₂, where x = 0, 10, .40 mol%. The results revealed that the attenuation parameters in all the samples decrease with increase in the energy, which implied that all the samples have better interaction with gamma photons at low energies and thus higher photon attenuating efficiency. From the three systems, the samples coded as PbZnBTe60, BaBTe70 and ZnPTe40 have the lowest half value layer values and accordingly have superior photon attenuation efficacy. The maximum effective atomic number values were found for energy less than 0.1 MeV particularly near the K-edges absorption of the heavy atomic number elements such as Te, Ba and Pb. At the lowest energy, the Z_eff values are found in the range of 62.33-66.25, 49.43-50.81 and 24.99-35.83 for series 1-3 respectively. Also, we found that the density of the glass remarkably affects the photon attenuation ability of the selected glasses. The mean free path results showed that the PbO-ZnO-TeO₂-B₂O₃ glass system has better radiation shielding efficiency than the glass samples in series 2 and 3.

• 한국전기전자재료학회논문지
• /
• 제24권12호
• /
• pp.955-961
• /
• 2011

We investigated the physical properties of stoichiometric and non-stoichiometric oxide doped complex perovskite, $Ba(Zn_{1/3}Ta_{2/3})O_3$ ceramics and their impacts on the microwave dielectric performances using various characterization techniques such as X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and network analyzer. According to the measurement of lattice constant changes, anomalous lattice volume contraction of $ZrO_2$ doped $Ba(Zn_{1/3}Ta_{2/3})O_3$ sample only showed the dielectric quality factor enhancements, which was due to the lattice volume contraction as well as the 1:2 B-site cation ordering. In addition, NiO doping was useful to the stabilization of temperature coefficient of resonance frequency.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.639-643
• /
• 2004

[ $Ta_2O_5$ ]가 첨가된 $Ba(Zn_{1/3}Ta_{2/3})O_3$[BZT] 세라믹은 1:2 규칙화 정도가 증가하고 $Ba_3Ta_5O_{15}의 이차상이 새롭게 형성된다. $1580^{\circ}C$ 보다 높은 온도에서 소결된 BZT 세라믹은 $Ta_2O_5$를 첨가하면 입자의 성장이 일어나고 액상이 형성된다. 품질계수(Q) 값은 $1580^{\circ}C$ 보다 높은 온도에서 소결할 경우 미량의 $Ta_2O_5$ 첨가만으로도 상당히 증가한다. 상대밀도는 $Ta_2O_5$ 첨가량에 따라 감소하기 때문에 Q값의 증가는 상대밀도와는 무관하다. 반면에, $Ta_2O_5$의 첨가량에 따라 입자의 성장은 증가하였기 때문에 Q값의 향상은 입자크기와 관계가 있음을 알 수 있다. 많은 양의 $Ta_2O_5$ 첨가시 비록 입자 크기가 증가했음에도 불구하고 Q값이 매우 낮은 것을 볼 때, Q값의 감소는 $Ba_3Ta_5O_{15}$ 상의 영향과 낮은 밀도 값에 기인한 것이다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1179-1180
• /
• 2006

Y-type barium ferrite ($Ba_2Me_2Fe_{12}O_{22};$ Me=Zn, Co, Cu) expected as an electromagnetic wave absorber were prepared by the glass-ceramic method. The glasses with composition of $0.1ZnO{\cdot}0.9(xB_2O_3{\cdot}yBaO{\cdot}(1-x-y)Fe_2O_3)$ were prepared. Single-phase powders of Y type barium ferrite were obtained with the composition $0.1ZnO{\cdot}0.9(0.2B_2O_3{\cdot}0.5BaO{\cdot}0.3Fe_2O_3)$. The shape of Y-type crystals depended strongly on the heating temperature and changed from a plate-like hexagon to a complex polyhedron with increasing heating temperature. Correlation was recognized between saturation magnetization and crystal shape. Electromagnetic wave absorption characteristics was affected by the saturation magnetization and crystal shape.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2000년도 하계학술대회 논문집 C
• /
• pp.1667-1669
• /
• 2000

The 0.8Ba($Zn_{1/3}Ta_{2/3})O_3$-0.2Ba($Co_{1/3}Nb_{2/3})O_3$ ceramics were prepared by conventional mixed oxide method. The structural properties of the 0.8BZT-0.2BCN ceramics with the sintering temperature were investigated by XRD and SEM. The 0.8BZT-0.2BCN ceramics had a superstructure reflection plane of (100), (200). Increasing the sintering temperature. the ordering parameter of B-site atoms were increased. The lattice constant of 0.8BZT-0.2BCN ceramics was 3.97${\AA}$. Increasing the sintering temperature, the average gram sizes were increased. In the case of the 0.8BZT-0.2BCN ceramics sintered at 1500$^{\circ}C$, the average grain size and bulk density were 1.56${\mu}m$, 6.93$g/cm^3$, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.876-879
• /
• 2003

The principal problems in development of dielectric paste materials for PDP(plasma display panel)are PbO free paste and low melting temperature. We prepared PbO free paste from glasses in the system $BaO-ZnO-B_2O_3-V_2O_5$. DTA, XRD and SEM were used to study and characterize $BaO-ZnO-B_2O_3-V_2O_5$ glasses. PbO free paste developed at this paper has thermal expansion of $74{\times}10^{-7}/^{\circ}C$, DTA transformation point of $460^{\circ}C$, and firing condition of $560^{\circ}C$, 10min.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2003년도 International Meeting on Information Display
• /
• pp.814-817
• /
• 2003

The sintering behavior of $BaO-B_{2}O_{3}-ZnO$, which is Pb-free glass-ceramic system, was examined as functions of the composition and the amount and particle size of $Al_{2}O_{3}$ filler. Different kinds of modifiers were added and $Al_{2}O_{3}$ fillers with different particle sizes ($1.5{\mu}m$ and $4.5{\mu}m$) were added. The glass frit-filler composites were sintered in the temperature range $520{\sim}580^{\circ}C$. X-ray diffraction results revealed that some of the composites crystallized during sintering. Dielectric constant and thermal expansion coefficient the glass-ceramics were analyzed.

• 한국세라믹학회지
• /
• 제39권5호
• /
• pp.438-445
• /
• 2002

본 연구에서는 $PbO-TiO_2-SiO_2-BaO-ZnO-Al_2O_3-CaO-B_2O_3-Bi_2O_3-MgO$계의 유리를 $1,400{\circ}C$에서 용융시킨 후, 급랭, 분쇄하여 glass frit을 제조하였다. Glass frit 분말을 일축가압성형한 후 $750~1,000{\circ}C$의 온도범위에서 2시간 동안 소성 및 결정화 하였다. Glass frit의 결정화는 $750{\circ}$ 전후의 온도에서 시작되었고, 저온에서의 주된 결정상은 $Al_2O_3$와 hexagonal celsian($BaAl_2Si_2O_8$)이었다. 소성온도가 높아지면서 monoclinic celsian, $ZnAl_2O_4,\;Zn_2SiO_4,\;CaTi(SiO_4)O,\;TiO_24 등이 주된 결정상으로 나타났고, 특히 celsian은 hexagonal에서 monoclinic으로 상전이가 발생하였다. 그리고 15wt%의 PbO를 첨가한 glass frit에만 $PbTiO_3-CaTiO_3$ 고용체가 나타났다. 1MHz 대역에서 유전특성을 살펴본 결과 유전상수는 11~16이었고, 유전손실은 0.020 미만이었다. 그러나 15wt%의 PbO를 첨가한 glass frit의 경우는 $PbTiO_3-CaTiO_3$ 고용체 결정상의 존재로 유전상수가 17~26으로 높았고, 유전손실은 0.010~0.015로서 다른 조성들에 비하여 우수한 특성을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 영호남 학술대회 논문집
• /
• pp.48-52
• /
• 2003

Low melting crystalline solder glasses for CRT sealing were prepared from the composition of PbO 73.0~75.5 wt%, ZnO 12~15 wt%, $B_2O_3$ 7.0~9.0 wt%, BaO 1.5~3.5 wt%, $P_2O_5$ 1.0~2.5 wt%, $Bi_2O_3$ 0.5~20 wt%. The nucleation and crystallization of the crystalline solder glasses were studied by DTA, SEM and XRD. $2PbO{\cdot}ZnO{\cdot}B_2O_3$ crystalline phase was formed from glass matrix by heat-treatment of glass frits Crystalline solder glasses developed from this paper have good firing condition of $430{\sim}440^{\circ}C$ for 10min and good physical properties